ABSTRACT
M. oleífera seed husks (H-MO) were used as adsorbent for the removal of methylene blue (MB) dye from an aqueous solution. The adsorbent was characterized by SEM, EDX, XRD, FTIR, BET, and pHpzc. To evaluate adsorption capacity, the influences of pH, kinetics, isotherms, and thermodynamic properties were analyzed. Characterization techniques indicated that H-MO has heterogeneous morphological characteristics with a specific surface area of 3.24 m2 g-1, mainly composed of cellulose distributed in an amorphous structure. MB adsorption was favorable at pH values higher than pHpzC of 6.6, using an adsorbent dosage of 1.0 g L-1. Equilibrium was achieved in the first 240 min, and the pseudo-second-order model was suitable for describing the kinetic data. Freundlich was the most adequate model for describing the isotherm curves, predicting a maximum adsorption capacity of 122.7 mg g-1 at 24°C, higher than other natural adsorbents. The adsorption process was spontaneous and exothermic, indicating that lower temperatures favor the adsorption and that it is controlled by physical forces. The data presented indicate the MB has the potential to be successfully treated by the eco-friendly and low-cost adsorbentM. oleífera seed husks.
Keywords: agricultural wastes, low-cost adsorbent, physisorption.
RESUMO
Cascas de sementes de M. oleífera (H-MO) foram usadas como adsorvente para remover o corante azul de metileno (MB) de uma soluçâo aquosa. O adsorvente foi caracterizado por MEV, EDS, DRX, FTIR, BET e pHpCz. Para avaliar a capacidade de adsorçâo, foi analisada a influencia do pH, cinética, isotermas e propriedades termodinámicas. Técnicas de caracterizaçâo indicaram que a H-MO possui características morfológicas heterogeneas com área superficial específica de 3,24 m2 g-1, composta principalmente por celulose distribuida em estrutura amorfa. A adsorçâo de MB foi favorável em valores de pH superiores a p?oz de 6,6, utilizando uma dosagem de adsorvente de 1,0 g L-1. O equilibrio foi alcançado nos primeiros 240 min, e o modelo de pseudo segunda ordem foi adequado para descrever os dados cinéticos. Freundlich foi o modelo mais adequado para descrever as curvas isotérmicas, prevendo uma capacidade máxima de adsorçâo de 122,7 mg g-1 a 24°C, superior a outros adsorventes naturais. O processo de adsorçâo foi espontáneo e exotérmico, indicando que temperaturas mais baixas favorecem a adsorçâo e que ela é controlada por forças físicas. Os dados apresentados indicam que o MB tem potencial para ser tratado com sucesso pelas cascas de sementes de M. oleífera, um adsorvente ecologicamente favorável e de baixo custo.
Palavras-chave: adsorventes de baixo custo, fisissorçâo, residuos agrícolas.
1.INTRODUCTION
In the last decades, a growing interest in the use of alternative, low-cost adsorbents (LCAs) has been observed. LCAs are classified as natural materials (e.g., wood, coal, clays), industrial wastes/by-products (e.g., fly ash, red mud), and agricultural wastes/by-products (e.g., seed, seed husk, corn cob waste) (Gupta et al., 2009). In this sense, the seed husk of Moringa oleífera is included as agricultural waste. This plant has several applications in the food, pharmaceutical, cosmetics, and food nutrition industries due to its properties (Ueda Yamaguchi et al., 2021). Also, for many years, several studies have been investigating the potential of its seeds in drinking water treatment (Ribeiro et al., 2019), and in domestic (Vega Andrade et al., 2021) and industrial wastewater treatment (Villaseñor-Basulto et al., 2018) due to its coagulant properties. In addition to its use as a coagulant, M. oleífera seed has also been investigated as an alternative in the treatment of drinking water and wastewater as an adsorbent, for example, in the removal of heavy metals (Araújo et al., 2013) and dyes (Reck et al., 2018). However, the use of theM. oleífera seed generates the seed's husk waste. The potential advancement in the use of this seed as a coagulant and adsorbent on a commercial scale requires better management of its waste (husk) through the evaluation of possible scientific and technological applications.
The use of M. oleífera seed husk has not proved to be efficient as a coagulant (Kansal and Kumari, 2014). However, recent studies have been conducted to evaluate the possibility of using the husk as an adsorbent to remove pollutants from water, such as atrazine herbicide (Cusioli et al., 2019), acetaminophen analgesic (Quesada et al., 2019), diuron pesticide (Bezerra et al., 2018), trihalomethanes (Okoya et al., 2020), and cyanobacterial hepatotoxin microcystinLR (Warhurst et al., 1997). The capacity of M. oleífera seed husk to remove those pollutants shows its potential application as a LCA in the treatment of drinking water and wastewater, and new studies for removal of different problematic pollutants are required, such as dyes from textile wastewaters.
Dye industry effluents, when not properly treated, can cause an oxygen imbalance in ecosystems by dissolved oxygen depletion, in addition to preventing sunlight penetration, thereby altering the photosynthetic activity of the environment, which results in water quality deterioration and, consequently, in adverse effects to the local fauna and flora (Yagub et al., 2014). Methylene blue (MB) dye is a synthetic and cationic dye, from the group of thiazines, soluble in water and widely used in the textile industry to color silk, cotton, wool, leather, and paper coating. This dye shows toxicity such as teratogenicity, mutagenicity, neurotoxicity, nucleic acid damage, etc. (Sabnis, 2010) An aggravating factor is that dyes are resistant to degradation, and this property becomes an obstacle to effluent treatment, since they are substances that have highly stable chemical structures, making their removal difficult whether by biological, chemical, or physical process (Yagub et al., 2014). Several methods are used for the removal of dyes from wastewater, such as adsorption, coagulation, advanced oxidation, and membrane separation (Gupta et al., 2009). Many textile industries use commercial activated carbon for the treatment of dye waste, as adsorption is one of the most effective processes of advanced wastewater treatment (Yagub et al., 2014). Several types of adsorbents have been evaluated for MB dye removal as a cost-effective alternative to commercial activated carbons, such as the agricultural wastes/by-products LCAs apple pomace (Bonetto et al., 2021), Brazilian berry seeds (E. uniflora) (Georgin et al., 2020), and sorghum husk (Adeogun et al., 2019).
In this context, considering the need for better use of M. oleífera seed husk as a low-cost adsorbent from agricultural waste and the risks associated with the discharge of MB dye from an industrial effluent, a systematic investigation, including equilibrium, thermodynamics, kinetics, and mechanism of the adsorption of MB dye by M. oleifera seed husk, is a subject of interest and is discussed in this paper.
2.MATERIAL AND METHODS
2.1. Adsorbent preparation and characterization
Moringa oleífera seeds were purchased from Arbocenter, and the seeds were harvested in the city of Araçatuba (20°56'19.72" S, 50°40'6.17" W), São Paulo - Brazil. First, the seeds were manually peeled. Seed kernels were segregated for future studies related to oil extraction and further use as a coagulant. The husks were then washed with deionized water and dried in a SolidSteel's 42L SSDc oven at 60°C for 24 h. After drying, the husks were ground using a commercial blender and sieved to be standardized on a maximum particle size of 600 pm. The powder obtained was used as adsorbent, and hereinafter will be called "H-MO".
The surface functional groups of H-MO were determined by Fourier Transform Infrared (FTIR) Spectroscopy (Shimadzu IRAffinity-1), in which the samples were scanned in the region of 4000 - 650 cm-1, in transmittance mode. The structural properties of the powder samples were determined by X-ray diffractometer (Rigaku Ultima IV), equipped with CuKa radiation (X = 0.154 nm) at 40 kV, 30 mA and 29 scan ranging from 5° to 80° with 2° min-1 step. Surface morphology was evaluated by scanning electron microscopy (SEM) (Tescan Vega 3), with 15.0 kV acceleration voltage. The energy dispersive X-ray spectroscopy (EDX) provided the elemental analysis of the H-MO through the SEM coupled with the EDX detector (Oxford X-act). For this analysis, the samples were previously covered with gold at a thickness of approximately 25 nm. The point of zero charge (pHpzc) was measured by the salt addition method with 0.1M NaNO3 (purity > 98%, Exodo), proposed by Bakatula et al. (2018). To determine the specific surface area, the BET method was used by adsorption/desorption isotherms of N2 at -196°C in a Nova 4200e (Quantachrome). Before the adsorption of N2, the samples were dried for 24 h at 60°C and subjected to degassing for 3 h at 90°C.
2.2. H-MO adsorption studies
The adsorption assays were conducted using methylene blue dye (MB) hydrate (purity > 82%, Neon) as adsorbate. From a MB stock solution (1 g L-1), dilutions with demineralized water were made for the adsorption study. The experiments were conducted in triplicate in a batch mode on a thermostatic stirring bath (Dubnoff 304-TPA) at 100 rpm. After adsorption time, the solutions were then centrifuged (Excelsa II 206-BL) at 3,000 rpm for 5 min and the MB concentration was measured by UV-Vis spectrophotometer (Shimadzu UV 1800), operating at Xmax = 664 nm wavelength. The percentage of dye removal (R, % - Equation 1), adsorption capacity at any time (qt, mg g-1 - Equation 2) and at equilibrium (qe, mg g-1 - Equation 3) were calculated as follows:
... (1)
... (2)
... (3)
Where Co is the initial concentration of MB, Ct is the concentration of MB at any time, Ce is the equilibrium concentration of MB, V is the volume of solution, and m is the mass of the adsorbent.
The H-MO dosage effect was analyzed for the values of 0.2, 0.6, 1.0, 1.6, 2.0, 2.6, 3.0, and 4.0 g L-1. For these assays, the pH was set at 7.0. The different H-MO dosages were put in contact with 50 mL of MB solution with an initial concentration of 50 mg L-1. Since the equilibrium time was not determined yet, solutions were stirred during 1,200 min at 24°C. Based on the percentage of dye removal (R), the ideal dosage of adsorbent for the next tests was determined.
The pH effect test was conducted for the pH values of 5.0, 6.0, 7.0, 8.0, and 9.0, using 1.0 g L-1 of H-MO adsorbent, previously defined by the dosage effect. The pH adjustments were made with HNO3 0.1M (purity > 66%, LS Chemicals) or NaOH 0.1M (purity 99.67%, Neon). H-MO adsorbent was added to 50 mL of MB solutions with initial concentration of 50 mg L-1, and the solutions were stirred for 1,200 min at 24°C.
The kinetic adsorption experiments were conducted using the best conditions found in the pH (9.0) and dosage (1.0 g L-1) tests. H-MO adsorbent was added to 50 mL of MB solutions with an initial concentration of 50 mg L-1, and the solutions were agitated at 24°C. Samples were collected at predefined times of 5, 20, 40, 60, 120, 240, 360, 480, 600, 720, and 1440 min. Through adsorption kinetics, the equilibrium time was determined, which was used in the adsorption isotherm test.
The adsorption isotherms were determined by varying the initial MB concentration (5, 10, 15, 20, 30, 40, 50, 60, 70, 80 and 90 mg L-1) in 50 mL of solution with dosage of adsorbent (1.0 g L-1), pH value (pH = 9), and equilibrium time (240 min) previously determined. The temperatures evaluated were 24°C, 34°C, and 44°C.
3.RESULTS AND DISCUSSION
3.1. H-MO adsorbent characterization
The morphology H-MO's SEM images are shown in Figure 1, where non-uniform complex fiber matrix with no particular shape can be observed, in agreement with other authors (Araujo et al., 2018; Quesada et al., 2019). The overall H-MO chemical composition, as a result of semi-quantitative EDX spectrometry, presented a major presence of carbon (69.4% of weight) and oxygen (30.4% of weight), which are related to the natural organic structure of the lignocellulosic structure of the material, such as cellulose, hemicellulose, and lignin (Bezerra et al., 2018; Garcia-Fayos et al., 2016).
The N2 adsorption-desorption isotherm of H-MO adsorbent is presented in Figure 2, in which one can notice a typical behavior of a Type II isotherm with Type H3 hysteresis. Type II isotherms are given by the physisorption of most gases on nonporous or microporous adsorbents. The shape is the result of unrestricted monolayer-multilayer adsorption up to high P/P0. Since the curvature in Figure 2 is more gradual, this is an indication of a great amount of overlap of monolayer coverage and the onset of multilayer adsorption. When P/P0 = 1, the thickness of the adsorbed multilayer usually appears to increase without limit (Thommes et al., 2015). The open-loop presented in the N2 adsorption-desorption isotherm (Figure 2) is probably related to the pressure-dependent elastic deformation behavior, which is in accordance with low surface area adsorbents (Tang et al., 2017).
The BET textural parameters of H-MO indicate a low specific surface area and total pore volume of 3.24 m2 g-1 and 0.010 cm3 g-1, respectively. These results are expected, as the seed husks have not been activated, and are in accordance with the literature relating to in natura M. oleífera seed husks. Cusioli et al. (2019) reported 1.52 m2 g-1 and 0.021 cm3 g-1, and Quesada et al. (2019) reported 1.2 m2 g-1 and 0.002 cm3 g-1 of specific surface area and total pore volume, respectively. The results are also in agreement with the behavior of a Type II isotherm, shown in Figure 2, of nonporous adsorbents.
The XRD pattern was conducted to determine the degree of crystalline or amorphous nature of the H-MO adsorbent and is presented in Figure 3(a). One can see, from the wide shape of the pattern, the material presents a predominance of an amorphous characteristic, suggesting a more disordered structure of the carbonaceous matrix. The main peak is detected at the 20 value of around 22°, and the small peaks at around 16° and 35°, and they are attributed to crystalline cellulose (Barnette et al., 2012). Similar peaks have been also found for modified M. oleífera seed husk (Bezerra et al., 2018) and Brazilian berry seeds (Eugenia uniflora) (Georgin et al., 2020).
The FTIR spectrum of H-MO is shown in Figure 3(b), exhibiting characteristic bands of lignocellulosic materials (Li et al., 2018). The broad peak in 3370 cm-1 indicates hydroxyl bonds O-H. Smaller peak in 2922 cm-1 could describe symmetric and asymmetric C-H stretching vibrations. The 1638 cm-1 peak can appear due to the interactions between water and C=O or N-H stretching vibrations. Finally, the strong peak at 1032 cm-1 can be originated by C-O bonds. The FTIR spectra also agrees with the literature relating to in natura M. oleifera seed husks (Tavares et al., 2017; Garcia-Fayos et al. 2016). One can thus conclude that, according to the FTIR spectra found, the surface of the adsorbent possesses a wide variety of functional groups that favor the adsorptive process.
3.2.Effect of adsorbent dosage on adsorption capacity
The effect of H-MO adsorbent dosage on the percentage removal of the adsorbate MB is shown in Figure 4. Initially, the percentage of MB removal increases sharply as the adsorbent dosage increases. Such an increase might be attributed to the higher number of available adsorbent active sites for adsorption (Shah et al., 2015). A maximum removal value of 98% is achieved at a dosage of 4 g L-1. However, considering that in the dosage of 1 g L-1 an MB removal greater than 90% was achieved, and that the increase in this dosage did not bring significant increases in removal, the dosage of 1 g L-1 of adsorbent is justified for economic purposes and was chosen for this study.
3.3.Point of zero charge (pHPZC) and effect of the solution pH on adsorption capacity
Figure 5(a) shows the influence of pH value on the adsorption of MB by H-MO. One can observe that pH values increase from 5 to 9 to enhance the adsorption capacity. This effect is a result of the MB characteristics, as well as the H-MO surface properties when submitted to solutions with different pH values. Figure 5(b) shows that the pHpzc of H-MO is 6.6. The value of pHpzc is an important property to understand the adsorption process, since when the solution is at a pH value above pHpzc, the functional groups of the adsorbent are deprotonated, resulting in a negatively charged surface, and contributing to the favorable adsorption of the cationic adsorbates. MB has a pKa value of 2.6, so MB dye is in the cationic form at pH value greater than 2.6 (Sabnis, 2010). This effect enhances the electrostatic attraction between the negatively charged surface of H-MO and positively charged MB dye. Considering the results obtained for the pH effect and pHpzc, the maximum value of adsorption capacity on this study is reached at pH 9 (qe = 52.02 mg g-1), and this pH value was set for the other tests.
3.4.Adsorption kinetics and modeling
Adsorption kinetics were determined to evaluate the effect of contact time on MB dye adsorption on H-MO adsorbent. To better understand the MB dye adsorption process, the kinetic models of pseudo-first-order (Lagergren, 1898) and pseudo-second-order (Blanchard et al., 1984) were fitted to the experimental data using nonlinear method (Equations 4 and 5, respectively) and are represented in Figure 6.
... (4)
... (5)
Where qt is the amount of adsorbate uptake per mass of adsorbent at time t, qe is the amount of adsorbate uptake per mass of adsorbent at equilibrium, k1 is the rate constant of the pseudo-first-order equation, and k2 is the rate constant of the pseudo-second-order equation.
The adsorption kinetics presented in Figure 6 shows that H-MO adsorption capacity increases sharply at the beginning of the process, and it can be associated with the large number of active sites available. But the adsorption capacity reaches stability with a contact time of 240 min (qe = 48.6 mg g-1). This stability of qe values indicates that equilibrium was achieved. This may be explained by the fact that almost all empty sites of the H-MO surface adsorbed the MB molecules available on the solution, making it difficult for new MB molecules to be adsorbed.
Correlation coefficients and parameters of the kinetic models for MB dye adsorption on H-MO are presented in Table 1. The pseudo-second-order was better fitted to the experimental data, since the coefficient of determination (R2) value was higher (0.946); the chi-square (X2) value, related to the error, was lower (0.326); and the adsorption capacity calculated (48.4 mg g-1) strongly agreed with that obtained experimentally (48.6 mg g-1). This means it is likely that both external and intraparticle diffusion steps control the total kinetics of the adsorption process (Ho and McKay, 1999). The pseudo-second-order model is a good fit to the kinetics data for most adsorption processes involving dyes (Yagub et al., 2014).
3.5.Adsorption isotherms
The adsorption isotherms were determined to better understand the interaction mechanisms between MB dye and the H-MO adsorbent. The isotherm models of Langmuir (Langmuir, 1918) and Freundlich (Freundlich, 1906) were fitted to the experimental data using nonlinear methods (Equations 6 and 7, respectively) and are represented in Figure 7.
... (6)
... (7)
Where qe is the amount of adsorbate uptake at equilibrium, Ce is the equilibrium concentration of adsorbate, qmax is the maximum adsorption capacity, Kl is adsorbent/adsorbate interaction constant, Kf is Freundlich adsorption capacity constant, and 1/n is the Freundlich intensity parameter, which indicates the magnitude of the adsorption driving force or the surface heterogeneity.
(6.25 to 13.23) when compared to Langmuir model (11.29 to 21.98) for the three temperatures studied, indicating that the Freundlich model was better fitted to the experimental data. The Freundlich model assumes the adsorbent surface energy is heterogeneous with the strongest binding sites being occupied first and the binding force decreasing with the increasing degree of site occupancy (Febrianto et al., 2009). A better suitability of the Freundlich model compared to the Langmuir model for the adsorption of MB dye was also reported by Tuli et al. (2020) using activated tea waste carbon, and by Khodaie et al. (2013) using activated corn husk carbon.
From the temperature effect on the equilibrium curves shown in Figure 7 and Table 2, one may notice the temperature increase provided a little decrease in adsorption capacity (qmax), from 122.7 (24°C) to 119.8 mg g-1 (44°C).
The adsorption capacity of various adsorbents is commonly compared by the parameter qmax. Table 3 shows the maximum adsorption capacity of different adsorbents used for MB dye removal. The value obtained for qmax in this study is higher than those of other adsorbents produced with agricultural wastes. M. oleífera seed husk is shown to be a good adsorbent for MB dye, although the result for qmax is quite lower than those obtained with activated carbon. However, the adsorbent used in this study does not require high temperatures during its processing or activation steps, meaning that this material has a lower operating cost than activated carbon.
3.6.Thermodynamic parameters
Thermodynamic adsorption plays a key role in predicting viability, spontaneity, and adsorptive mechanisms (Tran et al., 2016). The thermodynamic parameters can be computed according to the laws of thermodynamics, using the following Equation 9:
... (9)
The relationship between the three thermodynamic parameters, Gibbs energy (ДG°), enthalpy (AH°), and entropy (AS°) is described by Equation 10:
... (10)
By substituting Equation 9 in Equation 10, one can obtain Equation 11, known as van't Hoff equation.
... (11)
Where R is the universal constant (8.314 J mol-1 K"1) and T is the solution temperature (K). Enthalpy (AH°) and entropy (AS°) changes were determined from the slope and intercept, respectively, of a plot of lnKc versus 1/t (Equation 11). Gibbs energy change (AG°) was directly calculated from Equation 9.
The dimensionless thermodynamic equilibrium constant Kc in Equations 9 and 11 was calculated from the Freundlich adsorption isotherm constant Kf, since this model was better fitted to the experimental data, through Equation 12 (Tran et al., 2016; Ghosal and Gupta, 2015).
... (12)
Where p is the density of pure water (assumed as - 1 g mL"1) and 1/n is the Freundlich intensity parameter.
The MB adsorption thermodynamic parameters onto H-MO are shown in Table 4. Evidence that suggests the appropriate application of the Freundlich constant Kf in estimating the thermodynamic parameters is the high determination coefficient of the van't Hoff equation (R2 = 0.991). A critical factor for determining the degree of spontaneity of the adsorption process is the Gibbs energy variation: the negative values of Gibbs energy (AG°) shown in Table 4 denote that the adsorption is energetically favorable; in other words, the process tends to be spontaneous. In addition, the decreasing of the magnitude of AG° with temperature means the process tends to a less thermodynamically favorable process at higher temperatures, which can be confirmed by the enthalpy value. Similar results were found for the adsorption of MB by apple pomace (Bonetto et al., 2021).
The negative value of the enthalpy parameter (AH°) shown in Table 4 indicates the adsorption process is exothermic, which means the decrease in temperature results in an increase in adsorption capacity (qe) (Table 2) and in the equilibrium constant (Kc) (Table 4). Furthermore, the type of interaction can be assigned, to a certain extent, by the magnitude of enthalpy change. Physisorption, such as van der Waals interactions, is usually lower than 20 kJ mol-1. Electrostatic interaction ranges from 20-80 kJ mol-1 and they are also frequently classified as physisorption, while a value in the range of 80-450 kJ mol-1 indicates a chemisorption (Alencar et al., 2012; Ghosh et al., 2021). Therefore, the typical physisorption enthalpy value for this study (AH° = -45.8 kJ mol-1) may be related to the sum of different molecular interactions, such as hydrogen bonding and electrostatic interactions between active sites on the adsorbent and the cationic dye. An exothermic adsorption process was also reported elsewhere (Ghosh et al., 2021). Finally, the negative sign in entropy (AS°) indicates the organization of the adsorbate at the solid/solution interface during the adsorption process becomes less random, also implying the adsorption phenomenon involves an associative mechanism.
3.7.Adsorption mechanism
Figure 8 shows the proposed interaction between the MB and the H-MO. Based on the dataset discussed in this study, one could show that MB dye removal by H-MO occurs mainly due to electrostatic interactions, which is evidenced by the adsorption capacity enhancement in pH values above pHPZC. Similar conclusions were reported by other authors who investigated the adsorption of MB by agricultural wastes (Bonetto et al., 2021; Ghosh et al., 2021). Additionally, the value found for AH° (-45.8 kJ mol-1) reinforces that these interactions are in the range of electrostatic interaction, also classified as physisorption, with no sharing or exchange of electrons.
Moreover, H-MO composition presents several oxygenated functional groups, as presented by crystalline cellulose shown in XRD pattern (Figure 3(a)), and by O-H, C=O, N-H and C-O groups by FTIR spectrum (Figure 3(b)), which can also interact with MB molecules through dipole-dipole hydrogen bonds (Tran et al. 2017). The incidence of aromatic rings, both in the chemical structure of H-MO (cellulose) and in MB dye molecules, can also favor n- n interactions, contributing to the adsorption process (Cemin et al., 2021).
4.CONCLUSIONS
This study evaluated the adsorption capacity of methylene blue (MB) dye using Moringa oleífera seed husks (H-MO). The kinetic model that showed the best fit was the pseudo-second-order model, and the isotherm that presented the best fit was a Freundlich model, indicating a favorable adsorption process (1/n from 0.60 to 0.63) with a maximum adsorption capacity of MB by H-MO of 122.7 mg g-1 at 24°C, higher than some recently published studies in the literature. The thermodynamic data indicated that the adsorption process is spontaneous (AG° from -3.88 to -1.06 kJ mol-1) and exothermic (AH° of -45.80 KJ mol-1), showing that lower temperatures favor MB adsorption by H-MO and that adsorption is controlled by physical forces. The disadvantage of the adsorbent preparation method of presenting low surface area (3.24 m2 g-1) and total pore volume (0.010 cm3 g-1) were expected, as the seed husks have not been previously activated, but were compensated by the electrostatic attraction at pH values above 6.6 (pHpzC) and by dipole-dipole hydrogen bonds and n-n interactions due to its surface composition, at any pH, resulting in a favorable adsorption process. Thus, from the results obtained, one can conclude that H-MO has promise for use in the adsorption process to remove MB in aqueous solution. Considering that seed husks are an agricultural waste, their use as adsorbents of agricultural waste is a promising and low-cost option, which can also minimize the environmental impacts of their improper disposal.
5. ACKNOWLEDGEMENTS
The authors are grateful to National Council for Scientific and Technological Development (CNPq) - [grant PIBIC 123798/2020-5] for the partial financial support.
6. REFERENCES
ADEOGUN, A. I.; AKANDE, J. A.; IDOWU, M. A.; KAREEM, S. O. Magnetic tuned sorghum husk biosorbent for effective removal of cationic dyes from aqueous solution: isotherm, kinetics, thermodynamics and optimization studies. Applied Water Science, v. 9, n. 160, 2019. https://doi.org/10.1007/s13201-019-1037-2
ALENCAR, W. S.; LIMA, E. C.; ROYER, B.; DOS SANTOS, B. D.; CALVETE, T.; DA SILVA, E. A. et al. Application of aqai stalks as biosorbents for the removal of the dye procion blue MX-R from aqueous solution. Separation Science and Technology, v. 47 n. 3, p. 513-526, 2012. https://doi.org/10.1080/01496395.2011.616568
ARAÚJO, C. S. T; CARVALHO, D. C; REZENDE, H. C.; ALMEIDA, I. L. S.; COELHO, L. M.; COELHO, N. M. M. et al. Bioremediation of Waters Contaminated with Heavy Metals Using Moringa oleífera Seeds as Biosorbent. In: PATIL, Y. B.; RAO, P. (eds.). Applied Bioremediation - Active and Passive Approaches. London: IntechOpen, 2013. http://dx.doi.org/10.5772/56157
ARAUJO, L. A.; BEZERRA, C. O.; CUSIOLI, L. F.; SILVA, M. F.; NISHIB, L.; GOMES, R. G. et al. Moringa oleifera biomass residue for the removal of pharmaceuticals from water. Journal of Environmental Chemical Engineering, v. 6, n. 6, p. 7192-7199, 2018. https://doi.org/10.1016/jjece.2018.11.016
BAKATULA, E. N.; RICHARD, D.; NECULITA, C. M.; ZAGURI, G. J. Determination of point of zero charge of natural organic materials. Environmental Science and Pollution Research, v. 25, p. 7823-7833, 2018. https://doi.org/10.1007/s11356-017-1115-7
BARNETTE, A. L.; LEE, C.; BRADLEY, L. C.; SCHREINER, E. P.; PARK, Y. B.; SHIN, H. et al. Quantification of crystalline cellulose in lignocellulosic biomass using sum frequency generation (SFG) vibration spectroscopy and comparison with other analytical methods. Carbohydrate Polymers, v. 89, n. 3, p. 802-809, 2012. https://doi.org/10.1016/j.carbpol.2012.04.014
BEZERRA, C. O.; CUSIOLI, L. F.; QUESADA, H. B.; NISHI, L.; MANTOVANI, D.; VIEIRA, M. F. et al. Assessment of the use of Moringa oleifera seed husks for removal of pesticide diuron from contaminated water. Environmental Technology, v. 41, n. 2, p. 191-201, 2018. https://doi.org/10.1080/09593330.2018.1493148
BLANCHARD, G.; MAUNAYE, M.; MARTIN, G. Removal of heavy metals from waters by means of natural zeolites. Water Research, v. 18 n. 12, p. 1501-1507, 1984. https://doi.org/10.1016/0043 -1354(84)90124-6
BONETTO, L. R.; CRESPO, J. S.; GUÉGAN, R.; ESTEVES, V. I.; GIOVANELA, M. Removal of methylene blue from aqueous solutions using a solid residue of the apple juice industry: Full factorial design, equilibrium, thermodynamics and kinetics aspects. Journal of Molecular Structure, v. 1224, n. 15, p. 129296, 2021. https://doi.org/10.1016/j.molstruc.2020.129296
CEMIN, A.; FERRARINI, F.; POLETTO, M.; BONETTO, L. R.; BORTOLUZ, J.; LEMÉE, L. et al. Characterization and use of a lignin sample extracted from Eucalyptus grandis sawdust for the removal of methylene blue dye. International Journal of Biological Macromolecules, v. 170, n. 15, p. 375-389, 2021. https://doi.org/10.1016/j.ijbiomac.2020.12.155
CUSIOLI, L. F.; BEZERRA, C. O.; QUESADA, H. B.; BAPTISTA, A. T. A.; NISHI, L.; VIEIRA, M. F. et al. Modified Moringa oleífera Lam. Seed husks as low-cost biosorbent for atrazine removal. Environmental Technology, v. 42, p. 1092-1103, 2019. https://doi.org/10.1080/09593330.2019.1653381
FEBRIANTO, J.; KOSASIH, A. N.; SUNARSO, J.; JU, Y. H.; INDRASWATI, N.; ISMADJI S. Equilibrium and kinetic studies in adsorption of heavy metals using biosorbent: a summary of recent studies. Journal of Hazardous Materials, v. 162, n. 2-3, p. 616-645, 2009. https://doi.org/10.1016/j.jhazmat.2008.06.042
FREUNDLICH, H. Über die Adsorption in Lösungen. Zeitschrift für Physikalische Chemie, v. 57, p. 385-471, 1906.
GARCIA-FAYOS, B.; ARNAL, J. M.; PIRIS, J.; SANCHO, M. Valorization of Moringa oleifera seed husk as biosorbent: isotherm and kinetics studies to remove cadmium and copper from aqueous solutions. Desalination and Water Treatment, v. 57, n. 48-49, p. 23382-23396, 2016. https://doi.org/10.1080/19443994.2016.1180473
GEORGIN, J.; FRANCO, D. S. P.; NETTO, M. S.; ALLASIA, D.; OLIVEIRA, M. L. S.; DOTTO, G. L. Treatment of water containing methylene by biosorption using Brazilian berry seeds (Eugenia uniflora). Environmental Science and Pollution Research, v. 27, p. 20831-20843, 2020. https://doi.org/10.1007/s11356-020-08496-8
GHOSH, I.; KAR, S.; CHATTERJEE, T.; BAR, N.; DAS, S. K. Removal of methylene blue from aqueous solution using Lathyrus sativus husk: Adsorption study, MPR and ANN modeling. Process Safety and Environmental Protection, v. 149, n. 345-361, 2021. https://doi.org/10.1016/j.psep.2020.11.003
GHOSAL, P. S.; GUPTA, A. K. An insight into thermodynamics of adsorptive removal of fluoride by calcined Ca-Al-(NO3) layered double hydroxide. RSC Advances, v. 5, n. 128, p. 105889-105900, 2015. https://doi.org/10.1039/C5RA20538G
GUPTA, V. K.; CARROTT, P. J. M.; RIBEIRO CARROTT, M. M. L.; SUHAS. Low-cost adsorbents: growing approach to wastewater treatment - a review. Critical Reviews in Environmental Science and Technology, v. 39, n. 10, p. 783-842, 2009. https://doi.org/10.1080/10643380801977610
HALL, K. R.; EAGLETON, L. C.; ACRIVOS, A.; VERMEULEN, T. Pore- and solid-diffusion kinetics in fixed-bed adsorption under constant-pattern conditions. Industrial & Engineering Chemistry Fundamentals, v. 5, n. 2, p. 212-223, 1966. https://doi.org/10.1021/i160018a011
HO, Y. S.; MCKAY, G. Pseudo-second order model for sorption processes. Process Biochemistry, v. 34, n. 5, p. 451-465, 1999. https://doi.org/10.1016/S0032-9592(98)00112-5
KANSAL, S. K.; KUMARI, A. Potential of M. oleifera for the treatment of water and wastewater. Chemical Reviews, v. 114, n. 9, p. 4993-5010, 2014. https://doi.org/10.1021/cr400093w
KHODAIE, M.; GHASEMI, N.; MORADI, B.; RAHIMI, M. Removal of methylene blue from wastewater by adsorption onto ZnCh activated corn husk carbon equilibrium studies. Journal of Chemistry, v. 2013, p. 383985, 2013. https://doi.org/10.1155/2013/383985
LAGERGREN, S. About the theory of so-called adsorption of soluble substances. Kungl. Svenska vetenskapsakademiens handlingar, v. 24, n. 4, p. 1-39, 1898.
LANGMUIR, I. The adsorption of gasses on plane surfaces of glass, mica and platinum. Journal of the American Chemical Society, v. 40, n. 9, p. 1361-1403, 1918.
LI, X.; WEI, Y.; XU, J.; HE, Y. Quantitative visualization of lignocellulose components in transverse sections of moso bamboo based on FTIR macro- and micro-spectroscopy coupled with chemometrics. Biotechnology for Biofuels, v. 11, n. 263, 2018. https://doi.org/10.1186/s13068-018-1251-4
OKOYA, A. A.; OLAIYA, O. O.; AKINYELE, A. B.; OCHOR, N. O. Efficacy of Moringa oleífera Seed Husk as Adsorptive Agent for Trihalomethanes from a Water Treatment Plant in Southwestern, Nigeria. Journal of Chemistry, v. 2020, p. 3450954, 2020. https://doi.org/10.1155/2020/3450954
QUESADA, H. B.; CUSIOLI, L. F.; BEZERRA, C. O.; BAPTISTA, A. T. A.; NISHI, L.; GOMES, R. G. et al. Acetaminophen adsorption using a low-cost adsorbent prepared from modified residues of Moringa oleífera Lam. seed husks. Journal of Chemical Technology and Biotechnology, v. 94, p. 3147-3157, 2019. https://doi.org/10.1002/jctb.6121
RECK, I. M.; PAIXÄO, R. M.; BERGAMASCO, R.; VIEIRA, M. F.; VIEIRA, M. A. S. Removal of tartrazine from aqueous solutions using adsorbents based on activated carbon and Moringa oleífera seeds. Journal of Cleaner Production, v. 171, n. 10, p. 85-97, 2018. https://doi.org/10.1016/jjclepro.2017.09.237
RIBEIRO, J. V. M.; ANDRADE, P. V.; REIS A. G. Moringa oleífera seed as a natural coagulant to treat low-turbidity water by in-line filtration. Revista Ambiente & Água, v. 14, n. 6, p. e2442, 2019. https://doi.org/10.4136/ambi-agua.2442
SABNIS, R. W. Biological Dyes and Stains Synthesis and Industrial Applications. Hoboken : John Wiley & Sons, 2010.
SHAH, I.; ADNAN, R.; NGAH, W. S. W; MOHAMED, N. Iron impregnated activated carbon as an efficient adsorbent for the removal of methylene blue: regeneration and kinetics studies. PLoS One, v. 10, p. e0122603, 2015 https://doi.org/10.1371/journal.pone.0122603
TANG, J.; YANG, M.; YU, F.; CHEN, X.; TAN, L.; WANG, G. 1-Octadecanol@hierarchical porous polymer composite as a novel shape-stability phase change material for latent heat thermal energy storage. Applied Energy, v. 187, p. 514-522, 2017. https://doi.org/10.1016/j.apenergy.2016.11.043
TAVARES, F. O.; PINTO, L. A. M.; BASSETTI, F. J.; VIEIRA, M. F.; BERGAMASCO, R.; VIEIRA, M. A. S. Environmentally friendly biosorbents (husks, pods and seeds) from Moringa oleifera for Pb(II) removal from contaminated water. Environmental Technology, v. 38, n. 24, p. 3145-3155, 2017. https://doi.org/10.1080/09593330.2017.1290150
THOMMES, M.; KANEKO, K.; NEIMARK, A. V.; OLIVIER, J. P.; RODRIGUEZ-REINOSO, F.; ROUQUEROL, J. et al. Physisorption of gasses, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure and Applied Chemistry, v. 87, p. 1051-1069, 2015. https://doi.org/10.1515/pac-2014-1117
TRAN, H. N.; YOU, S. J.; CHAO, H. P. Thermodynamic parameters of cadmium adsorption onto orange peel calculated from various methods: A comparison study. Journal of Environmental Chemical Engineering, v. 4, n. 3, p. 2671-2682, 2016. https://doi.org/10.1016/jjece.2016.05.009
TRAN, H. N.; YOU, S. J.; NGUYEN, T. V.; CHAO, H. P. Insight into adsorption mechanism of cationic dye onto biosorbents derived from agricultural wastes. Chemical Engineering Communications, v. 204, n. 9, p. 1020-1036, 2017. https://doi.org/10.1080/00986445.2017.1336090
TULI, F. J.; HOSSAIN, A.; FAZLE KIBRIA, A. K. M.; TAREQ, A. R. M.; MAMUN, S. M. M. A.; ATIQUE ULLAH, A. K. M. Removal of methylene blue from water by low-cost activated carbon prepared from tea waste: A study of adsorption isotherm and kinetics. Environmental Nanotechnology, Monitoring & Management, v. 14, p. 100354, 2020. https://doi.org/10.1016/j.enmm.2020.100354
UEDA YAMAGUCHI, N.; CUSIOLI, L. F.; QUESADA, H. B.; CAMARGO FERREIRA, M. E.; FAGUNDES-KLEN, M. R.; SALCEDO VIEIRA, A. M. et al. A review of Moringa oleífera seeds in water treatment: Trends and future challenges. Process Safety and Environmental Protection, v. 147, p. 405-420, 2021. https://doi.org/10.1016/j.psep.2020.09.044
VEGA ANDRADE, P.; PALANCA, C. F.; OLIVEIRA, M. A. C.; ITO, C. Y. K.; REIS, A. G. Use of Moringa oleifera seed as a natural coagulant in domestic wastewater tertiary treatment: Physicochemical, cytotoxicity and bacterial load evaluation. Journal of Water Process Engineering, v. 40, p. 101859, 2021. https://doi.org/10.1016/jjwpe.2020.101859
VILLASEÑOR-BASULTO, D. L.; ASTUDILLO-SÁNCHEZ, P. D.; REAL-OLVERA, J.; BANDALA, E. R. Wastewater treatment using Moringa oleifera Lam seeds: A review. Journal of Water Process Engineering, v. 23, p. 151-164, 2018. https://doi.org/10.1016/jjwpe.2018.03.017
YAGUB, M. T.; SEN, T. K.; AFROZE, S.; ANG, H. M. Dye and its removal from aqueous solution by adsorption: a review. Advances in Colloid and Interface Science, v. 209, p. 172-184, 2014. https://doi.org/10.1016/j.cis.2014.04.002
WARHURST, A. M.; RAGGETT, S. L.; MCCONNACHIE, G. L.; POLLARD, S. J. T.; CHIPOFYA, V.; CODD, G.A. Adsorption of the cyanobacterial hepatotoxin microcystin-LR by a low-cost activated carbon from the seed husks of the pan-tropical tree, Moringa oleifera. Science of The Total Environment, v. 207, n. 2-3, p. 207-211, 1997. https://doi.org/10.1016/S0048-9697(97)00260-X.
You have requested "on-the-fly" machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Show full disclaimer
Neither ProQuest nor its licensors make any representations or warranties with respect to the translations. The translations are automatically generated "AS IS" and "AS AVAILABLE" and are not retained in our systems. PROQUEST AND ITS LICENSORS SPECIFICALLY DISCLAIM ANY AND ALL EXPRESS OR IMPLIED WARRANTIES, INCLUDING WITHOUT LIMITATION, ANY WARRANTIES FOR AVAILABILITY, ACCURACY, TIMELINESS, COMPLETENESS, NON-INFRINGMENT, MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE. Your use of the translations is subject to all use restrictions contained in your Electronic Products License Agreement and by using the translation functionality you agree to forgo any and all claims against ProQuest or its licensors for your use of the translation functionality and any output derived there from. Hide full disclaimer
© 2022. This work is published under https://creativecommons.org/licenses/by/4.0/ (the “License”). Notwithstanding the ProQuest Terms and Conditions, you may use this content in accordance with the terms of the License.
Abstract
Cascas de sementes de M. oleífera (H-MO) foram usadas como adsorvente para remover o corante azul de metileno (MB) de uma soluçâo aquosa. O adsorvente foi caracterizado por MEV, EDS, DRX, FTIR, BET e pHpCz. Para avaliar a capacidade de adsorçâo, foi analisada a influencia do pH, cinética, isotermas e propriedades termodinámicas. Técnicas de caracterizaçâo indicaram que a H-MO possui características morfológicas heterogeneas com área superficial específica de 3,24 m2 g-1, composta principalmente por celulose distribuida em estrutura amorfa. A adsorçâo de MB foi favorável em valores de pH superiores a p?oz de 6,6, utilizando uma dosagem de adsorvente de 1,0 g L-1. O equilibrio foi alcançado nos primeiros 240 min, e o modelo de pseudo segunda ordem foi adequado para descrever os dados cinéticos. Freundlich foi o modelo mais adequado para descrever as curvas isotérmicas, prevendo uma capacidade máxima de adsorçâo de 122,7 mg g-1 a 24°C, superior a outros adsorventes naturais. O processo de adsorçâo foi espontáneo e exotérmico, indicando que temperaturas mais baixas favorecem a adsorçâo e que ela é controlada por forças físicas. Os dados apresentados indicam que o MB tem potencial para ser tratado com sucesso pelas cascas de sementes de M. oleífera, um adsorvente ecologicamente favorável e de baixo custo.