Abstract
Thermal and structural austenite to martensite reversible transition was studied in melt spun ribbons of Ni50Mn40Sn5Co5, Ni50Mn37.5Sn7.5Co5 and Ni50Mn35Sn10Co5 (at. %) alloys. Analysis of X-ray diffraction patterns confirms that all alloys have martensitic structure at room temperature: four layered orthorhombic 4O for Ni50Mn40Sn5Co5, four layered orthorhombic 4O and seven-layered monoclinic 14M for Ni50Mn37.5Sn7.5Co5 and seven-layered monoclinic 14M for Ni50Mn35Sn5Co5. Analysis of differential scanning calorimetry scans shows that higher enthalpy and entropy changes are obtained for alloy Ni50Mn37.5Sn7.5Co5, whereas transition temperatures increases as increasing valence electron density.
You have requested "on-the-fly" machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Show full disclaimer
Neither ProQuest nor its licensors make any representations or warranties with respect to the translations. The translations are automatically generated "AS IS" and "AS AVAILABLE" and are not retained in our systems. PROQUEST AND ITS LICENSORS SPECIFICALLY DISCLAIM ANY AND ALL EXPRESS OR IMPLIED WARRANTIES, INCLUDING WITHOUT LIMITATION, ANY WARRANTIES FOR AVAILABILITY, ACCURACY, TIMELINESS, COMPLETENESS, NON-INFRINGMENT, MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE. Your use of the translations is subject to all use restrictions contained in your Electronic Products License Agreement and by using the translation functionality you agree to forgo any and all claims against ProQuest or its licensors for your use of the translation functionality and any output derived there from. Hide full disclaimer