Investigation on two abnormal phenomena about thermal conductivity enhancement of BN/EG nanofluids

Abstract

The thermal conductivity of boron nitride/ethylene glycol (BN/EG) nanofluids was investigated by transient hot-wire method and two abnormal phenomena was reported. One is the abnormal higher thermal conductivity enhancement for BN/EG nanofluids at very low-volume fraction of particles, and the other is the thermal conductivity enhancement of BN/EG nanofluids synthesized with large BN nanoparticles (140 nm) which is higher than that synthesized with small BN nanoparticles (70 nm). The chain-like loose aggregation of nanoparticles is responsible for the abnormal increment of thermal conductivity enhancement for the BN/EG nanofluids at very low particles volume fraction. And the difference in specific surface area and aspect ratio of BN nanoparticles may be the main reasons for the abnormal difference between thermal conductivity enhancements for BN/EG nanofluids prepared with 140- and 70-nm BN nanoparticles, respectively.

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

NANO EXPRESS Open Access

Investigation on two abnormal phenomena about thermal conductivity enhancement of BN/EG nanofluids

Yanjiao Li1,2*, Jingen Zhou1, Zhifeng Luo1, Simon Tung3, Eric Schneider3, Jiangtao Wu4 and Xiaojing Li4

Abstract

The thermal conductivity of boron nitride/ethylene glycol (BN/EG) nanofluids was investigated by transient hot-wire method and two abnormal phenomena was reported. One is the abnormal higher thermal conductivity enhancement for BN/EG nanofluids at very low-volume fraction of particles, and the other is the thermal conductivity enhancement of BN/EG nanofluids synthesized with large BN nanoparticles (140 nm) which is higher than that synthesized with small BN nanoparticles (70 nm). The chain-like loose aggregation of nanoparticles is responsible for the abnormal increment of thermal conductivity enhancement for the BN/EG nanofluids at very low particles volume fraction. And the difference in specific surface area and aspect ratio of BN nanoparticles may be the main reasons for the abnormal difference between thermal conductivity enhancements for BN/EG nanofluids prepared with 140- and 70-nm BN nanoparticles, respectively.

Introduction

The concept nanofluids was proposed by Choi [1] in 1995. Roughly speaking, nanofluids are solid-liquid composite materials consisting of solid nanoparticles or nanofibers with typically of 1-100 nm suspended in base liquid. Nanofluids provide a promising technical selection for enhancing heat transfer because of its anomalous high thermal conductivity and appear to be ideally suited for practical application with excellent stability and little or no penalty in pressure drop. As a result, nanofluids attract more and more interests theoretically and experimentally.

In the past decades, many investigations on thermal conductivity enhancement of nanofluids have been reported. These papers mainly focused on factors influencing thermal conductivity enhancement [2-16], mechanism for thermal conductivity enhancement [17-22], model for predicting the enhancement of thermal conductivity [23-29]. Recently, controversy about whether the dramatic increase of thermal conductivity with small nanoparticle loading in nanofluids is true was

reported [30,31]. Some researches showed that no anomalous enhancement of thermal conductivity with small nanoparticle loading was achieved in the nano-fluids and the thermal conductivity enhancement is moderate and can be predicted by effective medium theories. Besides, the mechanism of thermal conductivity enhancement is a hotly debated topic now, and many researchers pay attention to the influence of aggregation, morphology, and size of nanoparticles on thermal conductivity enhancement of nanofluids [32-39].

Focus on the current research interest, boron nitride/ ethylene glycol (BN/EG) nanofluid was synthesized by a two-step method. The effect of particles volume fraction and size of nanoparticles on thermal conductivity enhancement were investigated and two abnormal phenomena were observed. In present paper, the two abnormal phenomena are reported and the mechanism of thermal conductivity enhancement is discussed.

Experimental

BN powder of 140 and 70 nm with purity more than 99% were used as additives, as shown in Figure 1a, b, and ethylene glycol in analytical grade was employed as basefluid to prepare BN/EG nanofluids. A two-step method was used to synthesize BN/EG nanofluids. Proper quantities of BN powder weighed by a mass

* Correspondence: mailto:[email protected]

Web End [email protected]

1State Key Laboratory for Mechanical Behavior of Materials, School of Materials Science and Engineering, Xian Jiaotong University, Xian, Shanxi, 710049, ChinaFull list of author information is available at the end of the article

2011 Li et al; licensee Springer. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0

Web End =http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 2 of 7

(a) (b)

Figure 1 SEM image of the BN nanoparticles. (a) 140nm (b) 70nm.

balance with an accuracy of 0.1 mg were dispersed into the ethylene alcohol base fluid. No dispersant was added. In order to assure uniform dispersion of nano-particles in the base fluid, magnetic force stirring and ultrasonic agitation for 30 min were then employed, respectively. The apparatus and parameters for preparing nanofluids are shown in Table 1. The morphology of the dry nanoparticles was observed by a JEOL JSM-7000F scanning electron microscope (JEOL Ltd., Tokyo, Japan) and the nanoparticles suspended in the nanofluid were observed by a JEM-200CX transmission electron microscope (TEM; JEOL Ltd). The specific surface area of the nanosized BN powders were measured by Brunnauer-Emmett-Teller methods using a micromeritics ASAP 2020 surface area and porosity analyzer (Micro-meritics Instrument Corp., Norcross, GA, USA). The Crystalline structure of the BN nanoparticles was investigated by means of Rigaku D/MAX-2400 x-ray diffraction analysis (Rigaku Corp., Tokyo, Japan) (XRD) using Cu Ka radiation (l = 0.15418nm) at room temperature. The thermal conductivity of the BN/EG nanofluids was measured by transient hot-wire apparatus [40]. The uncertainty of this apparatus is between 2.0%. To improve the accuracy of the data, the thermal conductivity of BN/EG nanofluids with lower nanoparticles volume fraction was measured by an improved transient hot-wire apparatus [41]. This improved transient hot-wire apparatus is simpler and more robust compared to previous ones besides the improvement on accuracy [42,43]. The uncertainty of the improved transient hot-wire apparatus is between 0.51%.

Results and discussion

To investigate the effect of nanoparticle volume fraction on thermal conductivity enhancement of BN/EG nano-fluids, 0.2, 0.6, 1.0, 2.0, 3.0, 4.0, and 5.5 vol.% BN/EG nanofluids were synthesized and thermal conductivity of them was measured. The average size of the BN nano-particles used in these nanofluids is 140 nm. BN/EG nanofluid (1.25 vol.%) with the BN nanoparticles of 140 nm was prepared and its thermal conductivity was measured after depositing for 216 days. The volume fraction of the 1.25 vol.% BN/EG nanofluids after the depositing was 0.025 vol.%. In order to examine the effect of nano-particle size on thermal conductivity enhancement, 70-nm BN nanoparticles were used as additives to synthesize BN/EG nanofluids with the nanoparticles volume fraction of 1.0% to 5.5% and thermal conductivity of them was measured. The thermal conductivity enhancement of these nanofluids was calculated, as shown in Table 2. The measured thermal conductivity of ethylene alcohol was 0.247 W/mK. The data marked with an asterisk (*) was measured by an improved transient hot-wire apparatus [41].

Figure 2 shows the thermal conductivity enhancement of BN/EG nanofluids as a function of particle volume fraction. For volume fraction varying from 0.2 vol.% to5.5 vol.%, data fitting indicates that the thermal conductivity enhancement of BN/EG nanofluids increases linearly with the increment of nanoparticle volume fraction. The R value is 0.9981. The thermal conductivity enhancement predicted by Maxwells model [44] and Nans model [27] were also illustrated in Figure 2. Based

Table 1 Apparatus for preparing nanofluidsApparatus Specification Power Revolution speed/

frequency

Magnetic force stirring

78HW-1 25 W 1,600 rpm

Ultrasonic agitation SK1200H 45 W 59 Hz

Table 2 Thermal conductivity enhancement of the BN/EG nanofluids

Volume fraction (vol.%)

0.025 0.2 0.6 1.0 2.0 3.0 4.0 5.5

k/k (%) 140 nm 2.0* 0.8* 3.2* 5.7* 10.8 14.9 20.3 30.3 70 nm - - - 4.5 7.2 11.8 18.3 24.5

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 3 of 7

35

= (1 + 2p)Rbdkf /a33

a11, a22 and a33 are, respectively, radii of the ellipsoid along the X 1, X 2 and X 3 axes of this ellipsoidal composite unit cell, Lii are well-known geometrical factors dependent on the particle shape, p is the aspect ratio of the ellipsoide, km is the thermal conductivity of the matrix phase, kcii is quivalent thermal conductivities along the X i symmetric axis of this ellipsoidal composite unit cell, and Rbd is the Kapitza interfacial thermal resistance.

The conventional Maxwell model and Nans model severely underestimates the enhancement of thermal conductivity for BN/EG nanofluids. It may be ascribed to that Maxwell model only takes the effect of particle volume fraction into account for thermal conductivity enhancement of nanofluids without considering the effect of particle shape, nanolayers at solid/liquid interface, and Brownian motion of nanoparticles and others. Nans model is for particulate composites not for nano-fluids. Although Nans model considered the effect of nanoparticle shape and finite interfacial resistance, the effects of Brownian motion and aggregation of nanoparticles on thermal conductivity of nanofluids cannot be ignored. Now, no suitable model proposed by other researchers can fit well with the data we got. It is necessary to develop a new model considering all important factors influencing the thermal conductivity enhancement of BN/EG nanofluids. The work about this issue is being done by our group and will be reported later.

Some investigations reported in literature indicate that thermal conductivity enhancement will increase with the increment of volume fraction of nanoparticle [4,9,10]. That is to say that the thermal conductivity enhancement for nanofluids with low nanoparticle volume fraction must be lower than that of nanofluids with high-volume fraction of nanoparticle. But an absolutely different phenomenon was observed in current experiment. A2.0% enhancement of thermal conductivity was obtained for 0.025 vol.% BN/EG nanofluids prepared by setting1.25 vol.% BN (140 nm)/EG nanofluids for 216 days, which is much higher than a 0.8% increment for 0.2 vol. % BN (140 nm)/EG nanofluids prepared by a two-step method, as shown in Figure 3. To find the reason for this abnormal thermal conductivity enhancement, high-resolution TEM (HRTEM) observation of the nanoparticles suspended in the nanofluids was conducted.

Figure 4a, b showed the morphology of nanoparticles suspended in 0.025 vol.% and 0.2 vol.% BN/EG nano-fluids, respectively. It can be seen that the morphology of BN nanoparticles suspended in 0.025 vol.% BN/EG nanofluids is chain-like loose aggregation while in0.2 vol.% BN/EG nanofluids is cloud-like compact

30

ExperimentMaxwellNanLinear Fit of Data1_Experiment

25

20

'k/k/%

15

10

5

0 0 1 2 3 4 5 6

Volume fraction/vol%

Figure 2 Comparison of experimental results and theoretical model on thermal conductivity enhancement of BN/EG nanofluids vs. volume fraction of BN nanoparticles.

on Maxwells work, the effective thermal conductivity of a homogeneous suspension can be predicted as (Maxwell, 1873)

kkf =

kp + 2kf + 2(kp kf ) kp + 2kf (kp kf )

(1)

where kp is the thermal conductivity of the dispersed particles, kf is the thermal conductivity of the dispersion liquid, and j is the particle volume concentration of the suspension.

Equation 1 is valid for well-dispersed non-interacting spherical particles with negligible thermal resistance at the particle/fluid interface. Considering the effects of particle geometry and finite interfacial resistance, Nan et al. generalized Maxwells model to yield the following expression for the thermal conductivity ratio:

kkf =

3 + [211(1 L11) + 33(1 L33)] 3 (211L11 + 33L33)

(2)

where for particles shaped as prolate ellipsoids with principal axes a11 = a22 >a33

L11 = L22 = P2

2(P2 1)

+ P 2(1 P

2)3/2

cos1p; L33 = 1 2L11; p = a33[slashbig]a11

ii = kcii kmkm + Lii(kcii km)

kcii =

kp1 + Liikp[slashbig]km

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 4 of 7

10

8

6

'k/k/%

4

2

0 0.0 0.2 0.4 0.6 0.8 1.0 1.2

Volume Fraction/vol%

Figure 3 Thermal conductivity enhancement of BN/EG nanofluids.

aggregation. This discrepancy may be the main reason for the abnormal difference between the thermal conductivity enhancements of them. Generally, Brownian motion, by which particles move through liquid, thereby enabling direct solid-solid transport of heat from one to another, is considered as a key mechanism governing the thermal behavior of nanofluids [17-20]. In 0.025 vol. % BN/EG nanofluids, many uniform distributed chain-like loose aggregations of nanoparticles, acting as a three-dimensional dense network, can improve the heat transfer efficiency by providing many rapid, longer heat flow paths through Brownian motion of nanoparticles. While in 0.2 vol.% BN/EG nanofluids, high efficient heat transfer was limited in cloud-like compact aggregation. Heat transfer among cloud-like compact aggregations would be weakened for the large regions of particle-free liquid with high thermal resistance. It can be speculated

that a more high thermal conductivity could be obtained when the volume fraction of these uniform distributed chain-like loose aggregations of nanoparticles in BN/EG nanofluid was increased because more efficient heat flow paths in the nanofluid could be provided.

The volume fraction of this 0.025 vol.% BN/EG nano-fluids was measured after sedimentation for 120 days and the value of it is 0.017 vol.%. This phenomenon indicated that the stability of the nanofluid is excellent. And the long-term stability of this nanofluid may be ascribed to the flake-like morphology and incompact aggregation of the BN nanoparticles, as showed in Figure 4a. It can be expected that the stability of this nanofluid can be improved further when some appropriate dispersant was used. The phenomenon mentioned above indicates that nanofluids with high thermal conductivity and long-term stability can be obtained by adding relatively lower volume fraction of nanoparticles when the nanoparticles suspended in base liquid with proper morphology and aggregation. This kind of nano-fluid is promising for engineering application.

Size of nanoparticles is an important factor influencing thermal conductivity of nanofluids because shrinking it down to nanoscale not only increases the surface area relative to volume but also generates some nanoscale mechanisms in the suspensions [18,24]. Theoretical evidence [18,24,35] indicate that the effective thermal conductivity of nanofluids increases with decreasing particle size. Some experimental research [36-39] showed that as the nanoparticle diameter is reduced, the effective thermal conductivity of nanofluids becomes larger. The reason for this phenomenon was interpreted as the high specific surface area of small nanoparticles and intensified micro-convection provoked by small nano-particles. While in present study, thermal conductivities of BN/EG nanofluids synthesized with 140- and 70-nm

(a) (b)

Figure 4 HRTEM micrographs of BN nanoparticles suspended in BN/EG nanofluids. (a) Chain-like loose aggregation of BN nanoparticles in0.025vol% BN/EG nanofluids. (b) Cloud-like compact aggregation of BN nanoparticles in 0.2Vol% BN/EG nanofluids.

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 5 of 7

BN nanoparticles were measured and a different phenomenon was observed, as shown in Figure 5. It can be found that the thermal conductivity enhancement of nanofluids synthesized with large size (140 nm) BN nanoparticles is higher than that synthesized with small size (70 nm) BN nanoparticles. Hong [4] and Xie [9] also found similar phenomenon. This phenomenon is much different from the normal rule. What was the reason for this abnormal difference in thermal conductivity enhancement? The author believed that it can be ascribed to the difference in shape of the BN nanoparticles by x-ray diffraction (XRD) analysis, HRTEM images, and specific surface area of the BN nanoparticles.

Figure 6a is an XRD pattern of the BN powder with different size. Figure 6b is a partial enlarged pattern of Figure 6a. From Figure 6b, we can observe that the BN powder was composed of different phases. Hexagonal BN and cubic BN are the main phases for 140-nm BN powder. The weight ratio of hexagonal BN and cubic BN is about 93:7 through qualitative analysis made by the software attached by the Rigaku D/MAX-2400 x-ray diffraction analysis. For 70-nm BN powder, hexagonal BN, rhombohedral BN, and cubic BN are the main phases and the weight ratio of these three different phases is about 62:35:3. So we can conclude that the 140-nm BN powder are mainly composed of flake-like hexagonal BN while 70-nm BN powder are composed of 62% flake-like hexagonal BN and 38% BN with different shape.

Further observation on HRTEM image of these two kinds of BN nanoparticles indicates that the qualitative analysis about the phase component of 140-nm BN nano-particles and 70-nm BN nanoparticles is correct, as shown in Figure 7a, b. The morphology of 140-nm BN

(a)

Intensity(cps)

20 30 40 50 60 70 80

2 (degree)

140nm

70nm

Hexagnoal BN Cubic BN Rhombohedral BN

(b)

Intensity(cps)

140nm

70nm

20 30 40 50 60 70 80

2 (degree)

Figure 6 XRD patterns of the BN nanoparticles. (a) Original pattern (b) partial enlarged pattern.

35

30

BN(140nm)/EG

BN(70nm)/EG

nanoparticles is nearly all ellipsoid. However, the morphology of 70-nm BN nanoparticles is composed of cubic, ellipsoid, and spherical shape, as marked by arrows 1, 2, and 3 in Figure 7b. Moreover, the shape for most 70-nm BN nanoparticles is cubic and spherical, only few ellipsoid nanoparticles are observed. This difference in morphology indicate that nearly all 140-nm BN nanoparticles is composed of flake-like H-BN nanoparticles while 70-nm BN nanoparticles is composed of fewer flake-like H-BN and many cubic and spherical BN nanoparticles. For the specific surface area of flake-like nanoparticles is higher than that of cubic and spherical nanoparticles, the specific surface area of 140-nm BN nanoparticles is expected to be higher than that of 70-nm BN nanoparticles. Experiment showed that the specific surface area of 140-nm BN powder is 40.6098 m2/g while that of 70-nm BN powder is

25

20

'k/k/%

15

10

5

0

1 2 3 4 5 6

Volume Fraction/vol%

Figure 5 Thermal conductivity enhancement vs. volume fraction for BN/EG nanofluids with different size of BN nanoparticles.

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 6 of 7

(a) (b)

2

3

1

Figure 7 HRTEM image of the BN nanoparticles. (a) 140 nm (b) 70 nm.

35.71 m2/g. Besides, the aspect ratio of ellipsoid nanoparticles is higher than that of cubic and spherical nanoparticles. So the aspect ratio of 140-nm BN nanoparticles is higher than that of 70-nm BN nanoparticles. These differences in specific surface area and aspect ratio of 140-nm BN nanoparticles and 70-nm BN nanoparticles may be the main reasons for the abnormal different in thermal conductivity enhancement because heat transfer between the nanoparticle and the base fluid can be promoted for the larger specific surface area. Furthermore, rapid, longer heat flow paths are apt to the formation between higher aspect ratio nanoparticles and these heat flow paths can promote heat transfer also. The action of these two aspects leads to the enhancement of thermal conductivity for BN/ EG nanofluids synthesis with 140-nm BN nanoparticles is higher than that synthesized with 70-nm BN nanoparticles.

Conclusions

In summary, two abnormal phenomena about thermal conductivity enhancement of BN/EG nanofluids was investigated. One is the abnormal increment of thermal conductivity for BN/EG nanofluids at very low volume fraction, and the other is the abnormal thermal conductivity enhancement for BN/EG nanofluids synthesized with different size of BN nanoparticles. The chain-like loose aggregation of nanoparticles is responsible for the abnormal increment of thermal conductivity in the BN/EG nanofluids with very low particles volume fraction. And the difference in specific surface area and aspect ratio of BN nanoparticles may be the main reason for the abnormal difference between thermal conductivity enhancements for BN/ EG nanofluids prepared with 140 and 70-nm BN nano-particles, respectively.

AcknowledgementsThe authors acknowledge the financial support from GM Corporation for this work.

Author details

1State Key Laboratory for Mechanical Behavior of Materials, School of Materials Science and Engineering, Xian Jiaotong University, Xian, Shanxi, 710049, China 2Xian Research Inst. Of Hi-Tech, Hongqing Town, Xian, 710025, China 3GM R &D Center, 480-106-160, 30500 Mound Road Warren, MI 48090-9055, USA 4State Key Laboratory of Multiphase Flow in Power Engineering, Xian Jiaotong University, Xian, Shanxi 710049, China

Authors contributionsYL carried out the experimental studies and drafted the manuscript. JZ guide the experimental studies and revised the manuscript. ZL carried out part of the experimental studies. ST and ES participated in experiment design and coordination. JW, XL participated in the measurement of part of the thermal conductivity data. All authors read and approved the final manuscript.

Competing interestsThe authors declare that they have no competing interests.

Received: 8 November 2010 Accepted: 9 July 2011 Published: 9 July 2011

References1. Choi SUS: Developments and Applications of Non-Newtonian Flows New York: ASME; 1995, (FED-vol.231/MD-vol 66:99).

2. Eastman JA, Choi SUS: Anomalously increased effective thermal conductivities of ethylene glycol-based nanofluids containing copper nanoparticles. Appl Phys Lett 2001, 78:718.

3. Liu MS, Lin MCC, Tsai CY, Wang CC: Enhancement of thermal conductivity with cu for nanofluids using chemical reduction method. Int J Heat Mass Transf 2006, 49:3028.

4. Hong TK, Yang HS, Choi CJ: Study of the enhanced thermal conductivity of Fe nanofluids. J Appl Phys 2005, 97:064311.

5. Patel HE, Das SK, Sundararagan T, Nair AS, Geoge B, Pradeep T: Thermal conductivities of naked and monolayer protected metal nanoparticle based nanofluids: manifestation of anomalous enhancement and chemical effects. Appl Phys Lett 2003, 83:2931.

6. Putnam SA, Cahill DG, Braun PV: Thermal conductivity of nanoparticle suspensions. J Appl Phys 2006, 99:084308.

Li et al. Nanoscale Research Letters 2011, 6:443 http://www.nanoscalereslett.com/content/6/1/443

Page 7 of 7

7. Zhu H, Zhang C, Liu S: Effects of nanoparticle clustering and alignment on thermal conductivities of Fe3O4 aqueous nanofluids. Appl Phys Lett 2006, 89:23123.

8. Murshed SMS, Leong KC, Yang C: Enhanced thermal conductivity of TiO2-

water based nanofluid. Int J Therm Sci 2005, 44:367.9. Xie H, Wang J, Xi T, Liu Y, Ai F: Thermal conductivity enhancement of suspensions containing nanosized alumina particle. J Appl Phys 2002, 91:4568.

10. Choi SUS, Zhang ZG, Yu W, Lockwood FE, Grulke EA: Anomalous thermal conductivity enhancement in nanotube suspension. Appl Phys Lett 2001, 79:2252.

11. Xie HQ, Lee H, Youn W, Choi M: Nanofluids containing multiwalled carbon nanotubes and their enhanced thermal conductivities. J ApplPhys 2003, 94:4967.

12. Yang B, Han ZH: Thermal conductivity enhancement in water-in-FC72 nanoemulsion fluid. Appl Phys Lett 2006, 88:261914.

13. Ma KQ, Liu J: Nano liquid-metal fluid as ultimate coolant. Phys Lett 2007, A361:252.

14. Wei X, Wang L: Synthesis and thermal conductivity of microfluidic copper nanofluids. Particuology 2010, 8:262.

15. Wang X, Zhu D, Yang S: Investigation of pH and SDBS on enhancement of thermal conductivity in nanofluids. Chem Phys Lett 2009, 470:107.

16. Wei X, Zhu H, Kong T, Wang L: Synthesis and thermal conductivity of Cu2O nanofluids. Int J Heat Mass Transf 2009, 52:4371.

17. Xuan Y, Li Q, Zhang X, Fujii M: Stochastic thermal transport of nanoparticle suspensions. J Appli Phys 2006, 100:043507.18. Keblinski P, Phillpot SR, Choi SUS: Mechanisms of heat flow in suspensions of nano-sized particles (nanofluids). Int J Heat Mass Transf 2002, 45:855.

19. Eastman JA, Phillpot SR, Choi SUS, Keblinski P: Thermal transport in nanofluids. Annu Rev Mater Res 2004, 34:219.

20. Xie HQ, Xi TG, Wang JC: Study on the mechanism of heat conduction in nanofluid medium. Acta Phys Sin 2003, 52:1444.

21. Prasher R, Phelan PE, Bhattacharya P: http://www.ncbi.nlm.nih.gov/pubmed/16834444?dopt=Abstract

Web End =Effect of aggregation kinetics on the http://www.ncbi.nlm.nih.gov/pubmed/16834444?dopt=Abstract

Web End =thermal conductivity of nanoscale colloidal solutions (nanofluid). Nano Lett 2006, 6:1529.

22. Evans W, Prasher R, Fish J, Meakin P, Phelan P, Keblinski P: Effect of aggregation and interfacial thermal resistance on thermal conductivity of nanocomposite and colloidal nanofluids. Int J Heat Mass Transf 2008, 51:1431.

23. Leong KC, Yang C, Murshed SMS: A model for the thermal conductivity of nanofluidsthe effect of interfacial layer. J Nanopart Res 2006, 8:245.24. Yu W, Choi SUS: The role of interfacial layers in the enhanced thermal of nanofluids: a renovated maxwell model. J Nanopart Res 2003, 5:167.

25. Xue QZ: Model for effective thermal conductivity of nanofluids. Phys Lett 2003, A307:313.

26. Xue Q, Xu WM: A model of thermal conductivity of nanofluids with interfacial shells. Mater Chemist Phys 2005, 90:298.

27. Nan CW, Birringer R, Clarke DR, Gleiter H: Effective thermal conductivity of particulate composites with interfacial thermal resistance. J Appl Phys 1997, 81:6692.

28. Nan CW, Shi Z, Lin Y: A simple model for thermal conductivity of carbon nanotube-based composites. Chem Phys Lett 2003, 375:666.

29. Murshed SMS, Leong KC, Yang C: A combined model for the effective thermal conductivity of nanofluids. Appli Therm Eng 2009, 29:2477.

30. Buongiorno J, Venerus DC, Prabhat N, McKrell T, Townsend J,Christianson R, Tolmachev YV, Keblinski P, Hu LW, Alvarado JL, Bang IC, Bishnoi SW, Bonetti M, Botz F, Cecere A, Chang Y, Chen G, Chen H,Chung SJ, Chyu MK, Das SK, Di Paola R, Ding Y, Dubois F, Dzido G, Eapen J, Escher W, Funfschilling D, Galand Q, Gao J, Gharagozloo PE, Goodson KE, Gutierrez J G, Hong H, et al: A benchmark study on the thermal conductivity of nanofluids. J Appl Phys 2009, 106:094312.

31. Keblinski P, Prasher R, Eapen J: Thermal conductance of nanofluids: is the controversy over? J Nanopart Res 2008, 10:1089.

32. Peasher R, Phelan PE, Bhattacharya P: http://www.ncbi.nlm.nih.gov/pubmed/16834444?dopt=Abstract

Web End =Effect of Aggregation Kinetics on http://www.ncbi.nlm.nih.gov/pubmed/16834444?dopt=Abstract

Web End =the Thermal Conductivity of Nanoscale Colloidal Solutions (Nanofluid). Nano Lett 2006, 6(7):1529.

33. Karthikeyan NR, Philip J, Raj B: Effect of clustering on the thermal conductivity of nanofluids. Mater Chemist Phys 2008, 109:50.

34. Chen G, Yu W, Singh D, Cookson D, Routbort J: Application of SAXS to the study of particle-size-dependent thermal conductivity in silica nanofluids. J Nanopart Res 2008, 10:1109.

35. Jang SP, Choi SUS: Role of Brownian motion in the enhanced thermal conductivity of nanofluids. Appli Physi Lett 2004, 84:4316.

36. Chon CH, Kihm KD, Lee SP, Choi SUS: Empirical correlation finding the role of temperature and particle size for nanofluid(Al2O3) thermal conductivity enhancement. Appl Phys Lett 2005, 87:153107.37. Kim SH, Choi SR, Kim DS: Thermal Conductivity of Metal-Oxide Nanofluids: Particle Size Dependence and Effect of Laser Irradiation. ASME J Heat Transfer 2007, 129:298.

38. Jang SP, Choi SUS: Effects of Various Parameters on Nanofluid Thermal Conductivity, Journal of Heat Transfer. J of Heat Transfer 2007, 129:617.

39. Peng XF, Yu XL, Zhong X, Yu QF: Experiments on thermal conductivity of nanofluids. J Zhejiang University (Engineering Science) (in Chinese) 2007, 41(7):1177.

40. Luo ZF: http://www.ncbi.nlm.nih.gov/pubmed/21748728?dopt=Abstract

Web End =Investigation on Preparation and Properties of Dielectric http://www.ncbi.nlm.nih.gov/pubmed/21748728?dopt=Abstract

Web End =Nanofluids. Masters thesis Xian Jiaotong University, School of Materials Science and Engineering; 2009.

41. Wu JT, Zheng HF, Qian XH, Li XJ, Assael MJ: Thermal Conductivity of Liquid 1, 2-Dimethoxyethane from 243K to 353K at Pressures up to 30Mpa. Int J Thermophys 2009, 30:385.

42. Wang YG, Wu JT, Liu ZG: Thermal Conductivity of Gaseous Dimethyl Ether from (263 to 383) K. J Chem Eng Data 2006, 51:164.

43. Jin XG, Wu JT, Liu ZG, Pan J: The thermal conductivity of dimethyl carbonate in the liquid phase. Fluid Phase Equilibria 2004, 220:37.

44. Maxwell JC: A Treatise on Electricity and Magnetism. 2 edition. Oxford: Clarendon; 1881.

doi:10.1186/1556-276X-6-443Cite this article as: Li et al.: Investigation on two abnormal phenomena about thermal conductivity enhancement of BN/EG nanofluids. Nanoscale Research Letters 2011 6:443.

Submit your manuscript to a journal and benet from:

7 Convenient online submission7 Rigorous peer review7 Immediate publication on acceptance7 Open access: articles freely available onlihttp://www.springeropen.com/

Web End =ne 7 High visibility within the eld7 Retaining the copyright to your article

Submit your next manuscript at 7 http://www.springeropen.com/

Web End =springeropen.com