Anomalous Magnetization Enhancement and Frustration in the Internal Magnetic Order on (Fe0.69Co0.31)B0.4 Nanoparticles

Abstract

We have studied the internal magnetic order of 3-nm (Fe0.69Co0.31)0.6B0.4 amorphous nanoparticles. These nanoparticles were dispersed in a non-magnetic matrix (non-interacting nanoparticles) to contrast them with the powder samples, where strong interparticle interactions are present. In similar fashion to the bulk alloy, this system exhibits a saturation magnetization maximum as a function of Fe composition near 69 at% Fe for the powder and dispersed samples at all temperatures. The saturation magnetization (MS) of the dispersed sample shows anomalous behavior, revealing frustration in the internal magnetic order of the particles. Unexpectedly, the MS of the non-interacting sample at low temperatures is larger than the corresponding bulk alloy or the calculated value of MS for the same Fe-Co composition. By contrast, the powder sample has low MS values and it is approximately constant in temperature.