Common electronic origin of superconductivity in (Li,Fe)OHFeSe bulk superconductor and single-layer FeSe/SrTiO3 films

Abstract

The mechanism of high-temperature superconductivity in the iron-based superconductors remains an outstanding issue in condensed matter physics. The electronic structure plays an essential role in dictating superconductivity. Recent revelation of distinct electronic structure and high-temperature superconductivity in the single-layer FeSe/SrTiO₃ films provides key information on the role of Fermi surface topology and interface in inducing or enhancing superconductivity. Here we report high-resolution angle-resolved photoemission measurements on the electronic structure and superconducting gap of an FeSe-based superconductor, (Li_0.84 Fe_0.16 )OHFe_0.98 Se, with a T_c at 41 K. We find that this single-phase bulk superconductor shows remarkably similar electronic behaviours to that of the superconducting single-layer FeSe/SrTiO₃ films in terms of Fermi surface topology, band structure and the gap symmetry. These observations provide new insights in understanding high-temperature superconductivity in the single-layer FeSe/SrTiO₃ films and the mechanism of superconductivity in the bulk iron-based superconductors.

ARTICLE

Received 29 Jun 2015 | Accepted 4 Jan 2016 | Published 8 Feb 2016

Lin Zhao1,*, Aiji Liang1,*, Dongna Yuan1,*, Yong Hu1,*, Defa Liu1, Jianwei Huang1, Shaolong He1,Bing Shen1, Yu Xu1, Xu Liu1, Li Yu1, Guodong Liu1, Huaxue Zhou1, Yulong Huang1, Xiaoli Dong1,Fang Zhou1, Kai Liu2, Zhongyi Lu2, Zhongxian Zhao1,3, Chuangtian Chen4, Zuyan Xu4 & X. J. Zhou1,3

The mechanism of high-temperature superconductivity in the iron-based superconductors remains an outstanding issue in condensed matter physics. The electronic structure plays an essential role in dictating superconductivity. Recent revelation of distinct electronic structure and high-temperature superconductivity in the single-layer FeSe/SrTiO3 lms provides key information on the role of Fermi surface topology and interface in inducing or enhancing superconductivity. Here we report high-resolution angle-resolved photoemission measurements on the electronic structure and superconducting gap of an FeSe-based superconductor, (Li0.84Fe0.16)OHFe0.98Se, with a Tc at 41 K. We nd that this single-phase bulk superconductor shows remarkably similar electronic behaviours to that of the superconducting single-layer FeSe/SrTiO3 lms in terms of Fermi surface topology, band structure and the gap symmetry. These observations provide new insights in understanding high-temperature superconductivity in the single-layer FeSe/SrTiO3 lms and the mechanism of superconductivity in the bulk iron-based superconductors.

1 National Lab for Superconductivity, Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China. 2 Department of Physics and Beijing Key Laboratory of Opto-electronic Functional Materials and Micro-nano Devices, Renmin University of China, Beijing 100872, China. 3 Collaborative Innovation Center of Quantum Matter, Beijing 100871, China. 4 Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China. * These authors contributed equally to the present work. Correspondence and requests for materials should be addressed to X.J.Z. (email: mailto:[email protected]

Web End [email protected] ) or to X.L.D. (email: mailto:[email protected]

Web End [email protected] ).

NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 1

DOI: 10.1038/ncomms10608 OPEN

Common electronic origin of superconductivity in (Li,Fe)OHFeSe bulk superconductor and single-layer FeSe/SrTiO3 lms

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608

Iron-based superconductors13 represent the second class of high-temperature superconductors after the rst discovery of high-temperature superconductivity in cuprates4. The

electronic structure of the iron-based compounds usually consists of hole-like bands near the Brillouin zone centre and electron-like bands near the Brillouin zone corners, leading to proposals that the electron scattering between the hole pockets around the Brillouin zone centre and the electron pockets around the Brillouin zone corners is a viable mechanism for electron pairing in the iron-based superconductors511. With the discovery of the AxFe2 ySe2 (A K, Cs, Rb, Tl and

so on) superconductors3,1214, such a Fermi surface nesting picture is challenged, because the superconducting phase in AxFe2 ySe2 superconductors does not contain hole pockets near

the Brillouin zone centre3,1418. The latest discovery of possible high-temperature superconductivity above 65 K in the single-layer FeSe lm grown on the SrTiO3 substrate (denoted as

FeSe/SrTiO3 lm hereafter) puts even stronger constraints on the Fermi surface nesting picture, because there is no Fermi surface present near the zone centre at all1923. Although the implications of the Fermi surface topology in the AxFe2 ySe2 superconductors

and superconducting single-layer FeSe/SrTiO3 lms are signicant, the material-specic complications make the conclusion on the role of Fermi surface topology ambiguous. The AxFe2 ySe2 superconductors are well-known to have

problems of inhomogeneity, phase separation and small superconducting volume fraction. The exact nature of the superconducting phase remains unclear and its coexistence with the insulating phase suggests that interface may play an important role in the superconductivity2427. There are strong indications that interface in the single-layer FeSe/SrTiO3 lms

plays an important role in giving rise to high-temperature superconductivity1923,2834. With the complications of the interface effect and phase separation problem involved in AxFe2 ySe2 superconductors and superconducting single-layer

FeSe/SrTiO3 lms, it becomes less straightforward to conclude whether the same effect of Fermi surface topology on superconductivity is operative in all the iron-based superconductors.

In this study, we report high-resolution angle-resolved photoemission (ARPES) measurements on a new FeSe-based superconductor, (Li1 xFex)OHFe1 ySe, with a superconducting

critical temperature at 41 K (refs 3540). We nd that this superconductor contains electron pocket(s) near the Brillouin zone conners without hole pockets near the zone centre. The superconducting gap around the electron-like Fermi surface near the zone corner is nearly isotropic without nodes and its temperature dependence follows the usual Bardeen-Cooper-Schrieffer form. These behaviours are strikingly similar to that of the superconducting single-layer FeSe/SrTiO3 lms. This is a single-phase bulk superconductor with a relatively high TcB41 K, free from the complication of phase separation and interface effect, which shows electron-like Fermi pockets only. Our observations provide insights on the superconductivity mechanism in the iron-based bulk superconductors and the origin of high-temperature superconductivity in the single-layer FeSe/SrTiO3 lms.

ResultsFermi surface and band structure. Figure 1a shows the crystal structure of the new FeSe-based superconductor: (Li1 xFex)OHFe1 ySe (refs 36,39). It consists of FeSe layers

a c

b

Fe

Se

Li/Fe

O

Fe

9.32 Se

(Li1xFex)OHFe1ySe, Tc=41 K Single-layer FeSe/SrTiO3, Tc>65 K

7.02

TiO2

SrO

SrTiO3

H

Tl,Rb,K

Fe Se

d

e f

(Tl,Rb)xFe2ySe2, Tc=32 K

2

2

2 2 1

2

2 2 1 0

M2

M3

M1

M4

1

1

1

k y(/a)

0

k y(/a)

0

k y(/a)

0

High

Low

1

1

1

E

2 2 1

kx (/a) kx (/a) kx (/a)

0 1 2

0 1 2

1 2

Figure 1 | Crystal structure and Fermi surface of three FeSe-based superconductors. (a) The crystal structure of (Li1 xFex)OHFe1 ySe. The c lattice

constant is 9.318 for optimally doped sample with a Tc at 42 K (refs 36,39). (b) Schematic structure of single-layer FeSe lm deposited on a SrTiO3 substrate19. The thickness of the FeSe layer is B5.5 . (c) Schematic structure of (Tl,Rb)xFe2 ySe2 (ref. 12). The distance of the adjacent FeSe layers is

B7.02 . (d) Fermi surface mapping of (Li0.84Fe0.16)OHFe0.98Se superconductor measured at 20 K. The spectral weight distribution was obtained by integrating the measured photoemission spectra (EDCs) within [ 10, 10] meV energy window with respect to the Fermi level as a function of kx and ky.

(e,f) Fermi surface of a superconducting single-layer FeSe/SrTiO3 lm20 and (Tl,Rb)xFe2 ySe2 (ref. 17). For convenience, the four equivalent M points are

labelled as M1(p,p), M2( p,p), M3( p, p) and M4(p, p). The light-grey arrow in d marks the main electric eld direction on the sample surface from

the light source. In df, the data around M1 and M4 are obtained from the data around M3 and M2, respectively, by applying the inversion symmetry.

2 NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608 ARTICLE

sandwiched in between the (Li,Fe)OH layers along the c direction. The in-plane lattice constant a or b is 3.78 , which is close to that(3.76 ) in the bulk FeSe superconductor (TcB8.5 K)41, but the distance of the two adjacent FeSe layers in (Li1 xFex)OHFe1 ySe

(9.32 ) is much larger than that in bulk FeSe (5.5 )41. This indicates a weak interaction between the two adjacent FeSe layers in (Li1 xFex)OHFe1 ySe and its enhanced two-dimensional

nature of the electronic structure compared with bulk FeSe. In comparison, the single-layer FeSe/SrTiO3 lm consists of a strictly two-dimensional Se-Fe-Se layer on the top of the SrTiO3 substrate; the thickness of the FeSe layer is 5.5 (Fig. 1b)19. The distance between the two adjacent FeSe layers in AxFe2 ySe2 is 7.02 ;

however, there is an in-plane displacement between the two adjacent FeSe layers (Fig. 1c)12. The latest success of growing high-quality large-sized (Li1 xFex)OHFe1 ySe single crystals39 makes it

possible to carry out ARPES measurements on the new superconductors. The sample we have measured in this study has a composition of (Li0.84Fe0.16)OHFe0.98Se (abbreviated as

FeSe11111 hereafter)39 with a superconducting transition temperature TcB41 K (Fig. 3d).

Figure 1d shows the Fermi surface mapping of FeSe11111 measured at 20 K. The spectral weight at each momentum is obtained by integrating the EDC (energy distribution curve) spectral weight within [ 10, 10] meV energy window with

respect to the Fermi level (EF). The measured Fermi surface contains a nearly circular electron-like Fermi surface around M points (Fig. 1d). There is no indication of Fermi crossing around the G (0,0) point, except that there is a very weak residual signal near the Fermi level. Such a Fermi surface topology is very similar to that found in the superconducting single-layer FeSe/SrTiO3 lm (Fig. 1e) with a superconducting temperature at B55 K

(ref. 20). In comparison, there are electron pockets around the Brillouin centre in the AxFe2 ySe2 superconductor (Fig. 1f)17,18.

The area of the electron pocket near M gives a good measure of the electron doping level for the strongly two-dimensional systems. Considering that the Fermi surface around M consists of two degenerate Fermi surface sheets, the estimated electron counting in FeSe11111 (Fig. 1d) is B0.08 electrons per Fe. The electron counting of B0.08 electrons per Fe is smaller than 0.10 electrons per Fe in single-layer FeSe lm (Fig. 1e) with a TcB55 K

(ref. 20) and 0.12 electrons per Fe in vacuum-annealed single-layer FeSe/SrTiO3 lm with a TcB65 K (ref. 21). We note that the electron counting in both FeSe11111 and superconducting single-layer FeSe/SrTiO3 lm is much smaller than 0.18 electrons per Fe in AxFe2 ySe2 superconductor (Fig. 1f)1518 when only

considering the M point electron Fermi surface sheet.

FeSe11111 consists of FeSe layers and (Li,Fe)OH layers; therefore, the natural cleavage surface can be either FeSe surface or (Li,Fe)OH surface. By simple electron counting, both the FeSe surface and the LiOH surface are charge neutral. Substitution in the (Li,Fe)OH layers or off-stoichiometry in the FeSe layers would lead to carrier doping in the FeSe layers. In this case, no charge self-doping is expected for this sample. The composition of (Li0.84Fe0.16)OHFe0.98Se is obtained by structure renement of the

single-crystal X-ray diffraction data39. By simple electron counting, the electron doping level would be 0.12 electrons per Fe. This is slightly larger than the B0.08 electrons per Fe we obtained from the Fermi surface measurement. We think this difference may be caused by the composition variation among different samples38 or uncertainty in the composition determination. For example, neutron scattering on related sample with comparable Tc gives a composition of (Li0.8Fe0.2)OHFeSe (ref. 36). It is also possible that

a

b

c

d

l m

R

X

0

A

M

E E F (eV)

50 meV

60 meV

70 meV

High

Low

0.1

Z

0.2

M2

M3

FeSe11111

0.4 0 0.4 1.6 1.2

0.4

0

0.4

0.4

0

0.4

Se Fe

H O Li

0

e

f

g

M2

M3

E E F (eV)

E E F (eV)

0.1

k

80 meV

n

1

0

1

0.2

SL FeSe

(Tl,Rb)x

M4

0.4 0 0.4

1.6 1.2

0.4 0 0.4

0

h

i

j

o

Systems

e-Band bottom

Gap size/Tc

FeSe11111

50 meV

14 meV/41 K

FeSe film

60 meV

15 meV/55 K

AxFe2Se2

50 meV

13 meV/31 K

E E F (eV)

50 meV

0.1

80 meV

0.2

Fe2-ySe2

0.4 0 0.4 0.4 0 0.4

1.6 1.2

M1

2

X

M Z R A M

Momentum (/a)

Figure 2 | Band structure and photoemission spectra of (Li0.84Fe0.16)OHFe0.98Se superconductor measured along high-symmetry momentum cuts. (a-c) Photoemission images of (Li0.84Fe0.16)OHFe0.98Se measured at a temperature of 20 K along three high-symmetry cuts, G cut, M2 cut and M3 cut, respectively. (d) The second-derivative image of c with respect to the energy, to reveal the band structure better. For comparison, ej show photoemission images of a superconducting single-layer FeSe/SrTiO3 lm and (Tl,Rb)xFe2 ySe2 measured along the same G cut, M2 cut and M3 cut, respectively.

The location of the three momentum cuts are shown in k. The red dashed lines in aj images are the guide to the eyes for the observed band structures. (ln) DFT calculation results. (l) The crystal structure for the DFT calculation. (m) The Fermi surface and band structures along high symmetry directions are shown in n. In o, the table lists the bottom position of the electron band near M, the superconducting gap size and corresponding Tc for these three systems. The gap size for FeSe11111 will be obtained in Fig. 3e.

NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 3

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608

the electrons in the (Li,Fe)OH layers may not be fully transferred into the FeSe layers.

Figure 2ac shows the band structure of FeSe11111 measured across three momentum cuts together with the density functional theory (DFT) calculated electronic structures (l n). For

comparison, the band structure measured on a superconducting single-layer FeSe/SrTiO3 lm20 (Fig. 3eg) and on (Tl,Rb)xFe2 ySe2 superconductor17 (Fig. 3h-j) along the same

three momentum cuts are also presented. Overall, the band structure of FeSe11111 is very similar to that of the superconducting single-layer FeSe/SrTiO3 lm with slight quantitative difference in the band position. Near the G point, two hole-like bands can be resolved for FeSe11111 (Fig. 2c) that are well below the Fermi level, as seen more clearly in the corresponding second-derivative image (Fig. 2d). We note that there is a very weak signal near the Fermi level at G point, which may be due to the leakage from a band above the Fermi level. Similar multiple hole-like bands have also been observed near G in the superconducting single-layer FeSe/SrTiO3 lms21 and in

KxFe2 ySe2 superconductor18, with slight variation in the band

top position. In comparison, the electronic structure of (Tl,Rb)xFe2 ySe2 superconductor shows two electron-like bands

crossing the Fermi level (Fig. 2j)17. Around M2 and M3 points, we observed in FeSe11111 parabolic electron-like bands crossing the Fermi level (Fig. 2a,b), forming the electron pocket around M. These are very similar to those observed in the superconducting single-layer FeSe/SrTiO3 lm (Fig. 2e,f). Careful examination

indicates that the Fermi momentum ( kF) for the electron pocket of FeSe11111 is B0.22 p/a (lattice constant a 3.78 )

(Fig. 2a,b), which is slightly smaller than 0.25 p/a in the superconducting single-layer FeSe/SrTiO3 lm (Fig. 2e,f)20, both being signicantly smaller than 0.35 p/a in (Tl,Rb)xFe2 ySe2

superconductor (Fig. 2h,i)17. As a summary in Fig. 2o, the bottom of the electron-like band in FeSe11111 is B50 meV below the

Fermi level(Fig. 2b), slightly shallower than the 60 meV in the superconducting single-layer FeSe/SrTiO3 lm (Fig. 2f)20 but similar to the B50 meV in the (Tl,Rb)xFe2 ySe2 superconductor

(Fig. 2i)17. The combined information of the Fermi momentum and the band width gives a good measure of the electron effective mass that is 2.9, 2.7 and 6.1 me (me is free electron mass) for

FeSe11111, superconducting single-layer FeSe/SrTiO3 lm and the (Tl,Rb)xFe2 ySe2 superconductor, respectively17,20. It is

interesting to note that electron effective mass for the electron-like band near M is similar for FeSe11111 and superconducting single-layer FeSe/SrTiO3 lm, but both are much smaller than that in (Tl,Rb)xFe2 ySe2 superconductor17.

To further understand the measured electronic structure, the rst-principles electronic structure calculations were carried out with the projector augmented wave method42,43 as implemented in the VASP software4446 with a electron doping 0.1e per Fe in the non-magnetic state, which is close to our sample state. The crystal structure (Fig. 2l) and lattice constant are from ref. 36. Overall, the calculated Fermi surface (Fig. 2m) shows similar result with that of the bulk FeSe (ref. 47) but with

a c

d

0

39.5 K

60 K

FC

kFL

kFR

BCS Fit

Intensity

M2

55 K

41 K

4[afii9851]

Before After

40

0 40 E EF

50 K

(meV)

45 K

ZFC

b

kFL

kFR

40 K

1

35 K

0

10

20

30

40

50

60

0

Temperature (K)

30 K

e

25 K

E E F (eV)

18 K

0.1

Gap (meV)

High

Low

18K

0.2

0.4 0.2 0 0.2 0.4 Momentum (/a)

EDC intensity (arb units)

0.2 0.1 0 0.1 0.2 E EF (eV)

15

10

5

0

0

10

20

30

40

50

60

Temperature (K)

Figure 3 | Temperature dependence of the superconducting gap of the (Li0.84Fe0.16)OHFe0.98Se superconductor. (a) Schematically, the electron-like Fermi surface near M2 point and the location of the momentum cut (blue line) across the Fermi surface. (b) Photoemission image measured at 18 K along the momentum cut near the M2 point (blue line in a). The data are divided by the corresponding Fermi distribution function, to highlight the opening of an energy gap around the Fermi level (the original data can be found in Fig. 2a). Two Fermi momenta are marked by arrows as kFL and kFR. (c). Symmetrized photoemission spectra (EDCs) at the Fermi momentum kFL measured at different temperatures. The middle-top inset shows the expanded region of the18 K symmetrized EDC around the Fermi level and the tting result (red line) using the formula from ref. 50 to get the gap size. (d) Magnetic measurement of the superconducting transition temperature (Tc) for the (Li0.84Fe0.16)OHFe0.98Se sample we measured. Both eld-cooled (FC) and zero-led-cooled

(ZFC) mode measurements show an onset Tc at B41 K with a sharp transition width of B1.5 K. (e) Temperature dependence of the measured superconducting gap. The gap size is obtained by picking up the peak position from the symmetrized EDCs (c) or by tting the near-EF symmetrized EDCs using the formula from ref. 50; both approaches give similar results within experimental uncertainty. The error bars are dened as s.d. The gap size from EDCs of both the left Fermi momentum (kFL) and the right Fermi momentum (kFR) are plotted. The red dashed line is a BCS gap form with a gap size of B14 meV at 0 temperature.

4 NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608 ARTICLE

enhanced two-dimensional characteristics, consistent with the larger spacing between the two adjacent FeSe layers in (Li,Fe)OHFeSe. Extra bands around 2.5 and 1.0 eV are

present that are from (Li,Fe)OH layers, which are too deep to give contribution around the Fermi level. It is apparent that there is an obvious discrepancy between the band structure calculations and our measurements. For example, the hole pockets near G point in the calculations are absent in the measured results. This situation is similar to that of the single-layer FeSe/SrTiO3 lms and other

FeSe-based materials23. More theoretical efforts are needed to understand the experimental results.

The natural cleavage surface of FeSe11111 consists of both the FeSe surface and the (Li,Fe)OH surface; therefore, our ARPES signal should come from both surfaces. We believe our ARPES signal is dominated by the FeSe layers because of the following reasons: (1) our density functional theory band structure calculations (Fig. 2) indicate that the bands from (Li,Fe)OH layers lie B2.51.0 eV below the Fermi level. Thus, the low-energy electronic states near the Fermi level are mainly from the FeSe layers. This is consistent with the electronic structure similarity between (Li,Fe)OHFeSe and the single-layer FeSe/ SrTiO3 that has no (Li,Fe)OH layers. (2) Recent scanning tunneling microscope (STM) study on cleaved (Li,Fe)OHFeSe also indicated that the low-energy signal is dominated by the FeSe cleavage surface48,49. We note that STM measurement on the (Li,Fe)OH layer reveals that there is a tiny electron pocket around G (ref. 49). As we mentioned above, we also observe a very weak signal near the Fermi level at G point (Figs 1d and 2c). Whether this weak signal near G is due to the tiny electron pocket identied from STM49 needs further investigation.

Superconducting gap. The clear identication of electron-like Fermi surface sheet near M point makes it possible to investigate the superconducting gap in this new FeSe11111 superconductor. We start by examining the temperature dependence of the superconducting gap. Figure 3b shows the original photoemission image measured at a low temperature of 18 K along the momentum cut (its location is shown in Fig. 3a) crossing the electron-like Fermi surface around M2. The data are divided by the corresponding Fermi distribution function; the spectral weight suppression near the Fermi level indicates the opening of the superconducting gap (Fig. 3b). Following the procedure commonly used in the study of high-temperature cuprate superconductors50, the symmetrized photoemission spectra (EDCs) measured on one Fermi momentum at different temperatures are shown in Fig. 3c. There is a clear gap opening at low temperatures, as indicated by a dip at the Fermi level in the symmetrized EDCs (Fig. 3c). With increasing temperature, the dip at EF is gradually lled up and becomes almost invisible above40 K. We used two methods to extract the gap size in the superconducting state. The rst method is to pick the peak position in the symmetrized EDCs, while the second one is to t the symmetrized EDCs with the phenomenological formula proposed by Norman et al.50. The top-middle inset of Fig. 3c shows the symmetrized EDC at 18 K and the tting result. Both methods give consistent gap size within an experimental uncertainty of 2 meV. Figure 3e shows the measured gap size at different temperatures from symmetrized EDCs for both Fermi momenta. The gap size basically follows a Bardeen-Cooper-Schrieffer form with a Tc around (422) K and a gap size of B14 meV at 0 temperature (Fig. 3e). This is in excellent agreement with the TcB41 K from direct magnetic measurement (Fig. 3d). We note that FeSe11111 is very sensitive to air and processing temperature. To make sure there is no change on the superconductivity of our sample

during the ARPES measurements, we carried out magnetic measurements on the measured sample before and after the ARPES experiment. Figure 3d shows the magnetic measurement before ARPES measurement; both the eld-cooled and zero-eld-cooled modes give similar magnetic onset TcB41 K with a sharp transition of B1.5 K. The sharp transition and its 100% diamagnetic shielding demonstrate the high quality of the measured single crystal. After ARPES experiment (Fig. 3d), the magnetic measurement on the cleaved sample shows an onset TcB40 K with a sharp transition of B1.5 K. These indicate that there is negligible superconductivity degradation on the sample during the sample handling and ARPES measurements.

Now we come to the momentum dependence of the super-conducting gap in the FeSe11111 superconductor. For this purpose, we took high-resolution Fermi surface mapping (energy resolution of 4 meV) of the electron pocket around M2 at 20 K in the superconducting state (Fig. 4a). The corresponding Fermi momenta are identied, marked by red empty circles and labelled by numbers from 1 to 16 in Fig. 4a. Figure 4b shows symmetrized photoemission spectra (EDCs) at the Fermi momenta around the Fermi surface. The extracted superconducting gap is plotted in Fig. 4c. The superconducting gap is nearly isotropic with a gap size at (132) meV; there is no gap node (zero gap) around the Fermi surface. For comparison, the gap size around the electron-like Fermi surface at M2 point for the superconducting single-layer FeSe/SrTiO3 lm20 is also plotted (Fig. 4c). It is also nearly isotropic without gap node, although its magnitude (B15 meV) is slightly larger than that in FeSe11111. In FeSe11111, the bonding between the FeSe layer and the adjacent (Li,Fe)OH layer is rather

1.5

1

a b

1

+13 meV

16

16

5

k y(/a)

M2

High

Low

12

12

8

8

0.5

5

1.5 1 0.5 kx (/a)

EDC intensity (arb units)

c

1

M2 10 15 20 meV

5

Li0.84Fe0.16OHFe0.98Se Single-layer FeSe/SrTiO3

13 meV

0.2

0.1

0

0.1

0.2

E EF (eV)

Figure 4 | Momentum dependence of the superconducting gap of (Li0.84Fe0.16)OHFe0.98Se superconductor. (a) Fermi surface mapping near

M2 point. The corresponding Fermi crossings are marked by red empty circles with numbers from 1 to 16 (for clarity, the intermittent points are not labelled). (b) Symmetrized EDCs measured at 20 K from Fermi crossing 1 to 16 along the measured electron-like Fermi surface around M2. The red dashed lines represent the energy positions of 13 meV with respect to the Fermi level. (c) Momentum dependence of the superconducting gap(red solid circles) along the Fermi surface around M2 for (Li0.84Fe0.16)

OHFe0.98Se superconductor. For comparison, the gap along the electron-like Fermi surface around M2 of the superconducting single-layer FeSe lm is also plotted (blue empty circles)20. The error bars are dened as s.d.

NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 5

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608

weak (van der Waals bonding). The separation between the two adjacent FeSe layers is large and their mutual interaction is expected to be rather weak. These make its behaviours close to the single-layer FeSe lm that shows strong two dimensionality. It is thus reasonable to conclude that there is no nodes of the superconducting gap in the FeSe11111 superconductor.

DiscussionFrom the above results, we have found that the FeSe11111 superconductor exhibits similar behaviours to the superconducting single-layer FeSe/SrTiO3 lm, in terms of the Fermi surface topology, band structure and the superconducting gap symmetry. Among all the iron-based superconductors discovered so far, the majority of them show common electronic structure with hole-like Fermi surface sheets around the G point and electron-like Fermi surface near the M point1. The AxFe2 ySe2 superconductor3,1418

and the superconducting single-layer FeSe/SrTiO3 lms2023 have been the only two exceptions that have distinct Fermi surface topology, that is, no hole-like Fermi surface at the G point and there are only electron pockets. The present work has established the FeSe11111 superconductor as a new third exception on the list. It has been proposed that the electron scattering between the hole-like bands near G and electron-like bands near M is the cause of electron pairing in the iron-based superconductors511. The discovery of only electron-like Fermi surface in the AxFe2 ySe2

superconductor and the superconducting single-layer FeSe/SrTiO3 lms challenges such a Fermi surface nesting scenario. However, some material-specic properties prevent us from making a decisive conclusion. The AxFe2 ySe2 superconductor is well

known for its phase separation problem; the superconducting phase occupies only a small fraction of the entire sample volume and the nature of the superconducting phase remains unclear3,14,2427. The coexistence of the superconducting phase and the insulating 245 phase makes people wonder whether the interface between them is responsible for the observed superconductivity. On the other hand, the surprising discovery of high-temperature superconductivity in the single-layer FeSe/ SrTiO3 lms indicates that interface may play a signicant role in inducing or enhancing superconductivity1923,2834. In this sense, the complications of phase separation and interface effect hinder the direct comparison of the AxFe2 ySe2 superconductors and

superconducting single-layer FeSe/SrTiO3 lms with most other iron-based superconductors. The newly discovered FeSe11111 superconductor is advantageous in that it is a single-phase bulk superconductor, free from complications of phase separation and interface effect, thus making it possible to compare directly with other iron-based bulk superconductors. The observation of high-temperature superconductivity with a Tc at 41 K in bulk FeSe11111 superconductor that has electron-pocket-only Fermi surface topology makes the strongest and most decisive case that the hole-like Fermi surface around G is not necessary for the superconductivity in the iron-based superconductors. This rules out Fermi surface nesting scenario as the common pairing mechanism for the iron-based superconductors and points to the signicant role of the electron pockets near M in governing high-temperature superconductivity in the iron-based superconductors.

The present work also has important implications on the high-temperature superconductivity in the single-layer FeSe/SrTiO3 lms. First, our results indicate that the electron-pocket-near-M-only Fermi surface topology is not conned to the super-conducting single-layer FeSe/SrTiO3 lms only; instead, it can also be present in bulk superconductors. Our experimental results have shown that this form of Fermi surface topology is favourable for achieving high-temperature superconductivity in the iron-based superconductors. Second, it is remarkable that Tc as high as

41 K can be achieved in the bulk FeSe11111 superconductor where there is no strain effect, no interface effect and no strong electronphonon coupling effect29 involved as in the superconducting single-layer FeSe/SrTiO3 lms. It is known from the superconducting single-layer FeSe/SrTiO3 lms that Tc can be tuned by varying the electron doping level21. Therefore, it is possible that Tc 41 K is lower in FeSe11111 than that in the

superconducting single-layer FeSe lms (B65 K or higher), because the electron doping level in FeSe11111 is low. This raises a big possibility that Tc of the FeSe11111 superconductor may be further increased if higher electron doping is made possible and the superconductorinsulator transition40 can be avoided. The high Tc and its possible enhancement with increasing doping in the FeSe11111 superconductor provide key insight on understanding the superconductivity in the single-layer FeSe/SrTiO3 lms. Third, we note that the in-plane lattice constant a or b of the FeSe11111 superconductor (3.78 )36,39 is comparable to the primary bulk FeSe superconductor (3.76 ), but signicantly smaller than the single-layer FeSe lm epitaxially grown on the SrTiO3 substrate (3.905 ). Considering high

Tc 41 K and its possible enhancement on further elecron doping

in the FeSe11111 superconductor, this indicates that the interface strain does not play primary role in determining Tc. On the other hand, the distance between the two adjacent FeSe layers seems to have strong correlation with superconductivity in the FeSe-based superconductors. As the distance changes from 5.5 for bulk FeSe to 9.32 in the FeSe11111 superconductor, and to innity in the single-layer FeSe/SrTiO3 lms, Tc increases from 8.5 K to41 K, to 65 K or higher (Fig. 1). In the meantime, the top of the hole-like band at G changes its position from above the Fermi level for bulk FeSe (ref. 51) to 50B70 meV below the Fermi level for FeSe11111, to 80 meV below the Fermi level for the superconducting single-layer FeSe lms (Fig. 2). These results again indicate that suppression of the hole-like bands near the G point is favourable for achieving high-temperature superconductivity in the iron-based superconductors.

In summary, by performing high-resolution ARPES measurements on the FeSe-based superconductor, FeSe11111, we have discovered that it exhibits strikingly similar electronic behaviours to the superconducting single-layer FeSe/SrTiO3 lm, in terms of the Fermi surface topology, band structure and the superconducting gap symmetry. This is the rst single-phase bulk superconductor with a relatively high TcB41 K that shows electron-like Fermi-pockets-only Fermi surface topology that offers a direct comparison with other iron-based bulk superconductors.

Methods

Single crystal preparation. High-quality (Li1 xFex)OHFe1 ySe single crystals

were grown by hydrothermal approaches39. Large crystals of K0.8Fe1.6Se2 (nominal 245 phase) are specially grown and used as a kind of matrix for a hydrothermal ionic exchange reaction. The K ions in K0.8Fe1.6Se2 are completely released into solution after the hydrothermal reaction process. Single-crystal X-ray diffraction (XRD) and powder XRD measurements conrm the high quality and high purity of the FeSe11111 single crystals. In particular, no trace of K ions in the FeSe11111 crystals is detected by energy dispersive X-ray spectrometry and Inductively-coupled plasma atomic emission spectroscopy (ICP-AES) analyses, conrming a complete release of K ions after the hydrothermal ionic exchange. The sample is sensitive to air and treatment temperature due to the existence of hydroxide. All the samples for ARPES measurements were prepared in glove box and vacuum case within a short time and then transferred to ARPES measurement chamber to be kept at low temperature during the ARPES experiments.

High-resolution ARPES measurements. High-resolution ARPES measurements were carried out on our lab system equipped with a Scienta R8000 electron energy analyser52. We use helium discharge lamp as the light source, which can provide photon energies of hu 21.218 eV (helium I). The energy resolution was set at

4 meV for both the Fermi surface mapping and band structure measurements (Figs 1 and 2) and for the superconducting gap measurements (Figs 3 and 4).

6 NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications

NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608 ARTICLE

The angular resolution is B0.3. The Fermi level is referenced by measuring on a clean polycrystalline gold that is electrically connected to the sample. The sample was cleaved and measured in vacuum with a base pressure better than5 10 11 Torr.

References

1. Stewart, G. R. Superconductivity in iron compounds. Rev. Mod. Phys. 83, 15891652 (2011).

2. Wang, F. et al. The electron-pairing mechanism of iron-based superconductors. Science 332, 200204 (2011).

3. Dagotto, E. Colloquium: the unexpected properties of alkali metal iron selenide superconductors. Rev. Mod. Phys. 85, 849867 (2013).

4. Bednorz, J. G. et al. Possible high Tc superconductivity in the BaLaCuO system.Z. Phys. B 64, 189193 (1986).5. Kuroki, K. et al. Unconventional pairing originating from the disconnected Fermi surfaces of superconducting LaFeAsO1 xFx. Phys. Rev. Lett. 101, 087004 (2008).

6. Mazin, I. I. et al. Unconventional superconductivity with a sign reversal in the order parameter of LaFeAsO1 xFx. Phys. Rev. Lett. 101, 057003 (2008).

7. Wang, F. et al. Functional renormalization-group study of the pairing symmetry and pairing mechanism of the FeAs-based high-temperature superconductor. Phys. Rev. Lett. 102, 047005 (2009).

8. Chubukov, A. V. et al. Magnetism, supercondcutivity, and pairing symmetry in iron-based superconductors. Phys. Rev. B 78, 134512 (2008).

9. Stanev, V. et al. Spin uctuation dynamics and multiband superconductivity in iron pnictides. Phys. Rev. B 78, 184509 (2008).

10. Wang, F. et al. Antiferromagnetic correlation and the pairing mechanism of the cuprates and iron pnictides: a view from functional renormalization group studies. Europhys. Lett. 85, 37005 (2009).

11. Mazin, I. I. et al. A key role for unusual spin dynamics in ferropnictides. Nat. Phys. 5, 141145 (2009).

12. Guo, J. G. et al. Superconductivity in the iron selenide KxFe2Se2 (0rxr1.0). Phys. Rev. B 82, 180520(R) (2010).

13. Fang, M. H. et al. Fe-based high temperature superconductivity with Tc 31 K

bordering an insulating antiferromagnet in (Tl,K)FexSe2 crystals. Europhys. Lett. 94, 27009 (2011).14. Mou, D. X. et al. Structural, magnetic and electronic properties of theiron chalcogenide AxFe2 ySe2 (A K, Cs, Rb, and Tl, etc.) superconductors.

Front. Phys. 6, 410428 (2011).15. Qian, T. et al. Absence of a holelike Fermi surface for the iron-based K0.8Fe1.7Se2 superconductor revealed by angle-resolved photoemission spectroscopy. Phys. Rev. Lett. 106, 187001 (2011).

16. Zhang, Y. et al. Nodeless superconducting gap in AxFe2Se2 (A K,Cs) revealed

by angle-resolved photoemission spectroscopy. Nat. Mater. 10, 273277 (2011).17. Mou, D. X. et al. Distinct Fermi surface topology and nodeless superconducting gap in a (Tl0.58Rb0.42)Fe1.72Se2 superconductor. Phys. Rev. Lett. 106, 107001 (2011).

18. Zhao, L. et al. Common Fermi-surface topology and nodeless superconducting gap of K0.68Fe1.79Se2 and (Tl0.45K0.34)Fe1.84Se2 superconductors revealed via

angle-resolved photoemission. Phys. Rev. B 83, 140508(R) (2011).19. Wang, Q. Y. et al. Interface-induced high-temperature superconductivity in single unit-cell FeSe lms on SrTiO3. Chin. Phys. Lett. 29, 037402 (2012).

20. Liu, D. F. et al. Electronic origin of high-temperature superconductivity in single-layer FeSe superconductor. Nat. Commun. 3, 931 (2012).

21. He, S. L. et al. Phase diagram and electronic indication of high-temperature superconductivity at 65 K in single-layer FeSe lms. Nat. Mater. 12, 605610 (2013).

22. Tan, S. Y. et al. Interface-induced superconductivity and strain-dependent spin density waves in FeSe/SrTiO3 thin lms. Nat. Mater. 12, 634640 (2013).

23. Liu, X. et al. Electronic structure and superconductivity of FeSe-related superconductors. J. Phys. Condens. Matter 27, 183201 (2015).

24. Yan, Y. J. et al. Electronic and magnetic phase diagram in KxFe2 ySe2

superconductors. Sci. Rep. 2, 212 (2012).25. Bao, W. et al. Superconductivity tuned by the iron vacancy order in KxFe2 ySe2. Chin. Phys. Lett. 30, 027402 (2013).

26. Wang, Z. et al. Microstructure and ordering of iron vacancies in the supercondcutor system KyFexSe2 as seen via transmission electron microscopy.

Phys. Rev. B 83, 140505(R) (2011).27. Li, W. et al. Phase seperation and magnetic order in K-doped iron selenide superconductor. Nat. Phys. 8, 126130 (2012).

28. Zhang, W. H. et al. Direct observation of high-temperature superconductivity in one-unit-cell FeSe lms. Chin. Phys. Lett. 31, 017401 (2014).

29. Lee, J. J. et al. Interfacial mode coupling as the origin of the enhancement of Tc in FeSe lms on SrTiO3. Nature 515, 245248 (2014).

30. Liu, X. et al. Dichotomy of the electronic structure and superconductivity between single-layer and double-layer FeSe/SrTiO3 lm. Nat. Commun. 5, 5047 (2014).

31. He, J. F. et al. Electronic evidence of an insulatorhsuperconductor crossover in single-layer FeSe/SrTiO3 lms. Proc. Natl Acad. Sci. 111, 1850118506 (2014).

32. Peng, R. et al. Tuning the band structure and superconductivity in single-layer hoFeSe by interface engineering. Nat. Commun. 5, 5044 (2014).

33. Peng, R. et al. Measurement of an enhanced superconducting phase and a pronounced anisotropy of the energy gap of a strained FeSe single layer in FeSe/Nb:SrTiO3/KTaO3 heterostructures using photoemission spectroscopy.

Phys. Rev. Lett. 112, 107001 (2014).34. Ge, J. F. et al. Superconductivity above 100 K in single-layer FeSe lms on doped SrTiO3. Nat. Mater. 14, 285289 (2015).

35. Lu, X. F. et al. Superconductivity in LiFeO2Fe2Se2 with anti-PbO-type spacer layers. Phys. Rev. B 89, 020507 (2014).

36. Lu, X. F. et al. Coexistence of superconductivity and antiferromagnetism in (Li0.8Fe0.2)OHFeSe. Nat. Mater. 14, 325329 (2015).

37. Pachmayr, U. et al. Coexistence of 3d-ferromagnetism and superconductivity in (Li1 xFex)OH(Fe1 yLiy)Se. Angew. Chem. Int. Ed. 54, 293297 (2015).

38. Dong, X. L. et al. Phase diagram of (Li1 xFex)OHFeSe: a bridge between iron

selenide and arsenide superconductors. J. Am. Chem. Soc. 137, 6669 (2015).39. Dong, X. L. et al. (Li0.84Fe0.16)OHFe0.98Se superconductor: ion-exchange

synthesis of large single crystal and anomalous normal state properties. Phys. Rev. B 92, 064515 (2015).40. Lei, B. et al.Gate-tuned superconductor-insulator transition in (Li,Fe)OHFeSe. Preprint at http://arxiv.org/abs/1503.02457

Web End =http://arxiv.org/abs/1503.02457 (2015).

41. Hsu, F. C. et al. Superconductivity in the PbO-type sructure a-FeSe. Proc. Natl Acad. Sci. 105, 1426214264 (2008).

42. Blchl, P. E. et al. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).

43. Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).

44. Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993).

45. Kresse, G. & Furthmller, J. Efciency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mater. Sci. 6, 1550 (1996).

46. Kresse, G. & Furthmller, J. Efcient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).47. Subedi, A. et al. Density functional study of FeS, FeSe, and FeTe: electronic structure, magnetism, phonons, and superconductivity. Phys. Rev. B 78, 134514 (2008).

48. Du, Z. et al. Scrutinizing the double superconducting gaps and strong coupling pairing in (Li1 xFexOH)FeSe, Preprint at http://arxiv.org/abs/1506.04645

Web End =http://arxiv.org/abs/1506.04645

(2015).49. Yan, Y. J. et al. Surface electronic structure and plain s-wave superconductivity of (Li0.8Fe0.2)OHFeSe revealed by scanning tunneling microscopy. Preprint at http://arxiv.org/abs/1507.02577

Web End =http://arxiv.org/abs/1507.02577 (2015).

50. Norman, M. R. et al. Phenomenology of the low-energy spectral function in high-Tc superconductors. Phys. Rev. B 57, 11093(R) (1998).

51. Maletz, J. et al. Unusual band renormalization in the simplest iron-based superconductor FeSe1 x. Phys. Rev. B 89, 220506 (2014).

52. Liu, G. D. et al. Development of a vacuum ultraviolet laser-based angle-resolved photoemission system with a superhigh energy resolution better than 1 meV. Rev. Sci. Instrum. 79, 023105 (2008).

Acknowledgements

We thank Dunghai Lee, Tao Xiang and Guangming Zhang for discussions. X.J.Z. thanks nancial support from the MOST of China (973 programme numbers 2011CB921703, 2015CB921000 and 2011CBA00110), the NSFC (11190022, 11334010 and 11374335) and the Strategic Priority Research Program (B) of CAS with Grant Number XDB07020300.X.L.D., F. Z. and Z.X.Z. thank nancial support from the NSFC(11274358), the MOST of China (973 programme number 2013CB921701) and the Strategic Priority Research Program (B) of CAS with Grant Number XDB07020100. Z.Y.L. thanks nancial support from the MOST of China (973 programme number 2011CBA00112). K.L. was supported by the Fundamental Research Funds for the Central Universities and the Research Funds of Renmin University of China (14XNLQ03). Computational resources have been provided by the PLHPC at RUC.

Author contributions

X.J.Z., L.Z., X.L.D. and Z.X.Z. proposed and designed the research. D.N.Y., H.X.Z, Y.L.H.,X.L.D., F.Z. and Z.X.Z. contributed to single crystal preparation. L.Z., A.J.L., Y.H., D.F.L., J.W.H., S.L.H., B.S., Y.X., X.L., L.Y., G.D.L., X.L.D., Z.Y.X., C.T.C. and X.J.Z. contributed to the development and maintenance of Laser-ARPES system. L.Z., A.J.L. and Y.H. carried out the experiment with D.F.L., J.W.H., S.L.H., B.S., Y.X. and X.L.D. L.Z., A.J.L., Y.H. and X.J.Z. analysed the data. K.L. and Z.Y.L. did the DFT calculations. X.J.Z. and L.Z. wrote the paper. All authors discussed the results and commented on the manuscript.

Additional information

Competing nancial interests: The authors declare no competing nancial interests.

NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications

Web End =www.nature.com/naturecommunications 7

ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms10608

Reprints and permission information is available online at http://npg.nature.com/reprintsandpermissions/

Web End =http://npg.nature.com/ http://npg.nature.com/reprintsandpermissions/

Web End =reprintsandpermissions/

How to cite this article: Zhao, L. et al. Common electronic origin of superconductivity in (Li,Fe)OHFeSe bulk superconductor and single-layer FeSe/SrTiO3 lms. Nat. Commun.

7:10608 doi: 10.1038/ncomms10608 (2016).

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articles Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Web End =http://creativecommons.org/licenses/by/4.0/

8 NATURE COMMUNICATIONS | 7:10608 | DOI: 10.1038/ncomms10608 | http://www.nature.com/naturecommunications