Goswami et al. AMB Express 2013, 3:16 http://www.amb-express.com/content/3/1/16
ORIGINAL ARTICLE Open Access
An Ecofriendly synthesis of silver nano-bioconjugates by Penicillium citrinum (MTCC9999) and its antimicrobial effect
Achintya Mohan Goswami1,2, Tuhin Subhra Sarkar1 and Sanjay Ghosh1*
Abstract
This report provides for the first time a novel environment friendly extracellular synthesis of stable silver nanobioconjugates (SNBCs) at room temperature at pH 5.0 using Penicillium citrinum MTCC 9999 biomass. The UV-Visible spectral scan of dispersed SNBCs solution showed absorption in the region 340450 nm due to surface plasma resonance (SPR). Typical Transmission Electron Microscopic (TEM) images showed that although two populations were present but most of them were in 2030 nm range. Average zeta potential of SNBCs was 21 mV suggesting some biomolecules capped the nanoparticles imparting a net negative charge over it. FTIR analysis also showed that biomolecules were involved in stabilization. SNBCs showed strong antibacterial activity against both Gram positive (Bacillus subtilis) and Gram negative bacteria (Escherichia coli). SNBCs also showed strong antifungal activity as assessed against Schizosaccharomyces pombe. In the case of E. coli the minimum inhibitory concentrations (MIC) of SNBCs was 4 g/ml while in B. subtilis it was 8 g/ml. In the case of E. coli the minimum bactericidal concentrations (MBC) of SNBCs was 8 g/ml while in B. subtilis it was 32 g/ml. The SNBCs exerted its antibacterial and antifungal activity through generation of reactive oxygen species (ROS) inside the cell.
Keywords: Green synthesis, Penicillium citrinum, Transmission Electron Microscopy (TEM), Zeta potential, Fourier Transformed Infra-Red Spectroscopy (FTIR), Minimum Inhibitory Concentrations (MIC), Minimum Bactericidal Concentrations (MBC), Reactive Oxygen Species (ROS)
Introduction
The field of nanotechnology has got major advances in various aspects of technology from biosensors to medicine (Velev and Kaler 1999; Nie and Emory 1997; Gu et al. 2003; Kim et al. 2008). Various optic based analytical techniques are designed based on the surface plasma resonance (SPR) properties of silver nanomaterials (Lee and EI-Sayed 2006). There is also growing interest in biomedical applications of silver nanoparticles (Sun et al. 2005). But synthesis of nanoparticles requires harsh reducing agents (e.g. sodium borohydride, hydroxyl amine), capping agents (e.g. trioctylphosphine oxide) and organic solvents (e.g. toluene, chloroform) as well as high temperature and pressure (Xie et al. 2007). So the focus is turned on to the environmental friendly synthesis of
nanoparticles, the so called Green Chemistry (Klaus et al. 1999; Raveendran et al. 2003). Complete green synthesis of silver nanoparticles requires environmentally acceptable solvent, eco friendly reducing and capping agents. In all these respects biological approach is more convenient.
A number of biological species has been shown to produce silver nanoparticles either intracellular or cell surface based or extracellular. A study with Pseudo-monas stutzeri AG259, a metal accumulating bacteria have been shown to synthesize silver nanoparticles in the periplasmic space with a size ranging from a few nanometers to 200 nm of different shapes and morphologies (spherical, triangular, truncated triangular) (Klaus et al. 1999). Lactobacillus strains have been shown to synthesize silver nanoparticles and these form clusters on the cell surface (Nair and Pradeep 2002). Vigneshwaran N et al. showed a cell-surface based synthesis of silver nanoparticles with a varying particle size
* Correspondence: mailto:[email protected]
Web End [email protected]
1Department of Biochemistry, University of Calcutta, 35, Ballygunge Circular Road, Kolkata, West Bengal 700 019, IndiaFull list of author information is available at the end of the article
2013 Goswami et al.; licensee Springer. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0
Web End =http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Goswami et al. AMB Express 2013, 3:16 Page 2 of 9 http://www.amb-express.com/content/3/1/16
from 414 nm by Aspergillus flavus (Vigneshwaran et al. 2007a). Extracellular biosynthesis of silver nanoparticles of 525 nm diameter by Aspergillus fumigatus and Penicillium fellutanum has been studied (Bhainsa and DSouza 2006; Kathiresan et al. 2009). Polydisperse silver nanoparticles of 2060 nm diameter are synthesized extracellularly by Alternaria alternata (Monali et al. 2009). Apart from using microorganisms as a factory of synthesizing nanomaterials, soluble starch has been used in the ecofriendly synthesis of silver nanoparticles with a size 2335 nm (Vigneshwaran and Nachane 2006). Spent mushroom substrate (SMS) has also been used as a simple root for the synthesis of silver-protein (core-shell) nanoparticles having average size around 30 nm (Vigneshwaran A and Kathe 2007).
There is also increasing demand for finding antimicrobial agents due to ever increasing bacterial resistance to antibiotics and consequent development of multidrug resistance in bacteria. Recently nanoparticles have been successfully used for the delivery of therapeutic agents (Zhang et al. 2008a), in chronic disease diagnostics (Hong et al. 2008), to reduce bacterial infections in skin and burn wounds (Rai et al. 2009), to prevent bacterial colonization on medical devices and in the food and clothing industries as an antimicrobial agent (Chau et al. 2007; Vigneshwaran et al. 2007b). For centuries, silver is known for its antimicrobial activity against a diverse group of bacteria and has been used for many years as an antimicrobial substance (Castellano et al. 2007). Silver nanoparticles have been shown to have potent antibacterial, antifungal and antiviral activities. Compared with other metals, silver nanoparticles show higher toxicity to microorganisms while exhibiting lower toxicity to mammalian cells (Zhao and Stevens 1998). A large number of researches were carried out to investigate the bactericidal activity of silver nanoparticles. Silver nanoparticles interact with gram-negative bacteria in a size dependent fashion (Sukdeb et al. 2007). It has been suggested that the antibacterial activity is due to silver ions, released from metallic bulk silver or from nanoparticle (NP) surfaces, which interact with the thiol groups in bacterial proteins or interfere with DNA replication (Feng et al. 2000; Wu et al. 2009). It has also been reported that silver ions can affect the respiratory chain in bacteria (Holt and Bard 2005). On the other hand, other authors have suggested that silver nanoparticle toxicity may arise directly from physical processes caused by nano-objects, like disruption of cell membrane and penetration of NPs into the cytoplasm (Xu et al. 2004). So, the scientific debate is still open concerning the mechanism of the antibacterial effect of silver nanoparticles (Sondi and Salopek-Sondi 2004; Dror-Ehre et al. 2009; Zhang et al. 2008b). It was reported that silver nanoparticles stabilized with sodium dodecyl sulfate (SDS) have no antibacterial activity
because the negatively charged SDS interferes with the absorption of microbes to the surface of the nanoparticles or silver ions (Cho et al. 2005). So the application of silver nanoparticles as antimicrobial agent requires appropriate coating of nanoparticle surface to avoid aggregation and to favour solubility in watery environment and attachment of nanoparticle to bacterial cell surface.
Until now, little research has been done on the antimicrobial activity of biologically produced nanosilver and its specific mode of action. The aim of this study was to examine the antimicrobial properties of biogenic silver. In the present work, we report an environment friendly procedure for synthesis of stable silver nano-bioconjugate (SNBC) and its potential application as antimicrobial agent. We prefer to use the term nano-bioconjugate because of the presence of biomolecules on the nanoparticle surface, which are used for further studies without any further chemical modification of nanoparticle surface.
Materials and methods
All chemical reagents were purchased from Sigma (St. Louis, MO, USA) and were of analytical grade. All components for growth media were purchased from Becton Dickinson (Rutherford, NJ, USA).
MicroorganismPenicillium citrinum (strain number MTCC 9999) was isolated in our laboratory from soil, collected from Dhapa situated near Kolkata, West Bengal. The strain was sent for identification to the Institute of Microbial Technology (IMTECH), Chandigarh, India, a centre for microbial strain identification and maintenance. The strain was identified as Penicillium citrinum by them and it was deposited in the IMTECH strain bank. The strain was subcultured on potato dextrose agar (PDA).
Biomass productionThe fungus (P. citrinum MTCC 9999) was grown aerobically in liquid media containing (g/l) KH2PO4: 7.0, K2H
PO4:2.0, MgSO4, 7H2O:0.1, (NH4)2SO4:1.0, yeast extract:0.6, glucose 10.0. The conical flask containing the above sterilized media was inoculated with fungal spores and incubated at orbital shaker at 29C for 84 hours at 140 rpm. Then the biomass was harvested by sieving through a plastic filter and washed several times with Milli-Q deionized water to remove any traces of media components. Biomass was placed in Mili Q water to collect the fungal cell surface biomolecule or any secretory materials which could have reducing power for the biological synthesis of nanoparticles. Typically 20 g biomass (fresh weight) was dispersed in 200 ml of deionized Milli-Q water. It was then kept for 72 hours at 25C at 120 rpm in an orbital shaker. After the incubation, cell filtrate was obtained by passing it through Whatman filter paper no1 for the synthesis of silver nano-
Goswami et al. AMB Express 2013, 3:16 Page 3 of 9 http://www.amb-express.com/content/3/1/16
bioconjugates by extracellular filtrate. Each experiment was repeated thrice using freshly grown culture of P. citrinum in PDA.
Synthesis of silver nano-bioconjugates by extracellular filtrateSilver nitrate (AgNO3) at a final concentration of 0.5 mM was added from a higher stock of 200 mM to the cell filtrate and agitated at 100 rpm in dark at 25C. Control set (only cell filtrate) without AgNO3 was also run side by side.
Another negative control containing only 0.5 mM AgNO3 were maintained under the same conditions. Silver nanobioconjugates were characterized by visual inspection. Sample was withdrawn at various time intervals for recording of UV-Visible spectra. UV-Visible spectra were recorded spectrophotometer (V-530) (JASCO Analytical Instruments, 28600 Marys Court, Easton, MD 21601).
Characterization of silver nano-bioconjugatesDynamic light scattering (DLS) analysis was performed in Zetasizer (MALVERAN Nano Series, Malvern Instruments Ltd, Enigma Business Park, Grovewood Road, Malvern, Worcestershire, UK. WR14 1XZ), to measure the hydrodynamic diameter and zeta potential of SNBCs.
Transmission electron microscopic (TEM) measurement The samples for transmission electron microscopy (TEM) analysis were prepared by drop-casting the SNBCs solution on a carbon-coated copper TEM grid. Before casting to the grid the SNBCs solution was centrifuged at 10000 rpm for 5 minutes and the isolated SNBCs were dispersed in 100 l double distilled water and sonicated in a bath sonicator for 15 minutes. The TEM images were recorded on a high resolution electron microscope (HRTEM: JEOL JEM 2010) operating at an accelerating voltage of 200 kV. Fast Fourier transform (FFT) images were recorded with built-in software for the FFT algorithm for image processing in HRTEM: JEOL JEM 2010 instrument.
Fourier transformed infra red spectroscopy (FTIR)
For FTIR spectrum analysis the SNBCs were centrifuged at 10,000 rpm for 10 minutes to remove free proteins or other compounds present in the solution. The SNBCs then resuspended in double distilled water and again centrifuged. The process was repeated for three times and finally the centrifuged part containing SNBCs were redispersed in double distilled water and subjected to FTIR spectroscopy.
Antimicrobial activity of silver nano-bioconjugates (SNBCs)
Antimicrobial activities of SNBCs were assayed by cup-plate method. Antimicrobial activity was assayed against following Gram positive bacteria Bacillus subtilis ATCC 6633, and Gram negative bacteria Escherichia coli ATCC
8739 and fungus Schizosaccharomyces pombe ATCC 24843. Zone of inhibition was determined by measuring the diameter of bacterial clearance after 24 hour. Minimum inhibitory concentrations (MIC) and minimal bactericidal concentration (MBC) of the SNBCs were determined following the guidelines of National Committee for Clinical Laboratory Standards (NCCLS, Approved standards M7A4 1997). Colony-forming unit (CFU) is an estimate of viable bacterial and fungal (yeast) growth measurement. The Spread Plate technique was used to determine the CFU. Bacterial suspensions were diluted in sterile Muller Hington Broth (MHB) to obtain a final inoculum of 106 CFU/ ml. The concentrations of SNBCs tested were 1, 2, 4, 8, 16, 32, 64 g/ml. The samples were then incubated at 37C at 140 rpm for 24 hours. We have also used a control set where P. citrinum biomass was placed in Mili-Q water under similar experimental condition like the silver nanobioconjugate production. Minimum inhibitory concentration was determined using the control fungual ell exudates, control 0.5 mM silver nitrate as well as the silver nanobioconjugates.
After incubation, minimum inhibitory concentrations (MIC) were read visually; all samples were plated to nutrient agar and incubated. The minimal bactericidal concentration (MBC) was defined as a 99.9% reduction in CFU from the starting inoculum after 24 h incubation interval. The minimal fungicidal concentration (MFC) was defined as a 99.9% reduction in CFU from the starting inoculum after 24 h incubation interval. Fungal strains of S. pombe were grown up in YES medium (0.5% yeast extract, 3% dextrose with proper supplements) at 32C.
Fluorescence imaging of reactive oxygen species (ROS) productionRadical production was quantified by the addition of the non-fluorescent precursor molecule 20, 70 dichlorodihydrofluorescein diacetate (DCFDA). In the presence of ROS, DCFDA is oxidized to a fluorescent molecule. Bacterial cells were grown in MHB up to 0.24 O.D. at 590 nm. Fungal strains of S. pombe were grown up in YES media up to 0.4 OD at 590 nm. The cells were then centrifuged at 5000 rpm for 5 minutes and cell pellet is collected and dispersed in 50 mM potassium phosphate buffer. And cells were washed to remove media. The cells were then again re-dispersed in 50 mM potassium phosphate buffer at a final cell O.D. of 0.5 at 600 nm. The cells were then treated with SNBCs at a final concentration of 40 g/ml for 1 hour and 2 hour. After treatment DCFDA was added to the cells at a final concentration of 10 M.
Results
Extracellular filtrate (pH 5.0) collected from P. citrinum was able to reduce silver nitrate (0.5 mM) to form silver nano-bioconjugates (SNBCs) resulting in the appearance
Goswami et al. AMB Express 2013, 3:16 Page 4 of 9 http://www.amb-express.com/content/3/1/16
Figure 1 UV-visible spectral scan of SNBCs by bio-reduction of silver nitrate in aqueous solution were recorded at various time points viz. 24 hours, 48 hours, 72 hours and 110 hours in Jasco UV-Visible spectrophotometer (V-530) operated at a resolution of 1 nm in absorption mode.
Figure 2 Characterization of SNBCs by TEM. (a) Typical TEM image of SNBCs. (b) A magnified TEM image. (c) HRTEM image of SNBCs. (d) SAED pattern of SNBCs which were indexed according to (111), (200), (220), and (311) reflections of fcc silver on the basis of their d-spacings of2.47 A0, 2.13A0, 1.49 A0, and 1.27 A0.
Goswami et al. AMB Express 2013, 3:16 Page 5 of 9 http://www.amb-express.com/content/3/1/16
Figure 3 SDS-PAGE profile of extracellular filtrate. 20 g sample protein was loaded in the well and was separated by 10% SDS-PAGE.
of the brown color indicating the presence of colloidal silver particles in SNBCs (Burda et al. 2005). However, no change in colour was observed in control sets (Additional file 1 Online Resource 1).
A time course study was conducted to follow the synthesis of SNBCs (Figure 1) by the extracellular filtrate of pH 5.0. Similar study was conducted with extracellular filtrate of pH 3.0, pH 7.0 and pH 9.0 (Data not shown). All the conditions at different pH generated SPR signal in the region 340450 nm of SNBCs by UV-visible spectroscopy. An increase in absorbance in the region 340 450 nm with time indicated the synthesis of SNBCs.
SNBCs were analyzed by Dynamic Light Scattering to measure hydrodynamic diameter immediately after synthesis (Additional file 2 Online Resource 2). Interestingly, SNBCs synthesized by extracellular filtrate of pH 5.0 showed a single population whose hydrodynamic diameter was centered on approximately 2040 nm. As in dynamic light scattering small particles could be masked by the large particles, so the Z average was 76.42 6.12 nm. SNBCs were further analyzed by TEM to understand the architecture, size and selected area electron diffraction (SAED) pattern. A typical TEM image of SNBCs (Figure 2a, 2b) revealed the presence of maximum number of spherical SNBCs. The average diameter of 281 particles measured in TEM was 9.46 6.45 nm. A high resolution TEM
(HRTEM) image of SNBCs synthesized at pH 5.0 (Figure 2c) showed the well resolved interference fringe patterns separated by 0.24 nm which corresponded well to the spacing between (111) plane of fcc silver crystal (JCPDS. No.01-087-0597). The patterns of SAED (Figure 2d) were indexed according to (111), (200), (220), and (311) reflections of fcc silver crystal on the basis of their d-spacings of 2.47 A, 2.13A, 1.49 A, and 1.27 A. The TEM, HRTEM and SAED pattern of SNBCs synthesized at pH 3.0, pH 7.0 and pH 9.0 showed similar pattern as obtained in SNBCs synthesized at pH 5.0 (Additional file 3 Online Resource 3) However, there were distinct differences in their hydrodynamic diameter and zeta potential values.
The zeta potential of SNBCs was measured to know their colloidal stability and the nature of the charge carried in their surface. The average zeta potential of SNBCs, synthesized by extracellular filtrate of pH 5.0, was approximately 21 mV (Additional file 4 Online Resource 4). In spite of this zeta potential value the SNBCs were well stabilized at room temperature as determined by measuring the hydrodynamic diameter by DLS, 30 days after synthesis, with little or no aggregation at all.
To investigate the reason for stabilization up to 30 days after synthesis of SNBCs, it was further characterized in SDS-PAGE (Figure 3) to find if any proteins were present on the surface of the nanoparticles or not. SDS-PAGE profile of the extracellular filtrate clearly shows the presence of proteins in the filtrate. SNBCs were then analyzed by FT-IR spectroscopy in solid mode to provide further evidence (Figure 4) and it showed both amide I (1642.06 cm-1) and amide II (1541.04 cm-1) stretching frequencies present in SNBCs (Caruso et al. 1998).
We have tested the antibacterial activity of SNBCs against E. coli and B. subtilis and antifungal activity againstS. pombe. Antimicrobial activity of SNBCs at a concentration of 200 g/ml was determined by agar diffusion assay (Additional file 5 Online Resource 5). Zone of inhibition determined for E. coli by measuring the diameter of bacterial clearance after 24 hour was 3.68 0.1 mm and that for B. subtilis was 2.81 0.2 mm. Zone of inhibition determined for S. pombe by measuring the diameter of fungal clearance after 24 hour was 1.87 0.15 mm. We have also used 0.5 mM silver nitrate and fungal cell exudates in MilliQ water as control to assess their antimicrobial potency. It was found that silver nitrate showed antimicrobial activity like that of SNBCs. But no zone of inhibition was observed in case of fungal cell exudates in MilliQ water.
The Minimum inhibitory concentrations (MIC) was defined as the lowest silver concentration, which showed no increase in optical density (OD), i.e. no bacterial or fungal growth during 24 hours of inoculation. MIC of SNBCs against E. coli, B. subtilis and S. pombe were represented in
Goswami et al. AMB Express 2013, 3:16 Page 6 of 9 http://www.amb-express.com/content/3/1/16
Figure 4 FT-IR spectra of SNBCs. SNBCs were centrifuged at 10,000 rpm for 10 minutes to remove free proteins or other compounds present in the solution. The SNBCs then resuspended in double distilled water and again centrifuged. The process was repeated for three times and finally the centrifuged part containg SNBCs were redispersed in double distilled water and subjected to FTIR spectroscopy.
Additional file 6 Online Resource 6. In the case of Gram negative bacteria E. coli the MIC was 4 g/ml while for Gram positive bacteria B. subtilis the MIC was 8 g/ml and for the S. pombe the value was 8 g/ml. The minimal concentration of SNBCs which gave rise to plates without bacterial colonies was considered as the minimal bactericidal concentration (MBC). The MBC (or MFC) of SNBCs in growth medium was 8 g/ml for E. coli and 32 g/ml for B. subtilis and 16 g/ml for S. pombe (Additional file 6 Online Resource 6).
To investigate the mechanism of action of SNBCs towards its antimicrobial activity, we found reactive oxygen species (ROS) generation inside both bacterial and fungal cells (Figure 5). E. coli cells (0.24 O.D. at 590 nm) when treated with SNBCs at a final concentration of 40 g/ml showed generation of ROS as studied by fluorescence microscopy. The control set showed no ROS generation. Treatment of B. subtilis (0.24 O.D. at 590 nm) with SNBCs at a final concentration of 40 g/ml showed generation of ROS as studied by fluorescence microscopy. The control set showed no ROS generation. S. pombe(0.4 OD at 590 nm) when treated with SNBCs at a final concentration of 40 g/ml also showed generation of ROS as studied by fluorescence microscopy. The control set showed no ROS generation.
Discussion
In our study SNBCs formed a single population as revealed by DLS analysis in the size range of 2040 nm. The physical nature of SNBCs as revealed by TEM images that most of the SNBCs were quite spherical in shape with their average diameter of 9.46 6.45 nm. It is true that quantification of Ag (0) is not accurate from the absorbance value of the SPR signal of the SNBCs. Concentration calculation from the molar extinction coefficient value depends on the size of the molecule in a homogeneous population. Although microbial synthesized SNBCs contain a heterogeneous population of different size, still we tried to quantitate the Ag (0) content of SNBCs with an average diameter 9.46 nm and 15.91 nm using the extinction coefficient value of 4.16 109 M-1 cm-1. (Yguerabide and Yguerabide 1998). It is observed that 15.69 10-2nM
Ag (0) is produced from 0.5 mM AgNO3.
Average zeta potential of SNBCs measured to be 21 mV suggesting that some biomolecules capped the surface imparting a net negative charge over it. It could be well assumed that the biomolecules present in extracellular filtrate not only involved in the synthesis but providing the surface coating of silver nanoparticles making them well stable. SDS-PAGE profile of the extracellular filtrate clearly showed the presence of proteins in the filtrate. It is
Goswami et al. AMB Express 2013, 3:16 Page 7 of 9 http://www.amb-express.com/content/3/1/16
Figure 5 (See legend on next page.)
Goswami et al. AMB Express 2013, 3:16 Page 8 of 9 http://www.amb-express.com/content/3/1/16
(See figure on previous page.)
Figure 5 Generation of reactive oxygen species (ROS) inside of bacteria in response to SNBCs action. ROS generation was monitored by using 20,70 dichlorodihydrofluorescein diacetate (DCFDA). (a) Control B.s subtilis fluorescent image. (b) Control B. subtilis bright field image. (c) Treated B. subtilis fluorescent image. (d) Treated B. subtilis bright field image. (e) Control E. coli fluorescent image. (f) Control E. coli bright field image (g) Treated E.coli fluorescent image (h) Treated E.coli bright field image. (i) Control S. pombe fluorescent image. (j) Control S. pombe bright field image. (k) Treated S. pombe fluorescent image. (l) Treated S. pombe bright field image.
conceivable that the biomolecules present in extracellular filtrate are not only involved in the synthesis but also providing the surface coating of silver nanoparticles making them well stable. So it is possible that some of these proteins and other biomolecules such as chitin, lipid etc. may be present on SNBCs and help to stabilize the SNBCs. It has been shown that silver nanoparticles have affinity for free amine groups or SH-group of cysteine residues of the proteins or through electrostatic attraction of negatively charged carboxylate groups (Gole et al. 2001). FT-IR analysis of SNBCs again confirmed the presence of bio-molecules in the SNBCs.
The ever growing bacterial resistance to antimicrobial agents poses a serious problem in the treatment of infectious diseases as well as in epidemiological practice (Neu 1992). The surface structures of silver nanoparticles are found to be become important in mediating its antimicrobial activity (Cho et al. 2005). Thus we wanted to know the antimicrobial property of SNBCs which have outer coating of biomolecules. In this study antibacterial activity of SNBCs was observed against E. coli and B. subtilis and antifungal activity against S. pombe. The zone of inhibition as determined by agar diffusion method for E. coli was larger than that for B. subtilis. This was most probably due to variation in cell wall composition between gram negative E. coli and gram positive B. subtilis. It was evident from Additional file 6 Online Resource 6 that both MIC and MBC values were higher for B. subtilis than E. coli. This may be due to the fact that cell wall structure in B. subtilis provided resistance against the diffusion and action of SNBCs.
Generation of reactive oxygen species (ROS) inside both bacterial and fungal cells provides the mechanism of action of SNBCs towards its antimicrobial activity. It is known that majority of nanomaterials such as zinc oxide, carbon nanotubes, and silicon dioxide exert their toxic effects through oxidative stress (Yang et al. 2008). It is believed that nanoparticle toxicity is multifactorial, where size, shape, surface functionalization and potential to release the corresponding metal ions could play pivotal roles. ROS generation in the presence of SNBCs could be explained by metabolic disturbances as well as other toxicological outcomes. It is also possible that surface oxidation of silver nanoparticle liberates Ag+ ions that could amplify the toxicity. Reactions between H2O2 and silver nanoparticle may be responsible for release of Ag+ ions in vivo (Kumar 2006).
A possible chemical reaction involves
Thus silver ions may be released from SNBCs upon its reaction with H2O2 which was produced by the action of
SNBCs on E. coli, B. subtilis and S. pombe. Proteomic analysis of the effect of silver ions (Ag+) on expression of various proteins in E. coli showed a reduction in expression of ribosomal subunit S2, succinyl coenzyme (CoA) synthetase, and maltose transporter (Yamanaka et al. 2005). It was quite obvious that the reduction in expression of ribosomal subunit S2 impairs the synthesis of proteins, whereas reduction in synthesis of succinyl CoA synthetase and maltose transporter causes suppression of intracellular production of ATP. All these factors were involved in killing mechanism of SNBCs.
In conclusion, the focus of this manuscript was on the antibacterial mechanism of stable silver nanobioconjugate, synthesized by an eco-friendly process. It was found that SNBCs exerted antimicrobial activity towards both Gram positive and Gram negative bacteria and fungus. The MIC and MBC values were higher for Gram positive bacteria(i.e. B. subtilis) than Gram negative bacteria (i.e. E. coli). We found generation of ROS as mediator of antimicrobial activity of SNBCs.
Additional files
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S1.pdf
Web End =Additional file 1: Online resource 1. Extracellular synthesis of Silver nano-bioconjugate at pH 5.0. (a) Picture of extracellular filtrate. (b) Picture of silver nano-bioconjugate.
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S2.pdf
Web End =Additional file 2: Online resource 2. Measurement of hydrodynamic diameter of SNBCs by Dynamic Light Scattering.
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S3.pdf
Web End =Additional file 3: Online resource 3. The TEM, HRTEM and SAED pattern of SNBCs synthesized at pH 3.0, pH 7.0 and pH 9.0. TEM image of SNBCs synthesized by extracellular fungal extract of pH 3.0 (a); pH 7.0 (d) and pH 9.0 (g). SAED pattern of SNBCs of pH 3.0 (b), pH 7.0 (e) andpH 9.0 (h) which were indexed according to (111), (200), (220), and (311) reflections of fcc silver crystal on the basis of their d-spacing. HRTEM image of SNBCs synthesized by extracellular fungal extract of pH 3.0 (c); pH 7.0 (f) and pH 9.0 (i).
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S4.pdf
Web End =Additional file 4: Online resource 4. Zeta potential of SNBCs.
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S5.pdf
Web End =Additional file 5: Online resource 5. Antimicrobial activity assay using agar diffusion. Determination of antimicrobial activity of SNBCs, silver nitrate (AgNO3) and fungal cell exudate in agar diffusion assay against E. coli and B. subtilis and S. pombe. The data was represented as mean SD.
http://www.biomedcentral.com/content/supplementary/2191-0855-3-16-S6.pdf
Web End =Additional file 6: Online resource 6. Minimum inhibitory concentrations, minimal bactericidal concentrations and minimal fungicidal concentrations of SNBCs. Minimum inhibitory concentrations (MIC) of SNBCs were determined against E.coli, B. subtilis and S. pombe.
Goswami et al. AMB Express 2013, 3:16 Page 9 of 9 http://www.amb-express.com/content/3/1/16
Minimal Bactericidal Concentrations (MBC) of SNBCs were determined against E.coli and B. subtilis and Minimal Fungicidal Concentrations (MFC) against S. pombe.
Competing interestsThe authors declare that they have no competing interests.
AcknowledgementThis work is supported by Centre for Research in Nano Science and Nanotechnology (CRNN), University of Calcutta. The authors would like to thank Shantiswarup Sinha and Prof. Anjan Dasgupta for assistance with the FTIR measurements. The authors would like to acknowledge DST-FIST, UGCCAS programme, DBT-IPLS programme Govt. of India, Indian Association for Cultivation of Science (I.A.C.S.), Jadavpur for equipment and infrastructural support.
Author details
1Department of Biochemistry, University of Calcutta, 35, Ballygunge Circular Road, Kolkata, West Bengal 700 019, India. 2Department of Physiology, Krishnagar Government College, Krishnagar, Nadia, West Bengal PIN-74101, India.
Received: 11 February 2013 Accepted: 13 February 2013 Published: 23 February 2013
ReferencesBhainsa KC, DSouza SF (2006) Extracellular biosynthesis of silver nanoparticles using the fungus Aspergillus fumigatus. Colloids and Surface B Biointerfaces 47:160164Burda C, Chen X, Narayanan R, EI-Sayed MA (2005) Chemistry and properties of nanocrystals of different shapes. Chem Rev 105:10251102Caruso F, Furlong DN, Ariga K, Ichinose I, Kunitake T (1998) Characterization of
Polyelectrolyte-Protein Multilayer Films by Atomic Force Microscopy, Scanning Electron Microscopy, and Fourier Transform Infrared Reflection-Absorption Spectroscopy. Langmuir 14:45594565Castellano JJ, Shafii SM, Ko F, Donate G, Wright TE, Mannari RJ, Pyne WG, Smith
DJ, Robson MC (2007) Comparative evaluation of silver-containing antimicrobial dressings and drugs. Int Wound J 4:114122Chau CF, Wu SH, Yen GC (2007) The development of regulations for food nanotechnology. Trends Food Sci Technol 18:269280Cho KH, Park JE, Osaka T, Park SG (2005) The study of antimicrobial activity and preservative effects of nanosilver ingredient. Electrochim Acta 51:956960 Dror-Ehre A, Mamane H, Belenkova T, Markovich G, Adin A (2009) Silver nanoparticle- E. coli colloidal interaction in water and effect on E-coli survival. J Colloid Interface Sci 339:521526Feng QL, Wu J, Chen GQ, Cui FZ, Kim TN, Kim JO (2000) A mechanistic study of the antibacterial effect of silver ions on Escherichia coli and Staphylococcus aureus. J Biomed Mater Res 52:662668Gole A, Dash C, Ramakrishnan V, Sainkar SR, Mandale AB, Rao M, Sastry M (2001)
Pepsin-gold conjugates: preparation, characterization, and enzymatic activity. Langmuir 17:16741679Gu H, Ho PL, Tong E, Wang L, Xu B (2003) Presenting vancomycin on nanoparticles to enhance antimicrobial activities. Nano Lett 3:12611263 Holt KB, Bard AJ (2005) Interaction of silver (I) ions with the respiratory chain of
Escherichia coli: an electrochemical and scanning electrochemical microscopy study of the antimicrobial mechanism of micromolar Ag+. Biochemistry 44:1321413223Hong B, Kai J, Ren Y, Han J, Zou Z, Ahn CH, Kang KA (2008) Highly sensitive rapid, reliable, and automatic cardiovascular disease diagnosis with nanoparticle fluorescence enhancer and MEMS. Adv Exp Med Biol 614:265273 Kathiresan K, Manivannan S, Nabeel MA, Dhivya B (2009) Studies on silver nanoparticles synthesized by a marine fungus, Penicillium fellutanum isolated from coastal mangrove sediment. Colloids Surf B Biointerfaces 71:133137 Kim KJ, Sung WS, Moon SK, Choi JS, Kim JG, Lee DG (2008) Antifungal effect of silver nanoparticles on dermatophytes. J Microbiol Biotechnol 18:14821484
Klaus T, Joerger R, Osson E, Granqvist CG (1999) Silver based crystalline nanoparticles, Microbially fabricated. Proc Natl Acad Sci 96:1361113614
Kumar C (2006) Nanomaterials-toxicity, health and environmental issues. Wiley-VCH Verlag GmbH & Co, Weinheim, Germany
Lee KS, EI-Sayed MA (2006) Gold and silver nanoparticles in sensing and imaging: sensitivity of plasmon response to size, shape, and metal composition. J Phys Chem B 110:1922019225
Monali G, Jayendra K, Avinash I, Aniket G, Mahendra R (2009) Fungus-mediated synthesis of silver nanoparticles and their activity against pathogenic fungi in combination with fluconazole. Nanomedicine: Nanotechnology, Biology, and Medicine 5:382386
Nair B, Pradeep T (2002) Coalescence of nanoclusters and formation of submicron crystallites assisted by Lactobacillus Strain. Cryst Growth des 2:293298 NCCLS, Approved standards M7A4 (1997) Methods for dilution antimicrobial susceptibility tests for bacteria that grow aerobically. National Committee for Clinical Laboratory Standards, Wayne, PA
Neu HC (1992) The crisis in antibiotic resistance. Science 257:10641073Nie S, Emory SR (1997) Probing single molecules and single nanoparticles by surface enhanced Raman scattering. Science 275:11021106Rai M, Yadav A, Gade A (2009) Silver nanoparticles as a new generation of antimicrobials. Biotechnol Adv 27:7683Raveendran P, Fu J, Wallen SL (2003) Completely green synthesis and stabilization of metal nanoparticles. J Am Chem Soc 125:1394013941Sondi I, Salopek-Sondi B (2004) Silver nanoparticles as antimicrobial agent: a case study on E. coli as a model for Gram-negative bacteria. J Colloid Interface Sci 275:177182Sukdeb P, Yu Kyung T, Joon Myong S (2007) Does the antibacterial activity of silver nanoparticles depend on the shape of the nanoparticle? a study of the Gram-negative bacterium Escherichia coli. Appl Environ Microbiol 73:17121720 Sun RWY, Chen R, Chung NPY, Ho CM, Lin CLS, Che CM (2005) Silver nanoparticles fabricated in HEPES buffer exihibit cytoprotective activities toward HIV-1 infected cells. Chem Commun 40:50595061Velev OD, Kaler EW (1999) In Situ Assembly of Colloidal Particles into Miniaturized
Biosensors. Langmuir 15:36933698Vigneshwaran A, Kathe AA (2007) Silver-protein (core-shell) nanoparticle production using spent mushroom substrate. Langmuir 23:71137117 Vigneshwaran N, Ashtaputre NM, Varadaranjan PV, Nachane RP, Paralikar KM,
Balasubramanya RH (2007a) Biological synthesis of silver nanoparticles using the fungus Aspergillus flavus. Mater Lett 61:14131418
Vigneshwaran N, Kathe AA, Varadarajan PV, Nachane RP, Balasubramanya RH (2007b) Functional finishing of cotton fabrics using silver nanoparticles.
J Nanosci Nanotechnol 7:18931897Vigneshwaran N, Nachane RP (2006) A novel one-pot green synthesis of stable silver nanoparticle using soluble starch. Carbohydrate Res 341:20122018Wu J, Hou SY, Ren DC, Mather PT (2009) Antimicrobial properties of nanostructured hydrogel webs containing silver. Biomacromolecules 10:26862693Xie J, Lee JY, Wang DIC, Ting YP (2007) Identification of active biomolecules in the high-yield synthesis of single-crystalline gold nanoplates in algal solutions. Small 3:672682Xu XHN, Brownlow WJ, Kyriacou SV, Wan Q, Viola JJ (2004) Real-time probing of membrane transport in living microbial cells using single nanoparticle optics and living cell imaging. Biochem 43:1040011043Yamanaka M, Hara K, Kudo J (2005) Bactericidal actions of a silver ion solution on
Escherichia coli, studied by energy-filtering transmission electron microscopy and proteomic analysis. Appl Environ Microbiol 71:75897593
Yang H, Liu C, Yang D, Zhang H, Xi Z (2008) Comparative study of cytotoxicity, oxidative stress and genotoxicity induced by four typical nanomaterials: the role of particle size, shape and composition. J Appl Toxicol 29:6978
Yguerabide J, Yguerabide EE (1998) Light-scattering submicroscopic particles as highly fluorescent analogs and their use as tracer labels in clinical and biological applications. Ana Biochem 262:137156
Zhang L, Gu FX, Chan JM, Wang AZ, Langer RS, Farokhzad OC (2008a)Nanoparticles in medicine: therapeutic applications and developments.
Clin Pharmacol Ther 83:761769Zhang Y, Peng H, Huang W, Zhou Y, Yan D (2008b) Facile preparation and characterization of highly antimicrobial colloid Ag or Au nanoparticles.
J Colloid Interface Sci 325:371376Zhao G, Stevens SE Jr (1998) Multiple parameters for the comprehensive evaluation of the susceptibility of Escherichia coli to the silver ion. BioMetals 11:2732
doi:10.1186/2191-0855-3-16Cite this article as: Goswami et al.: An Ecofriendly synthesis of silver nano-bioconjugates by Penicillium citrinum (MTCC9999) and its antimicrobial effect. AMB Express 2013 3:16.
You have requested "on-the-fly" machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Show full disclaimer
Neither ProQuest nor its licensors make any representations or warranties with respect to the translations. The translations are automatically generated "AS IS" and "AS AVAILABLE" and are not retained in our systems. PROQUEST AND ITS LICENSORS SPECIFICALLY DISCLAIM ANY AND ALL EXPRESS OR IMPLIED WARRANTIES, INCLUDING WITHOUT LIMITATION, ANY WARRANTIES FOR AVAILABILITY, ACCURACY, TIMELINESS, COMPLETENESS, NON-INFRINGMENT, MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE. Your use of the translations is subject to all use restrictions contained in your Electronic Products License Agreement and by using the translation functionality you agree to forgo any and all claims against ProQuest or its licensors for your use of the translation functionality and any output derived there from. Hide full disclaimer
The Author(s) 2013
Abstract
This report provides for the first time a novel environment friendly extracellular synthesis of stable silver nano-bioconjugates (SNBCs) at room temperature at pH 5.0 using Penicillium citrinum MTCC 9999 biomass. The UV-Visible spectral scan of dispersed SNBCs solution showed absorption in the region 340-450 nm due to surface plasma resonance (SPR). Typical Transmission Electron Microscopic (TEM) images showed that although two populations were present but most of them were in 20-30 nm range. Average zeta potential of SNBCs was -21 mV suggesting some biomolecules capped the nanoparticles imparting a net negative charge over it. FTIR analysis also showed that biomolecules were involved in stabilization. SNBCs showed strong antibacterial activity against both Gram positive (Bacillus subtilis) and Gram negative bacteria (Escherichia coli). SNBCs also showed strong antifungal activity as assessed against Schizosaccharomyces pombe. In the case of E. coli the minimum inhibitory concentrations (MIC) of SNBCs was 4 [mu]g/ml while in B. subtilis it was 8 [mu]g/ml. In the case of E. coli the minimum bactericidal concentrations (MBC) of SNBCs was 8 [mu]g/ml while in B. subtilis it was 32 [mu]g/ml. The SNBCs exerted its antibacterial and antifungal activity through generation of reactive oxygen species (ROS) inside the cell.
You have requested "on-the-fly" machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Show full disclaimer
Neither ProQuest nor its licensors make any representations or warranties with respect to the translations. The translations are automatically generated "AS IS" and "AS AVAILABLE" and are not retained in our systems. PROQUEST AND ITS LICENSORS SPECIFICALLY DISCLAIM ANY AND ALL EXPRESS OR IMPLIED WARRANTIES, INCLUDING WITHOUT LIMITATION, ANY WARRANTIES FOR AVAILABILITY, ACCURACY, TIMELINESS, COMPLETENESS, NON-INFRINGMENT, MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE. Your use of the translations is subject to all use restrictions contained in your Electronic Products License Agreement and by using the translation functionality you agree to forgo any and all claims against ProQuest or its licensors for your use of the translation functionality and any output derived there from. Hide full disclaimer