Cathodoluminescence spectra of gallium nitride nanorods

Abstract

Gallium nitride [GaN] nanorods grown on a Si(111) substrate at 720°C via plasma-assisted molecular beam epitaxy were studied by field-emission electron microscopy and cathodoluminescence [CL]. The surface topography and optical properties of the GaN nanorod cluster and single GaN nanorod were measured and discussed. The defect-related CL spectra of GaN nanorods and their dependence on temperature were investigated. The CL spectra along the length of the individual GaN nanorod were also studied. The results reveal that the 3.2-eV peak comes from the structural defect at the interface between the GaN nanorod and Si substrate. The surface state emission of the single GaN nanorod is stronger as the diameter of the GaN nanorod becomes smaller due to an increased surface-to-volume ratio.

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

NANO EXPRESS Open Access

Cathodoluminescence spectra of gallium nitride nanorods

Chia-Chang Tsai1, Guan-Hua Li1, Yuan-Ting Lin1, Ching-Wen Chang1, Paritosh Wadekar1, Quark Yung-Sung Chen1, Lorenzo Rigutti2, Maria Tchernycheva2, Franois Henri Julien2 and Li-Wei Tu1*

Abstract

Gallium nitride [GaN] nanorods grown on a Si(111) substrate at 720C via plasma-assisted molecular beam epitaxy were studied by field-emission electron microscopy and cathodoluminescence [CL]. The surface topography and optical properties of the GaN nanorod cluster and single GaN nanorod were measured and discussed. The defect-related CL spectra of GaN nanorods and their dependence on temperature were investigated. The CL spectra along the length of the individual GaN nanorod were also studied. The results reveal that the 3.2-eV peak comes from the structural defect at the interface between the GaN nanorod and Si substrate. The surface state emission of the single GaN nanorod is stronger as the diameter of the GaN nanorod becomes smaller due to an increased surface-to-volume ratio.

Keywords: gallium nitride, nanorod, cathodoluminescence, scanning electron microscopy

Introduction

Recently, the applications of semiconductor materials in optoelectronic devices grow rapidly. Among them, due to the high thermal conductivity, wide direct bandgap, and chemical stability, III-V family nitride-based semiconductors, including aluminum nitride [AlN], gallium nitride [GaN], and indium nitride [InN], and their alloys have attracted lots of studies in the applications on light-emitting diodes and laser diodes. The bandgaps for AlN, GaN, and InN are 6.2 eV, 3.4 eV, and 0.65 eV, respectively. By varying the composition of these three nitride-based materials, the emission light energy will range from 0.65 eV to 6.2 eV [1]. Through the studies of the fundamental properties of the nitride-based materials, one can get more insight into the applications of these materials.

Semiconductor nanowires have attracted a lot of attention due to the large surface-to-volume ratio in the nanoscale dimension and their applications on nanode-vices [2,3]. Since the first investigations of GaN nanorods (also called nanowires or nanocolumns) in 1997 [4,5], these one-dimensional [1D] GaN nanorods have

attracted a lot of studies on the growth methods [6-9], physical properties [10-13], and their applications [14-16]. The geometric structures will greatly affect the optical and electrical properties of these nitride-based materials. It has been reported that 1D GaN nanorods have higher photoluminescence intensity than two-dimensional GaN due to the large surface-to-volume ratio [16]. Furthermore, in the applications of GaN materials, the defects of GaN will affect the electrical and optical properties of the GaN-based devices greatly and thus affect the performance and reliability of the devices [17].

In this work, we studied the surface topography and optical properties of the GaN nanorod cluster and single GaN nanorod via field-emission scanning electron microscopy [FE-SEM] and cathodoluminescence [CL]. The vertically aligned GaN nanorods were grown on a Si(111) substrate at 720C without a buffer layer via plasma-assisted molecular beam epitaxy [PAMBE] [18,19]. Temperature-dependent CL spectra of the GaN nanorods were carried out to study the defect states of GaN nanorods. CL spectra at different positions along the length of the nanorod were also measured to investigate the size-dependent properties of GaN nanorods.

* Correspondence: mailto:[email protected]

Web End [email protected]

1Department of Physics and Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung, Taiwan, 80424, Republic of China Full list of author information is available at the end of the article

2011 Tsai et al; licensee Springer. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.0

Web End =http://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 2 of 7

ExperimentGaN nanorod growthThe PAMBE system used in the GaN nanorod growth was Veeco EPI 930 (Veeco Instruments Inc., Plainview, NY, USA). Ultra-high pure nitrogen gas(99.9999% purity) was supplied for the radio-frequency plasma source via a mass flow controller. The Ga source (99.999995% purity) was loaded in a Knudsen effusion cell. The base pressure of the PAMBE chamber was pumped down below 3 10-11 Torr by a

cryogenic pump. Before starting the growth process of the GaN nanorods, the Si substrate was cleaned by acetone, isopropanol, and deionized water, respectively, with ultrasonication to remove residual surface contamination. Then, the native oxide of the Si substrate was removed by a diluted hydrofluoric acid [HF] solution (HF:H2O = 1:5) for 5 min. The hydrogen-terminated Si(111) substrate was then transferred to the growth chamber. Prior to the growth of the GaN nanorods, the Si substrate was further annealed at 900C for 30 min to remove atomic hydrogen [20] and residual native oxide [21] with an orderly 7 7 reflection high-energy electron diffraction pattern. Thereafter, the substrate was cooled down to the growth temperature of 720C to adjust the beam equivalent pressure [BEP]. When Ga BEP was well-controlled to about 2.5 10-7 Torr by changing the temperature of the Knudsen effusion cell, N BEP was then adjusted to about 2.5 10-5 Torr. By preserving the growth temperature and the BEPs (Ga and N) for 3 h, the GaN nanorod cluster was successfully grown on the Si substrate.

Separation and position of a single GaN nanorodIn order to separate and position a single GaN nanorod for CL measurement, the nanorods were scratched from the as-grown GaN nanorod substrate by a small tweezer and then knocked down on a Si substrate with a little hammer. GaN nanorods were dissolved in ethanol with an ultrasonicator for 10 min. Thereafter, the GaN nanorods were dropped on a gold-coated Si substrate covered with a copper-based network for identifying the position of the GaN nanorods.

FESEM and CL measurement systems The measurement system used in this work is FE-SEM (JEOL JSM-7000F, JEOL Ltd., Akishima, Tokyo, Japan). The best resolution can be approximately 1.5 nm at an acceleration voltage of 35 kV. The CL measurement was performed by the JSM-7000F FE-SEM (JEOL Ltd., Akishima, Tokyo, Japan) equipped with a Gatan MonoCL system (Gatan, Inc., Pleasanton, CA, USA). The spectrum range of the CL measurement was 200 nm to 2,300 nm.

Results and discussion

Figure 1a, b shows the top view and the side view of the secondary electron images [SEIs] of the as-grown GaN nanorod cluster on the Si(111) substrate obtained by FE-SEM, respectively. The electron acceleration voltage is 20 kV and the magnifications of the top-view SEI and side-view SEI are 40,000 and 20,000, respectively. From the top-view SEI of the GaN nanorod cluster, the diameters of the nanorods on the Si substrate are about 50 to approximately 100 nm. The length of the GaN nanorods among the cluster is about 1.9 m. There are disordered GaN nanorods appearing at the junction between the GaN nanorods and silicon substrate indicated in Figure 1b.

The temperature-dependent CL spectra of the GaN nanorod cluster are measured at temperature T = 20 K to 300 K as shown in Figure 2a. The near-band-edge [NBE] emission of approximately 3.4 eV at T = 300 K reveals a blueshift with decreasing temperature as shown in Figure 2b. At T = 20 K, the peak energy of the NBE emission is about 3.45 eV. The peak energy change of the CL spectra for the decrease in temperature from 300 K to 20 K is 64 meV. When the temperature is lower than 100 K, the intensity of the CL spectra at 3.4 eV became stronger. The position of the peak appearing at 3.4 eV does not change with temperature, and it is ascribed to the surface state of the GaN nanorods [18] due to the low-dimensional structures of the GaN nanorods which can trap charge carriers. With the increasing temperature, the trapped charge carriers on surface states will become more unstable and thus reduce the intensity of the CL spectra. Furthermore, a peak at a photon energy of about 3.2 eV appeared at T = 20 K and became stronger with decreasing temperature. This peak is very weak at 300 K which cannot be easily recognized in the scale in Figure 2a. This peak corresponds to the defect state Y7 reported previously [17,22]. It is suggested that the Y7 peak comes from the recombination of an exciton bound to the point defect which is trapped by the stress field of the dislocation[17]. The temperature-dependent plots for the NBE and Y7 states are shown in Figure 2b. The results can be fitted with the Varshini equation [23]:

Eg (T) = Eg (0)

T2T + , (1)

where Eg(T) is the energy gap of the semiconductor at temperature T, Eg(0) is the energy gap at T = 0 K, a is Varshnis thermal coefficient, and b is the Debye temperature. The red and blue solid lines are obtained via least-square fitting according to the Varshni equation. The data were fitted well with a fixed parameter a = 5.3 10-4 eV K-1 because the thermal coefficient should be

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 3 of 7

(a)

(b)

Figure 1 FESEM images of GaN nanorods grown on Si(111) substrate. (a) Top view and (b) side view.

similar to that of the same materials grown in the same condition, e.g., GaN nanorods grown on the Si(111) substrate via the PAMBE system [24]. The fitted results for NBE state are Eg(0) = 3.46 eV and b = 515.7 K. As to the Y7 state, the results are Eg(0) = 3.12 eV and b = 598.6 K. To further investigate the source of the Y7 defect state, the CL spectrum at T = 20 K (Figure 2c) is carried out at the junction between the GaN nanorods and Si substrate as indicated in a red circle in Figure 1b. The CL spectrum is fitted with a multiple-peak Gaussian model:

y = y0 +

2(x xi)2w2i , (2)

where y0 is baseline offset, Ai is the area under each Gaussian curve from the baseline, xi is the center of each Gaussian peak, n = 3 is the number of peak, and wi is approximately 0.849 of the full width at half maximum for each peak. There exist three peaks of the photon energy at 3.21 eV, 3.35 eV, and 3.45 eV which

n

[summationdisplay]

i=1

Ai

wi

2

e

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 4 of 7

(a)

250000

Surface state

Intensity (arb. units)

200000

20 K

45 K

75 K

100 K

200 K

300 K

NBE

150000

100000

Y7

50000

0

3.0 3.1 3.2 3.3 3.4 3.5 3.6 3.7

Photon Energy (eV)

(b)

3.45

Photon Energy (eV)

3.40

NBE

Y7

Fitted NBE

Fitted Y7

3.20

3.15

0 50 100 150 200 250 300

Temperature (K)

(c)

25000

NBE

Intensity (arb. units)

20000

Y4

Y7

15000

10000

5000

0

3.0 3.1 3.2 3.3 3.4 3.5 3.6 3.7

Photon Energy (eV)

Figure 2 CL spectra and peak energies. (a) CL spectra of the GaN nanorods (as shown in Figure 1a) taken at temperatures of 20 K to 300 K. (b) Temperature-dependent NBE peak energy and defect-related (Y7) peak energy. The red and blue solid curves are the Varshni-equation-fitted curves of NBE and Y7 states, respectively. (c) The CL spectrum of the GaN nanorods was performed at a temperature of 20 K and at the position of the red-circled region indicated in (a). The CL spectrum was fitted by a three-peak Gaussian model.

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 5 of 7

correspond to Y7, Y4, and NBE, respectively. The 3.35 eV or Y4 peak observed in GaN has been assigned to the excitons bound to the stacking faults in the as-grown GaN samples [17]. Additionally, the Y4 and Y7 lines are reported to simultaneously appear among the GaN epilayers. For low-temperature CL measurements (T = 20 K), we can compare the CL spectra performed at different locations: the top of the GaN nanorod cluster and the side of the GaN nanorod cluster. The results show that the intensity ratio of the Y7/NBE as shown in

Figure 2c became larger than that measured in the GaN nanorod cluster (shown in Figure 2a). Accordingly, we could suggest that the Y7 line arises from the junction between the GaN nanorods and Si substrate because the junction contains more defects, owing to the broken GaN nanorods or randomly aligned short GaN nanorods. Furthermore, the CL spectra carried out on top of the GaN nanorod cluster show a strong surface-state peak but without the Y4 line. In contrast, the Y4 line appears in the CL spectra measured on the side of the GaN nanorod cluster. The result further reveals that the surface state is due to the tip of the GaN nanorod.

Figure 3a shows the FE-SEM image of an isolated GaN nanorod placed on a gold-coated Si substrate. The length of the isolated GaN nanorod is approximately 1.3 m which is shorter than that measured in the GaN nanorod cluster, mainly owing to the GaN isolation process. From bottom (R1) to top (R5) as indicated in Figure 3a, the diameters of the GaN nanorod which are located at the center position of each colored box are35.6, 50.6, 72.4, 86.2, and 85.1 nm, respectively. To compare the CL spectra of the GaN nanorod cluster and that of a single GaN nanorod, the temperature-dependent CL spectra of a single GaN nanorod is measured at temperature T = 25 K to 300 K as shown in Figure 3b. The measured spectra exhibit fluctuation noise, mainly owing to the weakness of the CL signal of a single GaN nanorod because of the small interaction volume between the electron beam and the individual GaN nanorod. The results show a single CL peak (about 3.4 eV to 3.45 eV) at various temperatures. This peak comes from the convolution of NBE and surface state of the single GaN nanorod and also revealed a blueshift (approximately 60 meV) as temperature decreased

(a)

(c)

1000

T = 20 K

R1 bottom

R2

R3

R4

R5 top

800

R4

Intensity (arb. units)

R5

600

R3

400

R2

200

R1

0 3.2 3.3 3.4 3.5 3.6 3.7 3.8

(b)

(d)

Photon Energy (eV)

3.36 30 40 50 60 70 80 90

1600

3.40

30 40 50 60 70 80 90

0

900

3.45 eV

1400

Intensity (arb. units)

25 K

45 K

75 K

200 K

300 K

1200

3.39

R4

R5

1000

600

600

Photon Energy (eV)

800

3.38

R3

Intensity (arb. unit)

R1

R2

400

300

200

3.37

0

-200

3.4 eV

3.2 3.3 3.4 3.5 3.6 3.7 3.8

Photon Energy (eV)

Diameter (nm)

Diameter (nm)

Figure 3 FESEM images, CL spectra, and peak energy. (a) FESEM images of a single GaN nanorod dispersed on a Si substrate. (b) Temperature-dependent CL spectra of a single GaN nanorod. The near-band-edge peaks were blueshifted as the temperature decreased. (c) Position-dependent CL spectra of the single GaN nanorod at T = 20 K. Each position of the GaN nanorod from top to bottom corresponds to the color box region indicated in (a). (d) The peak energy determined by Gaussian fitting and the peak intensity against the spectrum base line in (c) were plotted versus the GaN nanorod diameter.

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 6 of 7

because of the energy shift of the NBE line. In this measurement, the Y7 defect line is absent because the defect source of GaN could be broken and left on the Si substrate during the GaN nanorod isolation process. Furthermore, as the GaN nanorod was isolated from the Si(111) substrate which was the growth substrate and placed on the separated gold-coated Si substrate, the interface is different from that of the GaN nanorod grown on the Si(111) substrate. Additionally, the CL spectra along the GaN nanorod from bottom to top were also investigated as shown in Figure 3c. To further analyze the CL spectra of the single GaN nanorod, the CL spectra are fitted with a single Gaussian function (n = 1 in Equation 2). The fitted peak centers and the intensity of each peak against the base line of the CL spectra are plotted versus the GaN diameter from the bottom to the top as shown in Figure 3d. In our analysis, the peak center of the CL spectrum would be affected by the stability of the CL system and the data analysis of Gaussian fitting. In addition, the peak center will be influenced by the noise and baseline of the spectrum. Therefore, we just analyzed the peak shift between the position of the GaN nanorod at the bottom position (R1) and that at the top position (R5) measured. Compared to the top position, the CL peak shows a blueshift of about 15 meV at the bottom position. According to the quantum confinement theory developed for the Mott-Wannier type excitons of large Bohr radius (11 nm for GaN) [25] confined in nanometer-sized semiconductors, the energy shift of NBE can be expressed as[26]:

E =

[parenleftbigg]

1 me +

1 mh

[parenrightbigg][parenleftbigg]

h2 2D2

, (3)

where me, mh, h, and D are the effective electron mass, effective hole mass, Plank constant, and diameter of nanorod, respectively. For GaN, me and mh are 0.22 m0 and 1.1 m0 (m0 = 9.11 10-31kg is the electron mass) [27], respectively. The estimated E at the bottom of the GaN nanorod (D 35 nm) is larger than the E at the top of GaN nanorod (D 85 nm) by 5.3 meV which is smaller than the experimental value of 15 meV. Based on Equation 3, we can estimate that if the effective diameters of the GaN nanorod at R1 and R5 are 21 nm and 51 nm, respectively, which are about 60% of the measured values, the shifted energy will approach the experimental result of 15 meV. The reduction on the effective diameter of the GaN nanorod could be related to the band-bending effect caused by the Fermi level pinning of the GaN nanorod [28,29]. Furthermore, the peak intensity is strong as the CL spectra are carried out at the bottom of the GaN nanorod, which is mainly due to the size effects. The size effects come from the

increase of the surface state density of GaN due to the large surface-to-volume ratio and the variation of electronic states because of the diameter difference. However, in CL spectra measurements, the results cannot conclude which effect dominates the increased intensity. That can be further confirmed by other measurements or experimental setups in the future.

Conclusions

In summary, the as-growth GaN nanorod cluster and the single GaN nanorod via PAMBE growth were studied by FE-SEM and CL spectroscopy. The emissions from the NBE, surface state, Y4 and Y7 defect states of the GaN nanorod cluster, and the single GaN nanorod were investigated and analyzed. The results show that the CL spectra of the GaN nanorod cluster and the single GaN nanorod are sensitive to the change in temperature and structure of GaN. For the GaN nanorod cluster and the single GaN nanorod, the NBE line position will blueshift with the decreasing temperature, and the intensity of the CL spectra for the surface state of3.4 eV will increase with the decreasing temperature. However, the Y7 defect line did not appear in the single

GaN nanorod; therefore, we can deduce that the source of the Y7 line came from the structural defect existing between the GaN nanorods and the Si substrate. Furthermore, the position-dependent CL spectra of the single GaN nanorod revealed that the surface state of the single GaN nanorod is strongly influenced by the diameter of the GaN nanorod. These studies give us more insight in the fundamental properties of GaN nanomaterials and provide useful information in the applications of GaN nanorod-based devices.

AcknowledgementsThis work is supported by the National Science Council of Taiwan under the contract numbers NSC 99-2112-M-110-012-MY2 and NSC 98-2923-M-110-001-MY3. Additional funding support from the potential program project of National Sun Yat-sen University is also acknowledged.

Author details

1Department of Physics and Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung, Taiwan, 80424, Republic of China

2Institut dElectronique Fondamentale, UMR 8622 CNRS, University Paris Sud XI, Orsay Cedex, 91405, France

Authors contributionsGHL carried out the SEM and CL measurements and made the initial writings. CCT gathered the data and drafted of the manuscript. YTL and CWC grew the GaN nanorod samples. PW and QYSC participated in the data analyses. LR, MT, and FHJ participated in the experimental discussions and assistance. LWT conceived this study and supervised the whole work from the experimental design and data analyses to the final version. All authors read and approved the final manuscript.

Competing interestsThe authors declare that they have no competing interests.

Tsai et al. Nanoscale Research Letters 2011, 6:631 http://www.nanoscalereslett.com/content/6/1/631

Page 7 of 7

Received: 13 September 2011 Accepted: 14 December 2011 Published: 14 December 2011

References1. Schubert EF: Light-Emitting Diodes. 2 edition. New York: Cambridge University Press; 2006.

2. Lieber CM, Wang ZL: Functional nanowires. Mrs Bull 2007, 32:99.3. Tsai CC, Chiang PL, Sun CJ, Lin TW, Tsai MH, Chang YC, Chen YT: http://www.ncbi.nlm.nih.gov/pubmed/21343647?dopt=Abstract

Web End =Surface http://www.ncbi.nlm.nih.gov/pubmed/21343647?dopt=Abstract

Web End =potential variations on a silicon nanowire transistor in biomolecular http://www.ncbi.nlm.nih.gov/pubmed/21343647?dopt=Abstract

Web End =modification and detection. Nanotechnology 2011, 22:135503.4. Yoshizawa M, Kikuchi A, Mori M, Fujita N, Kishino K: Growth of self-organized GaN nanostructures on Al2O3(0001) by RF-radical source molecular beam epitaxy. J J Appl Phys 1997, 36:L459.

5. Han WQ, Fan SS, Li QQ, Hu YD: Synthesis of gallium nitride nanorods through a carbon nanotube-confined reaction. Science 1997, 277:1287.

6. Sanchez-Garcia MA, Calleja E, Monroy E, Sanchez FJ, Calle F, Munoz E, Beresford R: The effect of the III/V ratio and substrate temperature on the morphology and properties of GaN- and AlN-layers grown by molecular beam epitaxy on Si(111). J Cryst Growth 1998, 183:23.

7. Yoshizawa M, Kikuchi A, Fujita N, Kushi K, Sasamoto H, Kishino K: Self-organization of GaN/Al0.18Ga0.82N multi-layer nano-columns on (0001)

Al2O3 by RF molecular beam epitaxy for fabricating GaN quantum disks. J Cryst Growth 1998, 189:138.8. Guha S, Bojarczuk NA, Johnson MAL, Schetzina JF: Selective area metalorganic molecular-beam epitaxy of GaN and the growth of luminescent microcolumns on Si/SiO2. Appl Phys Lett 1999, 75:463.

9. Calleja E, Sanchez-Garcia MA, Sanchez FJ, Calle F, Naranjo FB, Munoz E, Molina SI, Sanchez AM, Pacheco FJ, Garcia R: Growth of III-nitrides on Si (111) by molecular beam epitaxy doping, optical, and electrical properties. J Cryst Growth 1999, 201:296.

10. Stach EA, Pauzauskie PJ, Kuykendall T, Goldberger J, He RR, Yang PD: Watching GaN nanowires grow. Nano Lett 2003, 3:867.

11. Seo HW, Chen QY, Iliev MN, Tu LW, Hsiao CL, Mean JK, Chu WK: Epitaxial GaN nanorods free from strain and luminescent defects. Appl Phys Lett 2006, 88:153124.

12. Ristic J, Calleja E, Fernandez-Garrido S, Cerutti L, Trampert A, Jahn U,Ploog KH: On the mechanisms of spontaneous growth of III-nitride nanocolumns by plasma-assisted molecular beam epitaxy. J Cryst Growth 2008, 310:4035.

13. Lefebvre P, Fernandez-Garrido S, Grandal J, Ristic J, Sanchez-Garcia MA, Calleja E: Radiative defects in GaN nanocolumns: correlation with growth conditions and sample morphology. Appl Phys Lett 2011, 98:083104.

14. Chiu CH, Lo MH, Lu TC, Yu PC, Huang HW, Kuo HC, Wang SC: Nano-processing techniques applied in GaN-Based light-emitting devices with self-assembly Ni nano-masks. J Lightwave Tech 2008, 26:1445.

15. Chen LY, Huang YY, Chang CH, Sun YH, Cheng YW, Ke MY, Chen CP, Huang JJ: http://www.ncbi.nlm.nih.gov/pubmed/20588606?dopt=Abstract

Web End =High performance InGaN/GaN nanorod light emitting diode http://www.ncbi.nlm.nih.gov/pubmed/20588606?dopt=Abstract

Web End =arrays fabricated by nanosphere lithography and chemical mechanical http://www.ncbi.nlm.nih.gov/pubmed/20588606?dopt=Abstract

Web End =polishing processes. Opt Express 2010, 18:7664.

16. Zang K, Chua S-J: GaN based nanorod light emitting diodes by selective area epitaxy. Phys Stat Sol C 2010, 7:2236.

17. Reshchikov MA, Morkoc H: Luminescence properties of defects in GaN. J Appl Phys 2005, 97:061301.

18. Tu LW, Hsiao CL, Chi TW, Lo I, Hsieh KY: Self-assembled vertical GaN nanorods grown by molecular-beam epitaxy. Appl Phys Lett 2003, 82:1601.

19. Tsai JK, Lo I, Chuang KL, Tu LW, Huang JH, Hsieh CH, Hsieh KY: Effect of N to Ga flux ratio on the GaN surface morphologies grown at high temperature by plasma-assisted molecular-beam epitaxy. J Appl Phys 2004, 95:460.

20. Gates SM, Kunz RR, Greenlief CM: Silicon hydride etch products from the reaction of atomic-hydrogen with Si(100). Surf Sci 1989, 207:364.21. Streit DC, Allen FG: Thermal and Si-beam assisted desorption of SiO2 from silicon in ultrahigh-vacuum. J Appl Phys 1987, 61:2894.

22. Reshchikov MA, Huang D, Yun F, Visconti P, He L, Morkoc H, Jasinski J, Liliental-Weber Z, Molnar RJ, Park SS, Lee KY: Unusual luminescence lines in GaN. J Appl Phys 2003, 94:5623.

23. Varshni YP: Temperature dependence of the energy gap in semiconductors. Physica (Amsterdam) 1967, 34:149.

24. Park YS, Kang TW, Taylor RA: http://www.ncbi.nlm.nih.gov/pubmed/21836271?dopt=Abstract

Web End =Abnormal photoluminescence properties of http://www.ncbi.nlm.nih.gov/pubmed/21836271?dopt=Abstract

Web End =GaN nanorods grown on Si(111) by molecular-beam epitaxy. Nanotechnology 2008, 19:475402.

25. Yoon JW, Sasaki T, Roh CH, Shim SH, Shim KB, Koshizaki N: Quantum confinement effect of nanocrystalline GaN films prepared by pulsed-laser ablation under various Ar pressures. Thin Solid Films 2005, 471:273.

26. Brus LE: A simple-model for the ionization-potential, eelctron-affinity, and aqueous redox potentials of small semiconductor crystallites. J Chem Phys 1983, 79:5566.

27. Perlin P, LitwinStaszewska E, Suchanek B, Knap W, Camassel J, Suski T, Piotrzkowski R, Grzegory I, Porowski S, Kaminska E, Chervin JC: Determination of the effective mass of GaN from infrared reflectivity and Hall effect. Appl Phys Lett 1996, 68:1114.

28. Waag A, Wang X, Fndling S, Ledig J, Erenburg M, Neumann R,Suleiman MA, Merzsch S, Wei J, Li S, Wehmann HH, Bergbauer W, Straburg M, Trampert A, Jahn U, Riechert H: The nanorod approach: GaN NanoLEDs for solid state lighting. Phys Stat Sol C 2011, 8:2296.

29. Polenta L, Rossi M, Cavallini A, Calarco R, Marso M, Meijers R, Richter T, Stoica T, Luth H: http://www.ncbi.nlm.nih.gov/pubmed/19206629?dopt=Abstract

Web End =Investigation on localized states in GaN nanowires. ACS Nano 2008, 2:287.

doi:10.1186/1556-276X-6-631Cite this article as: Tsai et al.: Cathodoluminescence spectra of gallium nitride nanorods. Nanoscale Research Letters 2011 6:631.

Submit your manuscript to a journal and benet from:

7 Convenient online submission7 Rigorous peer review7 Immediate publication on acceptance7 Open access: articles freely available onlihttp://www.springeropen.com/

Web End =ne 7 High visibility within the eld7 Retaining the copyright to your article

Submit your next manuscript at 7 http://www.springeropen.com/

Web End =springeropen.com