New Surface Properties in Porcelain Gres Tiles with a Look to Human and Environmental Safety

Abstract

Traditional photocatalysis is here brought forward for both the use of nanosized TiO2 crystallites and the possibility to have a release of TiO2 particles during the final use of the manufactured products. In the present paper both the preparation and characterization of a new generation of photocatalytic tiles are presented. The originality of these products is the surface presence of microsized TiO2 as it is not clear yet the impact of the nanoparticles on both human and environmental safety. TiO2 is here mixed with a silica compound and the final thermal treatment at 680°C allows the complete surface vitrification which, in turn, makes the tiles surface strongly resistant to abrasion. Photocatalytic efficiency towards the degradation of [subscript]NOx[/subscript] in gas phase was measured in both a batch and a plug-flow reactor. The latter reactor configuration was also modeled by digital simulations.

(ProQuest: ... denotes non-US-ASCII text omitted.)

C. L. Bianchi 1,2 and C. Pirola 1,2 and S. Gatto 1 and S. Nucci 1 and A. Minguzzi 1 and G. Cerrato 2,3 and S. Biella 2,4 and V. Capucci 5

Recommended by Wilson Acchar

1, Dipartimento di Chimica, Università degli Studi di Milano, Via Golgi 19, 20133 Milan, Italy
2, Consorzio Interuniversitario Nazionale per la Scienza e Tecnologia dei Materiali, Via G. Giusti 9, 50121 Florence, Italy
3, Dipartimento di Chimica and NIS Centre of Excellence, Università degli Studi di Torino, Via P. Giuria 7, 10125 Turin, Italy
4, Dipartimento di Chimica, Materiali e Ingegneria Chimica "Giulio Natta", Politecnico di Milano, Piazza Leonardo da Vinci 32, 20133 Milan, Italy
5, GranitiFiandre S.p.A, Via Radici Nord 112, 42014 Castellarano, Italy

Received 23 February 2012; Accepted 16 July 2012

This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

1. Introduction

Porcelain gres tiles are characterized by a very low water absorption rate (less than 0.5%) and are manufactured under high pressure by dry-pressing fine processed ceramic raw materials with large proportions of quartz, feldspar, and other fluxes. Afterwards, the body of these materials is fired at very high temperatures (1200-1300°C) in kilns [1]. The final material is thus characterized by lack of porosity, complete water-proofing, durability, hardness, wear resistance properties, and a complete frost resistance.

In the past decades porcelain gres tiles underwent significant transformations in terms of appearance and size. At the beginning of the industrial productions, porcelain gres tiles were considered as just a technical material characterized by strong resistance to both abrasion and acid attack, almost lack of porosity, but aesthetically not very beautiful. Today thanks to new industrial production methods, both properties and beauty of these materials completely fit the market requests. In particular, the possibility to prepare slabs of large sizes is the new frontier of building materials.

Beside these noteworthy architectural features, new surface properties have been introduced in the last generation of these materials. The present paper reports the preparation and characterization at the base of a new kind of fired tiles able to reduce polluting molecules present in air thanks to its new photocatalytic properties. The extreme originality of these products is the surface presence of microsized TiO₂ . In fact it is not clear yet the impact of the possible release in the atmosphere of nanoparticles, in particular nano-TiO₂ , on both human and environmental safety.

Man-made nanostructured materials such as fullerenes, nanoparticles, nanopowders, nanotubes, nanowires, nanorods, nanofibers, quantum dots, dendrimers, nanoclusters, nanocrystals, and nanocomposites are globally produced in large quantities due to their wide potential applications, for example, in skincare and consumer products, healthcare, electronics, photonics, biotechnology, engineering products, pharmaceuticals, drug delivery, and agriculture. Human exposure to these nanostructured materials is inevitable, as they can enter the body through the lungs or other organs via food, drink, air, and medicine and affect different organs and tissues such as the brain, liver, kidney, heart, blood, and so forth and may cause cytotoxic effects, for example, deformation and inhibition of cell growth leading to various diseases in both humans and animals. Since a very wide variety of nanostructured materials exists, their interactions with biological systems and possible toxicity largely depend upon their properties, such as particle size, concentration, solubility, chemical and biological properties, and stability [2].

Titanium dioxide nanoparticles are manufactured worldwide in large quantities for use in a wide range of applications including pigment and cosmetic manufacturing. Although TiO₂ is chemically inert, TiO₂ nanoparticles can cause negative health effects, such as respiratory tract cancer in rats. Trouiller et al. [3] investigate TiO₂ nanoparticles-induced genotoxicity, oxidative DNA damage, and inflammation in a mice model.

The possibility to use Microsized TiO₂ in a commercial manufactured product opens a new generation of material intrinsically safer than the traditional photocatalytic products for both workers in the factories and public safety, even though, with such materials that are surface vitrified, the release of TiO₂ particles is extremely remote.

In the present paper both preparation and characterization of photocatalytic porcelain gres tiles are reported, as well as specific tests, in gas phase, to verify the effective photocatalytic efficiency of the samples. A comparison is initially reported between the photoactivity in the photodegradation of N_Ox in gas phase of a pure commercial powdered nano-TiO₂ (AEROXIDE TiO₂ P25 by Evonik, P25 referred in the following) and the commercial powdered micro-TiO₂ (1077 by Kronos) used as starting material in the present tiles preparation. A specific session of the present paper will be also devoted to the discussion about the experimental setup to employ when tiles have to be investigated for the N_Ox photodegradation in air with a plug-flow reactor built following the ISO 22197-1 rule [4].

2. Experimental

2.1. Preparation

Industrial porcelain gres tiles are manufactured under high pressure by dry-pressing fine processed ceramic raw materials with large proportions of quartz, feldspar, and other fluxes and finally fired at high temperatures (1200-1300°C) in a kiln.

Photoactive porcelain gres tiles by GranitiFiandre S.p.A were subsequently covered at the surface with a mixture of pure anatase micro-TiO₂ (1077 by Kronos) and a commercial SiO₂ -based compound. To ensure the requested product stability, at the end of the preparation procedure tiles were treated at high temperature (min 680°C) for 80 min and then brushed to remove the powder present at the sample surface and not completely stuck (samples name: Orosei Active). For the sake of comparison, samples were also prepared with the same procedure but without adding the photoactive oxide into the SiO₂ -based compound (Orosei).

2.2. Characterization

Specific surface area (SA) of powdered samples has been determined by conventional N₂ absorption at 77 K (BET method) using a Sorptometer 1042 instrument (Costech). Before the analysis, the samples have been heated at 100°C for 12 h and then pretreated at 200°C in a nitrogen flow.

HR-TEM images were obtained by means of a JEOL 3010-UHR instrument (acceleration potential: 300 kV; LaB6 filament) equipped with an Oxford INCA X-ray energy dispersive spectrometer (XEDS) with a Pentafet Si(Li) detector. Samples were "dry" dispersed on lacey carbon Cu grids.

X-ray powder diffraction (XRD) patterns have been taken with a computerized Philips PW1710 diffractometer using the CuK α radiation, operating at 40 kV and 20 mA, step scan 1 min^-1 , and 1 s counting time in the 2-40° range at room temperature.

XPS measurements were performed in an M-Probe Instrument (SSI) equipped with a monochromatic Al K _α source (1486.6 eV) with a spot size of 200 × 750 μ m and a pass energy of 25 eV, providing a resolution for 0.74 eV. The energy scale was calibrated with reference to the 4f_7/2 level of a freshly evaporated gold sample, at 84.00±0.1 eV, and with reference to the 2p_3/2 and 3s levels of copper at 932.47±0.1 and 122.39±0.15 eV, respectively. With a monochromatic source, an electron flood gun was used to compensate the buildup of positive charge on the insulator samples during the analyses: a value of 10 eV was selected to perform measurements on these samples.

The surface wettability was evaluated by static contact angle (CA) measurements performed with an OCA20 instrument (DataPhysics Co., Germany) equipped with a CCD camera and a 500 μ L-Hamilton syringe to dispense liquid droplets. Measurements were made at room temperature (~ 22°C) by means of the sessile drop technique and were replicated at least 15 times on each sample. Ultrapure water (HPLC grade, Sigma-Aldrich) was used as probe liquids and the volume of drop was fixed at 2 μ L. The Young-Laplace fitting method was used in the calculation of static contact angles for all measurements giving an experimental error of ±5% due to the surface roughness of the samples [5, 6] that was experimentally determined by a laser profilometry (3D laser profilometer, UBM Microfocus Compact, NanoFocus AG, Germany) with vertical and lateral resolution of 10 nm. The parameters used during measurements follow the standard DIN 4768 and were adopted a transverse line measurement of 17.5 mm and a density of 150 dots per mm.

2.3. Photocatalytic Tests

Pure commercial powders (P25 and 1007) were tested towards the photodegradation of N_Ox in air in a static experimental setup already described in [7, 8] under the following conditions: RH: 50%, 10 Wm^-2 , _Vreactor =20 L, with a N_Ox starting value of 1000 ppb. Immobilized particulate TiO₂ layers (ca. 0.05 g) were prepared on glass sheets by deposition from a suspension of the oxide in isopropanol [9].

Pure 1077 and P25 powders (always immobilized on a glass sheet) and tiles were tested towards the same reaction but in flowing conditions using a plug-flow reactor built following strictly the ISO 22197-1 rule [4] with an effective volume of 0.025 L. Experimental conditions were maintained as follows: RH: 40%, 20 Wm^-2 , _{[NOx ]inlet} 500 ppb, and 180, 32.4, 9, and 4.2 L h^-1 total flow, respectively.

A chemiluminescent analyzer (Teledyne Instruments M200E) was used to check the final conversion of the pollutant in both batch and plug-flow reactor setpus.

The reactor configuration under flowing conditions was also modeled by digital simulations carried out using COMSOL Multiphysics 4.0a coupling the laminar flow (experimentally verified) with the transport of diluted species physics in a 3D space with each geometry resembling the relevant reactor dimensions and considering steady-state conditions. Each simulation was carried out using the following values: _C0,in = 2.04 × 10^-5 mol m^-3 (equivalent to 500 ppb of N_Ox ); ρ=1.165 kg m^-3 (air density at 30°C); μ=1.86×^10-5 Pa s (air dynamic viscosity at 30°C); D = 1.9 × 10^-5 m² s^-1 (diffusion coefficient of NO₂ in air [10]).

Simulations were performed considering six different inlet fluxes: _Vin (4.2, 9, 20, 32.4, 100, and 180 L h^-1 ) and three different apparent reaction rate values, two of them calculated on the basis of the experimental results obtained using two catalysts studied in this work (Orosei Active and pure 1077, resp.) at 32.4 L h^-1 and the third calculated at 180 L h^-1 . A first-order kinetic was considered for the reaction, as usual in photocatalysis with reactants such as N_Ox at sub-ppm level [11, 12]. The apparent kinetic constant was determined by performing simulations varying _kapp until the N_Ox conversion resembled the experimental one. After this, _kapp was used for the remaining _Vin values.

The reaction on the catalytic surface was simulated by imposing an outlet flux of matter through the central surface that corresponds to the photoactive tile. The flux, expressed in mol m^-2 s^-1 , is set as equal to _kapp ·_{[NOx ]s} (the subscript indicates that [N_Ox ] at the catalyst surface is considered). It follows that the rate constant values found in this work do not coincide with the real values of the chemical rate constant for the considered reaction. The following values were obtained: _kapp = 2.3 × 10^-3 m s^-1 (Orosei Active) or 4 × 10^-3 m s^-1 (pure 1077) at 32.4 L h^-1 and _kapp = 1.0 × 10^-4 m s^-1 for both Orosei Active and 1077 at 180 L h^-1 .

3. Results and Discussion

3.1. Sample Characterization

A feature comparison of both pure TiO₂ and TiO₂ + SiO₂ -based compound after the calcination treatment at 680°C shows the decrease of the surface area from 11.0 to 2.6 m² g^-1 (BET measurements). From the surface point of view, XPS analysis reveals the classical Ti2p doublet at 458.6 ev (Ti2p_3/2 ) attributed to Ti⁴⁺ with a Ti/Si ratio of 0.20.

The formulation with the SiO₂ -based compounds and the following calcination step lead to a decrease of the surface area but preservation of the pure anatase form verified by XRD measurements [13]. As reported by Anderson and Bard [14], the presence of SiO₂ , together with TiO₂ , enhances the formation of hydroxyl radical OH * , which would be achieved via strong Brønsted acid sites at the TiO₂ /SiO₂ interface region. Such incorporation inhibits the crystal growth of TiO₂ allowing the preservation of the anatase structure at high temperature [15].

In order to investigate the morphological features of the various samples, HR-TEM technique has been resorted to. P25 nano-sized TiO₂ has been also investigated, and its images are reported in Figures 1(a) and 1(b): it can be observed that the P25 material is made up of highly crystalline closely packed particles, as either thickness or Moirè's fringe patterns are evident (right-hand image) [16] with rather smooth edges. The average particle size is in agreement with literature data [17], that is, 20-50 nm range. The detailed inspection of the spacings among the interference fringes ( d = 0.357 nm) indicates that the most frequently exposed planes belong to the TiO₂ (101) anatase polymorph [18]. If both particle size and ultimate morphology of the plain Kronos TiO₂ sample (see Figures 1(c) and 1(d)) are compared to the P25 features, it can be evidenced that (i) particles are still packed, but to a limited extent if compared to the P25, and the edges of the particles are quite smooth; (ii) the size of the crystallites has enormously enlarged, as in the present case the average size varies in the 100-250 nm range; (iii) if we inspect the distances among the fringes, it is evident that the spacings ( d = 0.357 nm) are still ascribable to the anatase polymorph. When the presence of the SiO₂ -based compound is considered, it can be stated that, roughly morphologically speaking, the main features of the TiO₂ particles are maintained: see, for instance, Figures 1(e) and 1(f), in which the large dimensions of the particles are evident (50-200 nm range), beside rather smooth edges. Nevertheless, some peculiarities have to be mentioned: in particular, the presence of the SiO₂ -based compound is evident (see either the inset in Figure 1(e) or Figure 1(f)), in the form of either small protruding crystalline particles or an amorphous coating covering the TiO₂ particles. In any case, the very thin nature of these particles and/or coating allows to inspect the fringe patterns located below, confirming that the spacings among the fringes are still ascribable to the anatase TiO₂ polymorph.

HR-TEM images of the various TiO₂ materials. (a) and (b): P25. (c) and (d): 1077. (e) and (f): Orosei Active. (a), (c), and (e) refer to low magnification, here as (b), (d), and (f) to high magnification.

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

(c) [figure omitted; refer to PDF]

(d) [figure omitted; refer to PDF]

(e) [figure omitted; refer to PDF]

(f) [figure omitted; refer to PDF]

Wettability measurements were performed on 15 different areas of both Orosei and Orosei Active (Figures 2(a) and 2(b), resp.). Drop shapes are dramatically different enhancing a completely different surface. Orosei sample shows a mean contact angle value of 78.2°, while Orosei Active shows very hydrophilic surface features with an average angle of 23.0°. This very low value can be explained by the super-hydrophilic property of TiO₂ photocatalyst as already observed by other authors [19]. In particular the copresence of TiO₂ and SiO₂ can lead to a modification of the angle value depending on the TiO₂ /SiO₂ ratio [20] with values in the range of 20-25° with a SiO₂ content at 70-80% (molar basis), in agreement with the XPS Ti/Si ratio obtained on Orosei Active.

Contact angle: (a) Orosei; (b) Orosei Active tiles.

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

Samples roughness, measured as root mean squared ( _Rq ), was 19.354 μ m and 18.860 μ m for Orosei Active and Orosei (Ti-free), respectively.

3.2. Photocatalytic Tests

3.2.1. Batch Reactor

Figure 3 reports the rate of N_Ox degradation for P25 and 1077. The N_Ox concentration is the sum of the NO and NO₂ concentrations; the general mechanism of N_Ox oxidation by photocatalysts implies the oxidation of the nitric monoxide to nitric acid or nitrous by active oxygen species produced on the TiO₂ surface [21].

Figure 3: Comparison between P25 (... ) and 1077 (...) in the N_Ox photodegradation in a batch reactor.

[figure omitted; refer to PDF]

P25 is, as expected, more efficient than 1077 and it reaches a full N_Ox degradation (1000 ppb) in about 2 h. On the contrary, 1077 never reaches a complete N_Ox degradation within the 6 h of test but, notwithstanding the larger crystallite size and the lower surface area, shows a 90% conversion after 100 min of irradiation.

3.2.2. Plug-Flow Reactor

ISO 22197-1 rule provides for very sharp experimental conditions such as an inlet N_Ox concentration of 1000 ppb coupled with a low irradiation power (10 Wm^-2 ) and mainly with a very strong flow at 180 L h^-1 . These conditions are too extreme for our samples being vitrified at their surface and having no porosity.

For these reasons, the operating conditions have been softened cutting the inlet concentration by half (500 ppb), doubling the power irradiation (20 Wm^-2 ), and investigating the role of the flow per hour on the final N_Ox conversion. To check to have maintained the correct fluid dynamic conditions, the Reynolds number was calculated: [figure omitted; refer to PDF] where U is the is the velocity of the fluid (m s^-1 ), μ is the dynamic viscosity of the fluid (kg m^-1 s^-1 ), ρ is the density of the fluid (kg m^-3 ), and _De is the hydraulic diameter of the pipe (m), defined as 4 times the cross-sectional area (of the fluid), divided by the wetted perimeter. The wetted perimeter for a channel is the total perimeter of all channel walls that are in contact with the flow. In all chosen flows of the present paper, the laminar flow is confirmed (Table 1, second column).

Table 1: Data from continuous reactor and Comsol simulations (N _Ox 500 ppb, 20 Wm^-2 , sample size 0.005 cm² , RH: 40%, run time: 3 h. For the Comsol simulation: laminar flow).

Flow(L h-1 )	Reynold's number	Space velocity(h-1 )	Contact time(s)	1077 N Ox conversion (%)	Orosei Active N Ox conversion (%)
Experimentaldata	COMSOLsimulation	Experimentaldata	COMSOLsimulation
180.0	112	7200	0.5	5.0	36.8	1.3	25.6
32.4	20	1296	2.8	89.1	87.5	74.2	74.9
9.0	5.6	360	10.0	90.0	99.8	72.6	98.8
4.2	2.5	168	21.4	90.1	100.0	82.0	100.0

On the contrary, the modification of the flow per hour leads to the an evident change of the contact times that is the time the pollutant can stay "in contact" with the catalyst surface. As expected, increasing the contact time, the final conversion proportionally increases. This result is very evident for Orosei Active that shows a conversion varying from 1.3% to 82.0% at 180 L h^-1 and 4.2 L h^-1 , respectively (Table 1, seventh column). On the contrary, a sample of pure 1077, prepared on purpose on a glass sheet following the same procedure used for the batch setup, shows higher N_Ox conversion, but flattened towards the same value (ca. 90%).

This fact is very interesting and was observed also performing the test on a three-layer of P25. In this case a value of ca. 90% was observed at both 32.4 and 9 L h^-1 too, and a complete degradation (100%) was never present in our operative conditions as some fluid dynamics problems could exist inside the reactor configuration and part of the gas stream could pass undisturbed through the reactor. Moreover, the difference in the photocatalytic efficiency between P25 and 1077 evidenced by the tests performed in the batch reactor seems to be completely invalidated with this kind of reactor configuration.

The higher N_Ox conversion of pure 1077 than Orosei Active was fully expected as the number of surface of active sites on the tile surface is not comparable to a film of pure TiO₂ on a glass sheet. For this reason, the obtained 82% conversion at 4.2 L h^-1 flow can be considered a very good value.

3.3. Digital Simulations

Figure 4 reports a xz cross-section of the gas stream 3D fluid dynamics digital simulation in the two extreme flow rates: 180 and 4.2 L h^-1 . In more detail, the figure reports the local gas linear speed in the inlet side of the photoreactor. It is evident that the linear velocity of the gas stream is strongly influenced by the inlet flow rate: at 4.2 L h^-1 the gas stream follows a natural path from the inlet to the channel containing the photoactive material, while at 180 L h^-1 the inlet speed makes the gas to hit the wall in front of the inlet.

xy cross-sections of simulated fluid dynamic under steady-state conditions of the reactor used for the photocatalytic test (flowing conditions). (a) _Vin = 32.4 L h^-1 , (b) _Vin = 4.2 L h^-1 . The cross-section follows the longitudinal symmetry and is focused on the inlet gas chamber and a portion of the channel containing the photoactive tile.

(a) _Vin =32.4 L h^-1

[figure omitted; refer to PDF]

(b) _Vin =4.2 L h^-1

[figure omitted; refer to PDF]

Notwithstanding that this effect might generate some turbulence in the inlet chamber (not included in the present simulation), the fluid speed profile inside the channel containing the photoactive material remains homogeneous through the channel length. In both cases, in the channel containing the photoactive material, the gas follows speed profile typical of laminar flows.

Figure 5 represents the xz cross-section of the simulated N_Ox concentration profiles in the reactor volume under steady-state conditions. Note that the inlet is on the left side of the reactor (i.e., the same side considered in Figure 4), while the outlet is on the right. The color code represents in this case the concentration of N_Ox in the air stream, expressed in mol m^-3 (500 ppb corresponds to 2.04 × 10^-5 mol m^-3 ).

Figure 5: N_Ox local concentration in the reactor volume, expressed in mol m^-3 ( _kapp = 4 × 10^-3 m s^-1 , 32.4 L h^-1 ). Inset (a), zoom on the photoactive tile; inset (b), xz cross-section of the photoactive tile.

[figure omitted; refer to PDF]

It is evident that, as expected, the concentration gradient is located at the reactor center, in correspondence to the photoactive tile. This is better represented in the two insets, a (in which the 3D space is transparent) and b ( xz cross-section). In particular, inset b suggests the formation of a concentration gradient generated by the consumption of N_Ox at the photoactive surface. The gradient is at the origin of mass transport, that, at the lowest flow rate values, might become the rate determining step of the whole process, just before the maximum conversion (100%) is reached; see the simulated points (Figure 6) and values in Table 1.

Figure 6: Experimental (EXP) and simulated (SIM) percentage conversion in dependence on the flow rate, as reported in Table 1 relevant to the two samples considered in the flowing condition experiments (1077 and Orosei active) or the relevant simulated apparent kinetic constants (4 × 10^-3 and 2.3 × 10^-3 m s^-1 , respectively. The light blue curve corresponds to the simulated data adopting a lower apparent kinetic constant, 1 × 10^-4 m s^-1 .

[figure omitted; refer to PDF]

This is even more evident considering the experimental and simulated percentage N_Ox conversion values in dependence on the flow rate, reported in Figure 6. In the case of simulated results, which include the data at 20 L h^-1 and 100 L h^-1 as well as a set of data corresponding to _kapp = 1 × 10^-4 s^-1 it is evident that the trend follows the expected exponential decay predicted by a first-order kinetics: [figure omitted; refer to PDF]

In fact, the flow rate is inversely proportional to the contact time and thus to the reaction time, t . At the lowest flow rates (highest reaction times) a limiting-value results are reached, as indicated in Figure 6 by the colored ovals. These limiting values are 100% for the simulated data and about 90% for the experimental. This unexpected discrepancy can be explained considering the existence of preferential gas paths on the tiles sides (uncovered by the catalyst) that lead to the presence of unreacted N_Ox at the reactor outlet.

The figures also evidence that the only common points between simulated and experimental data are those obtained 32.4 L h^-1 , that is, the conditions at which the kinetic constants used in the simulations have been determined. In other words, this means that also the experimental results obtained at high flow rates do not find any correspondence with the simulated data. This might be explained by the formation, in the real reactor, of turbulence (likely in the inlet chamber) that can actually change the fluid dynamics of the whole system due to the reactor geometry.

4. Conclusions

Microsized TiO₂ can be really used as a valid choice for anti-pollutant photocatalytic processes avoiding the intrinsic risk due to the nanometric dimension. TiO₂ larger size compared to more traditional nano-sized crystallites allows to reach fully comparable results in the photodegradation of N_Ox , reference molecule for outdoor air pollution.

Good photocatalytic efficiency was achieved by the pure commercial microsized powder in comparison to P25. Porcelain gres tiles prepared entrapping micro-TiO₂ at the SiO₂ surface also show a stable and reproducible photocatalytic activity towards the degradation of N_Ox in air as expected by the surface feature results (surface wettability and Ti content).

Employed N_Ox photoreactor was built following the ISO 22197-1 rule but the requested ISO experimental conditions, such as inlet N_Ox concentration, low irradiation power, and high flow, are too extreme for our tiles samples being vitrified at their surface and having no porosity. For these reasons, the operating conditions have been softened and the role of the flow per hour on the final N_Ox conversion was fully investigated.

The discrepancies between the experimental data and the simulated ones might be related to the presence of preferential gas paths in the test reactor and to the formation of turbulence (due to the reactor geometry) in the case of the highest flow rate values.

Acknowledgment

A. Minguzzi is grateful to Università degli Studi di Milano for fundings (PUR 2009) and for a post-doc fellowship.

References

[1] R. Casasola, J. M. Rincón, M. Romero, "Glass-ceramic glazes for ceramic tiles: a review," Journal of Materials Science , vol. 47, no. 2, pp. 553-582, 2012.

[2] S. Singh, H. S. Nalwa, "Nanotechnology and health safety--toxicity and risk assessments of nanostructured materials on human health," Journal of Nanoscience and Nanotechnology , vol. 7, no. 9, pp. 3048-3070, 2007.

[3] B. Trouiller, R. Reliene, A. Westbrook, P. Solaimani, R. H. Schiestl, "Titanium dioxide nanoparticles induce DNA damage and genetic instability in vivo in mice," Cancer Research , vol. 69, no. 22, pp. 8784-8789, 2009.

[4] "ISO 22197-1--test method for air-purification performance of semiconducting photocatalytic materials. Part1: removal of nitric oxide," http://www.iso.org/iso/home.html

[5] J. Drelich, E. Chibowski, "Superhydrophilic and superwetting surfaces: definition and mechanisms of control," Langmuir , vol. 26, no. 24, pp. 18621-18623, 2010.

[6] T. Watanabe, S. Fukayama, M. Miyauchi, A. Fujishima, K. Hashimoto, "Photocatalytic activity and photo-induced wettability conversion of TiO₂ thin film prepared by sol-gel process on a soda-lime glass," Journal of Sol-Gel Science and Technology , vol. 19, no. 1-3, pp. 71-76, 2000.

[7] S. Ardizzone, C. L. Bianchi, G. Cappelletti, S. Gialanella, C. Pirola, V. Ragaini, "Tailored anatase/brookite nanocrystalline TiO₂ . the optimal particle features for liquidand gas-phase photocatalytic reactions," Journal of Physical Chemistry C , vol. 111, no. 35, pp. 13222-13231, 2007.

[8] C. Pirola, D. C. Boffito, S. Vitali, C. L. Bianchi, "Photocatalytic coatings for building industry: study of 1 year of activity in the NO_x degradation," Journal of Coatings Technology and Research , vol. 9, no. 4, pp. 453-458, 2012.

[9] C. L. Bianchi, C. Pirola, E. Selli, S. Biella, "Photocatalytic NO_x abatement: the role of the material supporting the TiO₂ active layer," Journal of Hazardous Materials , vol. 211-212, pp. 203-207, 2012.

[10] N. H. Chen, D. F. Othmer, "New generalized equation for gas diffusion coefficient," Journal of Chemical and Engineering Data , vol. 7, no. 1, pp. 37-41, 1962.

[11] T. N. Obee, R. T. Brown, "TiO₂ photocatalysis for indoor air applications: effects of humidity and trace contaminant levels on the oxidation rates of formaldehyde, toluene, and 1,3-butadiene," Environmental Science and Technology , vol. 29, no. 5, pp. 1223-1231, 1995.

[12] D. T. Tomkins, W. A. Zeltner, B. J. Lawnicki, M. A. Anderson, "Evaluation of Photocatalysis for Gas-Phase Air Cleaning Part 1: Process, Technical, and Sizing Considerations," ASHRAE Transactions , vol. 111, no. 2, pp. 64, 2005.

[13] C. L. Bianchi, S. Gatto, C. Pirola, M. Scavini, S. Vitali, V. Capucci, "Micro-TiO₂ as a Starting Material for New Photocatalytic Tiles," Cement and Concrete Composites . In press

[14] C. Anderson, A. J. Bard, "Improved photocatalytic activity and characterization of mixed TiO₂ /SiO₂ and TiO₂ /Al₂ O₃ materials," Journal of Physical Chemistry B , vol. 101, no. 14, pp. 2611-2616, 1997.

[15] T.-H. Xie, J. Lin, "Origin of photocatalytic deactivation of TiO₂ film coated on ceramic substrate," Journal of Physical Chemistry C , vol. 111, no. 27, pp. 9968-9974, 2007.

[16] R. I. Bickley, T. Gonzalez-Carreno, J. S. Lees, L. Palmisano, R. J. D. Tilley, "A structural investigation of titanium dioxide photocatalysts," Journal of Solid State Chemistry , vol. 92, no. 1, pp. 178-190, 1991.

[17] G. Cerrato, L. Marchese, C. Morterra, "Structural and morphological modifications of sintering microcrystalline TiO₂ : an XRD, HRTEM and FTIR study," Applied Surface Science , vol. 70-71, pp. 200-205, 1993.

[18] Anatase ICCD card File , no. 21-1272

[19] R. Wang, K. Hashimoto, A. Fujishima, M. Chikuni, E. Kojima, A. Kitamura, M. Shimohigoshi, T. Watanabe, "Light-induced amphiphilic surfaces," Nature , vol. 388, no. 6641, pp. 431-432, 1997.

[20] M. Machida, K. Norimoto, T. Watanabe, K. Hashimoto, A. Fujishima, "Effect of SiO₂ addition in super-hydrophilic property of TiO₂ photocatalyst," Journal of Materials Science , vol. 34, no. 11, pp. 2569-2574, 1999.

[21] Y. H. Tseng, C. S. Kuo, C. H. Huang, Y. Y. Li, P. W. Chou, C. L. Cheng, M. S. Wong, "Visible-light-responsive nano-TiO₂ with mixed crystal lattice and its photocatalytic activity," Nanotechnology , vol. 17, no. 10, pp. 2490-2497, 2006.