Optimal metal domain size for photocatalysis with hybrid semiconductor-metal nanorods

Abstract

Semiconductor-metal hybrid nanostructures offer a highly controllable platform for light-induced charge separation, with direct relevance for their implementation in photocatalysis. Advances in the synthesis allow for control over the size, shape and morphology, providing tunability of the optical and electronic properties. A critical determining factor of the photocatalytic cycle is the metal domain characteristics and in particular its size, a subject that lacks deep understanding. Here, using a well-defined model system of cadmium sulfide-gold nanorods, we address the effect of the gold tip size on the photocatalytic function, including the charge transfer dynamics and hydrogen production efficiency. A combination of transient absorption, hydrogen evolution kinetics and theoretical modelling reveal a non-monotonic behaviour with size of the gold tip, leading to an optimal metal domain size for the most efficient photocatalysis. We show that this results from the size-dependent interplay of the metal domain charging, the relative band-alignments, and the resulting kinetics.

ARTICLE

Received 10 Sep 2015 | Accepted 8 Dec 2015 | Published 19 Jan 2016

Semiconductor-metal hybrid nanostructures offer a highly controllable platform for light-induced charge separation, with direct relevance for their implementation in photocatalysis. Advances in the synthesis allow for control over the size, shape and morphology, providing tunability of the optical and electronic properties. A critical determining factor of the photocatalytic cycle is the metal domain characteristics and in particular its size, a subject that lacks deep understanding. Here, using a well-dened model system of cadmium sulde-gold nanorods, we address the effect of the gold tip size on the photocatalytic function, including the charge transfer dynamics and hydrogen production efciency. A combination of transient absorption, hydrogen evolution kinetics and theoretical modelling reveal a non-monotonic behaviour with size of the gold tip, leading to an optimal metal domain size for the most efcient photocatalysis. We show that this results from the size-dependent interplay of the metal domain charging, the relative band-alignments, and the resulting kinetics.

DOI: 10.1038/ncomms10413 OPEN

Optimal metal domain size for photocatalysis with hybrid semiconductor-metal nanorods

Yuval Ben-Shahar1, Francesco Scotognella2, Ilka Kriegel2, Luca Moretti2, Giulio Cerullo2, Eran Rabani3,4

& Uri Banin1

1 The Institute of Chemistry and Center for Nanoscience and Nanotechnology, The Hebrew University of Jerusalem, Edmond Safra Campus Givat-Ram, Jerusalem 91904, Israel. 2 Dipartimento di Fisica, IFN-CNR, Politecnico di Milano, 20133 Milan, Italy. 3 Department of Chemistry, University of California and Lawrence Berkeley National Laboratory, Berkeley, California 94720-1460, USA. 4 The Sackler Institute for Computational Molecular and Materials Science, Tel Aviv University, Tel Aviv 69978, Israel. Correspondence and requests for materials should be addressed to G.C. (email: mailto:Giulio.Cerullo@ polimi.it

Web End =Giulio.Cerullo@ polimi.it ) or to E.R. (email: mailto:[email protected]

Web End [email protected] ) or to U.B. (email: mailto:[email protected]

Web End [email protected] ).

NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 1

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413

The synergistic optical and chemical properties of semiconductor-metal hybrid nanoparticles lead to light-induced charge separation1,2, opening the path for their

function as photocatalysts in redox reactions, including hydrogen generation by water splitting37, generation of radicals and photodegradation of organic contaminants8. The complexity of the photocatalytic cycle, in particular for the fuel generating water splitting reaction, requires a reductionist approach to address separately the effect of size, shape and composition of each component towards the rational design of an efcient photocatalytic system.

The role of the exciton dynamics, related to the semiconductor component, has been investigated in particular in prototypical TiO2-based systems and in colloidal semiconductor-metal hybrid nanorods (NRs). These studies pointed out to the potential of tailoring the semiconductor component in the hybrid nanoparticles, permitting ne tuning of the light absorption and electronhole dissociation as preliminary steps to charge separation and catalysis911. The metal co-catalyst component has a particularly important role in the photocatalytic cycle. The charge separation from the semiconductor is directly affected by the metal domain characteristics and the actual catalysis occurs on its surface12,13. Control over the size of the metal domain and its optimization is an essential parameter for the rational photocatalytic system design. The size dependence of catalysis on bare Au islands deposited on titania was investigated revealing sharp optimal catalytic performance for CO oxidation at island thickness of B2 atomic layers corresponding to B3 nm in diameter14, and in the seminal work of Goodman and coworkers, this was attributed to a metal to non-metal transition15. In relation to photocatalytic activity, early studies discussed the effect of size on Fermi-level equilibration related to charging of the metal domain following irradiation of the system16,17. The effect of the metal co-catalyst size, particularly on the hydrogen generation, was addressed in the context of TiO2Au and CdS-Pt with multiple metal domains18,19. While the former observed no size effect for the Au domain varying between 3 and 12 nm, the latter has reported optimal hydrogen generation in extremely small Pt clusters (B50 atoms). However, a detailed mechanistic description, particularly in view of these diverse behaviours, is missing and is important for further development of such hybrid nanoparticles in the context of photocatalysis.

In this work we address the effect of the metal co-catalyst size on the photocatalysis process, using hybrid semiconductor-metal nanoparticles with a single catalytic domain as a model system. By a combination of ultrafast transient absorption measurements, hydrogen generation yield study and theoretical modelling, we observe and explain a non-monotonic metal domain size dependence of the hydrogen generation efciency.

ResultsSize-controlled Au tip growth on CdS NRs. CdS NRs of 31.6 nm length and 3.9 nm diameter were synthesized using modication of a previously reported procedure employing seeded growth20 (Supplementary Fig. 1). Site-selective Au deposition on a single-rod apex, with high control of the metal tip size, was achieved by combining two different synthetic approaches consecutively (Fig. 1a). First, a dark reaction was used to obtain site-selective small metal islands growth on the apexes of the CdS NRs (refs 21,22). As can be seen in the transmission electron microscopy (TEM) image in Fig. 1c, a single small metal-tip of B1.51.8 nm diameter grows on one apex with narrow size distribution (B7%). This selective growth takes place due to the favoured surface reactivity of the (001) facet of the CdS rod, that encourages the heterogeneous nucleation of gold. Furthermore,

the use of long alkyl chain amines such as octadecylamine, instead of shorter ones, minimizes Au nucleation on the less reactive facets such as the sides of the rod. Owing to the length of the alkyl chain a phase transition to a static phase occurs at lower temperatures thus blocking the Au precursors access to the NR surfaces23. These small Au domains serve as seeds for the second step, using light-induced Au growth under inert atmosphere and at low temperature, 24 C (Supplementary Methods). This approach allows for size control by changing the irradiation times and the Au3 /NRs ratio. Figure 1df show TEM images of

CdS-Au hybrid nanoparticles with different Au tip sizes and with narrow size distribution (Fig. 1g). Figure 1b presents the absorption spectra of the bare CdS NRs and CdS-Au hybrid nanoparticles with different Au tip sizes. All spectra exhibit a similar sharp rise at 460 nm related to the onset of the CdS NRs absorption. Several absorption features are seen to the blue of the onset, related to the band gap and to higher excited optical transitions of the CdS NRs, which signify the good size monodispersity of the sample. A plasmon peak develops at 540 nm, correlated with the increase of the metal tip size. Phase transfer to aqueous solution was performed with polyethyleneimine which was recently reported as high performance surface coating for photocatalytic applications and provides good colloidal stability11.

Transient absorption measurements of charge separation. The effect of the different Au domain sizes on charge carrier dynamics was studied using broadband ultrafast transient absorption spectroscopy. In Fig. 2a we show the time-resolved differential transmission (DT/T) spectra for the CdS NRs and the series of Au tip sizes. Following 450 nm optical excitation and formation of excited electronhole pairs, the DT/T spectra at early delay times reveal a pronounced bleach around 450 nm in both CdS NRs and CdS-Au hybrid NRs attributed to depletion of the rst excitonic transition in the CdS rods due to electron state lling24. In addition, for the larger Au tips, a broad bleach feature develops B540 nm, which corresponds to the plasmonic feature of the Au tips25. The decay of the plasmonic feature, by electronphonon scattering, showed no size dependence and the measured lifetime for all Au domain sizes was 1.51.7 ps (Supplementary Figs 68) consistent with prior reports for colloidal Au nanoparticles25,26.

Comparison between the normalized transient absorption dynamics for the bleach recovery in the spectral region of the CdS band gap exciton is presented in Fig. 2b for the different Au tip sizes. In the bare CdS NRs (upper panel, Fig. 2b), a fast decay component with a small amplitude is observed, and is related to residual cooling of the electrons to the CdS conduction band edge. This is followed by a long decay component, corresponding to exciton recovery to the ground state. These bleach recovery kinetics were tted to a bi-exponential function and resulted in a time constant for electronhole recombination of 3.4 ns (Supplementary Table 3). At the presence of a metal tip a clear additional timescale is introduced, slower than the rapid cooling and faster than the electronhole recombination. The amplitude of the intermediate decay process increases with increasing metal domain size. We assign this additional timescale to the electron transfer from the CdS to the metal tip. The measured kinetic decays were tted to a tri-exponential function (Supplementary Note 3). The charge transfer rates extracted from this t were found to be 16 ps for 6.2 nm, 29 ps for 4.8 nm, 103 ps for 3.0 nm and 770 ps for 1.6 nm Au tips sizes, with amplitudes decreasing from 40 to 15% for smaller tip sizes.

Photocatalytic hydrogen production efciency measurements. The photocatalytic activity of the same hybrid nanoparticles was

2 NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413 ARTICLE

a

c e

Step 1. Spontaneous growth

Step 2. Light-induced growth

AuCl3

AuCl3

RT

24C

g

6.2 nm

4.8 nm

3.0 nm

1.6 nm

Counts

100

80 60 40 20

0

0 2 4 6 8 10

Au domain diameter (nm)

b

d

f

Absorbance (normalized)

6.2 nm4.8 nm3.0 nm1.6 nm CdS NRs

1

0.8

0.6

0.4

0

0.2

400

500

600

700

800

900

1,000

Wavelength (nm)

Figure 1 | Growth of size-controlled semiconductor-metal nanohybrids. (a) A scheme of the two-step metal growth deposition. (b) UV-vis absorbance spectra of CdS-Au hybrid nanoparticles showing the development of the plasmonic feature B540 nm as the Au tip size increases.

TEM images of CdS-Au hybrid nanoparticles with 1.50.2 nm Au tip size after 1 h dark synthesis (c) and light-induced synthesis for 30 min with various CdS:Au molar ratio leading to Au tip size of of 3.00.5 nm (d) 4.80.7 nm (e), and 6.20.8 nm (f). Scale bars; c, 20 nm; df, 50 nm. (g) size distribution histogram of the Au metal tip diameters.

a b

i

0.1 ps0.5 ps 1 ps 5 ps

20 ps 100 ps 200 ps 300 ps

0.1

0.05

0.05

0

NRs

1

ii

0.6

0.2

1.6 nm

0.4

iii

T/T (%)

0.2

T/T normalized

0

3.0 nm

0.25

iv

0.15

0.05

4.8 nm

0.25

v

0.15

6.2 nm

450 500 550 600 650Wavelength (nm)

0 50 100 150 200 250 300 Time (psec)

Figure 2 | Ultrafast spectroscopy of nanohybrids. (a) Transient absorption spectra of CdS NRs (i) and CdS-Au hybrid nanoparticles for differentAu metal tip sizes including 1.6 nm (ii), 3.0 nm (iii), 4.8 nm (iv) and 6.2 nm (v) at 450 nm excitation. (b) Corresponding normalized transient absorption dynamics of the bleach recovery at 450 nm, attributed to the rst excitonic transition of the CdS NR component for CdS NRs and CdS-Au hybrid nanoparticles with different Au metal tip sizes.

measured via the light-induced reduction of water at 405 nm to produce hydrogen in the presence of Na2S-9H2O and Na2SO3, acting as sacricial hole scavengers as depicted schematically in Fig. 3a (inset)27. The amount of hydrogen gas produced was determined using a gas chromatograph equipped with a thermal conductivity detector. Figure 3a, blue curve, shows the hydrogen generation rate versus Au tip size. A weak dependence, observed for the two smallest sizes, is followed by a marked decrease of the rate in the larger tips, overall by a factor of nearly 10 comparing the maximum and the minimum rates.

These results represent the actual hydrogen evolution rates, but they do not account for photons that are absorbed directly by the intraband transitions of the metal tip and do not contribute to the generation of hydrogen due to their rapid relaxation. The total absorption of such CdS-Au hybrid nanoparticles can be considered in rst approximation as the superposition of the contributions of the exciton and the plasmon28. The red curve in Fig. 3a corrects for this, by normalizing the rates to the semiconductor component absorption. The actual concentration of each sample was obtained by inductively coupled plasma mass

NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 3

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413

a

b

15

0.15

Rate (g hr1)

Rate/Cd (g hr 1Cd 1)

eV NHE (pH 8) 3.6

4.0 0.47

0.88

CB

VB

10

0.1

kET kWR

H2/H2O

5.1

6.3

0.5

1.87

2e +2H O H +2OH

SO +OH +2h SO +H

e

Au

h+

NRs

5

0.05

Trap Au (bulk)

keh

kST krec

0

0 1 2 3

0

Au radius (nm)

c d

70

0.12

r 0

r

[afii9825]=0.25

[afii9828]=3.2 J m1

60

0.1

50

0.08

1 )

k ET (nsec

40

QY

0.06

30

0.04

20

10

0.02

0

0 0 0 2 4 6

1 1.5 2 2.5 3 3.5

Au radius (nm)

Au radius (nm)

Figure 3 | Understanding size-dependent hydrogen production yield. (a) Hydrogen production rate (blue) and Cd normalized rate (red) curves as a function of Au size domain in the hybrid nanoparticles. Negligible rates are measured for the CdS NRs. (b) Energy band alignment diagram with relevant photocatalytic processes kinetic routes. (c) Measured semiconductor-metal electron transfer (kET) rates (squares) and tting modied Fermi golden rule model for this process (solid line). (d) Measured QY (black squares connected by dashed line) along with the non-monotonic kinetic model behaviour (blue solid line). Green and red dotted lines present limiting behaviours of the model for zero and innite metal domain sizes, respectively. Error bars in a and d indicate the Au tip size distribution and the uncertainty in the hydrogen production rate.

spectrometry (ICP-MS) analysis to determine the Cd content. Therefore the red curve is normalized to the overall Cd content, which is proportional to the contribution of the semiconductor to the nanohybrid absorption. This normalization is therefore expressing more cleanly the essential metal domain size effect in hydrogen reduction. It reveals a non-monotonic dependence in which an intermediate Au tip size provides the optimal hydrogen evolution rate for the photocatalytic water reduction and the highest value for the hydrogen evolution quantum yield (QY).

Additional aspect of hydrogen generation rate normalization can be considered to isolate the Au metal domain effect on the efciency of this photocatalytic process. This may be considered by normalizing the hydrogen production rate to the loading of the co-catalyst component18. X-ray photoelectron spectroscopy measurements on the hybrid nanoparticles (HNPs) with different Au metal domain sizes show a dominant doublet at the Au 4f binding energy (BE) consistent with the zero-valent Au peak (84.0 eV), which designates the metallic nature of these domains. Intensities of the Au 4f7/2 and 4f5/2 peaks show a

pronounced increase in the intensity correlated to the larger metal domain sizes (Supplementary Fig. 4). Quantication of the atomic concentration percent of each element in the HNPs structure presented in Supplementary Table 2 allows the calculation of the Cd:Au ratio in each HNPs sample. The nearly 10-fold increase of this relative atomic concentration of the Au between the different metal domain sizes indicates the signicantly higher loading of the Au metal on the CdS semiconductor NR structure with increased Au tip size, while the minor change in the Cd or S atomic concentration implies lack of substantial change in the rod dimensions. Consequently, normalization of the hydrogen production rate by the Cd:Au ratio is considered as

normalization to the Au metal loading. The results of such correction for the measured hydrogen generation rates are fully consistent with the CdS absorption normalization obtained by ICP-MS discussed above, and reveal a similar non-monotonic behaviour as function of Au metal domain size (Supplementary Fig. 5 and Note 2).

DiscussionTo rationalize the size dependence of the non-monotonic photocatalytic behaviour along with the charge transfer dynamics we propose a minimalistic model consisting of several kinetic steps, as sketched in Fig. 3b and Supplementary Fig. 9. The photo-excited electron in the semiconductor can relax by electron transfer to the co-catalyst metal domain (with a rate given by kET)

or by electronhole recombination (with rate keh). The latter is

rather slow1 compared with the other processes and is assumed to be constant independent of the Au tip size (ke h 15 n sec 1).

The electron on the metal tip can either promote water reduction reaction (kWR) or undergo back recombination with the hole that is left behind on the semiconductor domain (krec), which is

modelled by the hole transfer from the semiconductor to the metal tip. An additional important process is the trapping of the hole (kST) with a rate that is comparable to that of electron transfer into the metal tip29. Once the hole is trapped it blocks the electron transfer channel by the electronhole Coulomb interaction, which also leads to a localization of the electron11,30.

The efciency of hydrogen production can be obtained in a closed form and is given by the t-N of the solution to the master equation (Supplementary Note 4):

QY

kETkWR

kWR krec

kET kST ke h

1

4 NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413 ARTICLE

to make contact with the measured hydrogen production efciency the different rates appearing in equation (1) need to be determined. In fact, some of these rates can be determined independently by combining the transient absorption measurements with a suitable theoretical model. The semiconductor-metal electron transfer (kET) and the back recombination (krec)

rates can be described by Auger processes with values given by Fermis golden rule:

kET

43 r3 te

j j2

32

2m e

2

p

2

ec

f r

eF r

and

32

krec

43 r3 th

j j2

2m h

2

p

3

where r is the metal domain radius, is the Plancks constant divided by 2p, m e and m h are the effective mass of the electron and the hole in the metal, te and th are the electron and hole tunnelling matrix elements (assumed to be independent of r), ec,

ev, f(r) and eF(r) are the semiconductor conduction and valance band energies, the metal work-function and the metal Fermi-level measured from the bottom of the energy band. Note that both rates depend on the metal tip radius r through the steep dependence of the density of states on the tip volume (r3), and weakly through the dependence of the Fermi energy31 (eF(r)) and work function32,33 on r

f r

fbulk

ev

f r

eF r

2gvMzFr 4 where g is the surface tension, vM is the molar volume, z is number of transferred electrons, F is Faradays constant.

The water reduction reaction on the metal co-catyalyst is described by the cathodic rate in the ButlerVolmer model34 for redox reactions. The electron transfer process is given by a Marcus-like expression35:

kWR k0WR exp

aeF

RT eW f r

5

where kWR is the electron reduction rate of an absorbed water molecule, k0WR is the standard rate constant, R is the gas constant,

T is the temperature, a is the electron transfer coefcient which determines the symmetry of the transition state (for example, a 12 corresponds to a transition state with equal contributions

from the reactants and products), and eW is the water reduction potential. The anodic rate for the hydrogen oxidation (back reaction) can be neglected because the hydrogen concentration is small compared with the proton concentration at the experimental pH level. In contrast to the electron transfer and recombination rates given by equations (2) and (3), kWR depends exponentially on size of the metal domain through the dependence of f(r).

We now have a working model to analyze the governing factors in the metal domain size effect on electron transfer and photocatalytic efciency, and compare them with the experimental results. First, in Fig. 3c we determine kET by tting the measured electron transfer rates obtained from the transient absorption to equation (2). The overall size dependence of kET is

in good agreement with the theoretical r3 prediction. The only tting parameter used is the tunnelling matrix element, te 5.6 10 5 eV. This seemingly small value is consistent with

the results of Kamat on semiconductor-metal oxide hybrid nanoparticles36. The remaining parameters were taken from the literature and are provided in Supplementary Note 4.

Next, we calculate the efciency of hydrogen production and compare the prediction to the experimental values, as shown in

Fig. 3d. To capture the essential non-monotonic behaviour observed experimentally, we studied the dependence of the QY on the various parameters as shown in detail in the Supplementary Figs 1012. In particular, the dependence on the hole tunnelling matrix element, th , was studied (Supplementary Fig. 10) and a reasonable description of the measured efciencies is obtained for th 1.1 10 6 eV, up to 50-folds smaller than te to yield

meaningful results. This low value corresponds to an electron residence time on the Au tip sufciently long to allow for effective water reduction. Indeed, the back recombination rate under these parameters for the different metal sizes is in the range of sub-msec to several msec for large to small Au domain sizes respectively, consistent with experimental results for Pt tips on CdS rods1.

Two other parameters are needed for the qualitative description of the experimental results by the model. For the metal surface tension, g, several reported values for gold nanoparticles were tested (Supplementary Fig. 11)32,37,38. Reasonable surface tension values (g) are between 2.5 and 4 J m 1. Higher surface tension values result in high work function values for the metal domain above the semiconductor conduction band minimum leading to vanishing electron injection rates. Furthermore, in larger tip sizes the efciency is overestimated due to large overpotential relative to the standard water reduction potential at the experimental pH. Finally, for the electron transfer coefcient, a, the ts yield values around a 0.25 (Supplementary Fig. 12),

in the range of values reported in the literature for similar systems34,39. This implies that the transition state for the water reduction is closer to the reactants.

A particular kinetic model solution is presented in Fig. 3d (solid blue curve) and manifests the non-monotonic dependence of the QY on the Au tip size consistent with the normalized experimental QY (squares connected by dashed line). The non-monotonic dependence arises from the opposing behaviour of the QY in the limits of r-0 and r-N. For the former, we nd that QYpr3 increases with the tip radius, as the rate determining step is electron injection into the metal tip. For the latter, QY / exp 2gevMazRT 1r

decreases exponentially with the tip radius where the rate determining step is the reduction of water as the back hole transfer competes with the reduction. Hence, an intermediate Au tip size provides an optimum balancing between the charge separation rate and efciency, and the back recombination competing with the water reduction.

In conclusion, an optimal metal domain size is found for photocatalytic water reduction using hybrid semiconductor-metal NRs. The optimal value is explained in terms of competing processes where for small tips the hydrogen evolution QY is mainly determined by the rate of electron injection to the metal tip, whereas for large tips it is determined mainly by the water reduction on the metal surface. These two limits show opposite dependence on the metal domain size, leading to an optimal value as explained by a minimalist and general kinetic model with parameters tted to reproduce qualitatively the experimental results, in particular after normalizing out the metal domain absorption effects. Thus, the behaviour is general and not limited to the metal type or the reduction reaction, and can be used for rational design of photocatalysts based on hybrid semiconductor-metal nanostructures.

Methods

Materials and syntheses. All chemical precursors used for this study were purchased from Sigma Aldrich, PCI Synthesis, and Merck. See Supplementary Methods for more details.

Synthesis and phase transfer of CdS NRs and CdS-Au hybrid nanoparticles are described in details in Supplementary Figs 1,2 and Supplementary Methods.

Nanoparticle characterization. TEM and high resolution scanning transmission electron microscope characterization was performed using a Tecnai T12 G2 Spirit

NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 5

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413

and Tecnai F20 G2, respectively. All size statistics are done with Scion image programme on 200 particles. Absorption was measured with a JASCO V-570 UV-vis-near IR spectrophotometer. Extinction coefcient values of the nanoparticles were calculated using a previously reported method40.

Inductively coupled plasma mass spectrometry measurements. Following hydrogen generation kinetic measurements a 100 ml of HNPs solution was etched overnight in 1 ml of 69% nitric acid. Following sonication, 100 ml of the HNPs solution was mixed with 3.35 ml of three distilled water and analysed by ICP-MS (c 7500, Agilent) for Cd. The quantity of Cd in each solution was calculated using

external calibration with standard Cd solutions (Supplementary Table 1).

Hydrogen evolution rate and efciency measurements. To determine and measure the evolved hydrogen gas from the photocatalytic reaction using the HNP model systems, the following set-up is used. The photocatalysts were dispersed in three distilled water solution (2 ml; optical density, OD B1 at 405 nm). The photocatalyst solution was placed in a quartz cuvette and hole scavengers, Na2S-

9H2O and Na2SO3, (typically 0.05 and 0.07 M, respectively), were added to the water. The solution is purged with argon for 20 min and stirred. The hybrid nanoparticles were then illuminated with 40 mW 405 nm laser. Aliquots of the reaction vessel head space were taken using a gas tight syringe at different time intervals and detected and quantied using Varian gas chromatograph (model 6820) equipped with a molecular sieve (5 ) packed column and a thermal conductivity detector. The resulting chromatograms and hydrogen concentration are obtained by the comparison to a calibration curve of known hydrogen amounts (Supplementary Fig. 3 and Note 1).

Ultrafast transient absorption measurements. The laser system employed for ultrafast transient absorption was based on a Ti-Sapphire chirped pulse amplied source, with maximum output energy of B800 mJ, 1 kHz repetition rate, central wavelength of 800 nm and pulse duration of about 150 fs. Excitation pulses at 400 nm were obtained by doubling the fundamental frequency in a b-barium borate crystal while other pump photons at different wavelength were generated by non-collinear optical parametric amplication in b-barium borate, with pulse duration B100 fs. Pump pulses were focused to 175 mm diameter spot. Probing was achieved in the visible range by using white light generated in a thin sapphire plate, and in the UV-visible range by using a thin Calcium Fluoride plate. Chirp-free transient transmission spectra were collected by using a fast optical multichannel analyser with dechirping algorithm. The measured quantity is the normalized transmission change, DT/T.

References

1. Wu, K. F., Zhu, H. M., Liu, Z., Rodriguez-Cordoba, W. & Lian, T. Q. Ultrafast charge separation and long-lived charge separated state in photocatalytic CdS-Pt nanorod heterostructures. J. Am. Chem. Soc. 134, 1033710340 (2012).

2. Kamat, P. V. Manipulation of charge transfer across semiconductor interface. a criterion that cannot be ignored in photocatalyst design. J. Phys. Chem. Lett. 3, 663672 (2012).

3. Kudo, A. & Miseki, Y. Heterogeneous photocatalyst materials for water splitting. Chem. Soc. Rev. 38, 253278 (2009).

4. Maeda, K. & Domen, K. Photocatalytic water splitting: recent progress and future challenges. J. Phys. Chem. Lett. 1, 26552661 (2010).

5. Wilker, M. B., Schnitzenbaumer, K. J. & Dukovic, G. Recent progress in photocatalysis mediated by colloidal IIVI nanocrystals. Isr. J. Chem. 52, 10021015 (2012).

6. Han, Z. J., Qiu, F., Eisenberg, R., Holland, P. L. & Krauss, T. D. Robust photogeneration of H-2 in water using semiconductor nanocrystals and a nickel catalyst. Science 338, 13211324 (2012).

7. Banin, U., Ben-Shahar, Y. & Vinokurov, K. Hybrid semiconductor-metal nanoparticles: from architecture to function. Chem. Mater. 26, 97110 (2014).

8. Mills, A., Davies, R. H. & Worsley, D. Water-purication by semiconductor photocatalysis. Chem. Soc. Rev. 22, 417425 (1993).

9. Amirav, L. & Alivisatos, A. P. Photocatalytic hydrogen production with tunable nanorod heterostructures. J. Phys. Chem. Lett. 1, 10511054 (2010).

10. OConnor, T. et al. The effect of the charge-separating interface on exciton dynamics in photocatalytic colloidal heteronanocrystals. ACS Nano 6, 81568165 (2012).

11. Ben-Shahar, Y. et al. Effect of surface coating on the photocatalytic function of hybrid CdS-Au nanorods. Small 11, 462471 (2015).

12. Yu, P. et al. Photoinduced ultrafast charge separation in plexcitonic CdSe/Au and CdSe/Pt nanorods. J. Phys. Chem. Lett. 4, 35963601 (2013).

13. Khon, E. et al. Improving the catalytic activity of semiconductor nanocrystals through selective domain etching. Nano Lett. 13, 20162023 (2013).

14. Bamwenda, G. R., Tsubota, S., Nakamura, T. & Haruta, M. The inuence of the preparation methods on the catalytic activity of platinum and gold supported on TiO2 for CO oxidation. Catal. Lett. 44, 8387 (1997).

15. Valden, M., Lai, X. & Goodman, D. W. Onset of catalytic activity of gold clusters on titania with the appearance of nonmetallic properties. Science 281, 16471650 (1998).

16. Wood, A., Giersig, M. & Mulvaney, P. Fermi level equilibration in quantum dot-metal nanojunctions. J. Phys. Chem. B 105, 88108815 (2001).17. Subramanian, V., Wolf, E. E. & Kamat, P. V. Catalysis with TiO2/gold nanocomposites. Effect of metal particle size on the Fermi level equilibration.J. Am. Chem. Soc. 126, 49434950 (2004).18. Murdoch, M. et al. The effect of gold loading and particle size on photocatalytic hydrogen production from ethanol over Au/TiO2 nanoparticles. Nat. Chem. 3, 489492 (2011).

19. Schweinberger, F. F. et al. Cluster size effects in the photocatalytic hydrogen evolution reaction. J. Am. Chem. Soc. 135, 1326213265 (2013).

20. Carbone, L. et al. Synthesis and micrometer-scale assembly of colloidal CdSe/CdS nanorods prepared by a seeded growth approach. Nano Lett. 7, 29422950 (2007).

21. Mokari, T., Sztrum, C. G., Salant, A., Rabani, E. & Banin, U. Formation of asymmetric one-sided metal-tipped semiconductor nanocrystal dots and rods. Nat. Mater. 4, 855863 (2005).

22. Mokari, T., Rothenberg, E., Popov, I., Costi, R. & Banin, U. Selective growth of metal tips onto semiconductor quantum rods and tetrapods. Science 304, 17871790 (2004).

23. Menagen, G., Macdonald, J. E., Shemesh, Y., Popov, I. & Banin, U. Au growth on semiconductor nanorods: photoinduced versus thermal growth mechanisms. J. Am. Chem. Soc. 131, 1740617411 (2009).

24. Wu, K. F., Rodriguez-Cordoba, W. E., Yang, Y. & Lian, T. Q. Plasmon-induced hot electron transfer from the Au Tip to CdS Rod in CdS-Au nanoheterostructures. Nano Lett. 13, 52555263 (2013).

25. Link, S. & El-Sayed, M. A. Spectral properties and relaxation dynamics of surface plasmon electronic oscillations in gold and silver nanodots and nanorods. J. Phys. Chem. B 103, 84108426 (1999).

26. Ahmadi, T. S., Logunov, S. L. & El-Sayed, M. A. Picosecond dynamics of colloidal gold nanoparticles. J. Phys. Chem. 100, 80538056 (1996).

27. Bao, N. Z., Shen, L. M., Takata, T. & Domen, K. Self-templated synthesis of nanoporous CdS nanostructures for highly efcient photocatalytic hydrogen production under visible. Chem. Mater. 20, 110117 (2008).

28. Shaviv, E. et al. Absorption properties of metal-semiconductor hybrid nanoparticles. ACS Nano 5, 47124719 (2011).

29. Wu, K. F. et al. Hole removal rate limits photodriven H-2 generation efciency in CdS-Pt and CdSe/CdS-Pt semiconductor nanorod-metal tip heterostructures. J. Am. Chem. Soc. 136, 77087716 (2014).

30. Berr, M. J. et al. Delayed photoelectron transfer in Pt-decorated CdS nanorods under hydrogen generation conditions. Small 8, 291297 (2012).31. Jakob, M., Levanon, H. & Kamat, P. V. Charge distribution between UV-irradiated TiO(2) and gold nanoparticles: determination of shift in the Fermi level. Nano Lett. 3, 353358 (2003).

32. Plieth, W. J. Electrochemical properties of small clusters of metal atoms and their role in surface enhanced raman-scattering. J. Phys. Chem. 86, 31663170 (1982).

33. Redmond, P. L., Hallock, A. J. & Brus, L. E. Electrochemical Ostwald ripening of colloidal Ag particles on conductive substrates. Nano Lett. 5, 131135 (2005).

34. Zhao, J., Holmes, M. A. & Osterloh, F. E. Quantum connement controls photocatalysis: a free energy analysis for photocatalytic proton reduction at CdSe nanocrystals. ACS Nano 7, 43164325 (2013).

35. Marcus, R. A. Chemical and electrochemical electron-transfer theory. Annu. Rev. Phys. Chem. 15, 155196 (1964).

36. Tvrdy, K., Frantsuzov, P. A. & Kamat, P. V. Photoinduced electron transfer from semiconductor quantum dots to metal oxide nanoparticles. Proc. Natl Acad. Sci. USA 108, 2934 (2011).

37. Jiang, Q., Liang, L. H. & Zhao, D. S. Lattice contraction and surface stress of fcc nanocrystals. J. Phys. Chem. B 105, 62756277 (2001).

38. Nanda, K. K., Maisels, A. & Kruis, F. E. Surface tension and sintering of free gold nanoparticles. J. Phys. Chem. C 112, 1348813491 (2008).

39. Meng, Y., Aldous, L., Belding, S. R. & Compton, R. G. The hydrogen evolution reaction in a room temperature ionic liquid: mechanism and electrocatalyst trends. Phys. Chem. Chem. Phys. 14, 52225228 (2012).

40. Shaviv, E., Salant, A. & Banin, U. Size dependence of molar absorption coefcients of CdSe semiconductor quantum rods. Chemphyschem. 10, 10281031 (2009).

Acknowledgements

We thank Dr Vitaly Gutkin from the Unit for Nanocharacterization at the Hebrew University for assistance in the X-ray photoelectron spectroscopy measurements. The research leading to these results has received funding from The Israel Science Foundation (grant no. 1560/13) and the Ministry of Science, Technology and Space, Israel & the Directorate General for Political and Security Affairs of the Ministry of Foreign Affairs, Italy. U.B. thanks the Alfred & Erica Larisch memorial chair. G.C. acknowledges support

6 NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10413 ARTICLE

by the EC under Graphene Flagship (contract no. CNECT-ICT-604391). Y.B.S. acknowledges support by the Ministry of Science, Technology and Space, Israel & the Camber Scholarship.

Author contributions

Y.B.S. and U.B. conceived and designed the experiments, Y.B.S. preformed the experiments, F.S., I.K., L.M. and G.C. contributed to transient absorption measurements and interpretation, Y.B.S., U.B. and E.R. provided and interpreted the kinetic model, Y.B.S., U.B., E.R. and G.C. co-wrote the paper.

Additional information

Supplementary Information accompanies this paper at http://www.nature.com/naturecommunications

Web End =http://www.nature.com/ http://www.nature.com/naturecommunications

Web End =naturecommunications

Competing nancial interests: The authors declare no competing nancial interests.

Reprints and permission information is available online at http://npg.nature.com/reprintsandpermissions

Web End =http://npg.nature.com/ http://npg.nature.com/reprintsandpermissions

Web End =reprintsandpermissions/

How to cite this article: Ben-Shahar, Y. et al. Optimal metal domain size for photocatalysis with hybrid semiconductor-metal nanorods. Nat. Commun. 7:10413 doi: 10.1038/ncomms10413 (2016).

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articles Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Web End =http://creativecommons.org/licenses/by/4.0/

NATURE COMMUNICATIONS | 7:10413 | DOI: 10.1038/ncomms10413 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 7