Characterization of Carbon Nanofibers Treated with Thermal Nitrogen as a Catalyst Support Using Point-of-Zero Charge Analysis

Abstract

The chemical and physical purification of carbon nanofiber exposes more anchoring sites between meal precursors and carbon surface but thermal N2 gas flow maintains the crystal's structure as well as its defect and edge sites, referred to as active sites or anchoring sites. After calcination in nitrogen at 450°C, samples were characterized by Raman spectra X-ray diffraction, as well as thermogravimetric and nitrogen physisorption analyses. Results showed a relatively lower fraction of amorphous carbon to graphite, indicating a greater removal of amorphous carbon. Moreover, the disorder intensity of carbon nanofibers that were treated in N2 flow rate of 1 L/min and 3 hours, called 1Gcom-3h sample, achieved far more defect sites compared with unmodified carbon nanofiber. In addition, the surface areas of mesoporous carbon nanofibers decreased over prolonged residence time. The carbon nanofiber support-metal cation interaction therefore improved the deposition of iron when the point-of-zero charge reading was greater than four.

Thien Duc Nguyen Van 1 and Suriati Sufian 1 and Nurlidia Mansor 1 and Noorhana Yahya 2

Academic Editor:Yongchun Hong

1, Chemical Engineering Department, Universiti Teknologi Petronas, 31750 Tronoh, Perak Darul Ridzuan, Malaysia
2, Fundamental and Applied Science Department, Universiti Teknologi Petronas, 31750 Tronoh, Perak Darul Ridzuan, Malaysia

Received 5 July 2014; Accepted 27 August 2014; 14 September 2014

This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

1. Introduction

A heterogeneous catalyst should possess active sites on its solid surface as a key property. In order to maximize the number of active sites, researchers typically distribute active sites on carbon supports rather than these on oxidic supports because of carbon surface inertness property in activity and selectivity of any chemical reactions [1]. Carbon nanofiber (CNF) which is one kind of carbon support has unique advantageous properties including chemical inertia as well as electrical and thermal stability [1, 2]. Carbon's hydrogen adsorption and activation may be the reason for its catalytic activity [3].

It is different from CNF structure, morphology, and chemistry surface that impact on metallic particles deposition [4-6]. CNFs consisting of strong tangled agglomeration structures establish an open pore volume and mesopore structure which reduce diffusion limited transfers that have a key role in heterogeneous catalysis [7]. CNF aggregates also display a high surface area of 100-250 m² /g. As synthesized, CNF exists in types of impurities (amorphous carbon) and graphite (graphene and defect structure) as well as metal based catalyst (metal carbide). Most scientists have successfully explored to modify graphite structure and remove amorphous carbon and metal carbide. They used refluxing acid, peroxide, or oxygen thermal treatment to attach more functional groups which become active sites or anchoring centers for the metal precursors [8-17], at preferred defect sites. Also, Mawhinney et al., 2000, suggested O₃ method for titrating surface defect site density on carbon nanofilaments [18]. Barranco et al., 2010, and Sadezky et al., 2005, suggested that Raman analysis can determine the degree of graphitization or defect (_IG /_ID +_IG or _ID /_ID +_IG , resp.) from CNF surface [19, 20].

Furthermore, there are many types of morphology as fishbone (f-), platelet (p-), ribbon (r-), and irregular CNF but fishbone and platelet CNF have high edge sites that are good position for adsorption or modification CNF structure surface [21]. Ochoa-Fernández et al. in 2005 said that f-CNF strongly influences metallic catalyst deposition more than other morphologies because of more curvature [22]. Based on treatments above, CNF structures of different morphology types such as f-CNFs, p-CNFs, r-CNFs, and irregular CNFs [23-26] may become damaged and pose difficulty when attempting to control the number of active sites. This, in turn, limits electron transfer between active sites of metal catalyst. Also, point-of-zero charge (PZC) analysis plays an important role in the evaluation of surface chemistry support as it influences the predictability of interactions between metal ions and the carbon support structure in suspended solutions of varied pH. Therefore, the interaction of CNF and deposited metal ion depends on the anion and cation balance [27] whilst carbon surface modification techniques have become essential for efficient deposition of metal precursors. However, using nitrogen treatment is different from common approaches using chemical reacting such as KMnO₄ , H₂ O₂ , and HNO₃ oxidation. It has been limited in modifying CNF surface structure.

This research utilized calcination in nitrogen gas flow to detach acidic and basic groups from the surface of as-synthesized CNF and remove the amorphous carbon phase because functional oxygen groups and the amorphous carbon phase inhibit the supported catalyst during nitrogen hydrogenation [28, 29]. As negative charges on the support surface affect interactions between iron colloids and the CNF support, the aim of this research was to explore CNF purification with thermal N₂ gas flow and CNF surface properties for purposes of supported catalyst preparation.

2. Materials and Methods

CNFs were purchased from Carbon Nanomaterial Co., LTD., and modified in a fixed-bed alumina reactor. Treatments were carried out under different conditions of residence time (1, 3, and 6 h) and nitrogen flow rate (0.5 and 1 L/min) at 450°C because CNF decomposes above 500°C (Figure 1). Degradation temperatures were determined by Pyris 1 thermogravimetric analysis (TGA) using the same gas at a heating rate of 20°C/min. Also, for instance, name code of sample is 1Gcom-1h. It means that 1 is symbol of 1 L/min; Gcom is name of CNF; and 1 h is calcination time.

Figure 1: Degradation behavior of CNF from TGA spectra.

[figure omitted; refer to PDF]

Samples were prepared in isopropanol under sonication and resultant structures were observed under field emission transmission electron microscopy (FETEM; Zeiss Libra @200) for all CNF samples. Surface area and pore size ranges were analyzed by nitrogen ASAP 2020 physisorption where samples were degassed at 250°C over four hours prior to analysis. The degree of graphitization of samples and their relative amorphous values were assessed by (i) obtaining the Raman spectra with a Horiba HR 800 spectrometer operating at 514.53 nm at room temperature and (ii) Bruker AXS D8-advance X-ray diffraction (XRD) using copper Kα radiation (wavelength, λ=0.154 nm) and 2 theta from 2-80°. The zeta potential for CNFs as a function of pH 2-10 was also tested with a Malvern Nano-ZS Zetasizer (DKSH Technology Sdn. Bhd.) in solutions of 0.01 M NaCl mixed with carbon nanofiber powder with either 0.5 M NaOH or 0.5 M HCl to alter pH [30].

3. Results and Discussion

Commercial carbon nanofiber (G-com) and as-synthesized carbon nanofiber (G-syn) [23] weight losses are shown in Figure 1. Changes were rapid at the beginning (500°C). G-com had one inclination at 550°C but G-syn had two inclination change stages (600 and 800°C). Overall, the degradation level of G-com was higher than that of G-syn because of G-syn's greater structural stability. The TGA curve shows three regions with the first between 50 and 200°C due to the loss of water. The second (200-500°C) shows a decomposition of light amorphous polycarbons from carbon dioxide that are easily vaporized [31]. The final region indicates the gradual destruction of the CNF's structure above 500°C for both G-com and G-syn. All observed changes were due to amorphous carbon layers and differences in morphological structure [32, 33]. Thus, the purpose of thermal treatment in an inert environment is to eliminate amorphous carbon layers and increase defective sites on the carbon surface (as shown in Table 1). This may enhance the ability of metal adsorption on CNF surfaces. As discussed, G-com and G-syn samples were calcinated at 450°C to avoid CNF structural breakdown; however, CNF surface defects remained.

Table 1: X-Ray diffraction intensity of carbon nanofiber.

Sample name	Calcinated conditions at 450°C	Intensity (counts)	d002 (nm)
G-com	--	21.0	0.344
1Gcom-1h	1 L/min, 1 h	21.0	0.343
1Gcom-3h	1 L/min, 3 h	25.0	0.343
1Gcom-6h	1 L/min, 6 h	23.7	0.343
0.5Gcom-3h	0.5 L/min, 3 h	25.4	0.343

Table 1 illustrates how the X-ray diffraction intensity was amplified over one to three hours (1Gcom-1h; 1Gcom-3h). However, intensity changed slightly as residence time increased to six hours (1Gcom-6h) and also when a reduction in flow rate to 500 mL/min (0.5Gcom-3h) occurred. These findings were similar to Raman's results for degrees of graphitization (see Table 2) as discussed below.

Table 2: Graphite nanofiber peak positions and the intensity ratio of Raman spectroscopy bands.

Sample name	I D (%) 1300-1400 cm-1	I G (%) 1580-1600 cm-1	Degree of graphitization	I A (%)	The relative value ratio of amorphous carbon to graphite intensity
G-com	180	150	0.454	65	0.433
1Gcom-1h	135	95	0.413	45	0.473
1Gcom-3h	110	85	0.435	35	0.411
1Gcom-6h	95	67	0.413	30	0.448
0.5Gcom-3h	115	85	0.425	40	0.471

_{I D} , _IG , _IA : disorder, graphite, and amorphous intensities, respectively.

D -band and G -band: disorder (^{_Csp 3} ) and graphite (^{_Csp 2} ) frequency.

The CNF XRD pattern in Figure 2 shows more information of d-spacing interlayer of graphite and existence elements in samples. The data of iron, iron carbide, and carbon nanofiber were matched with reference data of 13-0534, 35-0772, and 75-2078 based on JCPDS, respectively. Figure 2 displays that no change occurred in the d-spacing interlayer of crystalline graphite in 2θ = 20-30°. The iron carbide changes did occur in 2θ = 40-48° [23]. The modified samples (1Gcom-1h, 1Gcom-3h, 1Gcom-6h, and 0.5Gcom-3h) each displayed iron peaks between 30 and 40° that were not present in the G-com sample [34]. This indicated that treatment abolished amorphous carbon layers and revealed encapsulated iron.

Figure 2: X-ray diffraction results for CNFs and modified CNFs.

[figure omitted; refer to PDF]

We used Raman spectra analysis to explore intrinsic defects in the graphite lattice that were responsible for the symmetrical breakdown of the entire crystalline network [35]. Raman spectra of microcrystalline graphite showed a disordered band (D peak) between 1300 and 1400 cm^-1 due to lattice defects and a loss of long-range in-plane symmetry. However, a G-band peak (1580-1600 cm^-1 ) appeared due to in-plane bond stretching of carbon atom sp² hybridization. Also, the intensity of the D peak (Table 2) was higher than that of the G peak, implying high disordered graphitic structures [20] and corrugation of the CNF [36]. The degree of graphitization was estimated by the intensity ratio: _IG /(_ID +_IG ) [37] or else 1-_IG /(_ID +_IG ) is for defect degree. In addition, increased CNF graphitization results agreed with the sample (1Gcom-3h) because unstable carbon structures were removed via calcination. These findings also endorsed our XRD results as shown in Table 1, which, taken together, indicated that the majority of amorphous carbon was gradually eliminated. In Table 2 the graphitization degree value of modified samples decreases. It means that using N2 thermal treatment can improve the defect surface structure of CNF because of the defect or disordered degree value of modified samples increases.

We determined that the CNF's amorphous phase occurred at Raman shift 1550 cm^-1 [35]. Table 2 describes results indicating that thermal treatment enhanced the CNF by the incineration of amorphous carbon. The relative value of the amorphous carbon filament was estimated by the integrated intensity ratio of _IA /_IG [9], which decreased as residence time increased to 3 h with a nitrogen flow rate of 1 L per min (1Gcom-3h). However, the amorphous phase increased with diminishing nitrogen flow (500 mL per min) (0.5Gcom-3h). The relative value of amorphous carbon was lowest for sample 1Gcom-3h as shown in Figure 1. Amorphous carbon reflected a weight loss of approximately 15% (G-com) below 500°C. By reducing amorphous carbon, CNF pore size increased and could then be characterized as mesopores (Table 3) that allowed an easier internal diffusion of metal ions. Nevertheless, the defective surface of the CNF remained constant which also improved the adsorption of carbon filaments.

Table 3: Surface area and pore size of CNF.

Sample name	Pore size (nm) by BJH	Surface area (m2 /g) by BET	Pore width range (nm)
G-com	17.627	114.485	2.-267.3
1Gcom-1h	16.175	110.119	2.7-1226.5
1Gcom-3h	15.829	90.238	1.9-382.7
1Gcom-6h	15.627	97.731	1.9-1415.4
0.5Gcom-3h	17.757	95.011	1.8-211.9

Hence, it appeared that nitrogen physisorption (Table 3) established mesopores with diameters >2 nm [38]. With thermal N₂ flow rates of 500 mL/min and 1000 mL/min and over residence intervals of 1, 3, and 6 hours, both surface area and pore size decreased compared to nonmodified samples (G-com) due to amorphous phase removal of CNF and increased rearrangement of the graphite structure. In addition, there was a wide distribution of pore width ranging from 1.8 to 1415.4 nm. The range of pore size for modified samples was larger than that of G-com, indicating that the majority of pores allowed for more efficient metal ion adsorption on deposition.

Typical CNF TEM images of two types are shown in Figure 3 based on angles between graphene layers and the growth axis. CNF graphene layers called platelet CNFs (p-CNF) are arranged perpendicular to the axis (see Figure 3(a)). The G-com structure showed angles of approximately 30° between graphene layers and the CNF axis, also known as fishbone CNF (f-CNF), seen in Figure 3(b). This phenomenon indicated the existence of more edge sites on p-CNF and f-CNF structures, in addition to defect sites as active sites, all of which aid metal ion adsorption on the CNF surface [39, 40].

CNF TEM images: p-CNF, 3(a); f-CNF, 3(b).

(a) [figure omitted; refer to PDF]

(b) [figure omitted; refer to PDF]

CNF zeta potential characterization is shown in Figure 4. Varied relative point-of-zero charges (PZC) for p-CNF and f-CNF ranged between pH 3 and 4 and were lower than those for argon gas modified CNFs as reported by Zhu et al. [30], most likely due to extant iron within the CNF. Except for the 1Gcom-1h sample, PZC for all other CNF samples varied between pH 3.5 and 4. Vinke et al. [41] and Solar et al. [42] suggested that the PZC of carbon was subject to total surface oxygen and the nature and distribution of surface oxygen sites. These results therefore implied that oxygen was removed by heat treatment.

Figure 4: CNF zeta potential (PZC) under different treatment conditions.

[figure omitted; refer to PDF]

Furthermore, the PZC value aids our understanding of changes that occur in surface charges of the CNF support using impregnation of the supported catalyst preparation and consequently also for the dispersion of the metallic active phase as discussed by Regalbuto [43]. An electrostatic attraction between the CNF support and cation salt depends on the pH medium as formulated over or under PZC value. Figure 4 shows PZC values for a basic suspension (pH > 4) and for an acid medium (pH < 3). Rodríguez-Reinoso 1998 similarly reviewed that Pt complex salt can adsorb on surface of oxygen-free carbon by electrostatic force [1] and it belonged to precursor salt ion in acid or basic solution. Therefore, a deposition method can be developed for pH values greater than the CNF support's PZC since cation salts can interact with negative charges of surface carbons. Also, the larger the interaction, the higher the potential difference between the CNF support and metal ion [4, 30, 44]. This approach controls both metal loading and particle size for interaction and adsorption characteristics during the process of deposition.

4. Conclusion

Using thermal purification in nitrogen gas, p-CNF and f-CNF structures were broken down to release impurities during the amorphous phase and still retain iron metal and defect sites. Amorphous carbon layers were efficiently eliminated to minimize the ratio of amorphous carbon to graphite. Furthermore, CNF defect structures increase after modification and get minimum amorphous carbon with sample of 1Gcom-3h. The surface area of the sample was 90.238 m² /g, and pore width ranged from micro- to macropore. These results clearly indicated easier metal ion diffusion. Finally, electrostatic attraction between negative CNF support and cation salt improves when the pH medium is greater than a PZC value of four.

Acknowledgments

The authors gratefully acknowledge MOE for its financial support (LRGS-One Baja Funder and FRGS), Universiti Teknologi PETRONAS for its generous Graduate Assistantship scheme and lab facilities, and also Mr. Albert Lim and Mr. Simon Choo from DKSH Technology Sdn. Bhd. for supporting this research with the Malvern Nano-ZS Zetasizer equipment.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

[1] F. Rodríguez-Reinoso, "The role of carbon materials in heterogeneous catalysis," Carbon , vol. 36, no. 3, pp. 159-175, 1998.

[2] P. Sep, J. L. Figueiredo Carbon Nanomaterials for Catalysis , John Wiley & Sons, New York, NY, USA, 2009.

[3] E. Furimsky Carbons and Carbon Supported Catalysts in Hydroprocessing , The Royal Society of Chemistry, Cambridge, UK, 2008.

[4] I. Kvande, S. T. Briskeby, M. Tsypkin, M. Rønning, S. Sunde, R. Tunold, D. Chen, "On the preparation methods for carbon nanofiber-supported Pt catalysts," Topics in Catalysis , vol. 45, no. 1-4, pp. 81-85, 2007.

[5] M. A. Fraga, E. Jordão, M. J. Mendes, M. M. A. Freitas, J. L. Faria, J. L. Figueiredo, "Properties of carbon-supported platinum catalysts: role of carbon surface sites," Journal of Catalysis , vol. 209, no. 2, pp. 355-364, 2002.

[6] W. Raróg-Pilecka, E. Miskiewicz, M. Matyszek, Z. Kaszkur, L. K[ecedil];pinski, Z. Kowalczyk, "Carbon-supported cobalt catalyst for ammonia synthesis: effect of preparation procedure," Journal of Catalysis , vol. 237, no. 1, pp. 207-210, 2006.

[7] K. P. de Jong, "Synthesis of supported catalysts," Current Opinion in Solid State and Materials Science , vol. 4, no. 1, pp. 55-62, 1999.

[8] J. L. Figueiredo, M. F. R. Pereira, M. M. A. Freitas, J. J. M. Órfão, "Modification of the surface chemistry of activated carbons," Carbon , vol. 37, no. 9, pp. 1379-1389, 1999.

[9] J. Li, M. J. Vergne, E. D. Mowles, W.-H. Zhong, D. M. Hercules, C. M. Lukehart, "Surface functionalization and characterization of graphitic carbon nanofibers (GCNFs)," Carbon , vol. 43, no. 14, pp. 2883-2893, 2005.

[10] S. Lim, A. Shimizu, S.-H. Yoon, Y. Korai, I. Mochida, "High yield preparation of tubular carbon nanofibers over supported Co-Mo catalysts," Carbon , vol. 42, no. 7, pp. 1279-1283, 2004.

[11] J. S. Noh, J. A. Schwarz, "Effect of HNO₃ treatment on the surface acidity of activated carbons," Carbon , vol. 28, no. 5, pp. 675-682, 1990.

[12] R. A. Ross, C. Fairbridge, J. R. MacCallum, "Carbon fibres as supports for transition metal catalysts in hydrocarbon oxidation reactions," Carbon , vol. 23, no. 2, pp. 209-213, 1985.

[13] J.-F. Colomer, P. Piedigrosso, A. Fonseca, J. B. Nagy, "Different purification methods of carbon nanotubes produced by catalytic synthesis," Synthetic Metals , vol. 103, no. 1-3, pp. 2482-2483, 1999.

[14] W.-K. Choi, S.-G. Park, H. Takahashi, T.-H. Cho, "Purification of carbon nanofibers with hydrogen peroxide," Synthetic Metals , vol. 139, no. 1, pp. 39-42, 2003.

[15] T. Jeong, W.-Y. Kim, Y.-B. Hahn, "A new purification method of single-wall carbon nanotubes using H₂ S and O₂ mixture gas," Chemical Physics Letters , vol. 344, no. 1-2, pp. 18-22, 2001.

[16] K. B. Shelimov, R. O. Esenaliev, A. G. Rinzler, C. B. Huffman, R. E. Smalley, "Purification of single-wall carbon nanotubes by ultrasonically assisted filtration," Chemical Physics Letters , vol. 282, no. 5-6, pp. 429-434, 1998.

[17] M. L. Toebes, F. F. Prinsloo, J. H. Bitter, A. J. van Dillen, K. P. de Jong, "Influence of oxygen-containing surface groups on the activity and selectivity of carbon nanofiber-supported ruthenium catalysts in the hydrogenation of cinnamaldehyde," Journal of Catalysis , vol. 214, no. 1, pp. 78-87, 2003.

[18] D. B. Mawhinney, V. Naumenko, A. Kuznetsova, J. T. Yates Jr., J. Liu, R. E. Smalley, "Surface defect site density on single walled carbon nanotubes by titration," Chemical Physics Letters , vol. 324, no. 1-3, pp. 213-216, 2000.

[19] V. Barranco, M. A. Lillo-Rodenas, A. Linares-Solano, A. Oya, F. Pico, J. Ibañfez, F. Agullo-Rueda, J. M. Amarilla, J. M. Rojo, "Amorphous carbon nanofibers and their activated carbon nanofibers as supercapacitor electrodes," Journal of Physical Chemistry C , vol. 114, no. 22, pp. 10302-10307, 2010.

[20] A. Sadezky, H. Muckenhuber, H. Grothe, R. Niessner, U. Pöschl, "Raman microspectroscopy of soot and related carbonaceous materials: spectral analysis and structural information," Carbon , vol. 43, no. 8, pp. 1731-1742, 2005.

[21] P. Serp, J. L. Figueiredo Carbon Materials for Catalysis , John Wiley & Sons, 2009.

[22] E. Ochoa-Fernández, D. Chen, Z. Yu, B. Tøtdal, M. Rønning, A. Holmen, "Carbon nanofiber supported Ni catalyst: effects of nanostructure of supports and catalyst preparation," Catalysis Today , vol. 102-103, pp. 45-49, 2005.

[23] S. Sufian, "Irregular configurations of carbon nanofibers," Carbon and Oxide Nanostructures , vol. 5, pp. 125-141, Springer, Berlin, Germany, 2011.

[24] W. B. Downs, R. T. K. Baker, "Novel carbon fiber-carbon filament structures," Carbon , vol. 29, no. 8, pp. 1173-1179, 1991.

[25] X. Jian, M. Jiang, Z. Zhou, M. Yang, J. Lu, S. Hu, Y. Wang, D. Hui, "Preparation of high purity helical carbon nanofibers by the catalytic decomposition of acetylene and their growth mechanism," Carbon , vol. 48, no. 15, pp. 4535-4541, 2010.

[26] R. T. Yang, J. P. Chen, "Mechanism of carbon filament growth on metal catalysts," Journal of Catalysis , vol. 115, no. 1, pp. 52-64, 1989.

[27] E. Cristiano, Y.-J. Hu, M. Siegfried, D. Kaplan, H. Nitsche, "A comparison of point of zero charge measurement methodology," Clays and Clay Minerals , vol. 59, no. 2, pp. 107-115, 2011.

[28] Z. Li, C. Liang, Z. Feng, P. Ying, D. Wang, C. Li, "Ammonia synthesis on graphitic-nanofilament supported Ru catalysts," Journal of Molecular Catalysis A: Chemical , vol. 211, no. 1-2, pp. 103-109, 2004.

[29] C. H. Bartholomew, "Mechanisms of catalyst deactivation," Applied Catalysis A: General , vol. 212, no. 1-2, pp. 17-60, 2001.

[30] J. Zhu, T. Zhao, I. Kvande, D. Chen, X. Zhou, W. Yuan, "Carbon nanofiber-supported Pd catalysts for heck reaction: effects of support interaction," Chinese Journal of Catalysis , vol. 29, no. 11, pp. 1145-1151, 2008.

[31] T. G. Ros, A. J. van Dillen, J. W. Geus, D. C. Koningsberger, "Surface structure of untreated parallel and fishbone carbon nanofibres: an infrared study," ChemPhysChem , vol. 3, no. 2, pp. 209-214, 2002.

[32] A. B. Dongil, B. Bachiller-Baeza, A. Guerrero-Ruiz, I. Rodríguez-Ramos, A. Martínez-Alonso, J. M. D. Tascón, "Surface chemical modifications induced on high surface area graphite and carbon nanofibers using different oxidation and functionalization treatments," Journal of Colloid and Interface Science , vol. 355, no. 1, pp. 179-189, 2011.

[33] N. J. Welham, J. S. Williams, "Extended milling of graphite and activated carbon," Carbon , vol. 36, no. 9, pp. 1309-1315, 1998.

[34] M.-S. Wu, Y.-H. Ou, Y.-P. Lin, "Electrodeposition of iron oxide nanorods on carbon nanofiber scaffolds as an anode material for lithium-ion batteries," Electrochimica Acta , vol. 55, no. 9, pp. 3240-3244, 2010.

[35] T. V. Reshetenko, L. B. Avdeeva, Z. R. Ismagilov, V. V. Pushkarev, S. V. Cherepanova, A. L. Chuvilin, V. A. Likholobov, "Catalytic filamentous carbon: structural and textural properties," Carbon , vol. 41, no. 8, pp. 1605-1615, 2003.

[36] T. W. Ebbesen Carbon Nanotubes: Preparation and Properties , CRC, 1996.

[37] J.-H. Ting, C.-C. Chang, S.-L. Chen, D.-S. Lu, C.-Y. Kung, F.-Y. Huang, "Optimization of field emission properties of carbon nanotubes by Taguchi method," Thin Solid Films , vol. 496, no. 2, pp. 299-305, 2006.

[38] J. B. Condon Surface Area and Porosity Determinations by Physisorption: Measurements and Theory , Elsevier, New York, NY, USA, 2006.

[39] C. Park, R. T. K. Baker, "Catalytic behavior of graphite nanofiber supported nickel particles. 3. The effect of chemical blocking on the performance of the system," The Journal of Physical Chemistry B , vol. 103, no. 13, pp. 2453-2459, 1999.

[40] F. Rodríguez-Reinoso, M. Molina-Sabio, "Textural and chemical characterization of microporous carbons," Advances in Colloid and Interface Science , vol. 76-77, pp. 271-294, 1998.

[41] P. Vinke, M. van der Eijk, M. Verbree, A. F. Voskamp, H. van Bekkum, "Modification of the surfaces of a gasactivated carbon and a chemically activated carbon with nitric acid, hypochlorite, and ammonia," Carbon , vol. 32, no. 4, pp. 675-686, 1994.

[42] J. M. Solar, C. A. L. y Leon, K. Osseo-Asare, L. R. Radovic, "On the importance of the electrokinetic properties of carbons for their use as catalyst supports," Carbon , vol. 28, no. 2-3, pp. 369-375, 1990.

[43] J. Regalbuto Catalyst Preparation: Science and Engineering , Taylor & Francis, 2006.

[44] J. P. Tessonnier, D. Rosenthal, T. W. Hansen, C. Hess, M. E. Schuster, R. Blume, F. Girgsdies, N. Pfänder, O. Timpe, D. S. Su, R. Schlögl, "Analysis of the structure and chemical properties of some commercial carbon nanostructures," Carbon , vol. 47, no. 7, pp. 1779-1798, 2009.