Content area
Abstract
Low energy helium diffraction, a quantitative structural characterization tool, has been used to measure the growth kinetics of self-assembled monolayers (SAMs). Special attention was given to the growth of decanethiol monolayers deposited from a molecular beam onto the (111) face of gold single crystals especially at the initial stages of growth. The influence of changing impingement rate, substrate temperature, and annealing treatments was investigated. We also studied the structure and dynamics of physisorbed adlayers on top of the monolayers and structural variations in monolayers caused by changes in chemical composition such as the addition of phenyl groups, and hydroxyl groups.
Experimental work involved renovations to the existing diffractometer. The apparatus was improved with respect to its signal to noise ratio; efficiency in sample preparation and data collection; and the reproducibility of obtaining clean crystal surfaces. The renovations greatly extended the range of experiments of which the diffraction machine is capable.
The growth of n-decanethiol SAMs by gas deposition was identified as a multi-stage process where the initial "lying down" layer grows on the bare gold surface with a near unity sticking coefficient, while the subsequent, "standing-up" phase grows with a sticking coefficient of about $10\sp{-3}$.
The ordering and chemisorption of a single "lying down" layer of decanethiol was investigated by annealing a single layer physisorbed on a 130 K Au(111) surface to incrementally higher temperatures. The molecules first align themselves with the underlying gold substrate, then orient themselves in the "head to head" two molecule unit mesh, then chemisorb at still higher temperatures.
Overlayers of long chain molecules grown on top of monolayers on Au(111) are found to be more ordered than the underlying monolayers themselves. The energy of adsorption to the organic surface is found to be very close to that of the bulk value, even for a gold-adlayer separation distance of about 4 A. Debye-Waller experiments were done to measure the stiffness of monolayers of different chain lengths, coverages and functional groups as well as overlayers.