Structural analysis of the JBW (Na-J, barrer and white) zeotype obtained from kaolinite-rich clay

Abstract

The JBW zeolite was prepared from hydrogels under hydrothermal conditions by alkaline reaction, using NaOH as activating agent. The synthetic zeotype was studied by analytical techniques such as X-ray powder diffraction, scanning electron microscopy, Fourier transformed infrared spectroscopy and solid-state 29Si and 27Al Magic angle spinning nuclear magnetic resonance. Crystallographic data revealed that the JBW structure can be described by the orthorhombic space group Pna2\, with unit cell parameters a=16.409(2) Å, ¿=14.966(2) Å and c=5.2154(5) Å.

Alternate abstract:

La zeolita JBW fue preparada a partir de hidrogeles en condiciones hidrotérmicas por reacción alcalina, usando NaOH como agente activante. El zeotipo sintético se estudió por técnicas analíticas como difracción de rayos X en polvo, microscopía electrónica de barrido, espectroscopia infrarroja por transformada de Fourier y resonancia magnética nuclear de giro con ángulo mágico en estado sólido de 29Si y 27Al. Los datos cristalográficos revelan que la estructura JBW puede ser descrita por el grupo espacial ortorrómbico Pna21, con parámetros de celda unidad a=16.409(2) Å, ¿=14.966(2) Å y c=5.2154(5) Å.

Alternate abstract:

A zeolita JBW foi preparada a partir de hidrogeles em condiçöes hidrotérmicas por reaçâo alcalina, usando NaOH como agente ativante. O zeotipo sintético estudou-se por técnicas analíticas como difraçâo de raios X em pó, microscopia eletrônica de varredura, espectroscopia infravermelha por transformada de Fourier e ressonância magnética nuclear de giro com ángulo mágico em estado sólido de 29Si e 27Al. Os dados cristalográficos revelam que a estrutura JBW pode ser descrita pelo grupo espacial ortorrômbico Pna2i, com parámetros de célula unidade a=16.409(2) Å, ¿=14.966(2) Å e c=5.2154(5) Å.