Large enhancement in neurite outgrowth on a cell membrane-mimicking conducting polymer

Abstract

Although electrically stimulated neurite outgrowth on bioelectronic devices is a promising means of nerve regeneration, immunogenic scar formation can insulate electrodes from targeted cells and tissues, thereby reducing the lifetime of the device. Ideally, an electrode material capable of electrically interfacing with neurons selectively and efficiently would be integrated without being recognized by the immune system and minimize its response. Here we develop a cell membrane-mimicking conducting polymer possessing several attractive features. This polymer displays high resistance towards nonspecific enzyme/cell binding and recognizes targeted cells specifically to allow intimate electrical communication over long periods of time. Its low electrical impedance relays electrical signals efficiently. This material is capable to integrate biochemical and electrical stimulation to promote neural cellular behaviour. Neurite outgrowth is enhanced greatly on this new conducting polymer; in addition, electrically stimulated secretion of proteins from primary Schwann cells can also occur on it.

ARTICLE

Received 12 May 2014 | Accepted 25 Jun 2014 | Published 25 Jul 2014

Bo Zhu1,2, Shyh-Chyang Luo1,3, Haichao Zhao1, Hsing-An Lin1,4, Jun Sekine1, Aiko Nakao5, Chi Chen6, Yoshiro Yamashita4 & Hsiao-hua Yu1,7

Although electrically stimulated neurite outgrowth on bioelectronic devices is a promising means of nerve regeneration, immunogenic scar formation can insulate electrodes from targeted cells and tissues, thereby reducing the lifetime of the device. Ideally, an electrode material capable of electrically interfacing with neurons selectively and efciently would be integrated without being recognized by the immune system and minimize its response. Here we develop a cell membrane-mimicking conducting polymer possessing several attractive features. This polymer displays high resistance towards nonspecic enzyme/cell binding and recognizes targeted cells specically to allow intimate electrical communication over long periods of time. Its low electrical impedance relays electrical signals efciently. This material is capable to integrate biochemical and electrical stimulation to promote neural cellular behaviour. Neurite outgrowth is enhanced greatly on this new conducting polymer; in addition, electrically stimulated secretion of proteins from primary Schwann cells can also occur on it.

1 Responsive Organic Materials Laboratory, RIKEN, 2-1 Hirosawa, Wako, Saitama 351-0198, Japan. 2 State Key Laboratory for Modication of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201600, China. 3 Department of Materials Science and Engineering, National Cheng Kung University, Tainan 70101, Taiwan. 4 Department of Electronic Chemistry, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology, Yokohama, Kanagawa 226-8502, Japan. 5 RNC Nuclear Spectroscopy Laboratory, RIKEN, Wako, Saitama 351-0198, Japan. 6 Research Center for Applied Sciences, Academia Sinica, Nankang, Taipei 11529, Taiwan. 7 Institute of Chemistry, Academia Sinica,128 Academic Road, Sec. 2, Nankang, Taipei 11529, Taiwan. Correspondence and requests for materials should be addressed to H.-h.Y. (email: mailto:[email protected]

Web End [email protected] ).

NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 1 & 2014 Macmillan Publishers Limited. All rights reserved.

DOI: 10.1038/ncomms5523

Large enhancement in neurite outgrowth on a cell membrane-mimicking conducting polymer

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523

Bioelectronic devices for nerve regeneration and neuroprosthesis are advancing towards electrically interfacing with tissues with high selectivity, long-term stability and

spatial resolution1,2, with the ultimate goal of stimulating and guiding neurite outgrowth efciently within very short periods of time. Progress is currently reaching a bottleneck, however, because traditional electronic materials, mostly metals and inorganic semiconductors, cannot satisfy the requirements of matching mechanical strength with biological systems3,4, high biocompatibility5,6, and stable electrical transduction711 that are necessary for interfacial communication between materials and neural cells. Therefore, the focus has shifted recently towards the application of electrically conducting polymers (ECPs), which are conductors (or semiconductors) like metals, but with the ability to readily tailor their structures through covalent modication of their organic frameworks. Because ECPs have mechanical properties comparable with those of the extracellular matrix (ECM), they should be more compatible with neural cells and tissues than inorganic materials12,13. ECPs can conduct both electrons and ions, thereby facilitating effective electron ion transitions over devicetissue boundaries with low impedance1417.

Pioneering studies have demonstrated the efciency of using ECPs for electrical interfacing with neural cells and tissues1826. Langer and coworkers24 rst demonstrated a 90% enhancement in the length of neurite outgrowth after electrical stimulation on unfunctionalized polypyrrole. Subsequently, various means of integrating ECPs and biofunctional groups, through physical mixing or chemical immobilization, have been tested2730. For example, Schmidt and coworkers27 coated electrospun poly(lactic-co-glycolic acid) nanobres with polypyrrole and applied this material for neural engineering. Separately, the same group also immobilized nerve growth factor onto the surface of polypyrroles with the application of an adhesion layer for similar purpose29. Wallace and coworkers31 employed a different approach to form polypyrrole/collagen complexes stabilized through electrostatic interactions. Unfortunately, these modications usually lead to relatively lower degrees of enhancement in neurite outgrowth, presumably because of the lower conductivity of these materials29.

Recent research interests on ECP-based devices shift the focus to polyethylenedioxythiophenes (PEDOTs)25,26. PEDOTs display stability in aqueous solution when a voltage is applied, a critical feature for medical devices implanted for long periods of time1416,18,32. In addition, the interfacial impedance of PEDOT at 1 kHz is not only signicantly less than that of Pt33 but also smaller than that of iridium oxide10, one of the most investigated electrode materials. PEDOT also displays a large charge storage capability with a small potential excursion10,11. These outstanding electrical properties allow PEDOT to provide stable electrical communications with attached cells and tissues, and efciently deliver charges to them over extended periods of time34. PEDOTs have already been employed to interface with neural tissues and cells in many bioelectronic devices35, including electronic ion pumps for neural signal delivery36, transistors for biosensing37,38, cochlear implants39 and neural probes40.

An implanted bioelectronic device would, ideally, establish stable and long-term electrical communication with living tissues, thereby allowing regeneration of the tissues or an exchange of physiological signals to recover damaged biofunctions. Unfortunately, most commercially available ECPs, including unfunctionalized PEDOTs, are likely to encounter implant-induced inammation, even though the conditions after implantation may not be as severe as those resulting from implantation of metals and inorganic semiconductors15,41,42. If these ECPs cannot discriminate among proteins and cells, proteins,

microphages and astrocytes might also accumulate on the surface of the polymers. This phenomenon would initialize the inammatory response and scar formation, thereby insulating the electrodes from the targeted cells and tissues and causing the device to lose its ability to function43,44. To resolve this issue, several groups have focused on tuning the biological and physical functions of ECPs through chemical modication or dopant switching. For example, Povlich et al.45 conjugated RGD peptide onto PEDOT chemically and observed that the new polymer could induce neural differentiation. Although the introduction of oligopeptide ligands (for example, YIGSR46, RGD), collagen31, or nerve growth factor21 can enhance cellmaterial interactions, thereby stabilizing cell proliferation and differentiation, no corresponding decreases in immunogenic response have been observed43,46. When Wadhwa et al.47 doped anti-inammatory drugs and neurotrophic factors into polymer lms to enhance the biocompatibility of ECPs, they had limited success, controlling inammation for only short periods of time. This approach might not be promising for long-term implantation because the drug would eventually be consumed19,43.

Here, we show the design and synthesis of ethylenedioxythiophene (EDOT)based polymers that specically recognize neural cells, thereby endowing neural bioelectronics with the inherent capability to resist nonspecic binding of proteins and cells and, as a result, allowing electrical communication with cells over extended periods of time. We follow a cell membrane-mimicking approach to synthesize biomimetic PEDOTs consisting of two new EDOT monomers. Taking a cue from the structure of phospholipids, we prepare a phosphorylcholine-grafted EDOT to resist nonspecic binding to both proteins and cells; we also develop a maleimide-grafted EDOT for conjugation with peptide ligands to mimic specic integrinECM interactions. These biomimetic PEDOTs are not only inert in normal biological environments but also interact specically with target cells after covalent linking with peptide ligands. Moreover, this biomimetic design imparts the materials with low electrical impedance48,49, thereby allowing intimate and stable electrical communication between the materials and the cells/tissues over long periods of time. Utilizing this material, we observe the respective and integrated effects of biochemical and electrical stimulations for neural cell engineering and record large enhancement of neurite outgrowth and protein secretion on neural cells.

ResultsDesign and synthesis of biomimetic PEDOTs. To construct an ideal conducting polymer interface, we adopted an approach mimicking the inertness and specic binding properties of cell membranes (Fig. 1a), which mainly comprise phospholipid bi-layers with imbedded proteins, carbohydrates and other bio-polymers to direct surface functions50. The outer layer is predominated by the polar zwitterionic phosphorylcholine heads of phospholipids; the great hydrophilicity of these zwitterionic interfaces creates the inertness and nonthrombogenic properties5153. Moreover, specic binding between cells and the ECM is mediated by membrane integrins and ECM peptide segments, with the subsequent anchoring of cells onto the ECM promoting tissue formation. To integrate these features, we prepared two new EDOT monomers (Fig. 1b). Starting from hydroxymethyl-functionalized EDOT (EDOT-OH), we introduced a zwitterionic phosphorylcholine functional group, simulating a phospholipid, onto EDOT (giving the new monomer EDOT-PC), using a procedure similar to those reported previously for the preparation of phosphorylcholinefunctionalized polyacrylates and self-assembled monolayers5457.

2 NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications & 2014 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523 ARTICLE

N+(CH3)3

O-

O

Extracellular matrix

Integrin

OH

O

P O

Cl

O

1. , Et3N, THF2. (CH3)3N, CH3CN

HATU, DIPEA, CH2Cl2

H2N N

O

O

P O

O

O

O

O

Cell membrane

S

S

EDOT-OH EDOT-PC

EDOT-COOH EDOT-MI

O

O N

+(CH3)3

Hydrophilic

Hydrophobic O

O

O O

O

O P

1. NaH, NaI, THF, then2. NaOH, THF/H2O

Br

O

OCH3

O

O

Peptide ligand (specific to the integrin)

H N

OH

O

N

O

O

O

O

O

O

O

O O O O

S n S m

S

S

O

Figure 1 | Design and synthesis of the biomimetic conducting polymer. (a) Schematic representation of the approach leading to the design of the target conducting polymer, mimicking the interactions between a cell membrane and the ECM. (b) Syntheses of new EDOT-based monomers designed through the biomimetic approach.

EDOT-OH was rst reacted with 2-chloro-2-oxo-1,3,2-dioxaphospholane (COP); the dioxaphospholane ring was subsequently opened in the presence of trimethylamine to yield the phosphorylcholine functional group. The non-crystalline product was puried through normal-phase column chromatography with a high-polarity solvent (a combination of EtOAc, MeOH, water and MeCN). Under the optimized reaction and purication conditions, we could synthesize EDOT-PC in quantities greater than 10 g. We also synthesized a maleimidefunctionalized EDOT (EDOT-MI) for covalent conjugation to the integrin-recognized peptide sequence58.

Electropolymerization from a mixture of functionalized EDOT monomers directly onto electrode surfaces allowed the rapid formation of multifunctional conducting polymers. We found, however, that hydrophilic EDOT-PC could not be electrodeposited onto electrodes from aqueous electrolyte solutions; in addition, this monomer was almost insoluble in the organic solvents commonly used for electrochemistry. Moreover, the opposing polarities of EDOT-PC and EDOT-MI made it challenging to nd a co-solvent system for electropolymerization of these two monomers at different feed compositions. To overcome these challenges, we developed a protocol for electropolymerization using the surfactant dioctyl sodium sulphosuccinate (DSS). In the presence of DSS, EDOT-PC dissolved in MeCN without the need to introduce a secondary solvent, presumably because of strong ionic interactions between the zwitterionic phosphorylcholine head and the anionic surfactant. On applying a cyclic potential between 0.6 and 1.0 V, we could polymerize and deposit the dissolved EDOT-PC onto various electrode substrates, including indium tin oxide (ITO), gold and stainless steel (Supplementary Fig. 1). Using atomic force microscopy, we estimated the thickness of the polymer lm prepared from a single scan to be 20 nm, increasing with each subsequent scan.

Interfacial behaviours. The prepared poly(EDOT-PC) lms exhibited water droplet contact angles of less than 8. They displayed excellent resistance towards nonspecic binding of proteins, including bovine serum albumin, bronectin, brinogen,

lysozyme, and fetal bovine serum, as revealed in Fig. 2a. In contrast, poly(EDOT-OH) lms bound strongly to proteins. We also examined the binding of PC12 cells to these polymers. The poly(EDOT-PC) lms exhibited no adhesion (Fig. 2b); their resistance towards the adhesion of both proteins and cells most likely resulted from the highly hydrophilic yet net-neutral properties of the zwitterionic groups on their surfaces59. The poly(EDOT-PC) lms retained their good cell resistance after exposure for 30 days to a medium containing 10% horse serum and 10% FBS, suggesting that lms deposited from the monomer EDOT-PC would be promising for long-term recording applications.

The surfactant electropolymerization method also allowed us to copolymerize EDOT-PC with EDOT-MI in MeCN. Indeed, we could copolymerize these two immiscible monomers over an entire range of EDOT-MI feed compositions (molar percentage within the monomer mixture) from 0 to 100% (Supplementary Fig. 1). The water contact angles of the poly(EDOT-MI-co-EDOT-PC) lms increased almost linearly from 8 to 36.5 on increasing the EDOT-MI feed composition (Fig. 2c). X-ray photoelectron spectroscopy revealed that the binding energy of the N 1s electrons of EDOT-PC (396.3 eV) was higher than that of EDOT-MI (393.8 eV). Because the two N 1s signals overlapped, we used a non-linear least squares tting procedure to accurately calculate the compositions of the copolymer lms (Supplementary Fig. 2). As revealed in Fig. 2d, the measured EDOT-MI compositions in the copolymers were slightly lower than the feed EDOT-MI compositions. Nevertheless, the copolymer composition was almost linearly dependent on the monomer feed composition.

Although poly(EDOT-PC) was hydrophilic, it was very stable in aqueous buffers, even after applying a potential sweep over 1,000 cycles. The electroactivity of the lm decreased slightly, but the protein resistance remained intact, even when the maximum applied potential reached 1.2 V (Fig. 2e and Supplementary Fig. 3). Poly(EDOT-PC) and all copolymer lms were smooth and exhibited similar surface roughness (root mean square roughness (Rrms) ca. 3 nm; Supplementary Fig. 4), as

determined using atomic force microscopy. Instead of a linear relationship, the surface resistance of the copolymer lms

NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 3 & 2014 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523

Contact angle ()

40

0

3,000

30

Protein mass (ng cm2)

20

10

2,000

poly(EDOT-PC)

poly(EDOT-OH)

d

100

80

Measured

EDOT-MI (%)

1,000

60

40

20

0

0 20 40 60 80 100 Feed EDOT-MI (%)

Feed EDOT-MI (%)

0 BSA FN

FNG LYZ FBS

1,000

1,200

Protein mass (ng cm2)

Relative protein mass

Cell number (mm2)

800

500

400

0

0 0.6 0.7 0.8 1.0 Applied potential (Vmax)

0 20 40 60 80 100 Feed EDOT-MI (%)

1.2

0 20 40 60 80 100

Figure 2 | Characterization and interfacial properties of biomimetic PEDOTs. (a) Absorption of various proteins (bovine serum albumin, bronectin (FN), brinogen (FNG), lysozyme (LYZ), FBS) on poly(EDOT-PC) (black) and poly(EDOT-OH) (red). (b) Micrograph image of PC12 cells selectively attached and cultured on functionalized poly(EDOT) lms for 24 h. Poly(EDOT-PC) was selectively deposited onto the upper part of poly(EDOT-OH). (cf) Characterization and surface properties of poly(EDOT-MI-co-EDOT-PC)s prepared with different EDOT-MI feed compositions: (c) contact angles of water droplets; (d) measured compositions of EDOT-MI determined through X-ray photoelectron spectroscopy; (e) enzyme resistance tests of poly(EDOT-PC) after the polymer had been subjected to the applied potential for 1,000 cycles in aqueous solution (legends on the x axis indicate the maximum applied potential); (f) absorption of BSA (black), FN (blue), FNG (red), LYZ (green) and FBS (purple) (the absorbed protein mass relative to the value obtained from pure poly(EDOT-MI) is used as the y axis so that the absorption trends of different proteins can be compared); (g) density of PC12 cells attached to poly(EDOT-MI-co-EDOT-PC)s prepared with different feed compositions. The error bars in the graphs represent s.d. from at least three repeating experiments.

towards the binding of cells and proteins exhibited a sigmoidal dependence on the EDOT-MI feed composition (Fig. 2f,g). When the feed composition of EDOT-MI in the monomer mixture was less than 50%, the electropolymerized lms were highly resistant towards cells and proteins. In contrast, when the EDOT-MI content exceeded 50%, cells and proteins bound strongly to the copolymer lms. The phenomenon observed was similar to the studies on zwitterionic group-tailored self-assembled mono-layers54. Only for the experiments of FBS binding, the maleimide groups on poly(EDOT-MI-co-EDOT-PC)s needed to be blocked by cysteine before the protein resistance test. This was due to the large quantity of free thiol groups on FBS proteins. Therefore, instead of physical absorption, we observed chemical conjugation in quartz crystal microbalance (QCM) experiments without cysteine blocking.

Peptide bioconjugation and controlled adhesion of cells. The peptide Ile-Lys-Val-Ala-Val (IKVAV) is one of the active sites in laminin for neuron adhesion and neurite outgrowth60,61. This peptide ligand has been used extensively to support the adhesion and differentiation of neuronal origin cells, including PC12 cells, Granule cells, Purkinje cells, neural progenitor cells and hippocampal neurons. We achieved bioconjugation through reactions between maleimides and cysteine-terminated experimental (CSSSSIKVAV) and control (CSSSSGKVAV) peptides in phosphate buffer at an optimized pH of 5.6; these

reactions were complete within an hour, as monitored using an in situ QCM (Fig. 3a). In contrast, we detected no bioconjugation in the case of the non-cysteine-capped peptide SSSSIKVAV. The density of ligands grafted on the polymer lms could be controlled by varying the composition of the copolymers; it reached B3,000 ng cm 2 when the feed composition of

EDOT-MI was greater than 50% (Fig. 3b). PC12 cells are commonly employed as a model system for studies of neuronal development and function; they are also a robust model cell line for evaluating the performance of various platforms for electrically stimulated neurite outgrowth24,2730. To compare the performance of our materials with that of other reported platforms, we also adopted PC12 cells in this study to investigate neuron adhesion and differentiation. The introduction of IKVAV promoted PC12 cell binding on the originally bioinert poly(EDOT-MI-co-EDOT-PC), the result of specic ligand receptor interactions. The density of attached cells increased rapidly on increasing the content of EDOT-MI to 10%, becoming saturated thereafter (Fig. 3c). Control experiments with GKVAV revealed no attachment of PC12 cells. All of the PC12 cells were adhered and well extended on the IKVAV-grafted copolymer lms when the feed content of EDOT-MI was greater than 10%.

In earlier studies of ECPs for neural engineering, most research was focused on the performance of unfunctionalized ECP. In vivo applications of these materials may suffer, however, from the unwanted nonspecic binding of cells and biomacromolecules, leading to severe insulating scar formation and failure of electrical

4 NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications & 2014 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523 ARTICLE

4,000

1,000

1,600

3,000

1,200

Mass (ng cm2)

800

Normalized cell density

2,000

Peptide injection

400

0

0

0 2,000 4,000 0

10 20 30 40 50

0 10 20 30 40 50

PC12 NIH3T3

Time (sec)

Feed EDOT-MI (%)

Cell number (mm2)

Feed EDOT-MI (%)

24 h 48 h 120 h

24 h 48 h 120 h

Figure 3 | Ligand conjugation and controlled cellular behaviour on biomimetic PEDOTs. (a) In situ monitoring of CSSSSIKVAV (red), CSSSSGKVAV (blue) and SSSSIKVAV (black) conjugation on poly(EDOT-MI-co-EDOT-PC) lms polymerized from a monomer solution containing 5 mM EDOT-MI and 5 mM EDOT-PC. (b) Conjugation of CSSSSIKVAV (red) and CSSSSGKVAV (blue) on poly(EDOT-MI-co-EDOT-PC) lms prepared with various EDOT-MI feed compositions. (c) Density of PC12 cells attached to poly(EDOT-MI-co-EDOT-PC) lms, prepared with different feed compositions, after conjugation with the ligands CSSSSIKVAV (red) and CSSSSGKVAV (blue). The error bars in the graphs represent s.d. from at least three repeating experiments. (d) Selective adhesion of PC12 and NIH3T3 cells on a polystyrene culture dish (black), poly(EDOT-OH) (red) and a biomimetic PEDOT (prepared from 3 mM EDOT-MI and 7 mM EDOT-PC, conjugation with IKVAV; blue) after cell seeding for 1 day. (e) Proliferation and (f) differentiation (in the presence of NGF) of PC12 cells attached to CSSSSIKVAV-conjugated poly(EDOT-MI-co-EDOT-PC) lms after 24, 48 and 120 h. The insets are enlarged micrograph images of cultured cells to conrm the cellular morphologies. The length of the scale bars in the micrograph images is 200 mm.

communication with living tissues. Previous investigations of non-conductive materials have concluded that the presence of phosphorylcholine side chains can prevent microphages from recognizing articial implants as foreign bodies, leading to diminution/eradication of the inammatory response55. We expected the biomimetic PEDOTs developed herein to interact specically with targeted cells and prevent nonspecic binding. A standard cell culture dish and poly(EDOT-OH) revealed strong adhesion to both PC12 cells and NIH3T3 broblasts (Fig. 3d). In contrast, the biomimetic PEDOT lms presenting IKVAV ligands remained resistant to NIH3T3 cells (Supplementary Fig. 6), binding only to the PC12 cells. This behaviour resulted from the two principles we employed in the molecular design: the introduction of phosphorylcholine side chains to prevent nonspecic interactions and the presence of the conjugated IKVAV ligand for specic interactions with PC12 cells, but not with NIH3T3 broblasts. To the best of our knowledge, this paper is the rst to demonstrate neuron-targeting conducting polymers that function without nonspecic interactionsa highly attractive feature for in vivo applications because of the low host inammatory response towards the conducting polymers and the greater long-term performance of related materials and devices after implantation.

After the cells had attached to the surface of biomimetic PEDOTs, they proliferated in the presence of serum proteins (Fig. 3e), with the polymers sustaining culturing for more than 20 days. The cell viability and proliferation were similar to those when cultured on polylysine-coated dishes. PC12 cells also underwent normal differentiation in the presence of nerve growth factor (Fig. 3f). In control experiments performed using unfunctionalized PEDOT lms, most of the cells did not spread well and were presented in smaller, circular shapes. The results were even worse on the poly(EDOT-OH) lms. One major concern after chemical modication of ECPs is decreased conductivity because of distortion of their backbones, thereby diminishing orbital overlap and weakening intrachain conductivity. The introduction of insulating side chains to improve the solubility can also lead to the presence of insulating domains in bulk materials, again resulting in poor interchain conductivity. Accordingly, the electrical impedance would increase and the electrical communication would worsen. We suspected, however, that the introduction of a zwitterionic phosphorylcholine unit onto the EDOT monomer would not only interrupt the nonspecic interactions but also maintain the impedance of the PEDOT materials for electron/ion injection, due to its higher ionic conductivity48,49.

NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 5 & 2014 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523

40

30

Pulse generator

* *

Median neurite length (m)

NGF secretion (pg per 106 cells)

30

No stimulation

20 mV

40 mV

60 mV

20

* P < 0.001

20

PEDOTs

Probability

ITO

Glass

10

10

Applied voltage

0 100 150 200 250

50

0 PEDOT

Biomimetic PEDOT

0 No stimulation

20 mV 40 mV 60 mV

0.1 ms

3.8 ms

Neurite length (m)

Figure 4 | Electrically stimulated cell behaviour on biomimetic PEDOTs. (a) Schematic representation of the device used for cell growth with applied electrical stimulation. (b) Illustration of the electrical pulse used. (ce) Microscopy images of differentiated PC12 cells cultured in NGF-supplemented medium for 5 days on (c) a PEDOT lm, (d) a biomimetic PEDOT lm (prepared from 3 mM EDOT-MI and 7 mM EDOT-PC, conjugation with IKVAV), and (e) the biomimetic PEDOT lm with applied pulsed electrical stimulation at an amplitude of 60 mV. The insets are enlarged micrograph images of cultured cells to conrm the cellular morphologies. The length of the scale bars in the micrograph images is 200 mm. (fh) Corresponding neurite length distributions of (ce). (i) Median neurite length of PC12 cells on PEDOT and biomimetic PEDOT in the absence and presence of applied pulsed electrical stimulation at amplitudes of 20, 40 and 60 mV. (j) NGF secretion from primary Schwann cells cultured on biomimetic PEDOTs (prepared from 3 mM EDOT-MI and 7 mM EDOT-PC, conjugation with RGD) in the absence and presence of applied pulsed electrical stimulation at amplitudes of 20, 40 and 60 mV.

As revealed in Supplementary Fig. 5, the impedance of poly(EDOT-MI-co-EDOT-PC) was even lower than that of the unfunctionalized PEDOT lm, and almost one order of magnitude lower than that of a gold lm in the low frequency range. In general, the impedance could also be affected by the surface morphology of electrodes because the rougher surface with larger surface area allowed higher rate of charge injections. Therefore, rougher surfaces would result in lower impedance. As shown in Supplementary Fig. 4, both unfunctionalized PEDOT and poly(EDOT-MI-co-EDOT-PC) lms displayed surface Rrms of less than 10 nm. Actually, the

PEDOT lm showed larger Rrms than the poly(EDOT-MI-co-EDOT-PC) lm. However, its impedance was higher, thereby excluding the difference of surface area as the main factor for the low impedance of poly(EDOT-MI-co-EDOT-PC) lm. After the conjugation of insulating peptide (IKVAV) on poly(EDOT-MI-co-EDOT-PC), the impedance raised slightly but was still comparable to that of PEDOT. This low impedance of biomimetic PEDOT would ensure efcient delivery or recording of electrical signals.

Integration of biochemical and electrical stimulations. The most attractive feature of ECP-based materials over traditional polymer- or biopolymer-based materials is their ability to allow electrical stimulation of adhered cells and tissues. Conventional ECPs are, however, unlikely to possess the stability and biocompatibility required to sustain long-term electrical stimulation for tissue regeneration and function recovery after implantation. As a result of their designed ligandreceptor interactions and decreased nonspecic physical absorption of

cells, we suspected that the biological and electrical stability of our biomimetic PEDOTs would be much greater than those of PEDOTs that rely on physical absorption, doping or afnity binding18. We employed a home-designed cell culturing device to apply electrical stimulation during the culturing of the cells (Fig. 4a). We electrodeposited the biomimetic PEDOT lms onto an ITO-coated glass substrate featuring an insulating gap between the fabricated pairs of transparent electrodes. After the PC12 cells had been seeded onto the substrate under conditions to differentiate, we applied a biphasic electrical pulse (Fig. 4b) to the electrodes to stimulate the cells.

Our rst observation was that neurite outgrowth of PC12 cells was greatly promoted on the biomimetic PEDOTs. Because the neurite length displayed non-Gaussian distribution, following the previous studies24,31, we used median neurite length as the numerical indicator to evaluate and compare the experimental results. In a control experiment performed on PEDOT (Fig. 4c), the PC12 cells possessed a median neurite length of 15.9 mm after being differentiated in the presence of nerve growth factor for 5 days (Fig. 4f,i); some of these cells were not well spread and had a more circular shape. Moreover, the condition of the cells was even worse on the poly(EDOT-OH) lms. Compared with the cells differentiated on PEDOT, Fig. 4d reveals that the PC12 cells adhered and spread much better on the biomimetic PEDOT [IKVAV-conjugated poly(EDOT-MI-co-EDOT-PC)]; the median neurite length increased from 48% to 23.3 mm under the same conditions (cf. Fig. 4g,i). The presence of the IKVAV moieties not only ensured specic attachment of the PC12 cells but also stimulated the neurite outgrowth60,61.

Greater than 99% of the PC12 cells remained viable after we had applied pulsed electrical stimulation at an amplitude of

6 NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications & 2014 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523 ARTICLE

60 mV for 8 h per day and 5 days in a row (Fig. 4e). This stimulation time was signicantly longer than those reported from most previously conducted cell-based electrical stimulation experiments20,24,2730. In contrast, greater than 40% of the cells detached from unfunctionalized PEDOTs after only 1 day of electrical stimulation at an even lower voltage (20 mV). We observed substantial increases in neurite outgrowth on the biomimetic PEDOTs when the peak voltage was set at 20, 40 or 60 mV (Fig. 4i). The median neurite length was greatest at 60 mV, without any effect on cell viability. After we had stimulated the PC12 cells for 5 days, it was clearly observed that more longer neurites were formed. After electrical stimulation, the median neurite length reached 35.7 mm, corresponding to a 124%

enhancement of original value (15.9 mm) on PEDOT (cf. Fig. 4h,i). Comparison of cumulative distribution plots of neurite length (Supplementary Fig. 7) also revealed similar conclusion because greater number of long neurites were presented. This increase is signicantly greater than not only the values (2060%) typically reported on hybrid and functionalized conducting organic materials20,2730 but also the largest increase (90%) previously reported on polypyrrole24. We attribute this behaviour to the integrated stimulation of surface biochemical ligands and applied electrical pulses.

To demonstrate that our approach of preparing biomimetic PEDOT could also be applied to other cells as an integrated platform for biochemical and electrical stimulation, we turned our focus to primary Schwann cells (glial cells that function to support neurons in the peripheral nervous system). These cells play a key role in nerve regeneration by secreting neurotrophic factors that help the axon sprouts grow towards the injured neurons62. Several reports demonstrated that the secretion/expression of both brain-derived neurotrophic factor and neuron growth factor (NGF) were elevated on electrical stimulation6365. Similar to the situation described above, our poly(EDOT-MI-co-EDOT-PC) lms were inert towards the Schwann cells in the absence of attached ligands. On conjugation of the peptide GRGDSP, however, the Schwann cells adhered specically to the lms. We monitored the secretion of NGF in the absence of electrical stimulation and in the presence of the same electrical pulses as described above (that is, amplitudes of 20, 40 and 60 mV). Figure 4j reveals that NGF secretion from the Schwann cells was enhanced after electrical stimulation at amplitudes of 40 and 60 mV, relative to that from the control experiment performed without electrical stimulation. When applying a pulse having a peak voltage of 60 mV, the NGF secretion reached a level of 23.19 pg per 106 cellsan enhancement of 165% when compared with the original NGF secretion without stimulation (8.77 pg per 106 cells). When integrating biochemical and electrical stimulation, such biomimetic PEDOTs might allow rapid nerve regeneration after device implantation.

DiscussionIn a search for materials that would allow bioelectronic devices to interface with nerve cells and provide stable, efcient and long-term electrical communication, we have developed membrane-biomimicking conducting polymers based on EDOT. We synthesized these new polymer lms from a pair of monomers: a zwitterionic phosphorylcholine-functionalized EDOT (EDOTPC) and a maleimide-functionalized EDOT (EDOT-MI). These lms are easy to fabricate through a unique surfactant-assisted polymerization; their compositions can be tuned simply by varying the ratio of monomers in the initial mixture. These biomimicking PEDOTs display high electrical/ionic conductivities, enabling efcient electrical communication at cellmaterial interfaces. They also exhibit high resistance towards the nonspecic binding of enzymes and cells, allowing them to be

functional in aqueous buffers for extended periods of time and promising to diminish immunogenic responses. In addition, selective binding of desired cells can be achieved to ensure intimate electrical interfacing through specic ligandreceptor interactions (we demonstrate herein a unique example of a specic neuron-targeting conducting polymer). Finally, the biomimetic PEDOTs display low impedance in the low frequency range, ideal for biological applications. The combination of these features enables two desirable material characteristics. The rst is stable binding and electrical communication between the biomimetic PEDOTs and their attached neural cells. As a result, these cells can be electrically stimulated for 8 h a day for 5 days in a row without any observed cell detachment and death. We suspect that electrical stimulation can be extended even further. The second characteristic is that the ligands presented on the surface also provide biochemical stimulation to allow differentiation of the attached cells. Accordingly, this material integrates both biochemical and electrical stimulation.

Taking advantage of all of these attractive features, we achieved a 124% enhancementsignicantly greater than the 2090% enhancements previously reportedin the median neurite length of differentiated PC12 cells on electrical stimulation on the ECPs. Moreover, we have demonstrated enhanced NGF secretion by 165% from primary Schwann cells on similar electrical stimulation. If these biomimetic PEDOT materials were to be integrated with implanted bioelectronic devices, these features would ensure intimate electrical communication with targeted nerve tissues and efcient delivery of electrical signals, thereby enabling long-term electrical interfacing with tissues. The application of this approach towards biomimetic conducting copolymers is not be limited merely to the eld of neural interfacing; it can be extended further through specically targeted ligandreceptor interactions and cellelectronics interfaces. The features of these polymers are critical and desired for in vivo applications of bioelectronic devices. The stability and devicetissue electrical communication will be ensured by preventing severe immunogenic responses and formation of insulating scars. Together with our collaborating researchers, we are now investigating the promising applications of these materials for nerve regeneration and in neuroprosthetic devices and biosensors.

Methods

Synthesis of materials and measurements. EDOT-OH was purchased from a custom-synthesis company, where it had been prepared following procedures previously reported66,67. EDOT-COOH was synthesized following procedures previously reported68,69. 2-Maleimidoethylamine hydrochloride and 1-ethyl-3-(3-dimethyaminopropyl)-carbodiimide hydrochloride were purchased from Astatech and Tokyo Chemical Industry, respectively. The photoresist (5060% TCIR-ZR9000PB in propylene glycol monomethyl ether acetate) and developer(2.38% tetramethylammonium hydroxide in H2O) were purchased from Tokyo Ohka Kogyo and Tama Chemicals, respectively. All materials for cell culturing were purchased from Invitrogen. All other chemicals were purchased either from Sigma-Aldrich or Wako Pure Chemical Industries. CH2Cl2 and tetrahydrofuran were dried and puried using a PureSolv MD 5 Solvent Purication System (Innovative Technology); all other chemicals were of reagent grade and used as received. 1H and 13C NMR spectra were recorded at 25 C using a Varian 500 NMR spectrometer operated at 500 and 125 MHz, respectively; chemical shifts are reported relative to tetramethylsilane; the signal of the residual non-deuterated solvent was taken as the secondary reference.

EDOT-PC. COP (1.65 g, 11.6 mmol) was added slowly to a solution of EDOT-OH(2.00 g, 11.6 mmol) in dry tetrahydrofuran (30 ml) and triethylamine (20 ml) at

29 C while stirring under a N2 atmosphere. After maintaining the temperature at 20 to 30 C for 3 h, the mixture was heated slowly to 25 C and then stirred

for further 3 h. The precipitate (triethylamine hydrochloride) was ltered off and then the ltrate was concentrated in vacuo to provide (2-chloro-2-oxo-1,3,2-dioxaphospholoyloxy)-3,4-EDOT (EDOT-COP), quantitatively, as light yellow liquid. Trimethylamine (2.67 g, 4.52 mmol) was added rapidly to a solution of EDOT-COP (3.14 g, 11.3 mmol) in MeCN (10 ml) in a 100 ml pressure vesselat 29 C. After sealing, the pressure vessel was heated at 60 C for 16 h.

NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 7 & 2014 Macmillan Publishers Limited. All rights reserved.

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523

The formation of product was monitored by thin layer chromatography and observed by ultraviolet/visible light (365 nm wavelength). The products retardation factor was 0.14 using a mixed solvent of EtOAc/MeOH/H2O/MeCN (3/1/1/1).

The ask was cooled back to 29 C, causing a light yellow viscous liquid to

precipitate. This precipitate was ltered off and puried chromatographically (SiO2;

EtOAc/MeOH/H2O/MeCN) to give the yellow solid 1 (3.30 g, 9.78 mmol, 84.3% isolated yield). 1H NMR (500 MHz, D2O): 6.51 (s, 2 H), 4.464.43 (m, 1 H),4.314.24 (m, 3 H), 4.164.06 (m, 3 H), 3.653.56 (m, 2 H), 3.19 (s, 9 H) p.p.m. 13C NMR (125 MHz, D2O): 140.55, 140.38, 100.46, 72.74, 65.94, 65.30, 63.70, 59.41,53.92 p.p.m. High resolution mass spectrometry (FAB) [M H] calcd for

[C12H20O6NPS H] : m/z 338.0827; found 338.0844.

EDOT-MI. 2-Maleimidoethylamine hydrochloride (0.42 g, 2.39 mmol) and N,N-diisopropylethylamine (0.49 ml, 2.39 mmol) were added sequentially to a solution of EDOT-COOH (0.500 g, 2.17 mmol) and O-(7-azabenzotriazol-1-yl)-N,N,,-tetramethyluronium hexauorophosphate (0.91 g, 2.39 mmol) in dry dimethylformamide (15 ml) under an N2 atmosphere at 0 C. The formation of product was monitored by thin layer chromatography and observed by ultraviolt/visible light (365 nm wavelength). The products retardation factor was 0.33 using a mixed solvent of EtOAc/hexane (2/1). After stirring for 6 h at room temperature, the mixture was diluted with EtOAc (100 ml), washed with brine (3 100 ml), dried

(MgSO4), ltered and concentrated under reduced pressure. Chromatographic purication (SiO2; EtOAc/hexane gradient) afforded the white solid 2 (0.72 g,2.04 mmol, 85% isolated yield). 1H NMR (500 MHz, DMSO-d6): 7.87 (t, J 6.0 Hz,

1 H), 6.97 (s, 2 H), 6.57 (s, 2 H), 4.354.31 (m, 1 H), 4.27 (dd, J 11.5, 2.0 Hz, 1 H),

4.02 (dd, J 11.5, 7.5 Hz, 1 H), 3.83 (s, 2 H), 3.653.58 (m, 2 H), 3.48 (t, J 8.3 Hz,

2 H), 3.23 (q, J 6.1 Hz, 2 H) p.p.m. 13C NMR (125 Hz, DMSO-d6): 171.51, 169.60,

141.76, 141.70, 134.93, 100.19, 100.17, 72.67, 70.68, 69.61, 65.78, 40.46, 40.30,40.13, 39.96, 39.80, 39.63, 39.46, 37.47, 37.20 p.p.m. High resolution mass spectrometry (FAB) [M H] calcd for [C15H17N2O6S H] : m/z 353.08073;

found 353.08189.

Electropolymerization of EDOT and electrochemical analysis. Electrochemical experiments were performed using an Autolab PGSTAT128N potentiostat (Metrohm Autolab) and a three-electrode electrochemical cell, with a Pt electrode as the counter electrode and an Ag/AgNO3 electrode (0.01 M AgNO3 and 0.1 M

Bu4NPF6 in MeCN) as the reference electrode. Each measurement was calibrated using a standard ferrocene/ferrocenium redox system. EDOT-PC is highly hydrophilic, but could be dissolved in organic electrolytes with the aid of the surfactant DSS. EDOT-PC could be electropolymerized onto conducting substrates as thin lms under electrooxidation. If not stated otherwise, EDOT derivatives were electropolymerized or copolymerized on conducting substrates from 0.01 M solutions in MeCN containing 0.05 M DSS and 0.1 M LiClO4 on applying cyclic potential scans. Electrochemical impedance spectroscopy (EIS) was performed using a sinusoidal excitation signal with an excitation amplitude of 10 mV at 50 frequencies logarithmically spaced from 10 kHz to 1 Hz. The conducting polymer lms for measurements were coated on fresh Au substrates (area: 1 cm2). Before recording EIS spectra, samples were conditioned in PBS buffer at 0.23 V for60 s. EIS was registered at 25 C in the PBS buffer with 10 mM [Fe(CN)6]3 /4

(1:1, mol/mol) as the redox couple.

QCM measurements. QCM-D measurements were performed at 25 C on a Q-Sense AB system (Biolin Scientic) to monitor in situ the interactions of bio-molecules with the functionalized conducting polymer substrates. The conducting polymers were electrochemically deposited on the surface of a QSX 301 sensor crystal (Biolin Scientic) and then placed in the measurement chamber. Solutions of the biomolecules were delivered continuously to the measurement chamber at a ow rate of 20 ml min 1, pumping with an Ismatec ISM597D pump. On interaction of the matter in solution with the substrate on the sensor crystal, the changes in the resonance frequency of the sensor (Df), which is related to the attached mass, were recorded at a resolution of less than 1 s. If necessary, the pump was stopped for a few seconds to change the sample solutions without disturbing the QCM-D signal. The resonance frequencies were measured simultaneously at 5 MHz and its ve harmonics (15, 25, 35, 45, 55 and 65 MHz). If not stated otherwise, changes in frequency of the third overtone (n 3; that is, 15 MHz) are presented.

Cell culture with in vitro electrical stimulation. Rat pheochromocytoma (PC12) and NIH3T3 cells were obtained from the RIKEN Cell Bank. Primary rat Schwann cells were purchased from ScienCell Research Laboratories. Following typical procedures for cell differentiation, PC12 cells were seeded at a density of 1 104/cm2 onto EDOT polymer thin lms deposited on ITO glass substrates

assembled in a homemade culture chamber (Fig. 4a) and then incubated for 12 h to permit attachment and spreading before initiating electrical stimulation. The ITO substrate was separate into two equal parts by a 400-mm insulating linear gap (fabricated through conned acid etching). Charge-balanced biphasic electrical stimulation at 250 Hz (Fig. 4b) was produced using a B2912A precision source/ measure unit (Agilent); two parts of the EDOT polymer-coated ITO substrates served as electrodes to release electrical signals to the cells. The major advantage of the biphasic electrical stimulation was that it could maintain charge balance while

minimizing cell damage. After the initial 12 h of incubation, the PC12 cells were subjected to electrical stimulation for more than 5 days (8 h per day). The amplitude of the biphasic pulse was 20, 40 or 60 mV. The differentiation results for PC12 cells subjected to a 100-mV pulse for 5 days are not included because the viability of the PC12 cells was highly decreased in this case. PC12 cells plated on the same PEDOT thin lms, but not subjected to any electrical stimulation, served as controls; cells grown on unfunctionalized EDOT polymer thin lms, but not subjected to any electrical stimulus, served as additional controls. The morphological features of all cells were examined every 24 h. Primary rat Schwann cells were seeded at a density of 5 103 cm 2 on the polymer substrates. The settings,

programs and parameters for their electrical stimulation were the same as those adopted for the PC12 cells. The Schwann cells were cultured for 72 h and then they were subjected to the electrical pulse for more than 3 days (8 h every day). Schwann cells plated on the same PEDOT thin lms, but not subjected to any electrical stimulation, served as controls. The culture medium was refreshed every 24 h. After 3 days of electrical stimulation, the culture medium was accumulated for detection of NGF.

Detection of NGF secretion. Secretion of NGF by the Schwann cells was determined using a two-site ELISA assay (NGF Emax Immunoassay System, Promega). Experiments were performed as instructed by the technical bulletin, using the supernatant of the Schwann cells. The absorbance of each sample after colour development was measured using a Wallac Victor 1420 Multilabel Counter (PerkinElmer). A one-way analysis of variance was used to assess statistical differences between NGF samples secreted under different conditions.

References

1. Kozai, T. D. Y. et al. Ultrasmall implantable composite microelectrodes with bioactive surfaces for chronic neural interfaces. Nat. Mater. 11, 10651073 (2012).

2. Grill, W. M., Norman, S. E. & Bellamkonda, R. V. Implanted neural interfaces: biochallenges and engineered solutions. Annu. Rev. Biomed. Eng. 11, 124 (2009).

3. Subbaroyan, J., Martin, D. C. & Kipke, D. R. A nite-element model of the mechanical effects of implantable microelectrodes in the cerebral cortex.J. Neural Eng. 2, 103113 (2005).4. Lee, H., Bellamkonda, R. V., Sun, W. & Levenston, M. E. Biomechanical analysis of silicon microelectrode-induced strain in the brain. J. Neural Eng. 2, 8189 (2005).

5. Rousche, P. J. & Normann, R. A. Chronic recording capability of the Utah Intracortical Electrode Array in cat sensory cortex. J. Neurosci. Methods 82, 115 (1998).

6. Biran, R., Martin, D. C. & Tresco, P. A. Neuronal cell loss accompanies the brain tissue response to chronically implanted silicon microelectrode arrays. Exp. Neurol. 195, 115126 (2005).

7. Ward, M. P., Rajdev, P., Ellison, C. & Irazoqui, P. P. Toward a comparison of microelectrodes for acute and chronic recordings. Brain Res. 1282, 183200 (2009).

8. Cogan, S. F. Neural stimulation and recording electrodes. Annu. Rev. Biomed. Eng. 10, 275309 (2008).

9. Rose, T. L. & Robblee, L. S. Electrical stimulation with Pt electrodes. VIII. Electrochemically safe charge injection limits with 0.2 ms pulses (neuronal application). IEEE Trans. Biomed. Eng. 37, 11181120 (1990).

10. Gawad, S. et al. Substrate arrays of iridium oxide microelectrodes for in vitro neuronal interfacing. Front. Neuroeng. 2, 1 (2009).

11. Green, R. A. et al. Performance of conducting polymer electrodes for stimulating neuroprosthetics. J. Neural Eng. 10, 016009 (2013).

12. Discher, D. E., Janmey, P. & Wang, Y.-L. Tissue cells feel and respond to the stiffness of their substrate. Science 310, 1139 (2005).

13. Mitragotri, S. & Lahann, J. Physical approaches to biomaterial design. Nat. Mater. 8, 1523 (2009).

14. Otero, T. F., Martinez, J. G. & Arias-Pardilla, J. Biomimetic electrochemistry from conducting polymers. A review: articial muscles, smart membranes, smart drug delivery and computer/neuron interfaces. Electrochim. Acta 84, 112128 (2012).

15. Ludwig, K. A., Uram, J. D., Yang, J., Martin, D. C. & Kipke, D. R. Chronic neural recordings using silicon microelectrode arrays electrochemically deposited with a poly(3,4-ethylenedioxythiophene) (PEDOT) lm. J. Neural Eng. 3, 5970 (2006).

16. Cui, X. T. & Zhou, D. D. Poly(3,4-ethylenedioxythiophene) for chronic neural stimulation. IEEE Trans. Neural Syst. Rehabil. Eng. 15, 502508 (2007).

17. Wallace, G. G., Moulton, S. E. & Clark, G. M. Electrode-cellular interface. Science 324, 185186 (2009).

18. Guimard, N. K., Gomez, N. & Schmidt, C. E. Conducting polymers in biomedical engineering. Prog. Polym. Sci. 32, 876921 (2007).

19. Asplund, M., Nyberg, T. & Inganas, O. Electroactive polymers for neural interfaces. Polym. Chem. 1, 13741391 (2010).

20. Ghasemi-Mobarakeh, L. et al. Application of conductive polymers, scaffolds and electrical stimulation for nerve tissue engineering. J. Tissue Eng. Regen. M 5, e17e35 (2011).

8 NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications & 2014 Macmillan Publishers Limited. All rights reserved.

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms5523 ARTICLE

21. Thompson, B. C., Moulton, S. E., Richardson, R. T. & Wallace, G. G. Effect of the dopant anion in polypyrrole on nerve growth and release of a neurotrophic protein. Biomaterials 32, 38223831 (2011).

22. Richardson-Burns, S. M. et al. Polymerization of the conducting polymer poly(3,4-ethylenedioxythiophene) (PEDOT) around living neural cells. Biomaterials 28, 15391552 (2007).

23. Huang, L. et al. Synthesis and characterization of electroactive and biodegradable ABA block copolymer of polylactide and aniline pentamer. Biomaterials 28, 17411751 (2007).

24. Schmidt, C. E., Shastri, V. R., Vacanti, J. P. & Langer, R. Stimulation of neurite outgrowth using an electrically conducting polymer. Proc. Natl Acad. Sci. USA 94, 89488953 (1997).

25. Cui, X. & Martin, D. C. Electrochemical deposition and characterization of poly(3,4-ethylenedioxythiophene) on neural microelectrode arrays. Sensor Actuat. B Chem. 89, 92102 (2003).

26. Nyberg, T., Inganas, O. & Jerregrd, H. Polymer hydrogel microelectrodes for neural communication. Biomed. Microdevices 4, 4352 (2002).

27. Lee, J. Y., Bashur, C. A., Goldstein, A. S. & Schmidt, C. E. Polypyrrole-coated electrospun PLGA nanobers for neural tissue applications. Biomaterials 30, 43254335 (2009).

28. Moroder, P. et al. Material properties and electrical stimulation regimens of polycaprolactone fumarate-polypyrrole scaffolds as potential conductive nerve conduits. Acta Biomater. 7, 944953 (2011).

29. Gomez, N. & Schmidt, C. E. Nerve growth factor-immobilized polypyrrole: Bioactive electrically conducting polymer for enhanced neurite extension.J. Biomed. Mater. Res. A 81A, 135149 (2007).30. Lee, J. Y. et al. Nerve growth factor-immobilized electrically conducting brous scaffolds for potential use in neural engineering applications. IEEE Trans. Nanobioscience 11, 1521 (2012).

31. Liu, X., Yue, Z., Higgins, M. J. & Wallace, G. G. Conducting polymers with immobilised brillar collagen for enhanced neural interfacing. Biomaterials 32, 73097317 (2011).

32. Yamato, H., Ohwa, M. & Wernet, W. Stability of polypyrrole and poly(3,4-ethylenedioxythiophene) for biosensor application. J. Electroanal. Chem. 397, 163170 (1995).

33. Green, R. A., Lovell, N. H. & Poole-Warren, L. A. Cell attachment functionality of bioactive conducting polymers for neural interfaces. Biomaterials 30, 36373644 (2009).

34. Venkatraman, S. et al. in Proceedings of the 4th International IEEE EMBS Conference on Neural Engineering 383386 (Antalya, 2009).

35. Moulton, S. E., Higgins, M. J., Kapsa, R. M. I. & Wallace, G. G. Organic bionics: a new dimension in neural communications. Adv. Funct. Mater. 2, 20032014 (2012).

36. Simon, D. T. et al. Organic electronics for precise delivery of neurotransmitters to modulate mammalian sensory function. Nat. Mater. 8, 742746 (2009).37. Yang, S. Y. et al. Detection of transmitter release from single living cells using conducting polymer microelectrodes. Adv. Mater. 23, H184H188 (2011).

38. Lin, P., Yan, F., Yu, J., Chan, H. L. W. & Yang, M. The application of organic electrochemical transistors in cell-based biosensors. Adv. Mater. 22, 36553660 (2010).

39. Chikar, J. A. et al. The use of a dual PEDOT and RGD-functionalized alginate hydrogel coating to provide sustained drug delivery and improved cochlear implant function. Biomaterials 33, 19821990 (2012).

40. Abidian, M. R., Ludwig, K. A., Marzullo, T. C., Martin, D. C. & Kipke, D. R. Interfacing conducting polymer nanotubes with the central nervous system: chronic neural recording using poly(3,4-ethylenedioxythiophene) nanotubes. Adv. Mater. 21, 37643770 (2009).

41. Harris, A. R. et al. Conducting polymer coated neural recording electrodes.J. Neural Eng. 10, 16004 (2013).42. Asplund, M. et al. Toxicity evaluation of PEDOT/biomolecular composites intended for neural communication electrodes. Biomed. Mater. 4, 045009 (2009).

43. Polikov, V. S., Tresco, P. A. & Reichert, W. M. Response of brain tissue to chronically implanted neural electrodes. J. Neurosci. Meth. 148, 118 (2005).

44. Moxon, K. A. et al. Long-term recordings of multiple, single-neurons for clinical applications: the emerging role of the bioactive microelectrode. Materials 2, 17621794 (2009).

45. Povlich, L. K. et al. Synthesis, copolymerization and peptide-modication of carboxylic acid-functionalized 3,4-ethylenedioxythiophene (EDOTacid) for neural electrode interfaces. Biochim. Biophys. Acta 1830, 42884293 (2012).

46. Cui, X., Wiler, J., Dzaman, M., Altschuler, R. & Martin, D. In vivo studies of polypyrrole/peptide coated neural probes. Biomaterials 24, 777787 (2003).

47. Wadhwa, R., Lagenaur, C. & Cui, X. Electrochemically controlled release of dexamethasone from conducting polymer polypyrrole coated electrode.J. Control Release 110, 531541 (2006).48. Fang, J. et al. Conjugated zwitterionic polyelectrolyte as the charge injection layer for high-performance polymer light-emitting diodes. J. Am. Chem. Soc. 133, 683685 (2011).

49. Cardoso, J., Huanosta, A. & Manero, O. Ionic conductivity studies on salt-polyzwitterion systems. Macromolecules 24, 28902895 (1991).

50. Singer, S. J. & Nicolson, G. L. The uid mosaic model of the structure of cell membranes. Science 175, 720731 (1972).

51. Bangham, A. D. A correlation between surface charge and coagulant action of phospholipids. Nature 192, 11971198 (1961).

52. Zwaal, R. F. A., Comfurius, P. & van Deenen, L. L. M. Membrane asymmetry and blood coagulation. Nature 268, 358360 (1977).

53. Hayward, J. A. & Chapman, D. Biomembrane surfaces as models for polymer design: the potential for haemocompatibility. Biomaterials 5, 135142 (1984).

54. Chen, S., Zheng, J., Li, L. & Jiang, S. Strong resistance of phosphorylcholine self-assembled monolayers to protein adsorption: insights into nonfouling properties of zwitterionic materials. J. Am. Chem. Soc. 127, 1447314478 (2005).

55. Moro, T. et al. Surface grafting of articial joints with a biocompatible polymer for preventing periprosthetic osteolysis. Nat. Mater. 3, 829836 (2004).

56. Holmlin, R. E., Chen, X., Chapman, R. G., Takayama, S. & Whitesides, G. M. Zwitterionic SAMs that resist nonspecic adsorption of protein from aqueous buffer. Langmuir 17, 28412850 (2001).

57. Ishihara, K., Ueda, T. & Nakabayashi, N. Preparation of phospholipid polymers and their properties as polymer hydrogel membranes. Polym. J. 22, 355360 (1990).

58. Gorin, G., Martic, P. A. & Doughty, G. Kinetics of the reaction of N-ethylmaleimide with cysteine and some congeners. Arch. Biochem. Biophys. 115, 593597 (1966).

59. Rana, D. & Matsuura, T. Surface modications for antifouling membranes. Chem. Rev. 110, 24482471 (2010).

60. Tashiro, K. et al. A synthetic peptide containing the IKVAV sequence from the A chain of laminin mediates cell attachment, migration, and neurite outgrowth.J. Biol. Chem. 264, 1617416182 (1989).61. Silva, G. A. et al. Selective differentiation of neural progenitor cells by high-epitope density nanobers. Science 303, 13521355 (2004).

62. Bhatheja, K. & Field, J. Schwann cells: origins and role in axonal maintenance and regeneration. Int. J. Biochem. Cell B 38, 19951999 (2006).

63. Wan, L., Zhang, S., Xia, R. & Ding, W. Short-term low-frequency electrical stimulation enhanced remyelination of injured peripheral nerves by inducing the promyelination effect of brain-derived neurotrophic factor on Schwann cell polarization. J. Neurosci. Res. 88, 25782587 (2010).

64. Huang, J., Ye, Z., Hu, X., Lu, L. & Luo, Z. Electrical stimulation induces calcium-dependent release of NGF from cultured Schwann cells. Glia 58, 622631 (2010).

65. Hunag, J. et al. Electrical regulation of Schwann cells using conductive polypyrrole/chitosan polymers. J. Biomed. Mater. Res. 93A, 164174 (2010).

66. Lima, A., Schottland, P., Sadki, S. & Chevrot, C. Electropolymerization of 3,4-ethylenedioxythiophene and 3,4-ethylenedioxythiophene methanol in the presence of dodecylbenzenesulfonate. Synth. Met. 93, 3341 (1998).

67. Akoudad, S. & Roncali, J. Modication of the electrochemical andelectronic properties of electrogenerated poly(3,4-ethylenedioxythiophene) by hydroxymethyl and oligo(oxyethylene) substituents. Electrochem. Commun. 2, 7276 (2000).

68. Mohamed Ali, E., Kantchev, E. A. B., Yu, H.-h. & Ying, J. Y. Conductivity shift of polyethylenedioxythiophenes (PEDOTs) in aqueous solutions from side-chain charge perturbation. Macromolecules 40, 60256027 (2007).

69. Luo, S.-C. et al. PEDOT nanobiointerfaces: thin, ultrasmooth, and functionalized poly(3,4-ethylenedioxythiophene) lms with in vitro and in vivo biocompatibility. Langmuir. 24, 80718077 (2008).

Acknowledgements

This study was supported by RIKEN and a Grant-in-Aid for Young Scientist (No. 22681016) from JSPS/MEXT, Japan. This study was also supported by Academia Sinica, Taiwan. B.Z. thanks RIKEN for a Special Postdoctoral Researcher Fellowship. We also thank the Research Resources Center (RIKEN Brain Science Institute) for the peptide synthesis.

Author contributions

B.Z. and H.-h.Y. initiated the project and deigned the experiments. B.Z., H.Z., H.-A.L. and Y.Y. synthesized the monomers and polymers. B.Z., S.-C.L. and C.C. designed and fabricated the experimental devices. B.Z. and J.S. conducted the cell experiments. A.N. conducted the XPS experiments. B.Z., S.-C.L. and H.-h.Y. wrote the manuscript. All authors discussed the results and commented on the paper.

Additional information

Supplementary Information accompanies this paper at http://www.nature.com/naturecommunications

Web End =http://www.nature.com/ http://www.nature.com/naturecommunications

Web End =naturecommunications

Competing nancial interests: The authors declare no competing nancial interests.

Reprints and permission information is available online at http://npg.nature.com/reprintsandpermissions/

Web End =http://npg.nature.com/ http://npg.nature.com/reprintsandpermissions/

Web End =reprintsandpermissions/

How to cite this article: Zhu, B. et al. Large enhancement in neurite outgrowth on a cell membrane-mimicking conducting polymer. Nat. Commun. 5:4523 doi: 10.1038/ ncomms5523 (2014).

NATURE COMMUNICATIONS | 5:4523 | DOI: 10.1038/ncomms5523 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 9 & 2014 Macmillan Publishers Limited. All rights reserved.