Casein Phosphopeptide-Amorphous Calcium Phosphate Reduces Streptococcus mutans Biofilm Development on Glass Ionomer Cement and Disrupts Established Biofilms

Abstract

Glass ionomer cements (GIC) are dental restorative materials that are suitable for modification to help prevent dental plaque (biofilm) formation. The aim of this study was to determine the effects of incorporating casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) into a GIC on the colonisation and establishment of Streptococcus mutans biofilms and the effects of aqueous CPP-ACP on established S mutans biofilms. S. mutans biofilms were either established in flow cells before a single ten min exposure to 1% w/v CPP-ACP treatment or cultured in static wells or flow cells with either GIC or GIC containing 3% w/w CPP-ACP as the substratum. The biofilms were then visualised using confocal laser scanning microscopy after BacLight LIVE/DEAD staining. A significant decrease in biovolume and average thickness of S. mutans biofilms was observed in both static and flow cell assays when 3% CPP-ACP was incorporated into the GIC substratum. A single ten min treatment with aqueous 1% CPP-ACP resulted in a 58% decrease in biofilm biomass and thickness of established S. mutans biofilms grown in a flow cell. The treatment also significantly altered the structure of these biofilms compared with controls. The incorporation of 3% CPP-ACP into GIC significantly reduced S. mutans biofilm development indicating another potential anticariogenic mechanism of this material. Additionally aqueous CPP-ACP disrupted established S. mutans biofilms. The use of CPP-ACP containing GIC combined with regular CPP-ACP treatment may lower S. mutans challenge.

About the Authors:

Stuart G. Dashper

Contributed equally to this work with: Stuart G. Dashper, Deanne V. Catmull

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Deanne V. Catmull

Contributed equally to this work with: Stuart G. Dashper, Deanne V. Catmull

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Sze-Wei Liu

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Helen Myroforidis

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Ilya Zalizniak

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Joseph E. A. Palamara

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

N. Laila Huq

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Eric C. Reynolds

* E-mail: [email protected]

Affiliation: Oral Health Cooperative Research Centre, Melbourne Dental School, Bio21 Institute, The University of Melbourne, Melbourne, Australia

Introduction

Dental caries is one of the most prevalent chronic diseases of humans and affects the majority of individuals globally [1]. The disease is a dynamic process that is initiated in the bacterial biofilm (dental plaque) on the tooth surface by the production of organic acids from the fermentation of dietary sugar resulting in demineralisation of the tooth [2]. Caries is a multifactorial process that requires a shift in plaque ecology to favour acidogenic and aciduric microbial species that is usually driven by frequent consumption of simple carbohydrates and is modified by host factors such as saliva [3]. Although dental caries has a polymicrobial aetiology Streptococcus mutans is regarded as a major aetiological agent of this disease mainly due to its aciduric and highly acidogenic nature.

Casein phosphopeptide-stabilised amorphous calcium phosphate (CPP-ACP) acts as a salivary biomimetic that provides calcium and phosphate ions in a bioavailable form allowing these ions to inhibit demineralisation and promote the remineralisation of early caries lesions [4, 5]. The remineralisation of enamel subsurface lesions by CPP-ACP, mainly in the form of an applied tooth creme, has been demonstrated in numerous in vitro, in situ and in vivo studies [6–16]. In addition CPP-ACP incorporated into a sugar-free gum has been shown to slow the progression and enhance the regression of dental caries in a randomised, controlled clinical trial [17].

Studies on the mechanisms of action of CPP-ACP have focussed on its provision of bioavailable calcium and phosphate ions and its remineralisation capabilities however there have also been some reports of its ability to bind to S. mutans and inhibit adhesion to the tooth surface [18–20]. In addition two recent clinical studies demonstrated that CPP-ACP reduced S. mutans burden. Once daily treatment of children from 18 months to 24 months of age with a CPP-ACP containing tooth creme was shown to reduce recovery of S. mutans compared with the control [21]. In a clinical trial of 60 subjects, chewing CPP-ACP chewing gum three times daily resulted in a significant reduction in salivary S. mutans levels after three weeks [22]. This indicates that CPP-ACP has an inhibitory effect on S. mutans, and potentially other oral bacteria, that may contribute to its anticariogenicity in vivo.

Glass Ionomer Cements (GIC) have been used in a number of applications since their first introduction to the dental profession in 1972 [23]. GICs promote remineralisation of the tooth and inhibition of bacterial growth which has largely been attributed to the release of fluoride from the material [24, 25]. GC Fuji VII Enhanced Protection (EP) is a GIC containing 3% CPP-ACP (Recaldent^TM). It was proposed that by adding CPP-ACP to this GIC there would be a greater inhibition of bacterial binding and proliferation conferring greater protection of the tooth surface at risk of developing caries [26]. Previous studies have shown that CPP-ACP addition to a conventional GIC increased compressive and microtensile bond strength, enhanced release of calcium, phosphate and fluoride ions and enhanced protection of the adjacent dentine to acid demineralisation [27].

The aim of this study was to determine the antibiofilm effects of the incorporation of CPP-ACP into GIC to inhibit the colonisation of the surface and prevent the development of S. mutans biofilms and the effects of aqueous CPP-ACP on established S. mutans biofilms.

Materials and Methods

Growth and culture of S. mutans

S. mutans Ingbritt was propagated in Todd-Hewitt Yeast Extract medium (36.4 g/L Todd Hewitt broth, 8 g/L of yeast extract and 1 g of sucrose/L) at 37°C from freeze-dried bacterial stocks kept at the Melbourne Dental School.

All biofilm assays were performed using a 25% Artificial Saliva Medium containing (0.625 g/L type II porcine gastric mucin, 0.5 g/L bacteriological peptone, 0.5 g/L tryptone, 0.25 g/L yeast extract, 0.088 g/L NaCl, 0.05 g/L KCl, 0.05 g/L CaCl₂ and 1 mg/L haemin, pH 7.0; supplemented with 2.5 mM DTT and 0.5 g/L sucrose. The media was sterilised at 121°C for 15 min.

Preparation of Fuji VII and Fuji VII EP GIC

Fuji VII and Fuji VII EP containing 3% w/w CPP-ACP from a matching batch were provided by GC Corporation (Japan) in capsule form. Polyvinyl siloxane impression material (eliteHD+ light body, Zhermack SpA, Badia Polesine, Italy) moulds were used to create standardised GIC discs measuring 10 mm diameter x 1.5 mm thickness for flow cells and blocks of 10 mm² x 1.5 mm thickness for static biofilm assays. Each GIC disc was prepared by placing the materials in the mould with the top and bottom surfaces covered by plastic strips, held between two glass slides. The glass slides were pressed together to extrude excess material. The discs were allowed to set inside the moulds for 24 h in an incubator at 37°C with ~100% relative humidity. After cooling to room temperature the discs were removed from the moulds and lapped with 600 grit paper to mimic the finished restorative material applied in vivo. (Norton Tufbak, Saint-Gobain Abrasives Ltd., Auckland, NZ).

Static biofilm assay with Fuji VII GIC and Fuji VII EP

A 1 mL inoculum containing 1 x 10⁹ S. mutans cells were placed into each well of a 6 well Nunclon tissue culture chamber (Nunclon, NUNC) containing 1 mL of 25% ASM and one 10 mm² block of either Fuji VII or Fuji VII EP GIC (3 blocks of each type were tested per experiment). The chamber was wrapped with parafilm to prevent evaporation and incubated at 37°C for 16 h. After 16 h blocks were removed and washed in sterile distilled water to remove unbound cells and then stained with BacLight Live/Dead stain (Invitrogen) prepared as per manufacturer’s instructions for 15 min. The blocks were rinsed again to remove excess stain and placed into Coverwell imaging chambers (Invitrogen) containing custom made inserts to enable the undisturbed imaging of the biofilm. Prolong Gold anti-fade solution (Invitrogen) was then added to the block and the chamber sealed with a coverslip and clear nail varnish.

Flow cell biofilm assay with Fuji VII GIC and Fuji VII EP

Biofilm culture of S. mutans Ingbritt on Fuji VII GIC material in flow cells was carried out using custom designed flow cells made from Acetal plastic with an adjustable screw down lid, a disposable coverslip and rubber gasket to seal the system. The flow cell measured 50 mm in length x 30 mm wide with a volume of 1.5 mL and contained a single circular cut out of 10 mm diameter to secure the GIC block for imaging. Each flow cell contained three inlet ports and efflux ports to ensure laminar flow was achieved in the system. Each system contained three individual flow cells connected to an inlet and an efflux manifold using a three way adapter. The inlet ports were connected to the medium reservoir via a bubble trap and peristaltic pump. The efflux ports were connected to an effluent bottle (Fig 1).

[Figure omitted. See PDF.]

Fig 1. Three channel flow cell system for the visualisation and study of biofilm formation on GIC discs.

(A. Top view of the flow cell chamber B. Side view of the flow cell chamber). The system is made up of three custom made flow cells made from Acetal Plastic as above containing three stainless steel inlets and three outlets at each end to create laminar flow. Medium flows through a three way adapter via a three channel peristaltic pump to the bubble trap which captures small air bubbles and prevents them from passing through the system and disrupting biofilm formation. Immediately after the bubble trap there are three inoculation ports which are used to inoculate the flow cells. Each flow cell contains a 30 mm x 50 mm insert containing a 10 mm round diameter recess to fit GIC discs for testing. The volume of each flow cell was 1.5 mL.

https://doi.org/10.1371/journal.pone.0162322.g001

Flow cells and GIC discs were sterilised using gamma irradiation (4.1 kGy) and parts assembled aseptically in a Class II Biological Safety Cabinet (Contamination Control Laboratories Pty Ltd). Sterile 25% ASM was pumped through the system via a peristaltic pump for one min to coat the flow cells and remove air bubbles from the system. Each flow cell was inoculated with approximately 5 x 10⁷ S. mutans cells (1 x 10⁷ cells/mL) via a three way stop cock connected immediately preceding each flow cell. The flow cells were incubated for 1 h at 37°C prior to the commencement of a constant flow of 25% ASM through each cell at a rate of 5 mL h^-1 for 16 h. The cells were then stained with BacLight Live/Dead stain prepared as per manufacturer’s instructions for 15 min and imaged using confocal laser scanning microscopy.

Flow cell biofilm assay testing the effects of CPP-ACP challenge on established biofilms

Biofilm culture of S. mutans in flow cells was conducted similarly to Wen et al. [28] with several modifications. A 3-channel flow cell system (Stovall Life Science, Greensboro, North Carolina, USA) was modified with stopcocks for inoculation, testing and staining of the bacterial biofilms. All parts were assembled and 0.5% sodium hypochlorite was pumped in and left to stand overnight. Sterile water (200 mL) was then used to flush the system prior to the addition of 25% ASM.

Each channel of the system was inoculated with 1 mL of an exponentially growing S. mutans culture diluted to a cell density of 1×10⁷ cells/mL. The system was incubated for 1 h to allow bacterial cell attachment prior to constant flow of 12 mL h^-1 of 25% ASM. After 16 h, 1 mL of 1% w/v CPP-ACP (pH 8.0), 0.5% CPP (pH 8.0) or sterile water (pH 8.0; positive control) was slowly injected into each channel of the system and incubated for 10 min, followed by another 10 min flow of 25% ASM. BacLight LIVE/DEAD stain prepared as per manufacturer’s instructions was then used to stain the biofilm in situ for 15 min.

CPP-ACP complex was prepared as described previously [29] and the complex was desalted using reversed-phase HPLC to yield CPP free of calcium and phosphate ions. Briefly the CPP-ACP complex was dissolved in 50 mM EDTA, pH 4.5 and injected onto a C18 column equilibrated with 0.1% trifluoroacetic acid (TFA). After removal of the unbound salts with 0.1% TFA (v/v), the bound CPP were eluted with 0.1% TFA (v/v) 80% acetonitrile (v/v). The collected CPP were lyophilized. The CPP and CPP-ACP were dissolved in deionised water and the pH adjusted to 8.0 before use.

Confocal microscopy imaging

Confocal laser scanning microscopy (CLSM) was carried out on an LSM Meta 510 Confocal Microscope with an inverted stage (Carl-Zeiss, Oberkochen, Germany) essentially as described previously [30] with minor modifications. To determine reproducibility across the biofilm five images at random positions were obtained at wavelengths of 488 nm and 568 nm for each channel and three biological replicates were used. The images were 1024 x 1024 pixels (0.14 μm per pixel) with each frame at 142.72 μm (x) x 142.72 μm (y) for flow cell assays using GIC and (0.352 μm per pixel) with each frame 359.65 μm (x) x 359.65 μm (y) for the static assays using GIC. All CLSM images were analyzed using COMSTAT software [31].

Statistical analysis

The biometric data obtained from the COMSTAT program were initially examined to determine if they were normally distributed. If the data were not normally distributed, as was the case with the aqueous CPP and CPP-ACP treatments the Kruskal-Wallis test and a Mann-Whitney U Wilcoxon rank sum test with a Bonferroni correction for type 1 error were used. Paired t tests were used to compare the GIC with CPP-ACP vs GIC without the complex for the flow cell experiments.

Results

Effects of CPP-ACP incorporation into GIC on the colonisation and establishment of S. mutans biofilms in a static assay

Fuji VII and Fuji VII EP GIC blocks were placed into tissue culture wells containing 25% ASM and inoculated with S. mutans. After 16 h incubation S. mutans had formed extensive, structured biofilms on the Fuji VII material with a maximum thickness of 21.56 μm as determined by confocal microscopy image analysis (Table 1 and Fig 2). The inclusion of 3% CPP-ACP in Fuji VII EP significantly reduced the biovolume of the S. mutans biofilm by 50% relative to the Fuji VII control and average thickness of the biofilm was reduced by 66% (Table 1 and Fig 2). The structure of the biofilms formed on Fuji VII EP were significantly altered relative to Fuji VII with an increase to the surface area to volume ratio from 2.27 ± 0.45 to 3.24 ± 0.63, indicating a more open structure of the biofilms when CPP-ACP was present (Fig 2). There was no significant effect on the proportion of the substratum surface that was colonised by the bacterium.

[Figure omitted. See PDF.]

Fig 2.

Representative images of S. mutans biofilm formation on Fuji VII GIC (A) and Fuji VII EP GIC (B) after 16 h growth in a static biofilm model.

https://doi.org/10.1371/journal.pone.0162322.g002

[Figure omitted. See PDF.]

Table 1. Biometric parameters of 16 h static S. mutans biofilms cultured using Fuji VII or Fuji VII EP as the substratum.

Values are the mean and standard deviation of three biological replicates.

https://doi.org/10.1371/journal.pone.0162322.t001

Effects of Fuji VII EP on the colonisation and establishment of S. mutans biofilms in a flow cell

In order to better replicate the conditions observed in situ where exposed enamel is subjected to a constant flow of saliva containing fresh nutrients and imposing shear forces on biofilms, a custom made flow cell system was designed. This is the first time such a design, capable of imaging GIC discs undisturbed in real time has been reported in the literature. The system is similar in composition to some commercial systems with several improvements as it is composed of a re-useable flow cell with silicone rubber gasket seal and removable insert to accommodate the GIC blocks without disturbing the flow properties of the system (Fig 1).

Biofilms formed on Fuji VII GIC in the flow cell system were significantly more dense compared with biofilms formed on the same material in the static system (Figs 2 and 3). There was a nearly two-fold increase in biovolume, a four-fold increase in average thickness, yet there was a four-fold decrease in the proportion of the substratum colonised by bacteria in the flow cell relative to the static assay (Tables 1 and 2). These differences clearly show the effects of shear force and a constant flow of nutrients, resulting in denser, more tenacious biofilms in the flow cells.

[Figure omitted. See PDF.]

Fig 3.

Representative images of S. mutans biofilm formation on Fuji VII GIC (A) and Fuji VII EP GIC (B) after 16 h growth in a flow cell system.

https://doi.org/10.1371/journal.pone.0162322.g003

[Figure omitted. See PDF.]

Table 2. Biometric parameters of 16 h flow cell S. mutans biofilms cultured using Fuji VII or Fuji VII EP as the substratum.

Values are the mean and standard deviation of three biological replicates.

https://doi.org/10.1371/journal.pone.0162322.t002

After 16 h of incubation S. mutans formed highly structured biofilms on the GIC substratum with a biovolume of 2.74 μm³/μm² (Table 2 and Fig 3). The incorporation of 3% CPP-ACP into the GIC caused significant reductions in the biovolume, average thickness and maximum thickness of the S. mutans biofilms formed in the flow cells (Table 2). There was no significant effect on the proportion of the substratum that was colonised by bacteria or the surface to volume ratio of the biofilms (Table 2).

Effects of aqueous CPP-ACP treatment on established S. mutans biofilms in a flow cell

To examine the effects of CPP-ACP on established S. mutans biofilms, a flow cell system with a glass substratum was utilised. Biofilms were propagated within this system for the same time period as the previous experiment and then exposed to a single 10 min treatment of 1% CPP-ACP or 0.5% CPP. As approximately half the weight of CPP-ACP is CPP-stabilized amorphous calcium phosphate the 0.5% CPP treatment enabled the determination of the contribution of the CPP component to the effects seen with 1% CPP-ACP. S. mutans biofilms cultured in these flow cells that utilised the flow cell material as the substratum had a significantly higher biovolume than those cultured on GIC under similar conditions (Tables 2 and 3). The increase in biovolume was largely due to a significant increase in the proportion of the substratum colonised by S. mutans and the structure of the biofilm that displayed a significantly lower surface area to volume ratio of the biofilms cultured without GIC as the substratum (Tables 2 and 3). There was no significant difference in the average thickness of the biofilms. As this indicated an inhibitory effect of GIC itself on S. mutans biofilm development the effects of aqueous CPP-ACP on established S. mutans biofilms was determined without using GIC as the substratum.

[Figure omitted. See PDF.]

Table 3. Effect of a single CPP-ACP treatment on an established 16 h S. mutans biofilm cultured in a 3-channel flow cell system as determined using COMSTAT analysis of CLSM images.

Values are the mean and standard deviation of three biological replicates. The percentage change relative to the control is shown in brackets.

https://doi.org/10.1371/journal.pone.0162322.t003

A single ten min treatment with 1% CPP-ACP resulted in significant 58% decreases to both the biovolume of the biofilm and the average thickness (Table 3 and Fig 4). There was no significant change to the surface area:volume ratio of the biofilm on treatment with CPP-ACP. Treatment with 0.5% CPP had no significant effect on any of the biometric parameters of the S. mutans biofilm (Table 3 and Fig 4). A single 10 min treatment of the established 16 h S. mutans biofilms with 2% CPP-ACP resulted in such severe disruption of the biofilm that they could not be visualised and quantified by confocal imaging (data not shown).

[Figure omitted. See PDF.]

Fig 4.

Representative images of the effect of a ten minute treatment of 1.0% CPP-ACP (A) and 0.5% CPP (B) on 16 h S. mutans biofilms (C) cultured in a flow cell.

https://doi.org/10.1371/journal.pone.0162322.g004

Discussion

The use of amalgam in dental restorations has decreased over the last decade due to its potential health effects and biopersistence [32–34]. This has resulted in the increased use of alternative restorative materials including the relatively recently developed GICs. GICs have often been referred to as “smart materials” as they have a number of properties which may be altered in a controlled fashion in response to stimuli. These include ion exchange and recharge between the GIC and external environment, chemical adhesion to tooth enamel and dentin and a thermal expansion coefficient which is similar to teeth [35–37]. GICs also allow the incorporation of bioactive molecules including fluoride, strontium, calcium and phosphate that can be released to extend the influence of the material beyond its boundaries [27]. Previous studies have shown that GICs are capable of remineralising carious tissue due to their high content of apatite forming ions and can prevent secondary caries lesions through ion release and chemical bonding properties with tooth enamel [37]. Al Zraikat et al. [26] demonstrated that incorporation of 3% CPP-ACP into GIC resulted in an enhanced ability to inhibit enamel demineralization induced by exposure to lactic acid buffered at pH 4.8. This was attributed to the release of calcium, phosphate and fluoride in a bioavailable form mediated by CPP-ACP.

Bacterial biofilm formation on GICs can lead to increased roughness and surface deterioration which can further enhance microbial biofilm development [38]. This can eventually lead to the development of secondary caries around or below the GIC restoration [39, 40]. GICs have recently been used as delivery vehicles for specific antimicrobials and these materials were shown to inhibit S. mutans growth [41]. However little work has been published directly indicating antibiofilm activity of GICs containing these types of compounds.

We used two distinct biofilm assays to determine the effect of incorporation of CPP-ACP into GIC on S. mutans colonisation of the surface and biofilm development. The static biofilm assay is more reflective of protected, stagnant sites, such as interproximal areas that have limited saliva flow and low shear forces, whereas the flow cell assays are representative of more exposed enamel sites that have a higher saliva flow. Both assays used the same mucin-rich, artificial saliva growth medium. S. mutans biofilms cultured in the flow cell were significantly more dense than those cultured in the static assay for the same time period (Tables 1 and 2). This is reflective of the continuous supply of nutrients in the flow cell and may also be a response to the shear forces imposed in the flow cell model. A similar inhibition of S. mutans biofilm development by incorporation of 3% CPP-ACP was obtained with both assays showing significant reductions of over 50% in the biovolume of the 16 h S. mutans biofilms (Tables 1 and 2). This indicates that shear forces do not play a role in the mechanism of biofilm inhibition. CPP-ACP incorporation into the GIC also did not significantly reduce the proportion of the surface colonised by S. mutans indicating that the biofilm inhibitory effect is not related to attachment of the bacterial cells to the substratum.

In this study we showed that S. mutans biofilms formed on a glass substratum after 16 h had a significantly higher biovolume than those formed on GIC using the same growth medium with similar flow conditions and shear forces (Tables 2 and 3). This is consistent with recent studies that have indicated that GICs have an inherent inhibitory effect on bacterial growth, possibly due to the release of fluoride or other ions [42]. The incorporation of 3% CPP-ACP into the GIC further significantly inhibited S. mutans biofilm development by over 50% (Table 2). This is consistent with a recent in situ study that demonstrated a delay in plaque (biofilm) formation on Germanium surfaces treated with CPP-ACP in comparison to those without treatment [43]. In our study the proportion of the substratum that was colonised by S. mutans was not significantly different in the CPP-ACP containing GIC compared to the GIC alone, indicating that initial colonisation of the surface by the bacterium was not inhibited. This suggests that it was biofilm development that was inhibited by CPP-ACP that had diffused from the GIC [27]. CPP-ACP has been shown to bind to S. mutans and the intercellular plaque matrix [18, 19] and analysis of plaque samples demonstrated CPP-ACP nanocomplexes to be localized in plaque on the surfaces of bacterial cells [14]. The binding of the CPP-ACP nanocomplexes to the surface macromolecules of S. mutans is likely to be mediated by calcium cross-linking of cell surface phosphate moieties and by hydrophobic and hydrogen-bond mediated interactions [14, 44]. This binding by CPP-ACP would mask cell surface macromolecules essential for cell to cell adhesion and biofilm development.

To determine the effects of aqueous CPP-ACP treatment on established S. mutans biofilms we used the glass substratum to avoid the confounding effects of the inherent antibiofilm activity of the GIC. A single ten min treatment with 1% aqueous CPP-ACP resulted in a 58% decrease in both biovolume and average biofilm thickness (Table 3). There was no obvious increase in the number of dead cells in these analyses indicating that CPP-ACP did not have direct bactericidal activity. The disruption of these established biofilms was not due to the CPP component of the CPP-ACP as treatment with a 0.5% CPP had no significant effect on the biometric parameters of the established S. mutans biofilms (Table 3). Increasing the added CPP-ACP to 2% effectively eradicated the established S. mutans biofilm confirming that the intact nanocomplexes were essential for the dose-dependent disruptive effect on the established biofilm.

In this study we have shown that incorporation of CPP-ACP into GIC significantly reduced biofilm development and that treatment with aqueous CPP-ACP disrupted established biofilms. In the clinical setting the use of CPP-ACP containing GIC coupled with regular aqueous CPP-ACP treatment may reduce bacterial biofilm establishment and development and therefore may reduce bacteria-associated damage to the GIC surface and the development of caries.

Acknowledgments

David Stanton is thanked for technical assistance.

Author Contributions

1. Conceptualization: SGD ECR.

2. Funding acquisition: ECR.

3. Investigation: DVC SWL HM IZ NLH.

4. Methodology: SGD DVC SWL IZ JEAP ECR.

5. Project administration: SGD ECR.

6. Resources: ECR.

7. Supervision: SGD JEAP ECR.

8. Writing – original draft: DVC SWL NLH IZ.

9. Writing – review & editing: SGD DVC ECR.

Citation: Dashper SG, Catmull DV, Liu S-W, Myroforidis H, Zalizniak I, Palamara JEA, et al. (2016) Casein Phosphopeptide-Amorphous Calcium Phosphate Reduces Streptococcus mutans Biofilm Development on Glass Ionomer Cement and Disrupts Established Biofilms. PLoS ONE 11(9): e0162322. https://doi.org/10.1371/journal.pone.0162322

References

1. Selwitz RH, Ismail AI, Pitts NB. Dental caries. Lancet. 2007;369: 51–59. pmid:17208642

2. Loesche WJ. Role of Streptococcus mutans in human dental decay. Microbiological Rev. 1986;50: 353–380.

3. Marsh PD. Are dental diseases examples of ecological catastrophes? Microbiology. 2003;149: 279–294. pmid:12624191

4. Cochrane NJ, Saranathan S, Cai F, Cross KJ, Reynolds EC. Enamel subsurface lesion remineralisation with casein phosphopeptide stabilised solutions of calcium, phosphate and fluoride. Caries Res. 2008;42: 88–97. pmid:18204252

5. Reynolds EC. Anticariogenic complexes of amorphous calcium phosphate stabilized by casein phosphopeptides: a review. J Spec Care Dentist. 1998;18: 8–16.

6. Cai F, Shen P, Morgan MV, Reynolds EC. Remineralization of enamel subsurface lesions in situ by sugar-free lozenges containing casein phosphopeptideamorphous calcium phosphate. Aust Dent J. 2003;48: 240–243. pmid:14738126

7. Cochrane N, Shen P, Byrne S, Walker G, Adams G, Yuan Y, et al. Remineralisation by chewing sugar-free gums in a randomised, controlled in situ trial including dietary intake and gauze to promote plaque formation. Caries Res. 2012;46: 147–155. pmid:22488208

8. Milnar FJ. Considering biomodification and remineralization techniques as adjuncts to vital tooth-bleaching regimens. Compend Contin Educ Dent. 2007;28: 234–236, 238–240. pmid:17607888

9. Nongonierma AB, FitzGerald RJ. Biofunctional properties of caseinophosphopeptides in the oral cavity. Caries Res. 2012;46: 234–267. pmid:22572605

10. Oshiro M, Yamaguchi K, Takamizawa T, Inage H, Watanabe T, Irokawa A, et al. Effect of CPP-ACP paste on tooth mineralization: an FE-SEM study. J Oral Sci. 2007;49: 115–120. pmid:17634723

11. Peric T, Markovic D, Petrovic B, Radojevic V, Todorovic T, Radicevic BA, et al. Efficacy of pastes containing CPP-ACP and CPP-ACFP in patients with Sjögren’s syndrome. Clin Oral Investig. 2015;13: 1–13.

12. Rahiotis C, Vougiouklakis G. Effect of a CPP-ACP agent on the demineralization and remineralization of dentine in vitro. J Dent. 2007;35: 695–698. pmid:17614188

13. Reynolds EC. Remineralization of enamel subsurface lesions by casein phosphopeptide-stabilized calcium phosphate solutions. J Dent Res. 1997;76: 1587–1595. pmid:9294493

14. Reynolds E, Cai F, Shen P, Walker G. Retention in plaque and remineralization of enamel lesions by various forms of calcium in a mouthrinse or sugar-free chewing gum. J Dent Res. 2003;82: 206–211. pmid:12598550

15. Shen P, Cai F, Nowicki A, Vincent J, Reynolds EC. Remineralization of enamel subsurface lesions by sugar-free chewing gum containing casein phosphopeptide-amorphous calcium phosphate. J Dent Res. 2001;80: 2066–2070. pmid:11808763

16. Yamaguchi K, Miyazaki M, Takamizawa T, Inage H, Moore BK. Effect of CPP–ACP paste on mechanical properties of bovine enamel as determined by an ultrasonic device. J Dent. 2006;34: 230–236. pmid:16112336

17. Morgan MV, Adams GG, Bailey DL, Tsao CE, Fischman SL, Reynolds EC. The anticariogenic effect of sugar-free gum containing CPP-ACP nanocomplexes on approximal caries determined using digital bitewing radiography. Caries Res. 2008;42: 171–184. pmid:18446025

18. Rose RK. Binding characteristics of Streptococcus mutans for calcium and casein phosphopeptide. Caries Res. 2000;34: 427–431. pmid:11014910

19. Rose R. Effects of an anticariogenic casein phosphopeptide on calcium diffusion in streptococcal model dental plaques. Arch Oral Biol. 2000;45: 569–575. pmid:10785520

20. Schüpbach P, Neeser J-R, Golliard M, Rouvet M, Guggenheim B. Incorporation of caseinoglycomacropeptide and caseinophosphopeptide into the salivary pellicle inhibits adherence of mutans streptococci. J Dent Res. 1996;75: 1779–1788. pmid:8955673

21. Plonka KA, Pukallus ML, Holcombe TF, Barnett AG, Walsh LJ, Seow WK. Randomized controlled trial: a randomized controlled clinical trial comparing a remineralizing paste with an antibacterial gel to prevent early childhood caries. Pediatr Dent. 2013;35: 8E–12E.

22. Emamieh S, Khaterizadeh Y, Goudarzi H, Ghasemi A, Baghban AA, Torabzadeh H. The effect of two types chewing gum containing casein phosphopeptide-amorphous calcium phosphate and xylitol on salivary Streptococcus mutans. J Conserv Dent. 2015;18: 192–195. pmid:26069402

23. Wilson AD, Kent BE. A new translucent cement for dentistry. The glass ionomer cement. Br Dent J. 1972;132: 133–135. pmid:4501690

24. Forsten L. Fluoride release and uptake by glass-ionomers and related materials and its clinical effect. Biomaterials. 1998;19: 503–508. pmid:9645556

25. Ten Cate JM, Van Duinen RNB. Hypermineralization of dentinal lesions adjacent to glass-ionomer cement restorations. J Dent Res. 1995;74: 1266–1271. pmid:7629335

26. Al Zraikat H, Palamara JE, Messer HH, Burrow MF, Reynolds EC. The incorporation of casein phosphopeptide–amorphous calcium phosphate into a glass ionomer cement. Dent Mater. 2011;27: 235–243. pmid:21087789

27. Mazzaoui SA, Burrow MF, Tyas MJ, Dashper SG, Eakins D, Reynolds EC. Incorporation of casein phosphopeptide-amorphous calcium phosphate into a glass-ionomer cement. J Dent Res. 2003;82: 914–918. pmid:14578505

28. Wen ZT, Baker HV, Burne RA. Influence of BrpA on critical virulence attributes of Streptococcus mutans. J Bacteriol 2006;188: 2983–2992. pmid:16585759

29. Cross KJ, Huq NL, Reynolds EC. Casein Phosphopeptide-Amorphous Calcium Phosphate Nanocomplexes: A Structural Model. Biochemistry (Mosc). 2016;55: 4316–4325.

30. Dashper SG, Liu S-W, Walsh KA, Adams GG, Stanton DP, Ward BR, et al. Streptococcus mutans biofilm disruption by κ-casein glycopeptide. J Dent. 2013;41: 521–527. pmid:23583527

31. Heydorn A, Nielsen AT, Hentzer M, Sternberg C, Givskov M, Ersbøll BK, et al. Quantification of biofilm structures by the novel computer program COMSTAT. Microbiology. 2000;146: 2395–2407. pmid:11021916

32. Brownawell AM, Berent S, Brent RL, Bruckner JV, Doull J, Gershwin EM, et al. The potential adverse health effects of dental amalgam. Toxicol Rev. 2005;24: 1–10. pmid:16042501

33. Mackert JR, Berglund A. Mercury exposure from dental amalgam fillings: absorbed dose and the potential for adverse health effects. Crit Rev Oral Biol Medicine. 1997;8: 410–436.

34. Magos L, Clarkson TW. Overview of the clinical toxicity of mercury. Ann Clin Biochem. 2006;43: 257–268. pmid:16824275

35. McCabe J F., Yan Z, Al Naimi O T., Mahmoud G, Rolland S L.. Smart materials in dentistry-future prospects. Dent Mater. 2009;28: 37–43.

36. Okada K, Tosaki S, Hirota K, Hume WR. Surface hardness change of restorative filling materials stored in saliva. Dent Mater. 2001;17: 34–39. pmid:11124411

37. Paiva LFS, Fidalgo TKdS, Maia LC. Mineral content of ionomer cements and preventive effect of these cements against white spot lesions around restorations. Braz Oral Res. 2014;28: 1–9.

38. Beyth N, Bahir R, Matalon S, Domb AJ, Weiss EI. Streptococcus mutans biofilm changes surface-topography of resin composites. Dent Mater. 2008;24: 732–736. pmid:17897707

39. Busscher HJ, Rinastiti M, Siswomihardjo W, Van der Mei HC. Biofilm formation on dental restorative and implant materials. J Dent Res. 2010;89: 657–665. pmid:20448246

40. Sousa RP, Zanin ICJ, Lima JPM, Vasconcelos SMLC, Melo MAS, Beltrão HCP, et al. In situ effects of restorative materials on dental biofilm and enamel demineralisation. J Dent. 2009;37: 44–51. pmid:19026481

41. Xie D, Weng Y, Guo X, Zhao J, Gregory RL, Zheng C. Preparation and evaluation of a novel glass-ionomer cement with antibacterial functions. Dent Mater. 2011;27: 487–496. pmid:21388668

42. Łuczaj-Cepowicz E, Marczuk-Kolada G, Zalewska A, Pawińska M, Leszczyńska K. Antibacterial activity of selected glass ionomer cements. Postępy Higieny i Medycyny Doświadczalnej. 2014;68: 23–28. pmid:24491892

43. Rahiotis C, Vougiouklakis G, Eliades G. Characterization of oral films formed in the presence of a CPP–ACP agent: an in situ study. J Dent. 2008;36: 272–280. pmid:18291571

44. Allaker RP. The use of nanoparticles to control oral biofilm formation. J Dent Res. 2010;89: 1175–1186. pmid:20739694