Dark-field X-ray microscopy for multiscale structural characterization

Abstract

Many physical and mechanical properties of crystalline materials depend strongly on their internal structure, which is typically organized into grains and domains on several length scales. Here we present dark-field X-ray microscopy; a non-destructive microscopy technique for the three-dimensional mapping of orientations and stresses on lengths scales from 100 nm to 1 mm within embedded sampling volumes. The technique, which allows 'zooming' in and out in both direct and angular space, is demonstrated by an annealing study of plastically deformed aluminium. Facilitating the direct study of the interactions between crystalline elements is a key step towards the formulation and validation of multiscale models that account for the entire heterogeneity of a material. Furthermore, dark-field X-ray microscopy is well suited to applied topics, where the structural evolution of internal nanoscale elements (for example, positioned at interfaces) is crucial to the performance and lifetime of macro-scale devices and components thereof.

ARTICLE

Received 18 Sep 2014 | Accepted 12 Dec 2014 | Published 14 Jan 2015

DOI: 10.1038/ncomms7098 OPEN

Dark-eld X-ray microscopy for multiscale structural characterization

H. Simons1,2, A. King2, W. Ludwig3, C. Detlefs2, W. Pantleon4, S. Schmidt1, I. Snigireva2,A. Snigirev2,5 & H.F. Poulsen1

Many physical and mechanical properties of crystalline materials depend strongly on their internal structure, which is typically organized into grains and domains on several length scales. Here we present dark-eld X-ray microscopy; a non-destructive microscopy technique for the three-dimensional mapping of orientations and stresses on lengths scales from 100 nm to 1 mm within embedded sampling volumes. The technique, which allows zooming in and out in both direct and angular space, is demonstrated by an annealing study of plastically deformed aluminium. Facilitating the direct study of the interactions between crystalline elements is a key step towards the formulation and validation of multiscale models that account for the entire heterogeneity of a material. Furthermore, dark-eld X-ray microscopy is well suited to applied topics, where the structural evolution of internal nanoscale elements (for example, positioned at interfaces) is crucial to the performance and lifetime of macro-scale devices and components thereof.

1 Department of Physics, DTU, 2800 Kongens Lyngby, Denmark. 2 ESRF, CS 40220, 38043 Grenoble Cedex 9, France. 3 MATEIS, INSA-Lyon, 69621 Villeurbanne Cedex, France. 4 Department of Mechanical Engineering, DTU, 2800 Kongens Lyngby, Denmark. 5 Immanuel Kant Baltic Federal University, Kaliningrad 236041, Russian Federation. Correspondence and requests for materials should be addressed to H.F.P. (email: mailto:[email protected]

Web End [email protected] ).

NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 1

& 2015 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms7098

Crystalline materials are ubiquitous and include most metals, ceramics, semiconductors, rocks, ice, sand, bones and many artefacts of artistic and archaeological interest.

They tend to be composed of elements such as grains and domains that are structured hierarchically in a complex manner on several length scales. In materials science, major research efforts have been directed at establishing multiscale models1,2 that predict the evolution of the entire structure during important materials transformations such as processing or failure. At present, however, rigorous bottomup approaches are not computationally feasible, and coarse-scale modelling of average properties often fails as heterogeneous events, such as the nucleation of new grains or cracks tend to govern the structural evolution. As a result, state-of-the art models at best systematize generic features of the static structure. Such complicating factors are also pervasive in other elds such as geosciences, where the establishment of multiscale approaches would be equally important in understanding geological processes.

Simultaneous inspection of the structural dynamics inside crystalline materials on multiple length scales and in three dimensions (3D) would therefore be a major step forward. With a 3D multiscale microscope, the interdependence between various structural elements and their driving forces could be studied directly and without spurious effects from articial boundaries. Validation of material models could then progress from merely comparing their average properties with observations of the critical local events that determine the behaviour of the material.

Such a tool would ideally be based on diffraction, which readily yields information pertinent to both structure (phase, shape and crystallographic orientation of the structural elements) and, by monitoring the lattice strain, the local stress state. Within the last decade, several diffraction-based 3D mapping methods have appeared, however they are not well suited to simultaneous multiscale characterization. Specically, electron microscopy methods for 3D crystal mapping are either conned to thin foils3 or involve serial sectioning4,5, implying they are inherently destructive. X-ray diffraction tomography methods such as 3D X-ray Diffraction (3DXRD)610 and Diffraction Contrast Tomography (DCT)11,12 are now capable of mapping of up to 20,000 grains in a sample, but are limited by the detector to a spatial resolution of B1 mm. 3D methods based on scanning

X-ray nano-beams can provide resolutions of 100 nm, but are slow, and the mapped volume is therefore relatively small1315. Furthermore, in these X-ray methods, the overlap of diffraction signals from different volumes in the sample limits the ratio between the average size of the crystalline elements and the sample volume.

In this paper, we propose a strategy for simultaneous multiscale characterization based on a new concept: dark-eld X-ray microscopy. It is a full-eld imaging technique in which the camera records the image of a layer or the projection of a volume within the sample, enabling fast data acquisition. The technique is therefore highly suited to in situ studies of materials and their dynamics, which we demonstrate here by addressing an important topic from metallurgy: the annealing of plastically deformed aluminium.

ResultsPrinciple. The principle of the dark-eld X-ray microscope is shown in Fig. 1. The entire specimen is initially mapped on a coarse scale using 3DXRD or DCT and, if necessary, classical X-ray tomography. This survey facilitates identication of small-scale elements of interest such as grains or domains. Dark-eld microscopy then enables us to zoom in on these elements and record a magnied high-resolution 3D map. The basic principle

of the microscope is that the objective generates a real space image using the diffracted beam as the illumination. A more thorough discussion of dark-eld X-ray microscopy in the context of existing X-ray and electron-based microscopy techniques is provided in Supplementary Note 1.

At the nest scale, structural elements often exhibit a near-perfect lattice. A two-dimensional (2D) spatial map of such elements can be acquired in a few seconds, enabling monitoring of the local dynamics. If the element exhibits a minor internal orientation spread, the measurement procedure is repeated while tilting the sample around two perpendicular axes by the angles a and b in Fig. 1. Furthermore, scanning the scattering angle (labelled 2y in Fig. 1) facilitates 3D mapping of the local stresses through the direct measurement of lattice strain. Details of operation are provided in Methods, while estimates of the spatial and angular resolution and experimental validations of the optical approach are presented in Supplementary Note 2 and Supplementary Fig. 1.

The objective in the dark-eld microscope has an inherently small numerical aperture, the implications of which are twofold: rst, the angular resolution is superior to conventional transmission electron microscopes (TEMs)16. Second, the objective acts as a very effective lter, removing diffraction signals from other diffracting elements within the sample but outside the desired eld of view. In favourable circumstances, it then becomes possible to study a specic element out of 1010 or more within the illuminated volumea key requirement for multiscale studies in bulk materials.

Theoretical optics predicts that a spatial resolution of 10 nm is feasible with the dark-eld X-ray microscope. For weakly absorbing samples, X-rays of intermediate energies (515 keV) may be used in combination with high-quality Fresnel zone

q

G

Detector

p

Objective

Incident beam

Sample

Axis of rotation ([afii9853])

2[afii9835]

Figure 1 | Principle of dark-eld X-ray microscopy. A monochromatic beam from a synchrotron source illuminates the sample. An embedded crystalline element (for example, a grain or domain) of choice (green) is aligned such that the beam is diffracted. The objective magnies the diffracted beam by a factor M q0/p0 and generates an inverted 2D

projection of the grain. Through repeated exposures during a 360 rotation of the element around an axis parallel to the diffraction vector, G, several 2D projections of the grain are obtained from various angles30. A 3D map is

then obtained by combining these projections using reconstruction algorithms similar to those developed for CT scanning32. If the lattice of the crystalline element exhibits an internal orientation spread, this procedure is repeated for a number of sample tilts, indicated by the angles a and b. Using a compound refractive lens18,29 as the objective enables one to enlarge or reduce the spatial resolution and eld of view within the sample by varying the number of individual lenses and adjusting p0 and q0 correspondingly. The diffraction angle 2y is typically 1030.

2 NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

& 2015 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms7098 ARTICLE

plates17. Stronger absorbing samples such as those of prime interest to materials science necessitate X-ray energies above 15 keV and the use of compound refractive lenses instead of Fresnel zone plates1820. While the manufacturing technology for CRLs is still maturing, state-of-the-art optics currently yields a spatial resolution of B100 nm.

Study of recovery in aluminium. Here, we present an annealing study of commercial pure aluminium, which had been subjected to 10% tensile deformation. This is a prototypical multiscale material comprising grains with an average size of B80 mm, each subdivided into a 3D structure of subgrains. The boundaries of these subgrains comprise a dense 2D network of dislocations (line defects), while their interior is almost dislocation-free9,2123. From this material, a matchstick-shaped sample of dimensions0.3 0.6 8 mm3 was prepared.

The grains in this sample were rst mapped on a coarse scale with DCT (Fig. 2a), after which we identied an embedded grain with a 200 reection positioned within a few degrees of the original tensile axis. Subgrains of this orientation are equiaxed with an average size of B3 mm (ref. 24).

The grain initially selected for microscopy exhibited a total intrinsic orientation variation of 3. To map the entire grain, the sample was tilted in small steps around two orthogonal axes by the angles a and b (see Fig. 1). For each tilt position, the sample was rotated about the diffraction vector by 360, enabling a 3D volume of the grain to be reconstructed in a manner analogous with tomography (c.f. Supplementary Note 3). Combining the maps from different tilts enables a 3D map of local orientations to be reconstructed, shown in Fig. 2b. Here, an intermediate subdivision of the grain into regions on a 10 mm scale is

observable. Formation of such orientation domains is attributed to both the instability of homogeneous plastic deformation in the interior of the grain, and the inuence of neighbouring grains (evident in the green part of the grain at the top of the gure).

The highest 3D resolution, and thus the nal zoom state, can be obtained by illuminating individual layers in a grain using an X-ray beam focused to a sub-micron size in the vertical direction only (that is, a line beam), and then stacking these layers into a 3D volume. This approach illuminates a smaller volume of material containing fewer subgrains, allowing individual sub-grains to be more clearly visible in the raw dark-eld images (see Supplementary Fig. 1). As above, a map of the subgrain orientations within the layer of the sample can be constructed from a series of images at differing tilt angles (a, b). Then, by acquiring 40 layers of this kind, the subgrains within a 10

200 200 mm3 volume can be mapped with a resolution of

B300 nm. A part of this map is shown in Fig. 2c.

Tracking subgrain dynamics during the annealing process required sampling a large range of orientations with high spatial precision within a narrow time frame (minutes). As mapping the full volume of the grain in 3D would have been too time-consuming, we instead illuminated only a single layer using the line beam. Proceeding in this manner, a single layer was successively mapped while annealing the sample in steps of increasing temperature. The results for two subsequent temperature steps are shown in Fig. 3a,b. Experimental and analysis details are described in Methods, while an orientation map corresponding to an additional higher temperature is given in Supplementary Fig. 2.

The considerable softening of aluminium that occurs during annealing treatments is of key importance in many processing operations. The structural changes responsible for this effect are

Diffraction contrast tomography:

Dark field x-ray microscopy:

a b c

30 m

10 m

100 m

[111]

[101]

1 [afii9825]

1 [afii9826] 10

[001]

0 7

Figure 2 | Multiscale mapping of 10% tensile deformed aluminium. Above: (a) Part of the X-ray mapping of all grains in the specimen. (b) Zooming in on one embedded grain and mapping the intrinsic variation in orientation. A vertical section through the grain is shown for ease of inspection of the spatial heterogeneity. (c) Condensing the incoming beam vertically denes a sub-micron layer within the grain. Mapping individual subgrains in 3D is then obtained by stacking these layers. The spatial resolution from left to right is 3.5 mm, 1.5 mm and 300 nm, and the angular resolution is 0.5, 0.15 and 0.03, respectively. Below: The corresponding keys for the orientation maps. (a) the colour scheme is represented in an inverse pole gure. (b,c) the colour schemes symbolize the required tilts a and b to align the [200] direction with the diffraction vector.

NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 3

& 2015 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms7098

a b c

10 m 10 m 10 m

Figure 3 | Study of recovery in tensile deformed aluminium. Shown is a 2D map of one layer in the sample, (a) after annealing for 0.5 h at 246 C, and (b) after additional annealing for 0.5 h at 257 C. The colours symbolize the orientation of the [200] direction of the crystalline lattice with respect to the specimen reference system, cf. Fig. 1. Shown in (c) is a difference map with white, blue and red representing local changes in orientation below0.01 between 0.01 and 0.2 and above 0.2, respectively. The spatial resolution is 300 nm.

collectively known as recovery25; however, the underlying physical mechanisms have been difcult to ascertain without access to multiscale experimental methods. In particular, it is not clear whether observations by in situ TEM26 are inuenced by the free surfaces inherent to TEM. Our results, as evidenced from the orientation difference map in Fig. 3c, indicate that the majority of subgrains either exhibit no resolvable rotation (white areas within the grain) or small rotations of o0.2 (blue areas). The remaining red areas represent locations where the orientation has changed 40.2 during annealing. These areas are primarily located adjacent to subgrain boundaries and represent regions, which have been traversed by moving subgrain boundaries. After the passage of the subgrain boundary, these regions adapt their orientation to that of the adjacent subgrain. These ndings are consistent with conjectures in the literature of subgrain growth by subgrain boundary motion25, but this is the rst time the processes have been directly veried and quantied.

DiscussionThese results demonstrate the capability of dark-eld X-ray microscopy as a probe for studying the dynamics of a representative ensemble of subgrains during processes such as plastic deformation or recrystallization. More broadly, such studies serve to improve the general understanding of domain evolution in crystalline materials during phase transformations.

Beyond the work presented here, the dark-eld approach might also be applied to non-crystalline materials by performing microscopy on small angle X-ray scattering or amorphous scattering signals27. Furthermore, with a dedicated and optimized set-up at an upcoming diffraction-limited synchrotron storage ring28, we estimate that the data acquisition speed can be improved by several orders of magnitude, making this a promising technique for studying more challenging dynamic processes in situ or in operando.

In conclusion, we have demonstrated a non-destructive technique for the comprehensive multiscale 3D mapping of crystallographic information. Full orientation mapping may be achieved by acquiring two maps of the kind shown in Fig. 2b, corresponding to two independent diffraction vectors. Furthermore, the large sample-to-objective distance is favourable for in situ and in operando studies with complex sample environments. In addition to opening a new door to multiscale modelling, the technique is also highly suited to applied studies

of functioning devices and components, for example, where the behaviour of selected internal nanoscale grains or domains at interfaces or crack tips governs performance or lifetime.

Methods

Microscope conguration. This work was performed at beamline ID06 at the ESRF. A Si(111) BraggBragg double crystal monochromator located 35.8 m from the source selected 17 keV photons (l 0.728 ) emitted by a cryogenic

permanent magnet undulator. A primary condenser was used, comprising a CRL transfocator29 located 38.7 m from the source and congured with seven one-dimensional Be lenses with an apex radius of curvature of 200 mm and an effective aperture of 860 mm.

Situated 59 m from the source, the dark-eld microscope comprised an optional secondary condenser, a sample stage, a near-eld imaging detector, an objective and two far-eld detectors of differing eld of view and resolution. The objective projects a magnied and inverted image of the sample on one of the two far-eld detectors, both located at the downstream end of the hutch at p q 4.750 m.

The secondary condenser was used to make an incoming line beam through two congurations. In the rst, a Si-based CRL was used, positioned 232 mm from the sample and containing eight one-dimensional lenses with an apex radius of curvature of 6.2 mm, yielding an effective aperture of 40 mm and a divergence of0.01. In the second, a Be-based CRL was used, positioned 500 mm from the sample and containing 48 2D Be lenses with an apex radius of curvature of 50 mm, yielding an effective aperture of 277 mm and a divergence of 0.03 (see Supplementary Note 2 for description of the optical calculations performed here). The former conguration is associated with a superior denition of the beam (o1 mm versus 5 mm vertical full width at half maximum), and an improved angular resolution, while the latter provides more ux on the sample.

The sample tower required six degrees of freedom to enable the rotation of the sample around the diffraction vector necessary for 3D mapping with topo tomography30. As with the conguration of Ludwig et al.30, the base tilt is set to the Bragg angle y, while the two tilt angles a and b, situated above, are used to align the lattice planes of the selected grain with the axis of the rotation stage, o and thus the diffraction vector G.

The near-eld imaging detector consisted of a scintillator screen coupled to a FReLoN CCD camera by microscope optics, giving an effective spatial resolution of3.5 mm and a eld of view of 7 7 mm2. It was used to align the instrument and

sample, to characterize the beam and to perform the DCT mapping.

The objective was a CRL containing 72 2D Be lenses with an apex radius of curvature of 50 mm. In its focused position, the centre of the objective was aligned on the diffracted beam at a distance of 342 mm from the sample. Using the thick lens expressions given in Supplementary Note 2 the focal distance is f 244.7 mm,

and the magnication M 16.08. The resulting effective aperture becomes

Deff 235 mm and the numerical aperture NA 0.00035.

From these numbers it follows that the angular resolution (full width at half maximum) in directions b and y are Db 0.11 and D2y 0.039, respectively.

The corresponding resolution in reciprocal space becomes Dqradial |q200|D2y/

2tan (y) 0.0060 1and Dq

azimuth

|q200|Db 0.0058 1.

With our conguration, the angular resolution in a, Da, is dominatedby the divergence of the incoming beam. Using only the primary condenser, the resolution in the corresponding direction in reciprocal space is Dqrock |q200|Da

B0.0003 1. In this conguration the reciprocal space resolution is strongly

4 NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

& 2015 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms7098 ARTICLE

anisotropic with DqrockooDqradialEDqazimuth. The resolution can be made

approximately isotropic by rocking, in which images are acquired while rotating the sample in a. The microscopes 3D eld of view in direct space corresponds to a region in reciprocal space with a relative volume of order 10 9 in comparison with the Brillouin zone (the Voronoi cell around the origin in reciprocal space).

The far-eld detectors were (a) a high-resolution 2D detector comprising a scintillator screen coupled to a FReLoN CCD camera with microscope optics to give a spatial resolution and eld of view of 2.5 mm and 3 3 mm2, respectively,

and (b) a low-resolution 2D detector comprising a scintillator screen coupled to a Basler CCD camera with wide-angle optics to give a spatial resolution and eld of view of 55 mm and 50 50 mm2, respectively. The high-resolution FReLoN camera

was used for the microscopy images which, accounting for the X-ray magnication of 16.1, gave a resolution and eld of view at the sample position of 150 nm and0.2 0.2 mm2. However, to improve the signal-to-noise ratio, the detector pixels

were binned 2 2 to give a nal resolution of 300 nm. The large eld of view Basler

camera served to easily identify and align grains, and to facilitate high-resolution reciprocal space mapping of entire grains to determine their mosaic spread and strain heterogeneity. It may also be used to provide a fast overview of grain and subgrain dynamics in the sample9.

Beamtime details. This work was carried out during three beamtimes related to the 3D imaging and annealing studies illustrated in Fig. 2ac and Fig. 3, respectively. The optical congurations used in these beamtimes were individually optimized and therefore differed slightly from one another. The reconguration between these beamtimes meant that the grains investigated in the three beamtimes were not necessarily the same. The development of a dedicated dark-eld X-ray microscope would enable these three measurements in fast succession on a single element of interest.

The rst beamtime employed the topotomography approach without use of a secondary condenser. The spatial resolution of each image was close to the predicted value of 300 nm. The resolution in 3D, however, was limited by the sphere-of-confusion of the rotation and tilt stages below the sample, estimated to be B1.5 mm. The grain map shown in Fig. 2b is based on an importance-guided 3D scanning procedure, derived from intensities observed in the pole gure of the reection. A total of 106 topotomography scans were recorded at differing sample tilts a and b, each comprising 36 projections over a full 360 rotation in o. Each image was integrated over a range of 0.15 in the base tilt angle, y. The scanning procedure sampled a grid of 1.8 2.1 in a and b, respectively, with a step size of

0.15 for both tilts. Due to time constraints, this scan was limited to a sub-region corresponding to 60% of the total area around the most intense (a, b) position. The acquisition of the map took 9.5 h, of which only 20% corresponded to actual X-ray exposure due to overheads in the scanning procedure.

The second beamtime aimed to demonstrate the high-resolution 3D mapping by utilizing a Si secondary condenser to make an incident line beam with a vertical dimension of o1 mm. The narrow beam illuminates fewer subgrains, and these now become distinct in the raw data as shown in Supplementary Fig. 2a, while the sphere-of-confusion issue is much less pronounced. In this way, a200 200 10 mm3 volume was mapped layer-by-layer by acquiring 40 layers in

steps of 250 nm. Each layer involved a 2D scanning procedure with a range of 0.3 and steps of 0.03 in a at a constant value of b. Each image was integrated during a three-second exposure over a range of 0.03 in the base tilt angle, y. Having corrected for the nite beam height by a deconvolution procedure, a part of the resulting 3D map is shown in Fig. 2c. This map is not space lling due to the limited orientation range sampled.

For the third beamtime, the Be-based secondary condenser was used, which has a substantially larger numerical aperture and better transmission than the Si lenses used previously. This increased the ux. The incident line beam height is 5 mm and, as such, (possibly overlaying) 2D projections of grains are observed. For the time-resolved study, this set-up proved a good compromise between the image contrast of individual subgrains and counting statistics. Mapping a single layer of interest involved a 2D scanning procedure with a range of 0.8 and steps of 0.01 in a and a range of 0.8 and steps of 0.1 in b. Each image was integrated during a ve second exposure over a range of 0.01 in the base tilt angle, y. An example of raw data is shown in Supplementary Fig. 1b.

The CRL and the far-eld detector positions are pre-aligned in the direct beam with the sample removed. When a grain of interest has been identied, the grain is centred and the relevant diffraction vector and the rotation axis are aligned using the near-eld camera and a photodiode close to the sample. Next, the grain is rotated to scatter in the direction of the CRL and far-eld detector. Finally, the near-eld camera is translated out of the diffracted beam and the CRL is subsequently translated into it.

Sample. A tensile specimen of 1 mm thickness, 12 mm gauge length and 4 mm width was machined from a sheet of commercial aluminium (AA 1050), which had been rolled and annealed to an average grain size of B80 mm. The specimen was deformed in tension to 10% and exhibited only a weak crystallographic texture31. From the tensile specimen, a needle-shaped sample was cut and ground to its nal dimensions of 0.3 0.6 8 mm3, with its long direction parallel to the tensile axis.

The sample was subsequently placed in the dark-eld X-ray microscope with the tensile axis parallel to the axis of rotation. The illuminated volume of the

sample (0.3 mm in height) during the rst beamtime comprised 283 grains, identied by the DCT analysis.

The annealing study. To heat the sample in situ, a hot air blower was placed B3 mm from the sample. The true temperature at the position of the grain was determined by measuring the angular change of the (200) reection during heating, as observed on the large eld-of-view far-eld 2D detector. On the basis of the known linear expansion coefcient for pure aluminium, the change in d-spacing and temperature were inferred. The accuracy in temperature determined in this way is estimated to be better than 1 K.

The sample was annealed by progressively increasing the temperature in steps until recrystallization took place. At each step, the temperature remained constant for 0.5 h (annealing temperature), followed by reducing the temperature by 30 K (measuring temperature) and maintaining this temperature for 1.5 h during the measurements. The purpose of this 30 K temperature reduction was to arrest the structural change during the measurement periods. Our data pertains to three steps in the vicinity of the annealing temperature at 246, 257 and 268 C.

Care was provided in terms of ensuring thermal stability. During each of the three 1.5-h measurement intervals, the temperature stability determined from the Basler detector data was of the order of 0.1. To verify that the same layer was monitored at the various temperature steps, high-resolution X-ray radiography was performed on markers on the surface of the sample. As a result, we found that the layers mapped at lower temperatures are remarkably similar.

The high-resolution dark-eld microscopy images were post-processed in several steps: (1) the background was removed by subtracting an image of the detector dark current and (2) hot pixels were removed by interpolation. (3) The images were recombined into four-dimensional (x, y, a, b) space and (4) connected components with four-dimensional coordination were identied. The coordination range reected the differing angular resolution in a and b as determined by the numerical apertures of the condenser and objective. (5) Each component was assigned an average orientation corresponding to its centroid position in (a, b).

This process identied B1,800 components at each temperature, with a size distribution skewed towards small components of ve or less voxels, reecting ndings by TEM that well-identied subgrains at this level of deformation tend to be surrounded by even smaller dislocation-free units in the boundary regions surrounding the subgrains (the notion of subgrains for the connected components becoming therefore somehow ambiguous). Notably, the size distributions of the components identied at the three temperatures were almost identical. Hence, on average, little growth took place in the measured temperature regime; nevertheless, some subgrain boundary motion seem to occur.

To provide better insight in the subgrain dynamics and to ease visualization, we generated 2D maps by dening the orientation for each (x, y) position as the (a, b)

values that maximized the measured intensity. In this way, the maps presented in Fig. 3a,b (main article) and Supplementary Fig. 2a,b were generated. Connected components in these maps are dened as subgrains; the boundaries between them are marked with a black outline and reect orientation differences above the resolution limit of 0.01. The orientation difference maps in Fig. 3c and Supplementary Fig. 2c are constructed by comparing orientations in the two maps pixel by pixel. The subgrain boundaries associated with the lower temperature are overlaid for reference purposes.

By inspection of Fig. 3c, we nd that most subgrains can be traced from one temperature to the other as the local subgrain topology changes little during annealing. However, a sizeable area fraction undergoes a reorientation by an amount that is larger than the instrumental resolution of 0.01. A histogram of the local reorientation angles is shown in Supplementary Fig. 3. On the basis of this result, a level of 0.2 is used to distinguish between low-angle rotation and high-angle rotation in Fig. 3c. We nd that the high-angle part (shown in red) mainly appears in connection with small subgrains and near the interface between subgrains. Such reorientations are, therefore, seen as being consistent with the movement of a subgrain boundary, which changes the local orientation of a pixel to that of its neighbour.

Supplementary Figure 2 conveys the advances in the structural evolution during further annealing for 0.5 h at 268 C. Similar to the previous annealing step, individual subgrains can still be traced when comparing the maps before (Supplementary Fig. 2a) and after (Supplementary Fig. 2b) the annealing step. The orientation difference map highlights the same features with some ofthe area showing no (white) or small reorientations below 0.2 (blue) and larger reorientations (red) mainly located in the vicinity of subgrain boundaries.

As seen from the histogram in Supplementary Fig. 3, both the area undergoing reorientation and the reorientation angles during this step are larger than during the previous annealing step (0.5 h at 257 C). This may indicate a progress in the recovery due to the temperature increase, but could also be caused by increasing difculties in the alignment of the sample during heating.

During the annealing process studied here, the small rotations of entire subgrains are consistent with the small orientation changes associated with the climb and annihilation of dislocations, while the larger rotations in the vicinity of the subgrain boundaries indicate subgrain boundary motion. This is the rst time that such effects are quantied directly. More generally, this study demonstrates how dark-eld microscopy can be varied in terms of both direct space and reciprocal space resolution to optimize the statistics of structural units.

NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 5

& 2015 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms7098

References

1. Pippan, R. & Gumbsch, P. Multiscale Modelling of Plasticity and Fracture by Means of Dislocation Mechanic (Springer, 2010).

2. Horstemeyer, M. F. Integrated Computational Materials Engineering (ICME) for Metals: Using Multiscale Modeling to Invigorate Engineering Design with Science (Wiley, 2012).

3. Liu, H. H. et al. Three-dimensional orientation mapping in the transmission electron microscope. Science 332, 833834 (2011).

4. Uchic, M. D., Groeber, M. A., Dimiduk, D. M. & Simmons, J. P. 3D microstructural characterization of nickel superalloys via serial-sectioning using a dual beam FIB-SEM. Scripta Mater. 55, 2328 (2006).

5. Echlin, M. P., Husseini, N. S., Nees, J. A. & Pollock, T. M. A new femtosecond laser-based tomography technique for multiphase materials. Adv. Mater. 23, 23392342 (2011).

6. Poulsen, H. F. et al. Three-dimensional maps of grain boundaries and the stress state of individual grains in polycrystals and powders. J. Appl. Cryst. 34, 751756 (2001).

7. Poulsen, H.F. Three Dimensional X-ray Diffraction Microscopy: Mapping Polycrystals and Their Dynamics (Springer, 2004).

8. Schmidt, S. et al. Watching the growth of bulk grains during recrystallization of deformed metals. Science 305, 229232 (2004).

9. Jakobsen, B. et al. Formation and subdivision of deformation structures during plastic deformation. Science 312, 889892 (2006).

10. Hefferan, C. M. et al. Observation of recovery and recrystallization in high-purity aluminium measured with forward modeling analysis of high-energy diffraction microscopy. Acta Mater. 60, 43114318 (2012).

11. King, A., Johnson, G., Engelberg, D., Ludwig, W. & Marrow, J. Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal. Science 321, 382385 (2008).

12. Ludwig, W. et al. Three-dimensional grain mapping by X-ray diffraction contrast tomography and the use of Friedel pairs in diffraction data analysis. Rev. Sci. Instrum. 80, 033905 (2009).

13. Larson, B. C., Yang, W., Ice, G. E., Budai, J. D. & Tischler, J. Z. Three-dimensional X-ray structural microscopy with submicrometre resolution. Nature 415, 887890 (2002).

14. Bleuet, P. et al. Probing the structure of heterogeneous diluted materials by diffraction tomography. Nat. Mater. 7, 468472 (2008).

15. Hofmann, F. et al. X-ray micro-beam characterization of lattice rotations and distortions due to an individual dislocation. Nat. Commun. 4, 2774 (2013).

16. Williams, D. B. & Carter, C. B. Transmission Electron Microscopy (Springer,

2009).

17. Gorelick, S. et al. High-efciency Fresnel zone plates for hard X-rays by 100 keV e-beam lithography and electroplating. J. Synchrotron Radiat. 18, 442446 (2011).

18. Snigirev, A., Kohn, V., Snigireva, I. & Lengeler, B. A compound refractive lens for focusing high-energy X-rays. Nature 384, 4951 (1996).

19. Schroer, C. G. et al. Hard X-ray full eld microscopy and magnifying microtomography using compound refractive lenses. Nucl. Instr. Methods Phys. Res. A 467468, 966969 (2001).

20. Isakovis, A. F. et al. Diamond kinoform hard X-ray refractive lenses: design, nanofabrication and testing. J. Synchrotron Radiat. 16, 813 (2009).

21. Argon, A. S. & Haasen, P. A new mechanism of work hardening in the late stages of large plastic ow in F.C.C. and diamond cubic crystals. Acta Metall. Mater. 41, 32893306 (1993).

22. Jakobsen, B., Poulsen, H. F., Lienert, U. & Pantleon, W. Direct determination of elastic strains and dislocation densities in individual subgrains in deformation structures. Acta Mater. 55, 34213430 (2007).

23. Levine, L. E. et al. Disordered long-range internal stresses in deformed copper and the mechanisms underlying plastic deformation. Acta Mater. 59, 58035811 (2011).

24. Hansen, N., Huang, X. & Hughes, D. A. Microstructural evolution and hardening parameters. Mater. Sci. Eng. A317, 311 (2001).

25. Humphreys, F. J. & Hatherly, M. Recrystallization and Related Annealing Phenoma (Elsevier, 2004).

26. Hu, H. Direct observations on the annealing of a Si-Fe crystal in the electron microscope. Trans. Met. Soc. AIME 224, 7584 (1962).

27. Petukhov, A. V. et al. Microradian X-ray diffraction in colloidal photonic crystals. J. Appl. Cryst. 39, 137144 (2006).

28. Eriksson, M., van der Veen, J. F. & Quitmann, C. Diffraction-limited storage ringsa window to the science of tomorrow. J. Synchrotron Radiat. 21, 837842 (2014).

29. Vaughan, G. B. M. et al. A. X-ray transfocators: focusing devices based on compound refractive lenses. J. Synchrotron Radiat. 18, 125133 (2011).

30. Ludwig, W. et al. Three-dimensional imaging of crystal defects by topo-tomography. J. Appl. Cryst. 34, 602607 (2001).

31. Pantleon, W., Poulsen, H. F., Almer, J. & Lienert, U. In situ X-ray peak shape analysis of embedded individual grains during plastic deformation of metals. Mater. Sci. Eng. A 387389, 339342 (2004).

32. Herman, G. T. Fundamentals of Computerized Tomography: Image Reconstruction from Projection (Springer, 2009).

Acknowledgements

We thank ESRF for providing beamtime on beamline ID06, and E. Brok, X. Huang,D. Juul Jensen, E.M. Lauridsen, S. Poulsen, G.B.M. Vaughan and Y. Zhang for the discussions. This work was supported by an ERC Advanced Grant, d-TXM, and by the Danish Instrumentation Centre, DanScatt. A.S. and I.S. also acknowledge the support of the Ministry of Education and Science of the Russian Federation (Contracts14.Y26.31.0002 and 02.G25.31.0086).

Author contributions

H.S., A.K. and W.L. contributed equallythey developed most of the instrumentation and performed the data analysis. C.D. was in charge of the instrumentation programme at the beamline. W.P. provided the samples and expertise on recovery; S.S. was in charge of algorithms, I.S. of sample preparation and A.S. of CRL optics. H.F.P. conceived the idea of dark-eld microscopy and was responsible overall.

Additional information

Supplementary Information accompanies this paper at http://www.nature.com/naturecommunications

Web End =http://www.nature.com/ http://www.nature.com/naturecommunications

Web End =naturecommunications

Competing nancial interests: The authors declare no competing nancial interests.

Reprints and permission information is available online at http://npg.nature.com/reprintsandpermissions/

Web End =http://npg.nature.com/ http://npg.nature.com/reprintsandpermissions/

Web End =reprintsandpermissions/

How to cite this article: Simons, H. et al. Dark-eld X-ray microscopy for multiscale structural characterization. Nat. Commun. 6:6098 doi: 10.1038/ncomms7098 (2015).

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articles Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Web End =http://creativecommons.org/licenses/by/4.0/

6 NATURE COMMUNICATIONS | 6:6098 | DOI: 10.1038/ncomms7098 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

& 2015 Macmillan Publishers Limited. All rights reserved.