Simulation-Based Optimization of Cure Cycle of Large Area Compression Molding for LED Silicone Lens

Abstract

Three-dimensional heat transfer-curing simulation was performed for the curing process by introducing a large area compression molding for simultaneous forming and mass production for the lens and encapsulants in the LED molding process. A dynamic cure kinetics model for the silicone resin was adopted and cure model and analysis result were validated and compared through a temperature measurement experiment for cylinder geometry with cure model. The temperature deviation between each lens cavity could be reduced by implementing a simulation model on the large area compression mold and by optimizing the location of heat source. A two-step cure cycle was constructed to reduce excessive reaction peak at the initial stage and cycle time. An optimum cure cycle that could reduce cycle time by more than 29% compared to a one-step cure cycle by adjusting dwell temperature, heating rate, and dwell time was proposed. It was thus confirmed that an optimization of large area LED lens molding process was possible by using the present experiment and the finite element method.

Min-Jae Song 1, 2 and Kwon-Hee Kim 2 and Seok-Kwan Hong 1 and Jeong-Won Lee 1 and Jeong-Yeon Park 1 and Gil-Sang Yoon 1 and Heung-Kyu Kim 3

Academic Editor:Liyuan Sheng

1, Molds & Dies Technology R&BD Group, Korea Institute of Industrial Technology, 7-47 Songdo-dong, Yeonsu-gu, Incheon 406-840, Republic of Korea
2, Department of Mechanical Engineering, Korea University, Anam-dong, Seongbuk-gu, Seoul 136-713, Republic of Korea
3, Department of Automotive Engineering, Kookmin University, 77 Jeongneung-ro, Seongbuk-gu, Seoul 136-702, Republic of Korea

Received 5 December 2014; Revised 4 June 2015; Accepted 9 June 2015; 1 July 2015

This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

1. Introduction

LED has the merits of semipermanent life, low power consumption, safety, and environment friendliness. With these merits, LED has rapidly replaced existing light sources recently. As a material of encapsulant for the protection of chip and lens for the light distribution of this LED, transparent polymer is mainly used. The molding process for LED packaging to produce this LED lens and encapsulant is largely divided into cast molding, injection molding, transfer molding, and compression molding. Among these, compression molding is the most suitable for mass production and simple method [1]. It is a mass production method dispensing resin into a lower mold compressed by an upper mold onto which LED lead frame is attached. The merit of this process is an optimum resin usage efficiency of more than 95%, possible simultaneous forming of large numbers of encapsulants and lenses, and less damage in the LED chip and board due to low pressure forming. Therefore, it is one of the most cost-effective production methods with high efficiency (Figure 1).

Figure 1: Compression molding process for LED molding [1].

[figure omitted; refer to PDF]

Generally, a transparent thermoset resin such as epoxy or silicone resin is used for the encapsulant and lens for LED. However, epoxy which has been widely used has problems of impairing optical transmittance and yellowing at high temperature, making it difficult for practical implementation. While silicone resin, having excellent thermal and optical property compared with epoxy, is suitable for high-power LED requiring heat resistance and durability, its usage is being expanded to serve as backlight for large-sized LCD, UV lamp, and general lighting.

Silicone resin is manufactured through a process in which liquid-phase base and curing agent are mixed and input into mold and then cured by heat followed by cooling. However, abrupt temperature increase in the resin by excessive chemical reaction during curing leads to surface roughening, delamination from LED chip, residual void and moisture, and residual stress, resulting in the impairment of the mechanical and optical properties of LED product [2]. Therefore, a numerical simulation is tried to forecast abrupt temperature increases during the curing process and it has been applied as a means of optimal cure cycle [3-5]. However, research about cure simulation for silicone resin is lacking. The main focus in the related studies is on the epoxy among thermoset resins.

Loos and Springer [6] have analyzed a cure process for the two-dimensional composite flat-plate using an implicit finite difference method. Kim et al. [7] performed a one-dimensional analysis for prepreg composite using an explicit finite difference method and proposed a model that restricted excessive temperature increases inside a composite during curing process. Bogetti and Gillespie [8] have performed a one-dimensional and two-dimensional heat transfer and cure simulation for a thick composite using an implicit finite difference method. Heat conduction equations coupled to the cure kinetics of the resin were used in their simulation. Guo et al. [9] have carried out a one-dimensional transient heat transfer for the autoclave cycle of the thick carbon fiber/epoxy material using a commercial finite element program. They concluded that conventional cure cycle had to be modified to prevent excessive temperature increase. Cheung et al. [10] have performed thermokinetic three-dimensional finite element analysis which combined heat transfer and cure simulation for the liquid composite molding process. They compared simulation and experiment using a simple flat-plate while the degree of cure and temperature distribution was estimated for the thick, curved-shaped part. Hojjati and Hoa [11] performed analysis by coupling one-dimensional heat transfer, cure, and viscosity for a thick thermosetting composite. Rouison et al. [12] studied one-dimensional cure simulation for the RTM process with a natural fiber reinforced composite. They carried out simulation considering the heat conductivity and heat capacity changes during cure process and raised the accuracy of estimation by comparing the results with those by experiments. Kasza et al. [13] improved the accuracy of estimation in the cure kinetics model by considering a buoyancy flow during liquid phase and by carrying out a sensitivity analysis for a large epoxy sample having axis-symmetry. Liu et al. [14] performed three-dimensional finite element analysis by proposing a chemo-thermo-microwave curing model for the microwave cure epoxy in the flip chip packaging process. Behzad and Sain [15] conducted a three-dimensional heat transfer finite element analysis for the natural fiber reinforced composite. First, they analyzed a simple block model and validated the model by comparing it with experimental results. Additional analysis was carried out for a complicatedly shaped automotive mirror case. They forecasted temperature distribution and degree of cure. Shojaei et al. [16] have performed three-dimensional control volume/finite element analysis for simulation of filling and cure for the resin transfer molding process meant for the composite having a thick and complicated shape. Joshi et al. [17] have performed a finite element analysis for the cure process for one-, two-, and three-dimensional shapes of fiber reinforced composite and validated the results by comparing them with those by experiment. Sekula et al. [18] performed a three-dimensional finite element analysis for the fill and curing process for epoxy which was being used in the products for high voltage insulation. They validated the simulation results with experimental results through a simple cylindrical test. After the simulation for the industrial application example, they analyzed the degree of cure for the product during the process. Yi et al. [19] performed a three-dimensional finite element analysis for thermosetting the matrix composites and studied temperature distribution and degree of cure which became changed according to time step and boundary condition. Park et al. [20] performed a three-dimensional finite element analysis for the thick composite structure and validated the results with experimental results and two-dimensional analysis results. Choi et al. [21] have performed three-dimensional finite element analysis of the curing process for the hat-shaped material in the resin transfer molding process. They also analyzed temperature distribution and degree of cure by introducing a two-step cure cycle.

In the earlier studies, residual stress was simulated in the cure process for the silicone resin of simple cylindrical LED encapsulation [2]. In this study, three-dimensional heat transfer-cure simulation was performed for the large area compression molding process to simultaneously form silicone resin lenses and encapsulants for LED. A dynamic cure kinetics model for silicone resin was proposed and the simulation results were validated through a temperature measurement experiment for the simple cylindrical shape. Further, heat source position was optimized after the simulation of model for a large area mold having 10 × 5 cavities to reduce temperature distribution between each cavity. Further, an optimum cure cycle was investigated by constructing a two-step cure cycle to reduce abrupt reaction peak at the initial stage and to reduce molding cycle time.

2. Formulation

2.1. Governing Equation and Cure Kinetics

The temperature solution is based on Fourier's heat conduction equation and the exothermic heat of the curing reaction source term. By neglecting the energy transfer by convection, the energy solution for three-dimensional heat conduction can be expressed as follows [15, 17, 18, 20-23]: [figure omitted; refer to PDF] Here, [figure omitted; refer to PDF] is the temperature, [figure omitted; refer to PDF] is the thermal conductivity, [figure omitted; refer to PDF] is the specific heat, [figure omitted; refer to PDF] is the density, [figure omitted; refer to PDF] is the total heat of reaction, [figure omitted; refer to PDF] is the degree of cure, and [figure omitted; refer to PDF] is the rate of reaction.

The amount of heat liberated by the reaction is usually taken as a measure of the degree of cure, assuming that the fractional conversion is proportional to the number of bonds formed in linking the chains together and that each bond releases the same amount of heat. Thus, the fraction conversion, also called a degree of cure, can be defined as follows: [figure omitted; refer to PDF]

In this equation, [figure omitted; refer to PDF] is the total heat of reaction and [figure omitted; refer to PDF] is the amount of heat release up to the current time which can be defined by the following: [figure omitted; refer to PDF]

The degree of cure or conversion ( [figure omitted; refer to PDF] ) equals zero when there has been no reaction, and it equals 1 when the reaction is complete. Thus, the cure is a field quantity that varies in space and time. The rate of heat generated during curing can be expressed as follows: [figure omitted; refer to PDF]

Here, [figure omitted; refer to PDF] is the time rate of change in the degree of cure represented by an empirical model such as the one proposed by Kamal and Sourour [24]. For stepwise isothermal cure of a thermoset resin, the cure rate equation has the form of the following equation: [figure omitted; refer to PDF]

Here, [figure omitted; refer to PDF] at [figure omitted; refer to PDF] , [figure omitted; refer to PDF] and [figure omitted; refer to PDF] are the constants, and the term [figure omitted; refer to PDF] contains the temperature dependence of the curing rate as follows: [figure omitted; refer to PDF]

Meanwhile, [figure omitted; refer to PDF] is the preexponential factor, [figure omitted; refer to PDF] is the activation energy, [figure omitted; refer to PDF] is the absolute temperature, and [figure omitted; refer to PDF] is the universal gas constant.

The most commonly used method among empirical methods to experimentally obtain the cure characteristics by measuring exothermic heat during cure process is a test using Differential Scanning Calorimeter (DSC). DSC measurement method is further divided into dynamic DSC which measures heat capacity after increasing temperature at constant speed and isothermal DSC method wherein heat capacity is measured while maintaining temperature fixed the same as that of DSC. Initial reaction is highly important in isothermal DSC method. However, silicone which has been used in the present study had a problem of containing errors after having many data as initial reaction because the reaction was already started in the course of temperature increase from room temperature to reaction temperature. It would be better to measure heat capacity from this kind of fast curing resin by dynamic method rather than isothermal condition. However, dynamic method would not give an idea about the relation among three components since three components, namely, conversion from liquid to solid, rate of cure, and temperature, are simultaneously changed. Also it requires difficult advanced curve fit skills [25].

Further, as cure progressed, glass transition temperature of the resin was increased. However, if glass transition temperature was increased higher than cure temperature, and the cured materials were changed from rubbery to glassy, reaction was converted to diffusion-controlled, resulting in significantly slow reaction rate [26]. Though this diffusion-controlled effect was not prominent in the dynamic method compared to the isothermal method since the glass transition temperature of silicone resin used in the present study was 35°C, which was far lower than that of the cure temperature, the reaction speed by diffusion was not considered in this study.

In this study, heating rates were fixed as four types and dynamic cure kinetics that can determine degree of cure, while cure rate was introduced [27-29]. DSC Q100 from TA Instrument was used as DSC, and an experiment was conducted with the sample container under nitrogen atmosphere inside an aluminum hermetic pan. Heating rates were calculated from four zones of 5, 10, 15, and 20°C/min. Figure 2 shows the measured reaction heat capacity.

Figure 2: DSC exothermic curves of silicone.

[figure omitted; refer to PDF]

Autocatalyzed cure kinetics were applied as in (5) based on the above experimental results. However, (5) is isothermal reaction kinetics; thus, it becomes the same as (7) if this is converted to a dynamic reaction equation: [figure omitted; refer to PDF]

Here, [figure omitted; refer to PDF] is the DSC heating rate [figure omitted; refer to PDF] .

Activation energy [figure omitted; refer to PDF] was obtained by applying Kissinger equation as in (4), wherein activation energy could be obtained at the maximum reaction rate point under constant heating rate [16]: [figure omitted; refer to PDF] In this formula, [figure omitted; refer to PDF] is the maximum exothermic temperature.

Table 1 shows the constants of the obtained reaction equation. In Figure 3, experimental results and curve-fitting reaction equation are compared. As can be seen from the figure, the reaction equation relatively and exactly expresses the experimental results.

Table 1: Constant of cure kinetics for silicone.

Parameter	Value
[figure omitted; refer to PDF] (S-1 )	6.6e + 9
[figure omitted; refer to PDF] (KJ/Mol)	85.461
[figure omitted; refer to PDF]	0.4
[figure omitted; refer to PDF]	1.9
[figure omitted; refer to PDF] (J/mol·K)	8.31
[figure omitted; refer to PDF] (J/kg)	145,298

Figure 3: Comparison of the degree of cure between measurement and cure kinetics model.

[figure omitted; refer to PDF]

2.2. Thermal Properties

Thermal properties of silicone resin undergo changes according to temperature and degree of cure (conversion from liquid state to solid state) in the course of cure. In order to investigate these changes of thermal properties of the silicone resin, density, specific heat, and thermal conductivity were measured for the liquid resin before cure and cured solid resin.

A gravity bottle was used to measure the liquid resin, while a densimeter was used to measure the density of the solid resin. Meanwhile, thermal conductivity was measured with a laser flash for the two liquid zones (25°C, 50°C) as well as the three solid zones (25°C, 80°C, and 150°C). The specific heat was measured at temperature rise at a rate of 10°C/min for the liquid state and solid state of the resin using a DSC. The changes of specific heat were measured with a standard sample sapphire. The measurement results are arranged in Table 2.

Table 2: Thermal properties of silicone resin.

	Temp. °C	Density(kg/m3 )	Thermal conductivity(W/m/°C)	Specific heat(J/kg/°C)
Liquid	2550	1150	0.2130.210	15101547
Solid	2580150	1185	0.1510.1540.156	133614551597

Changes of density at solid and liquid states of the silicone resin can be referred to as cure shrinkage [30] and it has a linear relationship with the general degree of cure [31]. Therefore, this change is expressed as a function for the degree of cure as shown below: [figure omitted; refer to PDF]

Changes in the thermal conductivity were large at liquid state and solid state of the resin, but it was not greatly changed by the temperature. Therefore, thermal conductivity was expressed only in terms of degree of cure as seen below. The zone of degree of cure 0.5-0.6 is a gel point at which the silicone resin was changed from liquid state to solid state: [figure omitted; refer to PDF]

The changes in the specific heat are expressed as a function of temperature and degree of cure as shown below [32]. In the equation, [figure omitted; refer to PDF] is the specific heat of the liquid resin, while [figure omitted; refer to PDF] is the specific heat of the cured resin: [figure omitted; refer to PDF]

3. Validation

A simple experimental setup was constructed as shown in Figure 4 in order to compare and validate finite element analysis results with the experiment. Silicone resin was dosed with cylindrical aluminum mold 30 mm in diameter and 20 mm in height and this cylindrical resin underwent thermal curing. Mold was placed on the heating plate and it was heated at a rate of 15°C/min from the initial stage, while the temperature was maintained at 130°C for one hour. A glass chamber was added above the mold to prevent heat loss by outer atmosphere in order to raise the accuracy of the experiment. Thermocouples were inserted into the silicone, and mold and temperature were measured at real time using data acquisition (DAQ) device. Obtained temperature data were stored.

Figure 4: Experimental setup for silicone molding.

[figure omitted; refer to PDF]

Figure 5(a) shows the comparison result of measured temperature distribution results (3 points) and analysis results. After around eight minutes, a maximum reaction peak of 164°C occurred as an active cure reaction at center point 1. At point 2, a reaction peak lower than that was generated. Meanwhile, a reaction peak at point 3 at the adjourning mold wall did not occur; rather, temperature at point 3 displayed mold temperature profile as such. The analysis results as shown in Figure 5(b) showed that resin temperature increased from mold wall, and the largest reaction heat was generated near the center of resin due to the chemical reaction of resin when cure reaction became active. Though there was little difference from the experimental results, temperature distribution relatively followed the experimental results.

Figure 5: Comparison of the experimental data and simulation (points 1, 2, and 3). (a) Experiment and simulation. (b) Temperature contour (simulation).

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

4. Application of Large Area Compression Molding

This simulation model was applied in the large area LED lens compression molding which could be implemented in the actual site. Figure 6 shows a large area LED lens mold used during simulation. Figure 6(a) displays a layout comprised of upper mold, lower mold, silicone resin, lead frame, and cartridge heater. Meanwhile, Figure 6(b) shows the lower mold to perform simulation. The lower mold was arranged as 5 × 10 rows by selecting a semispherical type LED lens model with a total of 50 cavities. Heating for thermal cure, nine in number, having a diameter of 6 mm, was arranged in series with a 10 mm gap.

Figure 6: Analysis model for LED lens molding. (a) Layout of large area LED lens molding. (b) Lower mold specification for LED lens molding.

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

Modeling was done with lower mold and silicone as shown in Figure 7. All the rest of the parts were arranged as boundary condition. Cartridge heater was set to 130°C, while heat transfer coefficient 1000 W/m² was applied on the surface of hole where cartridge heater was installed. The surface, except the position where the heater was installed, was set with the insulation and initial temperature of mold and silicone resin set to 50°C.

Figure 7: F.E. model for LED lens molding.

[figure omitted; refer to PDF]

4.1. Optimization of Heater Location

Figure 8(b) shows temperature distribution according to mold location when an object is heated at an isothermal temperature of 130°C. Since the mold had a 1/4 symmetric geometry, temperature profile was observed from three points as shown in Figure 8(a). Mold temperature was observed by selecting the exact center of the mold. Simulation results yielded exothermic reaction as shown in Figure 8(b); that is, the reaction peak of temperature at 162°C was observed at 127 seconds from the center part point 1, while a temperature of 159°C was observed from point 2 after 134 sec. The corner reaction peak of temperature 152°C after 164 sec was observed from point 3. It was judged that heat energy was not transmitted because heater was not arranged evenly compared with other locations. A maximum temperature difference of 10°C was observed according to location. Precise temperature control is important because it affects the physical and mechanical properties of cured products [21]. Therefore, this uneven temperature distribution might adversely affect the degree of cure in the lens which may not be beneficial in producing LED products having even property.

Figure 8: Temperature profile of large area LED lens molding. (a) Measuring points of silicone resin and mold temperature. (b) Temperature profile of silicone resin and mold.

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

Therefore, the location of heat source was changed to make the degree of cure uniform according to location as shown in Figure 9(a); that is, the gap between heaters was increased linearly from the center where a large amount of heat was received. Simulation results showed that silicone was uniformly cured according to location as shown in Figure 8. At this time, all reaction peaks were observed after 140 sec and the temperature was in the range of 158.8°C-159.7°C with a much decreased temperature deviation of 0.9°C.

Figure 9: Temperature profile of silicone resin by heat source change: (a) optimized position of heat source for uniform heating and (b) optimized temperature profile of silicone resin and mold.

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

4.2. Reaction Peak Temperature and Cycle Time Reduction

Abrupt temperature peak was generated while material was cured at an isothermal temperature of 130°C even if temperatures were the same everywhere. This abrupt temperature and degree of cure occurring during curing reaction greatly affected the mechanical properties of the final products [19]. Therefore, it is necessary to make a process wherein mold is heated from a low temperature to prevent this abrupt cure reaction. Figure 10 shows an isothermal simulation at 130°C and dynamic one-step heating at a rate of 10°C/min. The measurement point of silicone resin was at point 1 as shown in Figure 8(a), while mold temperature was measured from the center of the mold. There was almost no reaction peak in the dynamic heating. The curing process was almost completed by dynamic heating at around 919 sec. Though isothermal cure was quickly completed in around 381 sec, the process was introduced to prevent this excessive reaction peak and to reduce the cycle time since cure accompanied excessive reaction peak.

Figure 10: Comparison of cure profile between one-step and isothermal curing.

[figure omitted; refer to PDF]

There is a step cure process to reduce reaction peak and to decrease cycle time; that is, by regulating dynamic heating and dwell time, abrupt exothermic reaction is prevented and uniform products are obtained [19, 21, 33-38]. Therefore, cure profile was introduced with a two-step heating rate and uniform temperature holding as shown in Figure 11. Further, optimization analysis was carried out to find an optimum cure condition to reduce cycle time and reaction peak. Here, [figure omitted; refer to PDF] is the cycle time (sec), [figure omitted; refer to PDF] is the cure temperature (°C), and [figure omitted; refer to PDF] is the heating rate (°C/min).

Figure 11: Schematic diagram of the two-step curing process.

[figure omitted; refer to PDF]

Optimum value [figure omitted; refer to PDF] as in (12) and constraints in (13) were set in order to obtain an optimum cycle; that is, reaction peak did not exceed 132°C and the total cycle time was set to a minimum, not exceeding 9 minutes and comprising a one-step cycle time as shown in Figure 10: [figure omitted; refer to PDF]

4.2.1. Changes according to Dwell Temperature ( [figure omitted; refer to PDF] )

First of all, the changes according to dwell temperature ( [figure omitted; refer to PDF] ) were investigated because Song et al. [2] reported that one-step dwell temperature affected most of the changes. [figure omitted; refer to PDF] was set to 103°C, 113°C, and 123°C. One-step heating rate ( [figure omitted; refer to PDF] ) was set to 30°C/min, while two-step heating rate ( [figure omitted; refer to PDF] ) was set to 10°C/min. Simulation results are presented in Figure 12 and it was observed that as dwell temperature was increased, the reaction peak was also increased. Peaks were not observed at 103°C and 113°C, while reaction peak at 145°C was observed under [figure omitted; refer to PDF] at 123°C condition. As far as degree of cure was concerned, cure was completed at 796 sec for [figure omitted; refer to PDF] at 103°C, at 716 sec for [figure omitted; refer to PDF] at 113°C, and at 632 sec for [figure omitted; refer to PDF] at 123°C, all of which were greatly reduced compared with cure by one-step (at 919 sec). Since temperature exceeded 123°C compared to the target reaction peak, it was clear that optimum dwell temperature ( [figure omitted; refer to PDF] ) was near 113°C.

Figure 12: Cure profile of silicone resin increasing dwell temperature ( [figure omitted; refer to PDF] ).

[figure omitted; refer to PDF]

4.2.2. Changes according to Heating Rate ( [figure omitted; refer to PDF] )

The heating rate ( [figure omitted; refer to PDF] ) of one-step was adjusted to investigate the cure profile changes according to heating rate. Cure cycle time ( [figure omitted; refer to PDF] ) was set constant during the experiment. Figure 13 shows the changes of reaction peak according to heating rate. Reaction peak was not generated greatly even if heating rate was increased but it was shifted horizontally, making cycle time reduced. Therefore, one-step heating rate ( [figure omitted; refer to PDF] ) was applied as an isothermal [figure omitted; refer to PDF] . However, cycle time was rather increased from 716 sec to 725 sec. This might be because protracted dwell time led to a temperature drop lower than 130°C after reaction peak which hindered the cure process. Therefore, an optimum condition was added, with the temperature of silicone resin maintained higher than 130°C after reaction peak: [figure omitted; refer to PDF]

Figure 13: Cure profile of silicone resin increasing heating rate ( [figure omitted; refer to PDF] ).

[figure omitted; refer to PDF]

4.2.3. Changes according to Dwell Time ( [figure omitted; refer to PDF] )

The reaction peak was observed while reducing dwell time ( [figure omitted; refer to PDF] ) with reference to the experimental results in Section 4.2.2. One-step heating rate [figure omitted; refer to PDF] was applied as an isothermal condition and [figure omitted; refer to PDF] was fixed at 10°C/min. Dwell time ( [figure omitted; refer to PDF] ) was changed to 145 sec and 115 sec which were isothermal conditions as shown in Figure 14. At 145 sec and 115 sec, reaction peaks of 131.7°C and 136.2°C were observed. As dwell time ( [figure omitted; refer to PDF] ) was reduced, reaction peak gradually increased. Therefore, optimum cure process which reduced cure cycle was drawn within the reaction peak of 132°C. Parameter values with optimum simulation were arranged as shown in Table 3.

Table 3: Optimized parameters for cure cycle reduction.

[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	[figure omitted; refer to PDF]	Reaction peak	[figure omitted; refer to PDF]
50	113	130	ISO	10	0	145	102	131.7°C	649 sec

Figure 14: Cure profile of silicone resin decreasing dwell time ( [figure omitted; refer to PDF] ).

[figure omitted; refer to PDF]

Figure 15 shows comparison results between one-step heating rate simulation at 10°C/min as in Figure 10 and the optimum simulation results. As can be seen from the figure, temperature increased without reaction peak but cycle time was greatly reduced. Optimum cure time was reduced from 919 sec to 649 sec which ultimately reduced cycle time by around 29%.

Figure 15: Comparison of cure profile between optimized and one-step curing process.

[figure omitted; refer to PDF]

5. Conclusions

In this study, a three-dimensional heat transfer-cure analysis was performed for the large area compression molding process for forming lens and encapsulants simultaneously. A dynamic cure kinetics model for the silicone resin was proposed and the analysis result was validated through experiments with a simple-shaped object. The position of heat source was optimized by carrying out simulation using a large area mold having 10 × 5 cavities to reduce temperature deviation between each cavity. A two-step cure cycle was also constructed to reduce excessive reaction peak at the initial stage and cycle time. An optimum cure cycle that could reduce cycle time by more than 29%, compared to one-step cure, by adjusting dwell temperature, heating rate, and dwell time, was then proposed.

It was confirmed that optimization could be achieved for the large area LED molding process through finite element technique and experiment. Cure process can be drawn for optimum LED molding by investigating material properties even when silicone resin was adopted as material and by performing finite element analysis for the various cure processes (cure temperature, cure time, and heating mold changes) based on the experiment.

Acknowledgments

This study was supported by a grant from the Fundamental R&D Program, "The Development of LED Chip/Package Phosphor Conformal Coating System for White LED" and "Development of Rapid Compression Molding Technology with Continuous Carbon Fiber Reinforced Composite for the Car Weight-Lightning" funded by the Ministry of Trade, Industry & Energy, Republic of Korea, and Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT & Future Planning (MSIP) (no. 2007-0056094).

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

[1] D. Lu, C. P. Wong Materials for Advanced Packaging , Springer, 2008.

[2] M. J. Song, K. H. Kim, G. S. Yoon, H. P. Park, H. K. Kim, "An optimal cure process to minimize residual void and optical birefringence for a LED silicone encapsulant," Materials , vol. 7, pp. 4088-4104, 2014.

[3] S.-Y. Lee, G. S. Springer, "Filament winding cylinders. I. Process model," Journal of Composite Materials , vol. 24, no. 12, pp. 1270-1298, 1990.

[4] E. P. Calius, S.-Y. Lee, G. S. Springer, "Filament winding cylinders: II. Validation of the process model," Journal of Composite Materials , vol. 24, no. 12, pp. 1299-1343, 1990.

[5] S. Y. Lee, G. S. Springer, "Filament winding cylinders: III selection of the process variables," Journal of Composite Materials , vol. 24, pp. 1270-1298, 1990.

[6] A. C. Loos, G. S. Springer, "Curing of epoxy matrix composites," Journal of Composite Materials , vol. 17, no. 2, pp. 135-169, 1983.

[7] C. Kim, H. Teng, C. L. Tucker III, S. R. White, "Continuous curing process for thermoset polymer composites. Part 1: modeling and demonstration," Journal of Composite Materials , vol. 29, no. 9, pp. 1222-1253, 1995.

[8] T. A. Bogetti, J. W. Gillespie, "Two-dimensional cure simulation of thick thermosetting composites," Journal of Composite Materials , vol. 25, no. 3, pp. 239-273, 1991.

[9] Z.-S. Guo, S. Du, B. Zhang, "Temperature distribution of thick thermoset composites," Modelling and Simulation in Materials Science and Engineering , vol. 12, no. 3, pp. 443-452, 2004.

[10] A. Cheung, Y. Yu, K. Pochiraju, "Three-dimensional finite element simulation of curing of polymer composites," Finite Elements in Analysis and Design , vol. 40, no. 8, pp. 895-912, 2004.

[11] M. Hojjati, S. V. Hoa, "Curing simulation of thick thermosetting composites," Composites Manufacturing , vol. 5, no. 3, pp. 159-169, 1994.

[12] D. Rouison, M. Sain, M. Couturier, "Resin transfer molding of natural fiber reinforced composites: cure simulation," Composites Science and Technology , vol. 64, no. 5, pp. 629-644, 2004.

[13] K. Kasza, L. Matysiak, L. Malinowski, "Method to describe curing in large epoxy samples," Advances in Polymer Technology , vol. 28, no. 4, pp. 267-275, 2009.

[14] L. Liu, S. Yi, L. S. Ong, K. S. Chian, "Finite element analysis for microwave cure of underfill in flip chip packaging," Thin Solid Films , vol. 462-463, pp. 436-445, 2004.

[15] T. Behzad, M. Sain, "Finite element modeling of polymer curing in natural fiber reinforced composites," Composites Science and Technology , vol. 67, no. 7-8, pp. 1666-1673, 2007.

[16] A. Shojaei, S. R. Ghaffarian, S. M. H. Karimian, "Three-dimensional process cycle simulation of composite parts manufactured by resin transfer molding," Composite Structures , vol. 65, no. 3-4, pp. 381-390, 2004.

[17] S. C. Joshi, X. L. Liu, Y. C. Lam, "A numerical approach to the modeling of polymer curing in fibre-reinforced composites," Composites Science and Technology , vol. 59, no. 7, pp. 1003-1013, 1999.

[18] R. Sekula, P. Saj, T. Nowak, K. Kaczmarek, K. Forsman, A. Rautiainen, J. Grindling, "3-D modeling reactive molding processes: from tool development to industrial application," Advances in Polymer Technology , vol. 22, no. 1, pp. 42-55, 2003.

[19] S. Yi, H. H. Hilton, M. F. Ahmad, "A finite element approach for cure simulation of thermosetting matrix composites," Computers and Structures , vol. 64, no. 1-4, pp. 383-388, 1997.

[20] H. C. Park, N. S. Goo, K. J. Min, K. J. Yoon, "Three-dimensional cure simulation of composite structures by the finite element method," Composite Structures , vol. 62, no. 1, pp. 51-57, 2003.

[21] M. A. Choi, M. H. Lee, J. Chang, S. J. Lee, "Three-dimensional simulations of the curing step in the resin transfer molding process," Polymer Composites , vol. 20, no. 4, pp. 543-552, 1999.

[22] J. Zhang, Y. C. Xu, P. Huang, "Effect of cure cycle on curing process and hardness for epoxy resin," Express Polymer Letters , vol. 3, no. 9, pp. 534-541, 2009.

[23] S. Teplinsky, E. M. Gutman, "Computer simulation of process induced stress and strain development during cure of thick-section thermosetting composites," Computational Materials Science , vol. 6, no. 1, pp. 71-76, 1996.

[24] M. R. Kamal, S. Sourour, "Kinetics and thermal characterization of thermoset cure," Polymer Engineering & Science , vol. 13, pp. 59-64, 1973.

[25] M.-K. Um, I. M. Daniel, B.-S. Hwang, "A study of cure kinetics by the use of dynamic differential scanning calorimetry," Composites Science and Technology , vol. 62, no. 1, pp. 29-40, 2002.

[26] G. Wisanrakkit, J. K. Gillham, "The glass transition temperature (T_g ) as an index of chemical conversion for a high-T_g amine/epoxy system: chemical and diffusion-controlled reaction kinetics," Journal of Applied Polymer Science , vol. 41, no. 11-12, pp. 2885-2929, 1990.

[27] F. Hernandez-Sanchez, R. Vera-Graziano, "Determination of the kinetic parameters for the polymerization of a polyurethane using an improved method of differential scanning calorimetry," Journal of Applied Polymer Science , vol. 46, no. 4, pp. 571-580, 1992.

[28] S. Vyazovkin, "A unified approach to kinetic processing of non-isothermal data," International Journal of Chemical Kinetics , vol. 28, no. 2, pp. 95-101, 1996.

[29] A. Atarsia, R. Boukhili, "Relationship between isothermal and dynamic cure of thermaosets via the isoconversion representation," Polymer Engineering and Science , vol. 40, no. 3, pp. 607-620, 2000.

[30] D. Lu, C. P. Wong, "Effects of shrinkage on conductivity of isotropic conductive adhesives," International Journal of Adhesion and Adhesives , vol. 20, no. 3, pp. 189-193, 2000.

[31] T. A. Bogetti, J. W. Gillespie Jr., "Process-induced stress and deformation in thick-section thermoset composite laminates," Journal of Composite Materials , vol. 26, no. 5, pp. 626-660, 1992.

[32] J.-L. Bailleul, V. Sobotka, D. Delaunay, Y. Jarny, "Inverse algorithm for optimal processing of composite materials," Composites Part A: Applied Science and Manufacturing , vol. 34, no. 8, pp. 695-708, 2003.

[33] M. Li, C. L. Tucker III, "Optimal curing for thermoset matrix composites: thermochemical and consolidation considerations," Polymer Composites , vol. 23, no. 5, pp. 739-757, 2002.

[34] E. Ruiz, F. Trochu, "Comprehensive thermal optimization of liquid composite molding to reduce cycle time and processing stresses," Polymer Composites , vol. 26, no. 2, pp. 209-230, 2005.

[35] S. R. White, H. T. Hahn, "Cure cycle optimization for the reduction of processing-induced residual stresses in composite materials," Journal of Composite Materials , vol. 27, no. 14, pp. 1352-1378, 1993.

[36] A. K. Gopal, S. Adali, V. E. Verijenko, "Optimal temperature profiles for minimum residual stress in the cure process of polymer composites," Composite Structures , vol. 48, no. 1, pp. 99-106, 2000.

[37] E. Ruiz, F. Trochu, "Numerical analysis of cure temperature and internal stresses in thin and thick RTM parts," Composites Part A: Applied Science and Manufacturing , vol. 36, no. 6, pp. 806-826, 2005.

[38] N. Rai, R. Pitchumani, "Optimal cure cycles for the fabrication of thermosetting-matrix composites," Polymer Composites , vol. 18, no. 4, pp. 566-581, 1997.