FIB-Assisted Fabrication of Single Tellurium Nanotube Based High Performance Photodetector

Abstract

Nanoscale tellurium (Te) materials are promising for advanced optoelectronics owing to their outstanding photoelectrical properties. In this work, high-performance optoelectronic nanodevice based on a single tellurium nanotube (NT) was prepared by focused ion beam (FIB)-assisted technique. The individual Te NT photodetector demonstrates a high photoresponsivity of 1.65 × 10⁴ AW⁻¹ and a high photoconductivity gain of 5.0 × 10⁶%, which shows great promise for further optoelectronic device applications.

1. Introduction

As one of the most important types of optoelectronic devices, photodetectors, (including photodiode, photoconductor and phototransistor), converting incident light into an electrical signal, have attracted great attention in the fields of flame sensing, ozone sensing, conversion communication, environmental monitoring, video imaging, night vision, material recognition, early detection of primary tumors and astronomical exploration because of their excellent photoelectrical properties [1,2,3,4]. Low dimensional Te nanomaterials, including Te nanowires (NWs) [5], Te nanobelt [6], Te nanotubes [7], and Te nanorods (NRs) [8] have been widely utilized as nonlinear optical response devices, optoelectronic devices, thermoelectric devices, piezoelectric devices, photonic crystal, self-developing holographic recording devices, radiative cooling devices, field-effect devices, and infrared acousto-optic deflector [9]. At present, the photoelectric properties of the low dimensional Te nanomaterials, including photoelectric conversion efficiency, photoconductivity gain and light responsivity, have attracted many researchers’ attentions, due to their high surface-area-to volume ratios and the reduced dimension of the effective conductive channel. Zhong et al. [10] prepared a photodetector based on the Te NWs with the photocurrent and responsivity reaching 0.17 mA and 25.8 AW⁻¹, respectively. Kang et al. [6] reported that a Te nanobelt photodetector fabricated in-situ on SrTiO₃ (001) substrate with the responsivity of 254.2 AW⁻¹ under bias voltage of 1 V. Flexible photodetectors based on Te NRs were prepared by Qi Xiao et al. [11] with a responsivity of 6.1 AW⁻¹. Zhang et al. [12] have reported the self-powered photoresponse behavior (2.79 µAW⁻¹) of Te nanosheets irradiated by light at 400 nm under bias voltage of 0.6 V. Nevertheless, the photoelectric performance of the Te nanoscale devices has not been significantly improved. For example, their photocurrent and light responsivity are small, which are not suitable for practical applications. Moreover, the methods reported for the fabrication of Te nanodevices suffer from some disadvantages, such as low successful probability, nanomaterials wasting, complicated fabricating process or low yield, which hinder the applications of Te semiconductor nanomaterials in the photoelectric field. In the process of the single nanotube photodetector fabrication, it is important for the nanotube photodetector to realize reliable single nanotube electrical contact. There are some potential methods to do this work, such as dielectrophoresis [13] and Focused ion beam (FIB) etc. [14]. Compared with the other methods, FIB-assisted method is easy to implement to form ohmic contact and reliable electrical contact between Te nanomaterials and the electrodes with the Pt or W gas injected system (GIS), as both Pt or W possess very good conductivity.

In this work, Te nanotubes (NTs) with different diameters are synthesized by solvothermal method. Further, photodetector based on an individual Te nanotube was rapidly prepared by FIB-assisted technique, which is easy to implement with high successful probability and repeatability. The photodetector based on the individual nanotube with a diameter of 40 nm demonstrates a high photoresponsivity of 1.65 × 10⁴ AW⁻¹ and a high photoconductivity gain of 5.0 × 10⁶%.

2. Experimental Section

2.1. Sample Preparation

Te nanotubes with different diameters are synthesized by solvothermal method. All the raw materials are commercially available and used without further purification. First, the tellurium powder (17.4 mg) and hydrazine hydrate (HH) (0.25 mL or 2.55 mL, 85%) were mixed in a 50 mL beaker, and then 40 mL deionized water was added into it. Next, the mixed solution was placed in the Teflon-lined autoclave (50 mL) and heated at 140 °C for 6 h in an oven. After cooling down to room temperature, the obtained products were cleaned by DI water and anhydrous alcohol for three times, respectively. Finally, the prepared powder was dried in a vacuum oven at 60 °C.

2.2. Sample Characterization

The crystal structures of as-synthesized samples were characterized by X-ray diffraction (D8tools, Bruker, Karlsruhe, Germany) with Cu Ka radiation. The microstructure was characterized by Raman spectra using a micro-Raman spectrometer (Jobin Yvon LabRAM HR 800UV, Paris, France) with a 532 nm laser source. Scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analysis were performed on Zeiss Gemini 450 equipped with an X-ray energy dispersive spectrometer (Ultim Extreme, Oxford, UK). The microstructure was further investigated by high-resolution transmission electron microscopy (JEM-2100F, JEOL, Tokyo, Japan). For atomic resolution imaging, the measurements were performed on an aberration-corrected high-angle annular dark field scanning transmission electron microscopy (JEM Grand ARM300F, JEOL, Tokyo, Japan). To improve the signal-to-noise ratio (SNR) and to minimize the drift and the image distortion of high-angle annular dark field (HAADF) images, 10 serial frames were acquired with short dwell time (2 μs pixel⁻¹). The image series were then aligned and superimposed.

2.3. Fabrication of Individual Te Nanotube Photodetector Assisted by FIB Technique

As illustrated in Figure 1, the individual Te nanotube photodetector was fabricated by dual beam FIB (Helios G4, Thermo Fisher Scientific, Waltham, MA, USA)-assisted technique. First, Te nanotubes were dispersed in anhydrous alcohol and then transferred on a clean Si wafer by pipette. Then after the Si wafer was put into FIB system, single Te nanotube was extracted and transferred onto the 10 nm Cr/100 nm Au electrodes with a gap of 10 μm which were prepared by photolithography on SiO₂/Si, by using nano-manipulator under SEM mode. In detail, the tungsten (W) probe of the nano-manipulator was inserted and moved to one end of the single Te nanotube. Then, Pt was deposited to contact W probe and Te nanotube under the acceleration voltage of 16 kV and the current of 0.23 nA to avoid the ion beam damage to Te nanotube. Next, the extracted Te nanotube was transferred on Au electrodes. Then, Pt pads were deposited at the contact between the Te nanotube and the Au electrodes under ion beam with the acceleration voltage of 30 kV and the current of 0.1 nA to eliminate the Schottky barriers between Te nanotube and Au electrodes and form high quality ohmic contacts [15].

3. Results and Discussion

3.1. Structural Analysis of Te Nanotubes

Figure 2a plots XRD patterns of the samples obtained in 0.25 mL and 2.55 mL HH. It can be seen that the as-prepared samples exhibit similar XRD patterns, and all prominent peaks can be indexed as the hexagonal tellurium with lattice constants of a = 0.450 nm and c = 0.592 nm, which matches well with the standard values of a = 0.446 nm and c = 0.593 nm (JCPDS Card No. 36-1452). As shown in Figure 2b, the Raman spectra of the samples features three dominant active phonon modes due to their large electronic polarizability. For the sample obtained in 0.25 mL HH, the weak peak at 90.8 cm⁻¹ is related to the E¹ mode of Te which is caused by the rigid-chain rotation over the a- and b-axis [16]. The peak at 119.8 cm⁻¹ is related to the A¹ mode of Te, corresponding to the chain expansion mode in which each atom moves in the basal plane. The peak at 139.2 cm⁻¹ related to the E² mode of Te is mainly related to the asymmetric stretching along the c-axis [17,18]. Moreover, there is a second-order weak peak at 268.9 cm⁻¹ which is related to the second order harmonic of the E mode of Te [19]. The E¹, A¹ and E² modes are at the peak of 92.8, 120.8 and 141.1 cm⁻¹, respectively, for the sample obtained in 2.55 mL HH, which has a small blue shift compared with the sample obtained in 0.25 mL HH. The observed blue shift is determined by the diminish of the intrachain bonds (covalent bonds) and the increase of the interchain interactions (van der Waals) [20]. It means that the sample synthesized in 2.55 mL HH might have stronger intrachain interactions (van der Waals) than that in 0.25 mL HH.

3.2. Morphology and Microstructure of Te Nanotubes

As shown in Figure 3a–d, it can be seen that the samples prepared with 0.25 mL and 2.55 mL HH are Te nano/micro tubes with different diameters (nanotube: around 70 nm in 0.25 mL HH, microtube: around 3 μm in 2.55 mL HH). Representative HRTEM images of the Te nano/micro tubes with diameter of around 70 nm and 4 μm are shown in Figure 3b,d, illustrating obvious bright and dark lattice fringes with the lattice spacings of 0.59 nm corresponding well with the lattice spacings of (001) planes for hexagonal tellurium, which matches well with the XRD results. The above HRTEM results confirm that the lattice fringe (001) is along the longitudinal axis of the Te tubes, which suggests that the Te N/MTs exhibits a preferential growth direction along the [001] zone axis (c-axis). Further, Figure 3f is typical atomic STEM-HAADF image of the Te nanotubes projected along the [001] zone axis, which fit well with the atomic simulated models (Figure 3e) using the P3121 space group.

3.3. Photoelectric Properties of Individual Te Nanotube Photodevice

The photoelectric properties of Te nanotubes are critical to their applications in the field of the photoconductive devices. In this work, photodevice based on a single Te NT with a diameter of around 70 nm was prepared by FIB-assisted method (the detailed procedure refers to the Experimental Section) with the SEM image of the Te-nanotube based photodetector shown in the inset of Figure 4a. The photoresponse of an individual Te nanotube photodevice was explored by studying on their output characteristics of photocurrent at room temperature using a two-probe method by a Keithley 4200 system with 405 nm UV light [9]. Figure 4b displays the I-V characteristics of the photodetector based on the Te NT under the irradiation of a wavelength of 405 nm with different power densities. With power density varying from 0.6 to 1.2 W/cm², the photocurrent monotonically increases, demonstrating an enhanced photoconductivity. Furthermore, the I-V curves bent obviously at the voltage of 0.3 V, suggesting the formation of the schottky contact between the Te NT and the Cr/Au electrodes. The photocurrent and dark current of the photodetector based on the Te NT reach 1.42 mA and 4.29 μA, respectively, at a voltage of 0.6 V under the power density of 1.2 W/cm². Figure 4c shows that the photocurrent is symmetric.

Figure 4d shows that the photocurrent responses increase steadily with increasing irradiation density. High power densities provide the Te NT with more photons, thus generating more non-equilibrium carriers in Te, and subsequently resulting high photocurrents. The dependence of the photocurrent on irradiance density can be fitted by the power law [21]: I_P = aP^θ, where θ is a parameter related to the trapping and recombination processes of the photocarriers in the photodetectors. Obviously, for Te NT, the photocurrent increases with an increasing power density, which is consistent with the results that the charge carrier photogeneration efficiency is proportional to the absorbed photon flux [22]. The θ obtained for the Te NT photodetector is 0.477 which is related to the processes of electron-hole generation, trapping and recombination [23,24].

The spectral responsivity (R), a vital parameter of a photodetector, is defined as the photocurrent generated by the irradiation on the effective area of Te and can be expressed as [25,26,27]: R = I_p/PA, where I_P = I_photo − I_dark ≈ I_photo, I_dark is the dark current, P is the incident light intensity irradiated on the single Te, and A is the effective illuminated area of the single Te. The photoconductive gain (G), another important performance parameter, is mainly defined as the number of carriers circulating through a photodetector per absorbed photon and per unit time and can be expressed as [28,29]: G = (I_p/e)/(PA/hʋ), where I_p is the photocurrent, P is the incident power density, A is the effective irradiated area on the Te, hʋ is the energy of an incident photon, and e is the electronic charge. Figure 4e shows the R and G values of a single Te NT photodetector reach 1.65 × 10⁴ AW⁻¹ and 5.0 × 10⁶%, respectively, at a voltage of 0.6 V and under the irradiation of a wavelength of 405 nm. The curves of the spectral responsivity (R) and the photoconductivity gain (G) show a downward trend with the light power density increasing, as a high light power density could reduce the trapped states with an increasing photogenerated holes, resulting in the photocurrent saturation. The process can be described as follow: under low light power density, excited holes are trapped by the surface trap states and the crystal structure defects of the Te NT with the reduction of the photo-generated carrier recombination at the recombination center and the prolong of the lifetime of photo-generated carriers. When the Te NT is irradiated with high light power density, the increasing photo-generated holes fill the surface trap states and the crystal structure defects of the Te NT. The photogenerated carriers are easy to recombine at the recombination center and not take part in the charge transfer process [30] resulting in the small R and G values under the high light power density.

As summarized in Table 1, the photoelectric performance of the nanodetector based on a single Te NT in this work are enhanced a lot comparing with that of other 1D and 2D nanomaterials, which exhibits high I_photo/I_dark, photoconductivity gain (G), and spectral responsivity (R), demonstrating that this nanodevice shows an extremely high sensitivity to violent light and possesses high effective availability. The superior performance of the individual Te nanotube photodetector might attribute to large surface-to-volume ratio of the nanotube, good crystallinity.

4. Conclusions

In summary, Te nanotubes with different diameters with hexagonal phase growing along [001] direction were synthesized by solvothermal method. With the assistance of FIB technique, Te photodetector based on a single nanotube with diameter of 40 nm was successfully prepared, which exhibits very high responsivity (1.65 × 10⁴ AW⁻¹) and photoconductivity gain (5.0 × 10⁶%). Our work provides a promising and effective way for the preparation of photodetectors based on one-dimensional Te nanostructures, which may further promote the application of one-dimensional semi-conductive nanostructures in the fabrication of high-performance optoelectronic nanodevices.

Author Contributions

Conceptualization, W.X., Y.L. and R.Q.; methodology, Y.L.; software, W.X. and W.L.; formal analysis, W.X.; investigation, W.L., F.S., Y.L. and R.M.; data curation, Y.L. and R.H.; writing-original draft preparation, W.X. and W.L.; writing—review and editing, R.Q.; supervision, R.Q.; funding acquisition, R.Q. and R.H. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Key Research and Development Program of China (2017YFA0303403) and the National Natural Science Foundation of China (Grant No. 61974042).

Conflicts of Interest

The authors declare no conflict of interest.

Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Figures and Table

Figure 1. The schematic illustration of the fabrication process of individual Te nanotube photodetector assisted by FIB technique. Insets are SEM images taken during the fabrication process.

Figure 2. (a) XRD patterns and (b) Raman spectra of the as-prepared samples.

Figure 3. (a) SEM and (b) HRTEM images of the Te NTs obtained in 0.25 mL HH. (c) SEM and (d) HRTEM images of the Te NTs obtained in 2.55 mL HH. (e) Schematic crystal structure image of Te projected along [001] axis. (f) HAADF images of the Te NTs obtained in 2.55 mL HH projected along [001] axis.

Figure 4. The photoresponse properties of the single Te NT detector: (a) SEM image and EDS maps of Te and Au; (b) I-V curve, (c) logarithmic plot of (b); (d) the relationship between the photocurrent and the optical power density; (e) photoresponsivity and photoconductivity gain.

Table 1

Comparison of the spectral responsivity, the photoconductivity gain, I_photo/I_dark and non-unity exponent θ of the Te NT with previous reported work.

Photodetector	Iphoto/Idark	θ (IP = aPθ)	Gain (%)	Responsivity (AW−1)	References
Te NT	331	0.76	5.0 × 106	1.65 × 104	this work
Er-CdSe NB	2.21 × 104	0.603	3.87 × 105	2.17 × 103	[31]
CdS FL	103	0.76	55.87	0.18	[25]
Se NR	—	0.57	88.4	0.408	[32]
CdTe NS	27	—	—	6.0 ×10−4	[33]
PbS	<2	—	—	1.6 × 103	[34]

Note: NB nanobelt, NS nanosheet, FL flake, NW nanowire, NR nanorod, I_dark: dark current, I_photo: photocurrent.

References

1. Kim, Y.; Kim, J.; Kim, H.-M.; Jang, J. Quantum-Dots Photosensor with Wide Bandgap P-Type and N-Type Oxide Semiconductors for High Detectivity and Responsivity. Adv. Mater. Technol.; 2020; 5, 1900857. [DOI: https://dx.doi.org/10.1002/admt.201900857]

2. Dan, Y.; Zhao, X.; Chen, K.; Mesli, A. A Photoconductor Intrinsically Has No Gain. ACS Photonics; 2018; 5, pp. 4111-4116. [DOI: https://dx.doi.org/10.1021/acsphotonics.8b00805]

3. Yoo, H.; Kim, W.-G.; Kang, B.H.; Kim, H.T.; Park, J.W.; Choi, D.H.; Kim, T.S.; Lim, J.H.; Kim, H.J. High Photosensitive Indium-Gallium-Zinc Oxide Thin-Film Phototransistor with a Selenium Capping Layer for Visible-Light Detection. ACS Appl. Mater. Interfaces; 2020; 12, pp. 10673-10680. [DOI: https://dx.doi.org/10.1021/acsami.9b22634] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/32052953]

4. Chen, Y.; Wang, B.; Hongfei, L.U.; Yang, K.; Chen, L.; Zhang, G.; Fan, X. Development of Photoelectric Detecting Circuit for Tdlas Type C_2h_2 Gas Detection System. Laser J.; 2018; 39, pp. 15-18.

5. Wang, W.; Liu, J.; Li, X.; Jiang, Q.; Xu, J.; Luo, C.; Liu, P.; Tan, R.; Du, Y.; Jiang, F. Galvanic Exchange Reaction Involving Te Nanowires and Ag Ions for N-Type Te/Ag₂Te Thermoelectric Nanofilms. J. Nanopart. Res.; 2019; 21, 131. [DOI: https://dx.doi.org/10.1007/s11051-019-4536-z]

6. Kang, S.; Dai, T.; Ma, X.; Dang, S.; Li, H.; Hu, P.; Yu, F.; Zhou, X.; Wu, S.; Li, S. Broad Spectral Response of an Individual Tellurium Nanobelt Grown by Molecular Beam Epitaxy. Nanoscale; 2019; 11, pp. 1879-1886. [DOI: https://dx.doi.org/10.1039/C8NR07978A] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/30643911]

7. Guascito, M.R.; Chirizzi, D.; Filippo, E.; Milano, F.; Tepore, A. Synthesis and Characterization of Te Nanotubes Decorated with Pt Nanoparticles for a Fuel Cell Anode/Cathode Working at a Neutral Ph. Catalysts; 2019; 9, 328. [DOI: https://dx.doi.org/10.3390/catal9040328]

8. Ullah, S.; Yasin, G.; Ahmad, A.; Qin, L.; Yuan, Q.; Khan, A.U.; Khan, U.A.; Rahman, A.U.; Slimani, Y. Construction of Well-Designed 1D Selenium-Tellurium Nanorods Anchored on Graphene Sheets as a High Storage Capacity Anode Material for Lithium-Ion Batteries. Inorg. Chem. Front.; 2020; 7, pp. 1750-1761. [DOI: https://dx.doi.org/10.1039/C9QI01701A]

9. Li, H.H.; Zhang, P.; Liang, C.L.; Yang, J.; Zhou, M.; Lu, X.H.; Hope, G.A. Facile Electrochemical Synthesis of Tellurium Nanorods and Their Photoconductive Properties. Cryst. Res. Technol.; 2012; 47, pp. 1069-1074. [DOI: https://dx.doi.org/10.1002/crat.201200273]

10. Zhong, B.N.; Fei, G.T.; Fu, W.B.; Gong, X.X.; Xu, S.H.; Gao, X.D.; Zhang, L.D. Controlled Solvothermal Synthesis of Single-Crystal Tellurium Nanowires, Nanotubes and Trifold Structures and Their Photoelectrical Properties. Crystengcomm; 2017; 19, pp. 2813-2820. [DOI: https://dx.doi.org/10.1039/C7CE00497D]

11. Xiao, Q.; Li, X.; Zhang, Z.; Hu, C.; Zhang, H. Facile Fabrication of Highly Uniform Tellurium Nanorods for Self-Powered Flexible Optoelectronics. Adv. Electron. Mater.; 2020; 6, 2000240. [DOI: https://dx.doi.org/10.1002/aelm.202000240]

12. Xie, Z.; Xing, C.; Huang, W.; Fan, T.; Li, Z.; Zhao, J.; Xiang, Y.; Guo, Z.; Li, J.; Yang, Z. et al. Ultrathin 2D Nonlayered Tellurium Nanosheets: Facile Liquid-Phase Exfoliation, Characterization, and Photoresponse with High Performance and Enhanced Stability. Adv. Funct. Mater.; 2018; 28, 1705833. [DOI: https://dx.doi.org/10.1002/adfm.201705833]

13. Jiangbo, Z.; Ning, X.; Hongzhi, C.; King, L.; Yilun, L. Carbon Nanotube Based Infrared Detector Array. Proceedings of the 2008 8th IEEE Conference on Nanotechnology; Arlington, TX, USA, 18–21 August 2008; IEEE: Piscatway, NJ, USA, 2008; pp. 100-103.

14. Fabrega, C.; Hernandez-Ramirez, F.; Daniel Prades, J.; Jimenez-Diaz, R.; Andreu, T.; Ramon Morante, J. On the Photoconduction Properties of Low Resistivity TiO₂ Nanotubes. Nanotechnology; 2010; 21, 445703. [DOI: https://dx.doi.org/10.1088/0957-4484/21/44/445703] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/20921596]

15. Wang, D.; Zhu, R.; Zhou, Z.; Ye, X. Contact Behaviors between Zinc Oxide Nanowires and Metal Electrodes. J. Nanosci. Nanotechnol.; 2009; 9, pp. 862-865. [DOI: https://dx.doi.org/10.1166/jnn.2009.C041] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/19441409]

16. Marini, C.; Chermisi, D.; Lavagnini, M.; Di Castro, D.; Petrillo, C.; Degiorgi, L.; Scandolo, S.; Postorino, P. High-Pressure Phases of Crystalline Tellurium: A Combined Raman and Ab Initio Study. Phys. Rev. B; 2012; 86, 064103. [DOI: https://dx.doi.org/10.1103/PhysRevB.86.064103]

17. Vasileiadis, T.; Dracopoulos, V.; Kollia, M.; Yannopoulos, S.N. Laser-Assisted Growth of T-Te Nanotubes and Their Controlled Photo-Induced Unzipping to Ultrathin Core-Te/Sheath-TeO₂ Nanowires. Sci. Rep.; 2013; 3, 1209. [DOI: https://dx.doi.org/10.1038/srep01209]

18. Pine, A.S.; Dresselhaus, G. Raman Spectra and Lattice Dynamics of Tellurium. Phys. Rev. B; 1971; 4, pp. 356-371. [DOI: https://dx.doi.org/10.1103/PhysRevB.4.356]

19. Liu, J.-W.; Xu, J.; Hu, W.; Yang, J.-L.; Yu, S.-H. Systematic Synthesis of Tellurium Nanostructures and Their Optical Properties: From Nanoparticles to Nanorods, Nanowires, and Nanotubes. ChemNanoMat; 2016; 2, pp. 167-170. [DOI: https://dx.doi.org/10.1002/cnma.201500206]

20. Silva, R.R.; Mejia, H.A.G.; Ribeiro, S.J.L.; Shrestha, L.K.; Ariga, K.; Oliveira, O.N., Jr.; Camargo, V.R.; Maia, L.J.Q.; Araujo, C.B. Facile Synthesis of Tellurium Nanowires and Study of Their Third-Order Nonlinear Optical Properties. J. Braz. Chem. Soc.; 2017; 28, pp. 58-67. [DOI: https://dx.doi.org/10.5935/0103-5053.20160145]

21. Yang, S.; Tongay, S.; Li, Y.; Yue, Q.; Xia, J.-B.; Li, S.-S.; Li, J.; Wei, S.-H. Layer-Dependent Electrical and Optoelectronic Responses of ReSe₂ Nanosheet Transistors. Nanoscale; 2014; 6, pp. 7226-7231. [DOI: https://dx.doi.org/10.1039/c4nr01741b]

22. Chen, G.; Yu, Y.; Zheng, K.; Ding, T.; Wang, W.; Jiang, Y.; Yang, Q. Fabrication of Ultrathin Bi₂S₃ Nanosheets for High-Performance, Flexible, Visible-Nir Photodetectors. Small; 2015; 11, pp. 2848-2855. [DOI: https://dx.doi.org/10.1002/smll.201403508] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/25703599]

23. Kind, H.; Yan, H.Q.; Messer, B.; Law, M.; Yang, P.D. Nanowire Ultraviolet Photodetectors and Optical Switches. Adv. Mater.; 2002; 14, pp. 158-160. [DOI: https://dx.doi.org/10.1002/1521-4095(20020116)14:2<158::AID-ADMA158>3.0.CO;2-W]

24. Guo, N.; Hu, W.; Liao, L.; Yip, S.; Ho, J.C.; Miao, J.; Zhang, Z.; Zou, J.; Jiang, T.; Wu, S. et al. Anomalous and Highly Efficient Inas Nanowire Phototransistors Based on Majority Carrier Transport at Room Temperature. Adv. Mater.; 2014; 26, pp. 8203-8209. [DOI: https://dx.doi.org/10.1002/adma.201403664]

25. Jin, B.; Huang, P.; Zhang, Q.; Zhou, X.; Zhang, X.; Li, L.; Su, J.; Li, H.; Zhai, T. Self-Limited Epitaxial Growth of Ultrathin Nonlayered CdS Flakes for High-Performance Photodetectors. Adv. Funct. Mater.; 2018; 28, 1800181. [DOI: https://dx.doi.org/10.1002/adfm.201800181]

26. Kuo, C.-H.; Wu, J.-M.; Lin, S.-J.; Chang, W.-C. High Sensitivity of Middle-Wavelength Infrared Photodetectors Based on an Individual InSb Nanowire. Nanoscale Res. Lett.; 2013; 8, 327. [DOI: https://dx.doi.org/10.1186/1556-276X-8-327] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/23866944]

27. Zheng, D.; Wang, J.; Hu, W.; Liao, L.; Fang, H.; Guo, N.; Wang, P.; Gong, F.; Wang, X.; Fan, Z. et al. When Nanowires Meet Ultrahigh Ferroelectric Field-High-Performance Full-Depleted Nanowire Photodetectors. Nano Lett.; 2016; 16, pp. 2548-2555. [DOI: https://dx.doi.org/10.1021/acs.nanolett.6b00104] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/26985983]

28. Soci, C.; Zhang, A.; Xiang, B.; Dayeh, S.A.; Aplin, D.P.R.; Park, J.; Bao, X.Y.; Lo, Y.H.; Wang, D. ZnO Nanowire UV Photodetectors with High Internal Gain. Nano Lett.; 2007; 7, pp. 1003-1009. [DOI: https://dx.doi.org/10.1021/nl070111x]

29. Liu, X.; Gu, L.; Zhang, Q.; Wu, J.; Long, Y.; Fan, Z. All-Printable Band-Edge Modulated ZnO Nanowire Photodetectors with Ultra-High Detectivity. Nat. Commun.; 2014; 5, 4007. [DOI: https://dx.doi.org/10.1038/ncomms5007] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/24898081]

30. Zhang, X.; Liu, B.; Liu, Q.; Yang, W.; Xiong, C.; Li, J.; Jiang, X. Ultrasensitive and Highly Selective Photodetections of UV-A Rays Based on Individual Bicrystalline Gan Nanowire. ACS Appl. Mater. Interfaces; 2017; 9, pp. 2669-2677. [DOI: https://dx.doi.org/10.1021/acsami.6b14907] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/28029770]

31. Huang, J.; Tan, Q.; Zhang, Z.; Wang, Q.; Feng, X.; Liu, Y. Photoconductive Properties of Er-CdSe Nanobelt Detectors. J. Mater. Sci.; 2019; 54, pp. 560-570. [DOI: https://dx.doi.org/10.1007/s10853-018-2845-8]

32. Chang, Y.; Chen, L.; Wang, J.; Tian, W.; Zhai, W.; Wei, B. Self-Powered Broadband Schottky Junction Photodetector Based on a Single Selenium Microrod. J. Phys. Chem. C; 2019; 123, pp. 21244-21251. [DOI: https://dx.doi.org/10.1021/acs.jpcc.9b04260]

33. Cheng, R.; Wen, Y.; Yin, L.; Wang, F.; Wang, F.; Liu, K.; Shifa, T.A.; Li, J.; Jiang, C.; Wang, Z. et al. Ultrathin Single-Crystalline CdTe Nanosheets Realized Via Van Der Waals Epitaxy. Adv. Mater.; 2017; 29, 1703122. [DOI: https://dx.doi.org/10.1002/adma.201703122] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/28707714]

34. Wen, Y.; Wang, Q.; Yin, L.; Liu, Q.; Wang, F.; Wang, F.; Wang, Z.; Liu, K.; Xu, K.; Huang, Y. et al. Epitaxial 2D PbS Nanoplates Arrays with Highly Efficient Infrared Response. Adv. Mater.; 2016; 28, pp. 8051-8057. [DOI: https://dx.doi.org/10.1002/adma.201602481] [PubMed: https://www.ncbi.nlm.nih.gov/pubmed/27376848]