Evaluation of two surfacing methods on black spruce wood in relation to gluing performance

Abstract

Surface quality and gluing performance of black spruce samples prepared by peripheral straight-edge knife planing and sanding were studied. Four wavelengths (1.5, 1.9, 3.1, and 6.5 mm) and four rake angles (15°, 20°, 25°, and 30°) were tested for peripheral planing. Three feed speeds (4, 10.5, and 17 m/min) and three grit size sandpapers (80, 100, and 120) were studied for sanding. The resulting surfaces were glued with an isocyanate adhesive and tested to evaluate their gluing performance (shear strength and percent wood failure). Results revealed that planing with a rake angle of 20° and wavelengths of up to 3.1 mm produced wood surfaces with adequate glueline shear strength. Sanding with 80-grit sandpaper produced the best glueline shear strength, regardless of feed speed. After accelerated aging, the loss of gluing performance was lower for the sanded samples compared with that of planed samples. In general, sanding process produced better wood surfaces for bonding with the adhesive studied.